CN102850998A - 一种耐腐蚀玻璃防雾剂 - Google Patents
一种耐腐蚀玻璃防雾剂 Download PDFInfo
- Publication number
- CN102850998A CN102850998A CN2012103154182A CN201210315418A CN102850998A CN 102850998 A CN102850998 A CN 102850998A CN 2012103154182 A CN2012103154182 A CN 2012103154182A CN 201210315418 A CN201210315418 A CN 201210315418A CN 102850998 A CN102850998 A CN 102850998A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion
- resistant glass
- antifogging agent
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种高效玻璃防雾剂,所述防雾剂的组份和重量百分比如下:乙二醇10~20份,丙三醇10~30份,硅溶胶10~20份,香精1~5份,壬基酚聚氧乙烯醚1~5份,去离子水30~70份,脲醛树脂1~3份,十二醇丁醚5~8份,聚丙烯酸钠1~2份,氯化锌0.5份、三乙烯二胺1~3份、铝溶胶2~4份。将以上成分按一定比例混合,搅拌均匀降至室温即可得到高效玻璃防雾剂。本发明使用简单,防雾效果好,持续时间长,干燥后玻璃表面不留痕迹,不吸附灰尘,制造工艺简单,防腐蚀性能好。
Description
技术领域
本发明涉及一种玻璃防雾剂,特别涉及一种耐腐蚀的玻璃防雾剂,属于日用化工领域。
背景技术
在冬季或者昼夜温差大的时期,由于室内外温差大会导致汽车玻璃、眼镜、玻璃窗户等表面产生雾气,极大的影响驾驶员的视线,迫使驾驶员不断去擦拭玻璃,容易导致交通事故的发生。眼镜、玻璃窗户表面的水雾对人的工作生产造成不便。为消除玻璃表面产生的水雾,市场上有少量除雾剂产品,但是含有大量易燃化学物质,而且持续时间短,而且,在腐蚀性条件下,这些除雾剂的性能退化很快,在一段时间后,需要重复擦试,造成使用成本增加。
发明内容
针对以上对现有技术的评述,本发明的目的在于提供一种具有较好耐腐蚀性能的玻璃防雾剂,采用如下的技术方案:
一种耐腐蚀玻璃防雾剂,包括按重量计的如下组分:乙二醇10~20份,丙三醇10~30份,硅溶胶10~20份,香精1~5份,壬基酚聚氧乙烯醚1~5份,水30~70份,脲醛树脂1-3份,十二醇丁醚5~8份,聚丙烯酸钠1~2份,氯化锌0.5份、三乙烯二胺1~3份、铝溶胶2~4份。
上述的铝溶胶优选为水分散型纳米级氧化铝,其粒度为10~40nm。
上述的硅溶胶优选为水分散型纳米级氧化硅,其粒度为10~40nm。
其制备方法如下:
首先在脲醛树脂、十二醇丁醚、聚丙烯酸钠、氯化锌、三乙烯二胺、铝溶胶和硅溶胶中加入一部分去离子水,搅拌均匀;再边搅拌边慢慢加入乙二醇、丙三醇、香精、壬基酚聚氧乙烯醚,搅拌均匀;最后再加入余下的水,搅拌均匀。
本发明携带方便,直接擦拭使用,防雾效果好,使用后玻璃表面不留痕迹,抗静电能力好,持续有效时间长,安全无毒,防腐蚀性能优于同类产品,在稀盐酸中浸泡48小时后,仍具有较好的防雾效果。
具体实施方式
按表1中的重量配比备取以下原料:
表1实施例1-实施例3的玻璃防雾剂的重量比
制备方法是:
首先在脲醛树脂、十二醇丁醚、聚丙烯酸钠、氯化锌、三乙烯二胺、铝溶胶和硅溶胶中加入一部分去离子水,搅拌均匀;再边搅拌边慢慢加入乙二醇、丙三醇、香精、壬基酚聚氧乙烯醚,搅拌均匀;最后再加入余下的水,搅拌均匀。
性能测试
对了对本本玻璃防雾剂的性能,采用专利CN201010550287中公开的玻璃防雾剂作为对照例。将制备好的玻璃防雾剂均匀喷涂于玻璃上后,再置于0.5%(w/w)稀盐酸中浸泡48后,自然晾干,再使用蒸汽喷在玻璃上,目测其表面的防雾情况。
性能测试结果如表2所示
表2实施例1-实施例3及对照例的性能对比
实施例1 | 实施例2 | 实施例3 | 对照例 | |
防雾性能(目测法) | 无雾滴 | 无雾滴 | 无雾滴 | 有雾滴出现 |
Claims (3)
1.一种耐腐蚀玻璃防雾剂,包括按重量计的如下组分:乙二醇10~20份,丙三醇10~30份,硅溶胶10~20份,香精1~5份,壬基酚聚氧乙烯醚1~5份,水30~70份,脲醛树脂1-3份,十二醇丁醚5-8份,聚丙烯酸钠1~2份,氯化锌0.5份、三乙烯二胺1~3份、铝溶胶2~4份。
2.根据权利要求1所述的耐腐蚀玻璃防雾剂,其特征在于:所述的铝溶胶是水分散型纳米级氧化铝,其粒度为10~40nm。
3.根据权利要求1所述的耐腐蚀玻璃防雾剂,其特征在于:所述的硅溶胶是水分散型纳米级氧化硅,其粒度为10~40nm。