CN101270557A - Method for preparing holography sputtering internal lining paper - Google Patents

Method for preparing holography sputtering internal lining paper Download PDF

Info

Publication number
CN101270557A
CN101270557A CNA2008100159031A CN200810015903A CN101270557A CN 101270557 A CN101270557 A CN 101270557A CN A2008100159031 A CNA2008100159031 A CN A2008100159031A CN 200810015903 A CN200810015903 A CN 200810015903A CN 101270557 A CN101270557 A CN 101270557A
Authority
CN
China
Prior art keywords
paper
film
lining paper
coated
holography
Prior art date
Application number
CNA2008100159031A
Other languages
Chinese (zh)
Inventor
郑迪生
Original Assignee
博源科技材料(烟台)有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 博源科技材料(烟台)有限公司 filed Critical 博源科技材料(烟台)有限公司
Priority to CNA2008100159031A priority Critical patent/CN101270557A/en
Publication of CN101270557A publication Critical patent/CN101270557A/en

Abstract

The invention relates to a manufacture method for holographic direct plating lining paper which belongs to the technical field of an aluminum-plated paper manufacture method. The working procedures include: (1) providing a film; (2) carrying out laser holographic contour forging treatment on the film; (3) coating a layer of compound glue dope on the surface of the film with the holographic layer and then compounding with a lining paper base; (4) peeling off the film to obtain the paper base with holographic information and meeting the water requirements of aluminum plating; (5) plating aluminum on the coat of the paper base; (6) subsequent treatment of aluminum plating; core: compounding the coat printed with a holographic pattern on the paper base to replace the spreading pre-treatment on the paper base and directly carrying out vacuum aluminum plating on the surface of a dope layer. The invention has the effects that: 1, the quality of the holographic lining paper is high and completely removes various defects of the lining paper manufactured by a common direct plating method; 2 the technique step is simple; besides, as a BOPP film can be repeatedly used, the cost can be reduced, thus being suitable for batch manufacture; 3, compared with the common direct plating lining paper, the holographic pattern is added, thus being beneficial to anti-fake of the product and improving the grade of the product.

Description

A kind of preparation method of holography sputtering internal lining paper

One, affiliated technical field

The present invention relates to a kind of preparation method of vacuum aluminum-coated interior lining paper, especially a kind of preparation method of holography sputtering internal lining paper belongs to the Preparation Method technical field made of paper of aluminizing.

Two, background technology

Vacuum aluminium-plated paper can be divided into vacuum aluminum-coated interior lining paper and vacuum aluminum-coated wrapping paper by specification or purposes.Lining paper can be by direct vacuum aluminum-coated method and transfer or the vacuum aluminum-coated acquisition of radium-shine transfer in vacuum aluminum-coated.

Direct vacuum aluminum-coated method technology is fairly simple, carry out vacuum aluminum-coated and face aluminising protective layer and get final product after the paper base material surface coated aluminium lamination, so product cost is lower.Its shortcoming is that product surface poor flatness, brightness are not high, and defectives such as the crude porous of paper can not effectively be covered.

Shifting vacuum aluminum-coated method is to carry out gluing and compound with paper base material after placing vacuum aluminum-coated machine to aluminize the PET film, film is peeled off again, and the aluminium molecular layer is transferred to method on the paper base material by adhesive action.Therefore the vacuum aluminum-coated interior lining paper benefit of transfer method production is a lot, but technological process is long, and technology is complicated, and cost is higher.

Three, summary of the invention

The objective of the invention is to: 1, solve the not high many defectives of direct vacuum aluminum-coated method product surface quality, promote product quality; 2,, reduce supplies consumption and reduce product cost by improving technology; 3,, adds hologram patterns such as false proof and product mark for the needs that adapt to product false proof promote product specification.

The preparation method of a kind of holography sputtering internal lining paper of the present invention comprises following operation:

(1) provide a kind of surface to scribble the film of separation layer;

(2) carrying out laser holographic molding on above-mentioned film handles;

(3) on having the one side of hologram layer, above-mentioned film is coated with last layer compound adhesive coating, and compound with interior lining paper paper substrate then;

(4) stripping film obtains with holographic information and the paper substrate that meets the moisture requirement of aluminizing;

(5) on the coating of gained paper substrate, aluminize;

The subsequent treatment of (6) aluminizing is promptly coated the aluminium protective finish on aluminium coated.

