CN109345950A - A kind of high brightness imitates gold stamping aluminized paper label manufacturing process - Google Patents
A kind of high brightness imitates gold stamping aluminized paper label manufacturing process Download PDFInfo
- Publication number
- CN109345950A CN109345950A CN201811316562.1A CN201811316562A CN109345950A CN 109345950 A CN109345950 A CN 109345950A CN 201811316562 A CN201811316562 A CN 201811316562A CN 109345950 A CN109345950 A CN 109345950A
- Authority
- CN
- China
- Prior art keywords
- paper
- high brightness
- aluminized
- aluminized paper
- gold stamping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of high brightness and imitates gold stamping aluminized paper label manufacturing process, which comprises the following steps: 1) embosses, scheduled lines is suppressed on high brightness aluminized paper；2) break and open, by setting specification, the high brightness aluminized paper after embossing is divided into and is opened；3) overlap, the high brightness after removal disconnected are aluminized the burr of paper edge；4) it prints, gold ink is printed on high brightness aluminized paper and forms imitative bronzing effect.Compared with prior art, a kind of high brightness provided by the invention imitates gold stamping paper label of aluminizing, and saves gold stamping link, reduces cost, realizes integrated molding.Meanwhile can print in batches, performance advantage effect is prominent, belongs to advanced technology in label industry, requires height to coating, a variety of printings cooperation, hardly possible is imitated, plays certain anti-fake effect.
Description
Technical field
It aluminizes paper label manufacturer the present invention relates to label technique field more particularly to a kind of bloom of imitative bronzing effect
Method.
Background technique
Traditional gilding technology is that the color layers on electrochemical aluminum foil are transferred in printing under heat using hot stamping equipment
The special printing technology of one kind, through frequently as the post-press finishing technique for giving the unique decorative effect of label and cubic metal characters or patterns sense,
But the significant problems such as economy are always existed, including it is at high cost using electrochemical aluminum foil, production integrally formed can not be caused to imitate
Rate is low, remaining film causes secondary pollution to lack the feature of environmental protection, and printing picture and text are not clear enough, level is not abundant enough.
Summary of the invention
Aiming at the problems existing in the prior art, the purpose of the present invention is to provide high brightness to imitate gold stamping aluminized paper manufacturer
Method prints gold ink directly on high brightness aluminized paper and reaches imitative bronzing effect, no longer needs to overcome existing scald by post-processing
The economy problems of gold process.
To achieve the above objectives, the present invention adopts the following technical scheme that.
A kind of high brightness imitates gold stamping aluminized paper label manufacturing process, which comprises the following steps:
1) it embosses, scheduled lines is suppressed on high brightness aluminized paper；
2) break and open, by setting specification, the high brightness aluminized paper after embossing is divided into and is opened；
3) overlap, the high brightness after removal disconnected are aluminized the burr of paper edge；
4) it prints, gold ink is printed on high brightness aluminized paper and forms imitative bronzing effect.
As a further illustration of the above scheme, the gold ink is by weight, it is made of following raw material: removes light dose
5-10 parts, 0.5-1 parts of golden red ink, transparent yellow ink 1-5 parts.
As a further illustration of the above scheme, ink density value control after gold ink printing 1.5 ±
0.1。
As a further illustration of the above scheme, the bloom effect of the high brightness aluminized paper is by being coated with coating resin
Come what is formed.
As a further illustration of the above scheme, the bloom effect of the high brightness aluminized paper be using PET/BOPP film as
Transfer vector, carries out straight plating method on aluminized paper or BOPP moves what plating method was formed.
