CN102851556A - 一种高强度抗氧化铝合金铸件 - Google Patents
一种高强度抗氧化铝合金铸件 Download PDFInfo
- Publication number
- CN102851556A CN102851556A CN 201210344831 CN201210344831A CN102851556A CN 102851556 A CN102851556 A CN 102851556A CN 201210344831 CN201210344831 CN 201210344831 CN 201210344831 A CN201210344831 A CN 201210344831A CN 102851556 A CN102851556 A CN 102851556A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- alloy casting
- strength
- antioxidant aluminum
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度抗氧化铝合金铸件,包括下述重量百分含量的组分:钛0.002-0.15%,锶0.001-0.03%,锑0-0.0005%,硅2.5-7%,硼0.03-1.8%,稀土金属0.05-2%,余量为铝和杂质。本发明高强度,延展性和断裂韧性好,成型性和耐蚀性强,是铝合金铸件的理想材料。
Description
技术领域
本发明涉及铸件领域,特别是涉及一种高强度抗氧化铝合金铸件。
背景技术
铝是银白色轻金属,有延性和展性,在潮湿空气中能形成一层防止金属腐蚀的氧化膜。铝元素在地壳中的含量仅次于氧和硅,居第三位,是地壳中含量最丰富的金属元素。航空、建筑、汽车三大重要工业的发展,要求材料特性具有铝及其合金的独特性质,这就大大有利于这种新金属铝的生产和应用。
由于纯的铝很软,强度不大,在潮湿空气中能被氧化而变暗,失去金属的光泽,故不宜作结构材料。通过长期的生产实践和科学实验,人们逐渐以加入合金元素及运用热处理等方法来强化铝,这就得到了一系列的铝合金。然而,现有的铝合金在缺乏理想的强度、延展性和断裂韧性,在铸件中的应用还不是十分理想。
发明内容
本发明主要解决的技术问题是提供一种高强度,延展性和断裂韧性好的高强度抗氧化铝合金铸件。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种高强度抗氧化铝合金铸件,包括下述重量百分含量的组分:
钛 0.002-0.15%,
锶 0.001-0.03%,
锑 0-0.0005%,
硅 2.5-7%,
硼 0.03-1.8%,
稀土金属 0.05-2%,
余量为铝和杂质。
在本发明一个较佳实施例中,所述的稀土金属为钪、钇或镧系金属。
在本发明一个较佳实施例中,所述的钛的含量为0.09%。
在本发明一个较佳实施例中,所述的稀土金属的含量为0.15%。
在本发明一个较佳实施例中,所述的硅的含量为5.5%。
本发明的有益效果是:本发明高强度,延展性和断裂韧性好,成型性和耐蚀性强,是铝合金铸件的理想材料。
具体实施方式
下面对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
实施例1
一种高强度抗氧化铝合金铸件,包括下述重量百分含量的组分:
钛 0.09%,
锶 0.005%,
锑 0.0001%,
硅 5.5%,
硼 0.5%,
钪 0.15%,
余量为铝和杂质。
实施例2
一种高强度抗氧化铝合金铸件,包括下述重量百分含量的组分:
钛 0.09%,
锶 0.005%,
锑 0.0002%,
硅 5.5%,
硼 1.1%,
钇 0.15%,
余量为铝和杂质。
实施例3
一种高强度抗氧化铝合金铸件,包括下述重量百分含量的组分:
钛 0.12%,
锶 0.01%,
锑 0.0004%,
硅 6.0%,
硼 1.5%,
铕 0.5%,
余量为铝和杂质。
本发明高强度,延展性和断裂韧性好,成型性和耐蚀性强,是铝合金铸件的理想材料。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种高强度抗氧化铝合金铸件,其特征在于,包括下述重量百分含量的组分:
钛 0.002-0.15%,
锶 0.001-0.03%,
锑 0-0.0005%,
硅 2.5-7%,
硼 0.03-1.8%,
稀土金属 0.05-2%,
余量为铝和杂质。
2.根据权利要求1所述的高强度抗氧化铝合金铸件,其特征在于,所述的稀土金属为钪、钇或镧系金属。
3.根据权利要求1所述的高强度抗氧化铝合金铸件,其特征在于,所述的钛的含量为0.09%。
4.根据权利要求1所述的高强度抗氧化铝合金铸件,其特征在于,所述的稀土金属的含量为0.15%。
5.根据权利要求1所述的高强度抗氧化铝合金铸件,其特征在于,所述的硅的含量为5.5%。