CN102838785A - 轮胎及其制造方法 - Google Patents

轮胎及其制造方法 Download PDF

Info

Publication number
CN102838785A
CN102838785A CN2012103014187A CN201210301418A CN102838785A CN 102838785 A CN102838785 A CN 102838785A CN 2012103014187 A CN2012103014187 A CN 2012103014187A CN 201210301418 A CN201210301418 A CN 201210301418A CN 102838785 A CN102838785 A CN 102838785A
Authority
CN
China
Prior art keywords
rubber
tire
tyre
accelerant
glue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103014187A
Other languages
English (en)
Other versions
CN102838785B (zh
Inventor
夏宝山
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Dima Rubber Co Ltd
Original Assignee
Zhejiang Dima Rubber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Dima Rubber Co Ltd filed Critical Zhejiang Dima Rubber Co Ltd
Priority to CN201210301418.7A priority Critical patent/CN102838785B/zh
Publication of CN102838785A publication Critical patent/CN102838785A/zh
Application granted granted Critical
Publication of CN102838785B publication Critical patent/CN102838785B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

轮胎，按重量比原辅材料配比包括如下组分：a、帘布胶：天然胶1900~3000，丁苯胶750~1000、轻钙5700~7700、硫磺50~75、氧化锌120~200、钛白粉250~350、硬脂酸2~4、促进剂M 6~8、促进剂DM50~80；b、胎面胶：天然胶1000~2000、再生胶3500~4500、硫磺45~70、轻钙 3000~4000、炭黑500~700、树脂40~70、氧化锌100~150、白矿油100~250、硬脂酸30~50、促进剂M6~8、促进剂DM20~30。上述轮胎的制造方法：a、炼胶；b、胎面压出；c、贴合成型； d、硫化。本发明使橡胶婴童车、自行车轮胎稳定达到目前欧洲标准(主要是16项PAHS总和≤200mg/kg)，打破欧美技术壁垒，进入欧美市场。

Description

轮胎及其制造方法
技术领域
本发明涉及一种轮胎及其制造方法。
背景技术
国内生产的橡胶婴童车、自行车轮胎常因多环芳香烃（PAHS）指标不能稳定达到欧洲标准（16项PAHS总和≤200mg/kg）要求，产品很难打入欧美市场，也常因此而发生贸易纠纷。
发明内容
本发明要解决的技术问题是提供一种能够稳定达到目前欧洲标准、耐磨耗能力好、老化率低，同时生产成本没有明显增加的用于橡胶婴童车、自行车的轮胎及其制造方法。
本发明的技术方案是：
一种轮胎，其特征在于，按重量比原辅材料配比包括如下组分：
a、帘布胶
Figure BDA0000204602661
b、   胎面胶
上述材料中，
①     再生胶最好用40目无味精细再生橡胶或更优质再生胶；
②     炭黑以CF703或N330为佳；
③     树脂最好为1102树脂；
④    轻钙即碳酸，轻钙为碳酸钙的商业名。
上述轮胎的制造方法：
a、 炼胶：各原辅材料在密炼机中搅拌时间由原来的（6~7）分钟，延长至（8~9）分钟，排胶温度相应提高10℃左右，即从130℃提高到140℃，以利于部分多环芳香烃从胶料中排放出去；炼好的胶料必须存放48小时以上再用于胎面压出；
b、 胎面压出：胎面的冠宽部分需作打孔处理，以有利于轮胎硫化时气体的排放（气体中包括部分多环芳香烃）；
c、 贴合成型：以普通无胶钢丝为佳，若用覆胶多股钢丝，必须要求多股钢丝覆胶的PAHS总含量在200 mg/kg以下；
d、硫化：硫化脱模剂每天更换一次；且所使用的风胎PAHS总含量在200 mg/kg以下。
本发明使橡胶婴童车、自行车轮胎稳定达到目前欧洲标准(主要是16项PAHS总和≤200mg/kg)，打破欧美技术壁垒，进入欧美市场。
具体实施方式
实施例1
一种轮胎，其特征在于，按重量比原辅材料配比包括如下组分：
a、帘布胶
Figure BDA0000204602664
b、   胎面胶
Figure BDA0000204602665
上述材料中，
①     再生胶最好用40目无味精细再生橡胶或更优质再生胶；
②     炭黑以CF703或N330为佳；
③     树脂最好为1102树脂；
④    轻钙一般为碳酸钙。
上述轮胎的制造方法：
a、 炼胶：各原辅材料在密炼机中搅拌时间由原来的（6~7）分钟，延长至（8~9）分钟，排胶温度相应提高10℃左右，即从130℃提高到140℃，以利于部分多环芳香烃从胶料中排放出去；炼好的胶料必须存放48小时以上再用于胎面压出；
b、 胎面压出：胎面的冠宽部分需作打孔处理，以有利于轮胎硫化时气体的排放（气体中包括部分多环芳香烃）；
c、 贴合成型：以普通无胶钢丝为佳，若用覆胶多股钢丝，必须要求多股钢丝覆胶的PAHS总含量在200 mg/kg以下；
d、硫化：硫化脱模剂每天更换一次；且所使用的风胎PAHS总含量在200 mg/kg以下。
实施例2
一种轮胎，其特征在于，按重量比原辅材料配比包括如下组分：
a、帘布胶
Figure BDA0000204602666
b、   胎面胶
Figure BDA0000204602667
上述轮胎的制造方法同实施例。
本发明使橡胶婴童车、自行车轮胎稳定达到目前欧洲标准(主要是16项PAHS总和≤200mg/kg)，打破欧美技术壁垒，进入欧美市场。

Claims (7)

1.一种轮胎，其特征在于，按重量比原辅材料配比包括如下组分：
a、帘布胶
Figure RE-FDA0000226992341
b、胎面胶
Figure RE-FDA0000226992342
2.根据权利要求1所述的一种轮胎，其特征在于，所述的再生胶为40目无味精细再生橡胶。 
3.根据权利要求1所述的一种轮胎，其特征在于，所述的炭黑为CF703或N330。
4.根据权利要求1所述的一种轮胎，其特征在于，所述的树脂为1102树脂。
5.根据权利要求1所述的一种轮胎，其特征在于，所述的 轻钙为碳酸钙。
6.一种轮胎，其特征在于，按重量比原辅材料配比包括如下组分：
a、帘布胶
Figure FDA0000204602653
b、   胎面胶
Figure FDA0000204602654
7.如权利要求1或6所述的轮胎的制造方法：
a、 炼胶：各原辅材料在密炼机中搅拌时间为8~9分钟，排胶温度为140℃，炼好的胶料必须存放48小时以上再用于胎面压出；
b、 胎面压出：胎面的冠宽部分需作打孔处理；
c、 贴合成型：钢丝用普通无胶钢丝或覆胶的PAHS总含量在200 mg/kg以下的覆胶多股钢丝；
d、硫化：硫化脱模剂每天更换一次；且所使用的风胎PAHS总含量在200 mg/kg以下。 
CN201210301418.7A 2012-08-23 2012-08-23 轮胎及其制造方法 Active CN102838785B (zh)