CN102828444A - Direct-plating tipping paper with laser effect for cigarette and production process thereof - Google Patents
Direct-plating tipping paper with laser effect for cigarette and production process thereof Download PDFInfo
- Publication number
- CN102828444A CN102828444A CN2012102953506A CN201210295350A CN102828444A CN 102828444 A CN102828444 A CN 102828444A CN 2012102953506 A CN2012102953506 A CN 2012102953506A CN 201210295350 A CN201210295350 A CN 201210295350A CN 102828444 A CN102828444 A CN 102828444A
- Authority
- CN
- China
- Prior art keywords
- layer
- tipping paper
- coating
- paper
- laser effect
- Prior art date
Abstract
The invention belongs to the technical field of cigarette packaging paper, and relates to direct-plating tipping paper with laser effect for cigarettes and a production process thereof. The direct-plating tipping paper with laser effect for cigarettes disclosed by the invention comprises, from the bottom up, a back coating layer 2, common tipping paper base paper 1, a surface coating layer 3, a direct-plating glue layer 4, and a laser grain decoration layer 5; the decoration layer has a vacuum aluminized layer 6 on the laser grain decoration layer 5; a printing ink layer or paint layer 7, and an electrochemical aluminium stamped foil layer 8 are on the vacuum aluminized layer 6. The invention also discloses a production process, which comprises the following steps: performing back coating and surface coating of waterborne coatings on common direct-plating paper, coating the direct-plating glue, manufacturing patterns with laser effect on the front surface layer by mold pressing equipment, performing vacuum aluminizing, printing or printing ink or paint coating, embossing or non-embossing, electrochemical aluminium gold stamping, and slitting. The direct-plating tipping paper with laser effect for cigarettes manufactured by the invention has good decoration effect, is simple and environment-friendly in production process.
Description
Technical field
The invention belongs to cigarette and use the wrapping paper field, particularly a kind of cigarette with laser effect is with straight plating type tipping paper and production technology thereof.
Background technology
Cigarette tipping paper has experienced the upgrading of several times technology such as printing (coating) type tipping paper, gold stamping type tipping paper, transfevent tipping paper and decorative effect, and the decorative effect of its supporting tobacco package decoration progressively promotes.The transfevent tipping paper that particularly has laser effect; It not only has all characteristics of transfevent tipping paper; And, promote the decoration quality effect of cigarette greatly because the strong decorating feature of its laser effect is widely used on the packing of medium-to-high grade cigarette its favor that receives tobacco package more.At present, known tipping paper divides from process characteristic has: three types of printing (coating) type tipping papers, gold stamping type tipping paper, transfevent tipping paper.Printing (coating) type tipping paper process characteristic is for adopting common tipping paper body paper through several times printing ink (or coating) printing (or coating), one type of tipping paper that road, the back processing and fabricatings such as (also can not punching) of cutting afterwards, punch forms; Gold stamping type tipping paper process characteristic is for adopting common tipping paper body paper through several times printing ink (or coating) printing (or coating); It is gold stamping to adopt one type of coloured alumite thermoprinting foil with metal-like to carry out through the heat of transfer ironing process then, one type of tipping paper that road, the back processing and fabricatings such as (also can not punching) of cutting afterwards, punch forms; Transfevent tipping paper process characteristic is for adopting the transfevent body paper with metal-like through several times printing ink (or coating) printing (or coating), carries out one type of tipping paper that surperficial embossing (also not embossing), gold stamping (also can be not gold stamping), road, the back processing and fabricatings such as (also can not punching) of cutting, punch form afterwards again.Printing (coating) type tipping paper decorative effect is general; The gold stamping partial graph stationery of gold stamping type tipping paper has metal-like, thereby local decorative effect gets a promotion, but can't large tracts of land promote decorative effect, and alumite thermoprinting foil can only use limited waste of material bigger; The transfevent tipping paper is owing to adopt the transfer paper with metal-like to make as body paper; Tipping paper integral body all has metal-like; Decorative effect promotes greatly, but because need to use reusable basement membrane to do when make shifting body paper auxiliary, and production technology is relatively complicated.
Laser-type transfevent tipping paper is better than transfevent tipping paper packing and decorating effect; Its laser effect is strong, full of moving sense; The packing class is high; Need be on the basement membrane of making the transfevent tipping paper in the manufacturing process molding laser decorative pattern, through aluminizing, compound, transfer on the tipping paper body paper after peeling off, further produce radium-shine transfer tipping paper thereby produce radium-shine transfer body paper.But along with the requirement of society to safety, environmental protection, green, the gold stamping and transfer area of gold stamping type tipping paper and transfevent tipping paper receives strict control, can't large tracts of land promote the tipping paper surface decoration effect.
