CN104119777B - 一种用于包装机的水性金属防腐漆及其制备方法 - Google Patents

一种用于包装机的水性金属防腐漆及其制备方法 Download PDF

Info

Publication number
CN104119777B
CN104119777B CN201410295308.3A CN201410295308A CN104119777B CN 104119777 B CN104119777 B CN 104119777B CN 201410295308 A CN201410295308 A CN 201410295308A CN 104119777 B CN104119777 B CN 104119777B
Authority
CN
China
Prior art keywords
packing machine
anticorrosion paint
preparation
paint
waterborne metallic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410295308.3A
Other languages
English (en)
Other versions
CN104119777A (zh
Inventor
李峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Saiya Aerosol Co ltd
Original Assignee
SHENZHEN SEA AEROSOL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHENZHEN SEA AEROSOL Co Ltd filed Critical SHENZHEN SEA AEROSOL Co Ltd
Priority to CN201410295308.3A priority Critical patent/CN104119777B/zh
Publication of CN104119777A publication Critical patent/CN104119777A/zh
Application granted granted Critical
Publication of CN104119777B publication Critical patent/CN104119777B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种用于包装机的水性金属防腐漆及其制备方法。该水性金属防腐漆由包含以下重量份的组分制成：双酚A型环氧树脂75-90份、环氧丙烷丁基醚15-20份、聚环氧琥珀酸10-20份、三羟甲基丙烷8-18份、聚环氧乙烷10-15份、聚二甲基硅氧烷5-12份、十二烷基磺酸钠1-3份和炭黑0.05-0.5份。通过本发明的方法制得的水性金属漆使用方便，可用于包装机的表面涂层，能够起到保护金属部件的作用，提高了机器的使用寿命，同时本发明的水性金属漆环保无污染，且制备方法简单，适合于工业生产。