As a further illustration of the above scheme, the high brightness aluminized paper is fabricated through following steps:
1) it is molded, suppresses to obtain paper product in moulding press upper mold；
2) rewinding carries out product examine on rewinding machine, such as to cut, then carving knife is added on rewinding machine；
3) compound, it is on compounding machine that paper is compound with transfer membrane；
4) it removes, transfer membrane and paper is removed by stripping machine, are transferred to the hologram image on transfer membrane in paper
On；
5) it dries；
6) it aluminizes, aluminizes to the paper of drying, aluminized paper is made；
7) face painting/back applies, and generates bloom effect in the front and back coating coating resin of aluminized paper；
8) it gets damp again, gets damp again to the aluminized paper for being coated with coating resin, it is made to restore moisture；
9) it is put in storage.
As a further illustration of the above scheme, the coating resin is prepared from the following raw materials by mass percentage: propylene
Acid resin 20-30%, leveling auxiliary agent 0.1-1%, antifoam additives 0.1-1%, wetting agent 0.1-1%, hinge agent 0.1-1% prevent
Rotten agent 0.1-1%, water 70-78%.
As a further illustration of the above scheme, further comprising the steps of after the print steps: selecting paper-neat paper-
Cut paper-punch die-ties up paper-vanning-strip of paper used for sealing.
The beneficial effects of the present invention are:
One, imitative bronzing effect directly is formed in high brightness aluminized paper printing gold ink, no longer needed to by post-processing, same
While sample reaches patch bottle performance and paper performance, it can directly one-pass molding print, remove the gold stamping use of metal aluminum foil, gram
The economy problems of original gilding technology are taken.
Two, can print in batches, using high brightness aluminized paper technology printing than directly adopt line it is gold stamping and print
It is gold stamping at low cost afterwards；Performance advantage effect is prominent, belongs to advanced technology in label industry, requires coating, a variety of printings cooperation
Height, hardly possible is imitated, plays certain anti-fake effect.
Detailed description of the invention
Fig. 1 show high brightness provided by the invention and imitates gold stamping aluminized paper label manufacturing process flow chart.
Specific embodiment
In the description of the present invention, it should be noted that " transverse direction ", " vertical if any term " center " for the noun of locality
To ", " length ", " width ", " thickness ", "upper", "lower", "front", "rear", "left", "right", "vertical", "horizontal", "top",
The indicating positions such as "bottom", "inner", "outside", " clockwise ", " counterclockwise " and positional relationship are orientation based on the figure or position
Relationship is set, the narration present invention is merely for convenience of and simplifies description, rather than the device or element of indication or suggestion meaning are necessary
It constructs and operates with specific orientation, with particular orientation, should not be understood as limiting specific protection scope of the invention.
In addition, being used for description purposes only if any term " first ", " second ", it is not understood to indicate or imply relatively heavy
The property wanted or the quantity for implicitly indicating technical characteristic." first " is defined as a result, " second " feature can be expressed or implicit include
One or more this feature, in the present description, " at least " are meant that one or more, unless otherwise clearly having
The restriction of body.
In the present invention, except as otherwise clear stipulaties and restriction, should make if any term " assembling ", " connected ", " connection " term
Broad sense goes to understand, for example, it may be being fixedly connected, may be a detachable connection, or be integrally connected；It is also possible to mechanical connect
It connects；It can be directly connected, be also possible to be connected by intermediary, can be and be connected inside two elements.For ability
For the those of ordinary skill of domain, the concrete meaning of above-mentioned term in the present invention can be understood as the case may be.
In invention, unless otherwise specified and limited, fisrt feature second feature "upper" or "lower" may include
First and second features directly contact, also may include fisrt feature and second feature be not direct contact but by them it
Between other characterisation contact.Moreover, fisrt feature second feature " on ", " under " and " above " include fisrt feature
Right above two features and oblique upper, or be only to indicate that first feature horizontal height is higher than the height of second feature.Fisrt feature
Second feature " on ", " under " and " below " include that fisrt feature is directly under or diagonally below the second feature, or only table
Show first feature horizontal height lower than second feature.
Below with reference to the attached drawing of specification, a specific embodiment of the invention is further described, is made of the invention
Technical solution and its benefits are clearer.It describes embodiment below with reference to attached drawing to be exemplary, it is intended to solve
The present invention is released, and is not considered as limiting the invention.