Country's tobacco package tipping paper industry has carried out stipulating requirement gold stamping, the transfer area to gold stamping type tipping paper, transfevent tipping paper, and further improves tipping paper safety and sanitation index.In this case; Straight plating type material is because of its green, environmental protection, the explained hereafter characteristic of safety and the outward appearance of metal-like decorative effect thereof; With constantly being adopted in packing, a kind of straight plating type packaging material safer, green, environmental protection are approved by society and tobacco package industry gradually at cigarette.Along with the continuous application of straight plating type cigarette with paperboard, directly plating type tobacco lining paper, the inventor improves with test through continuous technological innovation and has produced the straight plating type tipping paper with laser effect.Such tipping paper not only has the exterior decorative effect of radium-shine transfevent tipping paper, and its manufacture craft process is simple relatively, environmental protection, and product each item index is safer, green.What the present invention relates to is a kind ofly to manufacture radium-shine directly plating type of effect tipping paper through special process method; The characteristic that it is different from ordinary straight plating type tipping paper is that it has laser effect, can promote the decoration quality effect of cigarette as radium-shine transfevent tipping paper greatly.
Summary of the invention
Technical problem of the present invention is through the surface treatment to common tipping paper body paper; It is vacuum aluminum-coated that it can directly be carried out on the surface; Utilize molding apparatus to produce decorative pattern then with laser effect on its positive top layer; Produce common directly plating papers, and make it can adapt to the making of tipping paper later process with laser effect.
A kind of cigarette with laser effect is with straight plating type tipping paper; Comprise directly plating papers body paper and its surperficial decorative layer with laser effect; Described directly plating papers body paper with laser effect is followed successively by back coating (2), common tipping paper body paper (1), finishing coat (3) from the bottom to top, directly plates glue-line (4), radium-shine decorative pattern layer (5), and described decorative layer is vacuum aluminium coated layer (6).
In a preferred embodiment of the present invention, described surface decoration layer can have ink lay or dope layer (7) on vacuum aluminium coated layer (6).
In a preferred embodiment of the present invention, described surface decoration layer can also have alumite thermoprinting foil layer (8) on ink lay or dope layer (7).
A kind ofly make aforesaid production technology, comprise the steps: with cigarette of laser effect with straight plating type tipping paper
Steps A, common tipping paper body paper (1) be with the speed of 90-100m/min, even back-coating of coating at its back side, and coating pressure is 2.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5 ± 0.5%;
Step B, the tipping paper after the back of the body is coated with evenly are coated with the secondary painting coating with the speed of 90-100m/min on its surface, and coating pressure is 3.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5% ± 0.5%;
Step C, the tipping paper after face is coated with once directly plate glue with the speed of 90-100m/min in its surperficial evenly coating, and coating pressure is 3.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5 ± 0.5%;
The radium-shine decorative pattern layer (5) with laser effect is produced with the speed of 50 ± 10m/min, 160 ± 10 ℃ molding temperature, the molding pressure of 3.5 ± 1KG in step D, the positive top layer of the tipping paper after utilizing molding apparatus with the positive and negative coating of above-mentioned process;
Step e, utilize vacuum aluminum-coated machine; Aluminize with the speed of 2-4 meter per second in the tipping paper body paper surface that above-mentioned steps completion coating, oven dry and mold pressing is gone out radium-shine decorative pattern layer (5); Formation has the vacuum aluminium coated layer (6) of radium-shine decorative pattern, make have laser effect cigarette with straight plating type tipping paper body paper;
Step F, the cigarette with laser effect after aluminizing can utilize printing (or coating) equipment making to go out ink lay or dope layer (7) on vacuum aluminium coated layer (6) with straight plating type tipping paper body paper;
Step G, carry out the embossing operation at the upper surface of ink lay or dope layer (7);
Step H, cut check, warehouse-in.
In a preferred embodiment of the present invention, described production technology, also embossing not among the described step G with cigarette of laser effect with straight plating type tipping paper.
In a preferred embodiment of the present invention, described production technology with cigarette of laser effect with straight plating type tipping paper, described step G also can carry out electrochemical aluminium gold-stamped formation alumite thermoprinting foil layer (8) after surperficial embossing operation.
In a preferred embodiment of the present invention, described production technology with cigarette of laser effect with straight plating type tipping paper, described step G also can carry out electrochemical aluminium gold-stamped formation alumite thermoprinting foil layer (8) without embossing.
