CN102842721A - 一种提高铅酸蓄电池循环寿命的方法 - Google Patents

一种提高铅酸蓄电池循环寿命的方法 Download PDF

Info

Publication number
CN102842721A
CN102842721A CN2012102701261A CN201210270126A CN102842721A CN 102842721 A CN102842721 A CN 102842721A CN 2012102701261 A CN2012102701261 A CN 2012102701261A CN 201210270126 A CN201210270126 A CN 201210270126A CN 102842721 A CN102842721 A CN 102842721A
Authority
CN
China
Prior art keywords
plate grid
anode plate
cycle life
curing
lead
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102701261A
Other languages
English (en)
Inventor
包有富
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHEJIANG ZHONGYI POWER SUPPLY CO Ltd
Original Assignee
ZHEJIANG ZHONGYI POWER SUPPLY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG ZHONGYI POWER SUPPLY CO Ltd filed Critical ZHEJIANG ZHONGYI POWER SUPPLY CO Ltd
Priority to CN2012102701261A priority Critical patent/CN102842721A/zh
Publication of CN102842721A publication Critical patent/CN102842721A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种提高铅酸蓄电池循环寿命的方法，包括以下步骤：步骤一、用合金铅铸造正极板栅；步骤二、将铸造好的正极板栅放入固化干燥室进行固化和干燥；步骤三、将正极活性物质涂于固化干燥后的正极板栅上得到湿生极板；步骤四、湿生极板经固化干燥后得到干生极板。本发明能够使正极板栅与正极活性物质之间不存在界面现象，从而提高铅酸蓄电池的循环寿命。

Description

一种提高铅酸蓄电池循环寿命的方法
技术领域
本发明涉及铅酸蓄电池生极板制造领域，具体涉及一种提高铅酸蓄电池循环寿命的方法。
背景技术
传统方法制备铅酸蓄电池正极生极板的工艺过程是：在正极板栅铸造完成后，用铅粉制成的铅膏作为正极活性物质涂板得到湿生极板，然后湿生极板经固化干燥得到干生极板；这样制得的干生极板，正极板栅与正极活性物质之间存在界面现象，影响了铅酸蓄电池的使用寿命。
发明内容
本发明所要解决的技术问题在于提供一种提高铅酸蓄电池循环寿命的方法，能够使正极板栅与正极活性物质之间不存在界面现象，从而提高铅酸蓄电池的循环寿命。
为解决上述现有的技术问题，本发明采用如下方案：一种提高铅酸蓄电池循环寿命的方法，包括以下步骤：步骤一、用合金铅铸造正极板栅；步骤二、将铸造好的正极板栅放入固化干燥室进行固化和干燥；步骤三、将正极活性物质涂于固化干燥后的正极板栅上得到湿生极板；步骤四、湿生极板经固化干燥后得到干生极板。采用该工艺铸造的正极板栅表面经过固化干燥后形成一层铅氧化物，而该铅氧化物与正极活性物质中的部分铅氧化物一致，使得正极板栅与正极活性物质之间不存在界面现象，从而提高了铅酸蓄电池的循环寿命。
作为优选，所述正极板栅在固化干燥室进行固化时，固化温度为45~55℃，固化湿度为90%以上，固化时间为2～4h。此范围下正极板栅的固化效果好，形成的氧化物层较均匀。
作为优选，所述正极板栅在固化干燥室进行干燥时，干燥温度为60～70℃，干燥时间为12~20小时。正极板栅经固化干燥后板栅表面氧化效果好，形成的氧化物层较均匀。
有益效果：
本发明采用上述技术方案提供的一种提高铅酸蓄电池循环寿命的方法，能够使正极板栅与正极活性物质之间不存在界面现象，从而提高铅酸蓄电池的循环寿命。
具体实施方式
实施例一：
一种提高铅酸蓄电池循环寿命的方法，包括以下步骤：步骤一、用合金铅铸造正极板栅；步骤二、将铸造好的正极板栅放入固化干燥室进行固化和干燥；步骤三、将正极活性物质涂于固化干燥后的正极板栅上得到湿生极板；步骤四、湿生极板经固化干燥后得到干生极板。所述正极板栅在固化干燥室进行固化时，固化温度为45℃，固化湿度为90%以上，固化时间为2h。所述正极板栅在固化干燥室进行干燥时，干燥温度为60℃，干燥时间为12小时。
实施例二：
与实施例一的不同之处在于：正极板栅在固化干燥室进行固化时，固化温度为50℃，固化湿度为90%以上，固化时间为3h。正极板栅在固化干燥室进行干燥时，干燥温度为65℃，干燥时间为16小时。
实施例三：
与实施例一和实施例二的不同之处在于：正极板栅在固化干燥室进行固化时，固化温度为55℃，固化湿度为90%以上，固化时间为4h。正极板栅在固化干燥室进行干燥时，干燥温度为70℃，干燥时间为20小时。
本发明在正极板栅铸造完成后用正极活性物质涂板前，通过增加将正极板栅放入固化干燥室进行固化和干燥的工序，使得铸造好的正极板栅表面经过固化干燥后形成一层铅氧化物，而该铅氧化物与正极活性物质中的部分铅氧化物一致，使得正极板栅与正极活性物质之间不存在界面现象，从而提高了铅酸蓄电池的循环寿命。

Claims (3)

1.一种提高铅酸蓄电池循环寿命的方法，其特征在于：包括以下步骤：步骤一、用合金铅铸造正极板栅；步骤二、将铸造好的正极板栅放入固化干燥室进行固化和干燥；步骤三、将正极活性物质涂于固化干燥后的正极板栅上得到湿生极板；步骤四、湿生极板经固化干燥后得到干生极板。
2.根据权利要求1所述的一种提高铅酸蓄电池循环寿命的方法，其特征在于：所述正极板栅在固化干燥室进行固化时，固化温度为45~55℃，固化湿度为90%以上，固化时间为2～4h。
3.根据权利要求1或2所述的一种提高铅酸蓄电池循环寿命的方法，其特征在于：所述正极板栅在固化干燥室进行干燥时，干燥温度为60～70℃，干燥时间为12~20小时。
CN2012102701261A 2012-08-01 2012-08-01 一种提高铅酸蓄电池循环寿命的方法 Pending CN102842721A (zh)