Embodiment one
As shown in Figure 1, a kind of high brightness imitates gold stamping aluminized paper label manufacturing process, which comprises the following steps:
1) it embosses, scheduled lines is suppressed on high brightness aluminized paper.
2) break and open, by setting specification, the high brightness aluminized paper after embossing is divided into and is opened.
3) overlap, the high brightness after removal disconnected are aluminized the burr of paper edge.
4) it prints, gold ink is printed on high brightness aluminized paper and forms imitative bronzing effect.
5) paper, neat paper, cut paper, punch die are selected, the high brightness aluminized paper after printing is screened, be aligned, is cut, punch die system
Shape.
6) paper, vanning, strip of paper used for sealing are tied up, gold stamping aluminized paper is imitated to obtained high brightness and bundled, encapsulate.
Wherein, the gold ink is made of following raw material by mass parts: remove light dose 8.00 parts, 0.80 part of golden red ink,
2.00 parts of transparent yellow ink.Ink density value after the gold ink printing is controlled 1.5 ± 0.1.
The bloom effect of the high brightness aluminized paper is formed by coating coating resin, and following step is specifically included
It is rapid: 1) to be molded, suppress to obtain paper product in moulding press upper mold；2) rewinding carries out product examine on rewinding machine, such as to cut, then exist
Carving knife is added on rewinding machine；3) compound, it is on compounding machine that paper is compound with transfer membrane；4) it removes, will be turned by stripping machine
It moves film and paper is removed, be transferred to the hologram image on transfer membrane on paper；5) it dries；6) it aluminizes, to the paper of drying
It aluminizes, aluminized paper is made；7) face painting/back applies, and generates bloom effect in the front and back coating coating resin of aluminized paper；
The coating resin by mass percentage, is made of following raw material: acrylic resin: leveling auxiliary agent: antifoam additives: wetting agent:
Hinge agent: preservative: water=24%:0.3%:0.3%:0.2%:0.5%:0.2%:74.5%.8) it gets damp again, to being coated with
The aluminized paper of material resin gets damp again, it is made to restore moisture；9) it is put in storage.
Using high brightness aluminized paper made from the above method, surface very gloss, brightness promotes 50% on year-on-year basis, does not influence oil
The wearability of layer of ink soaked do not fall off, is wrinkle resistant etc.；Paper surface shrinkage stress is effectively reduced simultaneously, makes becoming for deformation of products
Gesture decline, reduces deformation of products probability.In terms of heatproof: paper toasts 5 minutes, 105 degree of temperature, does not occur the hair that obviously whitens
Coloured silk, gloss is still more bright-coloured, year-on-year plain paper, promotes 200% temperature tolerance, reduces ambient temperature effect.At alkaline-resisting aspect: resistance to
Ammonia alkali test is greater than 30 minutes without nigrescence, and year-on-year plain paper promotes 50% alkaline resistance properties.In terms of moisture-proof: humidity 75% is placed,
Paper is not easy to deform or mouldy, and water curling is greater than 20 seconds, promotes sheet stabilizers.
Compared with prior art, a kind of high brightness provided in this embodiment imitates gold stamping paper label of aluminizing, and saves gold stamping link,
Cost is reduced, realizes integrated molding.Meanwhile can print in batches, performance advantage effect is prominent, belongs in label industry advanced
Technology requires height to coating, a variety of printings cooperation, and hardly possible is imitated, plays certain anti-fake effect.
Embodiment two
A kind of high brightness provided in this embodiment imitates gold stamping aluminized paper label manufacturing process, manufacturing step and embodiment one
Almost the same, difference is,
One, the bloom effect of the high brightness aluminized paper be using PET/BOPP film as transfer vector, it is enterprising in aluminized paper
The straight plating method of row or BOPP move what plating method was formed.