In a preferred embodiment of the present invention, described making has the production technology of the cigarette of laser effect with straight plating type tipping paper, and described back-coating and painting coating are water-soluble.
Coating one deck water soluble paint at tipping paper body paper (1) back side makes its back side when carrying out the straight plating of the positive coating of paper glue, influences vacuum aluminum-coated effect and helps the cigarette of directly plating type tipping paper finished product on cigarette machine to back side of paper thoroughly; Tipping paper body paper surface coated one deck water soluble paint, one deck after the back of the body is coated with directly plates glue then, makes its surface can be more smooth, directly carries out vacuum aluminum-coated and makes aluminium lamination can be evenly distributed in tipping paper body paper coating surface to satisfy; The tipping paper body paper that will pass through then after positive and negative is coated with is produced the decorative pattern with laser effect with molding apparatus on its positive top layer; Once aluminize through vacuum aluminum-coated machine again; Make its surface plate aluminium lamination uniformly; Before because aluminize the paper front mold pressing gone out to have the decorative pattern of laser effect, thereby just have laser effect on this aluminium lamination, thereby be made into directly plating papers with laser effect; The directly plating papers that will have laser effect then carries out several times printing ink (or coating) printing (or coating) as body paper; Surface embossing (also not embossing), gold stamping (also can be not gold stamping), cut, punch (also can not punching) wait the road, back to process, and are made into the straight plating type cigarette tipping paper with laser effect.
Beneficial effect
The straight plating type tipping paper with laser effect that the present invention produces is compared with printing (coating) type tipping paper, and decorative effect better and more can carry out the processing and fabricating of deeper function, effect; Compare with gold stamping type tipping paper, decorative effect is better and the manufacture craft process is simpler, safety, green, environmental protection; Compare with radium-shine transfevent tipping paper, it is manufactured, and process is simpler, safety, and the product index performance is more green, environmental protection.
Description of drawings
Fig. 1 is the directly plating papers structural representation with laser effect
Wherein 1, the tipping paper body paper, 2, back coating, 3, finishing coat, 4, directly plate glue-line, 5, radium-shine decorative pattern layer, 6, vacuum aluminium coated layer, 7, printing ink (coating) layer, 8, the alumite thermoprinting foil layer.
The specific embodiment
Specific embodiment of the present invention below is provided, supply those skilled in the art to understand technical thought of the present invention better, but the present invention is not limited to present embodiment.
Be coated with one deck water soluble paint at common tipping paper body paper 1 back side with printing the speed of (or coating) equipment online (or distribution) with 90-100m/min, coating pressure is 2.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5 ± 0.5%; The back of the body is coated with the primary water soluble paint, influences vacuum aluminum-coated effect and is beneficial to the cigarette of straight plating type tipping paper on cigarette machine to back side of paper thoroughly when preventing paper front coating composition and straight plating glue;
Tipping paper after the back of the body is coated with evenly is coated with the secondary painting coating with the speed of 90-100m/min on its surface, and coating pressure is 3.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5% ± 0.5%; Tipping paper after face is coated with once directly plates glue with the speed of 90-100m/min in its surperficial evenly coating, and coating pressure is 3.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5 ± 0.5%; Positive coating two coatings and straight plating glue are to make the tipping paper body paper surface can be more smooth, to satisfy vacuum aluminum-coated and to make aluminium lamination can be evenly distributed in tipping paper body paper coating surface;
The common tipping paper body paper that will pass through after positive and negative is coated with utilizes molding apparatus to produce the radium-shine decorative pattern layer with laser effect with the speed of 50 ± 10m/min, 160 ± 10 ℃ molding temperature, the molding pressure of 3.5 ± 1KG;
Utilize vacuum aluminum-coated machine; Aluminize with the speed of 2-4 meter per second in the tipping paper body paper surface that above-mentioned steps completion coating, oven dry and mold pressing is gone out radium-shine decorative pattern layer; Formation has the vacuum aluminium coated layer of radium-shine decorative pattern, make have laser effect cigarette with straight plating type tipping paper body paper; Its surperficial aluminium lamination has laser effect, forms the directly plating papers body paper with laser effect, and it is had the stock of the straight plating type tipping paper of laser effect as making;
Go out printing ink (coating) layer that one deck have decorate and embody package brand picture and text or color through printing (or coating) equipment with some color inks (or coating) printings (coating) on directly plating papers body paper surface then with laser effect;
Can on its printing ink (coating) layer, make particular abrasive picture and text effect when needing, also can re-use the alumite thermoprinting foil layer that gold stamping equipment thermoprint one deck is decorated, embodied package brand picture and text with emebosser;
The straight plating type tipping paper semi-finished product with laser effect that will pass through after printing (coating), embossing (also can not embossing), gold stamping (also can be not gold stamping) with cutting apparatus at last cut into regulatory specifications; Carry out perforation processing (also can not punching) with punch device when needing, be made into straight plating type tipping paper product with laser effect.