Description

一种用于包装机的水性金属防腐漆及其制备方法
技术领域
本发明属于金属漆领域，特别涉及一种用于包装机的水性金属防腐漆及其制备方法。
背景技术
防腐漆是用于物体表面可以用来保护物体内部不受到腐蚀的一类油漆。近些年，大都采用工业防腐漆来保护金属的表面，使其免受腐蚀，使用寿命更加长，但是这些溶剂型油漆中溶剂含量一般高达50%以上，施工后，溶剂全部挥发到空气中，不仅浪费资源而且污染环境。为了找到替代有机溶剂的金属漆材料，研究者们做了大量研究，国内现有的水性金属漆，主要通过水性乳液来制备，这些水性漆虽然为环境友好型，但却各方面的性能不如含有机溶剂的金属漆。由于包装机在通常需要在各类条件下使用，使用环境通常较为复杂，存在着湿度大易腐蚀的问题。因而少有水性金属漆能够满足包装机表面涂层的性能要求。
发明内容
本发明提供了一种用于包装机的水性金属防腐漆及其制备方法。本发明的水性金属漆使用方便，可用于包装机的表面涂层，能够起到保护金属部件的作用，提高了机器的使用寿命，同时本发明的水性金属漆环保无污染，且制备方法简单，适合于工业生产。
本发明的目的可以通过以下技术方案实现：
一种用于包装机的水性金属防腐漆，由包含以下重量份的组分制成：
双酚A型环氧树脂75-90份，
环氧丙烷丁基醚15-20份，
聚环氧琥珀酸10-20份，
三羟甲基丙烷8-18份，
聚环氧乙烷10-15份，
聚二甲基硅氧烷5-12份，
十二烷基磺酸钠1-3份，
炭黑0.05-0.5份。
所述聚环氧乙烷的平均分子量为2000-4000。
所述聚环氧琥珀酸为18-20重量份。
一种用于包装机的金属防腐漆的制备方法，该方法包括以下步骤：
（1）称取双酚A型环氧树脂75-90份、环氧丙烷丁基醚15-20份、三羟甲基丙烷8-18份、聚环氧乙烷10-15份、聚二甲基硅氧烷5-12份、十二烷基磺酸钠1-3份混合均匀，缓慢加入聚环氧琥珀酸10-20份，超声分散均匀，得到混合料；
（2）将步骤（1）的混合料中加入炭黑0.05-0.5份，加入均质机中，通入氮气，在160-180℃下，混合3-5小时，得到水性金属防腐漆。
所述超声在60-80℃下进行。
所述超声时间为1-2小时。
本发明与现有技术相比，其有益效果为：
（1）本发明的水性金属漆使用方便，可用于包装机的表面涂层，能够起到保护金属部件的作用，提高了机器的使用寿命，同时本发明的水性金属漆环保无污染，且制备方法简单，适合于工业生产。
（2）本发明的水性金属漆使用方便，能够与金属表面很好的结合，具有较强的附着力，可以满足各类包装机的涂层性能需求，具有良好的耐热性，能进行加热和乙醇消毒，且没有小分子有害物质渗出，由于能满足食品包装机的涂层性能需求。
具体实施方式
以下结合实施例对本发明作进一步的说明。
实施例1
（1）称取双酚A型环氧树脂75kg、环氧丙烷丁基醚18kg、三羟甲基丙烷8kg、平均分子量为2000的聚环氧乙烷12kg、聚二甲基硅氧烷5kg、十二烷基磺酸钠3kg混合均匀，缓慢加入聚环氧琥珀酸18kg，在60℃下超声2小时，分散均匀，得到混合料；
（2）将步骤（1）的混合料中加入炭黑0.05kg，加入均质机中，通入氮气，在170℃下，混合3小时，得到水性金属防腐漆。
制得水性金属防腐漆的性能测试结果如表1所示。
实施例2
（1）称取双酚A型环氧树脂80kg、环氧丙烷丁基醚20kg、三羟甲基丙烷14kg、平均分子量为4000的聚环氧乙烷15kg、聚二甲基硅氧烷12kg、十二烷基磺酸钠2kg混合均匀，缓慢加入聚环氧琥珀酸20kg，在80℃下超声1小时，分散均匀，得到混合料；
（2）将步骤（1）的混合料中加入炭黑0.1kg，加入均质机中，通入氮气，在160℃下，混合5小时，得到水性金属防腐漆。
制得水性金属防腐漆的性能测试结果如表1所示。
实施例3
（1）称取双酚A型环氧树脂90kg、环氧丙烷丁基醚15kg、三羟甲基丙烷18kg、平均分子量为2000的聚环氧乙烷10kg、聚二甲基硅氧烷10kg、十二烷基磺酸钠1kg混合均匀，缓慢加入聚环氧琥珀酸10kg，在70℃下超声2小时，分散均匀，得到混合料；
（2）将步骤（1）的混合料中加入炭黑0.5kg，加入均质机中，通入氮气，在180℃下，混合4小时，得到水性金属防腐漆。
制得水性金属防腐漆的性能测试结果如表1所示。
表1
测试项目 实施例1 实施例2 实施例3
结合强度（MPa） 19.8 18.6 19.1
在18%的硫酸溶液中24小时 漆面无变化 漆面无变化 漆面无变化
本发明不限于这里的实施例，本领域技术人员根据本发明的揭示，不脱离本发明范畴所做出的改进和修改都应该在本发明的保护范围之内。

Claims (6)

1.一种用于包装机的水性金属防腐漆，其特征在于，由以下重量份的组分制成：
双酚A型环氧树脂75-90份，
环氧丙烷丁基醚15-20份，
聚环氧琥珀酸10-20份，
三羟甲基丙烷8-18份，
聚环氧乙烷10-15份，
聚二甲基硅氧烷5-12份，
十二烷基磺酸钠1-3份，
炭黑0.05-0.5份。
2.根据权利要求1所述的用于包装机的水性金属防腐漆，其特征在于，所述聚环氧乙烷的平均分子量为2000-4000。
3.根据权利要求1所述的用于包装机的水性金属防腐漆，其特征在于，所述聚环氧琥珀酸为18-20重量份。
4.一种用于包装机的水性金属防腐漆的制备方法，其特征在于，该方法包括以下步骤：
（1）称取双酚A型环氧树脂75-90份、环氧丙烷丁基醚15-20份、三羟甲基丙烷8-18份、聚环氧乙烷10-15份、聚二甲基硅氧烷5-12份、十二烷基磺酸钠1-3份混合均匀，缓慢加入聚环氧琥珀酸10-20份，超声分散均匀，得到混合料；
（2）将步骤（1）的混合料中加入炭黑0.05-0.5份，加入均质机中，通入氮气，在160-180℃下，混合3-5小时，得到水性金属防腐漆。
5.根据权利要求4所述的用于包装机的水性金属防腐漆的制备方法，其特征在于，所述超声在60-80℃下进行。
6.根据权利要求4所述的用于包装机的水性防腐漆的制备方法，其特征在于，所述超声时间为1-2小时。
CN201410295308.3A 2014-06-27 2014-06-27 一种用于包装机的水性金属防腐漆及其制备方法 Active CN104119777B (zh)