Two, the gold ink by weight, is made of following raw material: remove light dose 10 parts, it is 1 part of golden red ink, transparent
5 parts of yellow ink.The coating resin is prepared from the following raw materials by mass percentage: acrylic resin 20%, leveling auxiliary agent
0.1%, antifoam additives 0.3%, wetting agent 0.2%, hinge agent 0.4%, preservative 1%, water 70-78%.
Embodiment three
A kind of high brightness provided in this embodiment imitates gold stamping aluminized paper label manufacturing process, manufacturing step and embodiment one
Almost the same, difference is；
The gold ink by weight, is made of following raw material: remove light dose 5 parts, 0.5 part of golden red ink, and transparent yellow
1 part of ink.The coating resin is prepared from the following raw materials by mass percentage: acrylic resin 30%, leveling auxiliary agent 0.6%,
Antifoam additives 0.9%, wetting agent 0.3%, hinge agent 0.1%, preservative 0.2%, water 78%.
From the foregoing description of structures and principles it should be understood by those skilled in the art that, the present invention not office
It is limited to above-mentioned specific embodiment, this hair is all fallen within using the improvement of techniques well known and substitution on the basis of the present invention
Bright protection scope, protection scope of the present invention should limit it by each claim and its equivalent.In specific embodiment
The part not illustrated is the prior art or common knowledge.
Claims (8)
1. a kind of high brightness imitates gold stamping aluminized paper label manufacturing process, which comprises the following steps:
1) it embosses, scheduled lines is suppressed on high brightness aluminized paper；
2) break and open, by setting specification, the high brightness aluminized paper after embossing is divided into and is opened；
3) overlap, the high brightness after removal disconnected are aluminized the burr of paper edge；
4) it prints, gold ink is printed on high brightness aluminized paper and forms imitative bronzing effect.
2. a kind of high brightness according to claim 1 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that the gold
Color ink by weight, is made of following raw material: removing light dose 5-10 parts, 0.5-1 parts of golden red ink, transparent yellow ink 1-5 parts.
3. a kind of high brightness according to claim 1 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that the gold
Ink density value after color ink printing is controlled 1.5 ± 0.1.
4. a kind of high brightness according to claim 1 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that the height
The bloom effect of brightness aluminized paper is formed by coating coating resin.
5. a kind of high brightness according to claim 1 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that the height
The bloom effect of brightness aluminized paper is to carry out straight plating method on aluminized paper using PET/BOPP film as transfer vector or BOPP is moved
What plating method was formed.
6. a kind of high brightness according to claim 1 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that the height
Brightness aluminized paper is fabricated through following steps:
1) it is molded, suppresses to obtain paper product in moulding press upper mold；
2) rewinding carries out product examine on rewinding machine, such as to cut, then carving knife is added on rewinding machine；
3) compound, it is on compounding machine that paper is compound with transfer membrane；
4) it removes, transfer membrane and paper is removed by stripping machine, are transferred to the hologram image on transfer membrane on paper；
5) it dries；
6) it aluminizes, aluminizes to the paper of drying, aluminized paper is made；
7) face painting/back applies, and generates bloom effect in the front and back coating coating resin of aluminized paper；
8) it gets damp again, gets damp again to the aluminized paper for being coated with coating resin, it is made to restore moisture；
9) it is put in storage.
7. a kind of high brightness according to claim 6 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that the painting
Material resin is prepared from the following raw materials by mass percentage: acrylic resin 20-30%, leveling auxiliary agent 0.1-1%, antifoam additives
0.1-1%, wetting agent 0.1-1%, hinge agent 0.1-1%, preservative 0.1-1%, water 70-78%.
8. a kind of high brightness according to claim 1 imitates gold stamping aluminized paper label manufacturing process, which is characterized in that described
It is further comprising the steps of after print steps: paper-neat paper-cut paper-punch die-being selected to tie up paper-vanning-strip of paper used for sealing.