This cigarette with laser effect is with straight plating type tipping paper; Comprise directly plating papers body paper and its surperficial decorative layer with laser effect; Described directly plating papers body paper with laser effect is followed successively by back coating 2, common tipping paper body paper 1, finishing coat 3 from the bottom to top, directly plates glue-line 4, radium-shine decorative pattern layer 5, and described decorative layer is a vacuum aluminium coated layer 6.
Described surface decoration layer can have ink lay or dope layer 7 on vacuum aluminium coated layer 6.
Described surface decoration layer can also have alumite thermoprinting foil layer 8 on ink lay or dope layer 7.
Claims (8)
1. the cigarette with laser effect is with straight plating type tipping paper; Comprise directly plating papers body paper and its surperficial decorative layer with laser effect; It is characterized in that; Described directly plating papers body paper with laser effect is followed successively by back coating (2), common tipping paper body paper (1), finishing coat (3) from the bottom to top, directly plates glue-line (4), radium-shine decorative pattern layer (5), and described decorative layer is vacuum aluminium coated layer (6).
2. the cigarette with laser effect according to claim 1 is characterized in that with straight plating type tipping paper described surface decoration layer can have ink lay or dope layer (7) on vacuum aluminium coated layer (6).
3. the cigarette with laser effect according to claim 2 is characterized in that with straight plating type tipping paper described surface decoration layer can also have alumite thermoprinting foil layer (8) on ink lay or dope layer (7).
4. the described production technology with cigarette of laser effect with straight plating type tipping paper of a making such as above-mentioned claim 1 ~ 3 is characterized in that, comprises the steps:
Steps A, common tipping paper body paper (1) be with the speed of 90-100m/min, even back-coating of coating at its back side, and coating pressure is 2.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5 ± 0.5%;
Step B, the tipping paper after the back of the body is coated with evenly are coated with the secondary painting coating with the speed of 90-100m/min on its surface, and coating pressure is 3.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5% ± 0.5%;
Step C, the tipping paper after face is coated with once directly plate glue with the speed of 90-100m/min in its surperficial evenly coating, and coating pressure is 3.5 ± 1KG, at 110 ± 10 ℃ drying in oven to moisture 4.5 ± 0.5%;
The radium-shine decorative pattern layer (5) with laser effect is produced with the speed of 50 ± 10m/min, 160 ± 10 ℃ molding temperature, the molding pressure of 3.5 ± 1KG in step D, the positive top layer of the tipping paper after utilizing molding apparatus with the positive and negative coating of above-mentioned process;
Step e, utilize vacuum aluminum-coated machine; Aluminize with the speed of 2-4 meter per second in the tipping paper body paper surface that above-mentioned steps completion coating, oven dry and mold pressing is gone out radium-shine decorative pattern layer (5); Formation has the vacuum aluminium coated layer (6) of radium-shine decorative pattern, make have laser effect cigarette with straight plating type tipping paper body paper;
Step F, the cigarette with laser effect after aluminizing can utilize printing (or coating) equipment making to go out ink lay or dope layer (7) on vacuum aluminium coated layer (6) with straight plating type tipping paper body paper;
Step G, carry out the embossing operation at the upper surface of ink lay or dope layer (7);
Step H, cut check, warehouse-in.
5. the production technology with cigarette of laser effect with straight plating type tipping paper according to claim 4 is characterized in that among the described step G also not embossing.
6. the production technology with cigarette of laser effect with straight plating type tipping paper according to claim 4 is characterized in that described step G after surperficial embossing operation, also can carry out electrochemical aluminium gold-stamped formation alumite thermoprinting foil layer (8).
7. the production technology with cigarette of laser effect with straight plating type tipping paper according to claim 5 is characterized in that described step G can carry out electrochemical aluminium gold-stamped formation alumite thermoprinting foil layer (8).
8. have the production technology of the cigarette of laser effect according to claim 4 or 5 described making, it is characterized in that described back-coating and painting coating are water-soluble with straight plating type tipping paper.