Described film adopts the surface to scribble the polypropylene screen (BOPP film) of separation layer;

The lining paper paper substrate is the single face art paper in described, quantitatively can determine according to product needed, as interior lining paper the 30-120 gram/square metre.

In the operation (2), described mold pressing treatment process is that laser holographic pattern is embossed on the surface that scribbles the isolation aspect of described film, it is radium raster to be replicated on the surface that scribbles the isolation aspect of described film with molding apparatus under 110 ℃-145 ℃ that mold pressing is handled, mold pressing speed be 20-50 rice/minute.

In the operation (3), adopt water base compound adhesive to make the isolation aspect and the paper substrate of the described film that has a hologram pattern compound.The solid content of described water base compound adhesive is preferably 20-60%, the dry-coated amount of described water base compound adhesive be preferably 1.5-9 gram/square metre.Preferably down to measure the viscosity of described compound adhesive be 40-150 second with examining No. 4 cups of grace at 25 ℃.With the oven dry of gained paper substrate, bake out temperature is preferably 80-120 ℃ after compound.Recombination velocity be 80-110 rice/minute.

In the operation (4), peeling rate be preferably 120-180 rice/minute.

In the operation (5), preferably be not less than 4.0 * 10 with vacuum aluminum-coated machine -4Under the vacuum of milli handkerchief the aluminium atom of high temperature melting evaporation evenly is sprayed on the dry paper substrate coating after peeling off and forms aluminium coated.The preferred speed of service of vacuum aluminum-coated machine is the 3-10 meter per second.

In the operation (6), protection layer for paint is to be applicable to the coating that can shield or desired any coating painted and printing.

The preparation method of holography sputtering internal lining paper of the present invention both had been different from ordinary straight and had connect vacuum aluminum-coated method and the vacuum aluminum-coated method of common transfer, was different from the vacuum aluminum-coated method of radium-shine transfer again, was a kind of brand-new process.

The core of the inventive method is: the coating that will be printed on hologram pattern is compound to the coating preliminary treatment that replaces on the paper substrate paper substrate, directly carries out vacuum aluminum-coated on coat side.

Use the beneficial effect of holographic direct vacuum aluminum-coated method to be:

1, the holographic liner paper product of gained quality height has been eliminated lining paper defective in the ordinary straight plating method fully.

2, processing step is simple, and because the BOPP film can repeat repeatedly to use, therefore can reduce cost, and is suitable for producing in batches.

3,,, help the class of the false proof of product and lifting product owing to increased hologram pattern than lining paper in the ordinary straight plating.

Four, description of drawings

Fig. 1; Preparation method's process route view of a kind of holography sputtering internal lining paper of the present invention.

Five, the specific embodiment

Following with reference to accompanying drawing, provide the specific embodiment of the present invention, be used for formation of the present invention is further specified.

Embodiment

The preparation method of a kind of holography sputtering internal lining paper of present embodiment is that the conventional vacuum Alplate method is improved the formed new process in back with reference to figure 1, comprises following operation

Holography sputtering internal lining paper of the present invention comprises following operation:

(1) polypropylene screen (BOPP film) that provides commercially available surface to scribble separation layer;

(2) carrying out laser holographic molding on above-mentioned film handles, mold pressing procedure is that laser holographic pattern is embossed on the surface that scribbles the isolation aspect of described film, it is radium raster to be replicated on the surface that scribbles the isolation aspect of described film with molding apparatus under 110 ℃-145 ℃ that mold pressing is handled, mold pressing speed be 20-50 rice/minute;

(3) be coated with last layer compound adhesive coating on above-mentioned film has the one side of hologram layer, compound with interior lining paper paper substrate then, interior lining paper paper substrate is the single face art paper, quantitatively can determine according to product needed, as interior lining paper the 30-120 gram/square metre; Make the isolation aspect and the paper substrate of the described film that has a hologram pattern compound with water base compound adhesive, recombination velocity be 80-110 rice/minute; The solid content of water base compound adhesive is 20-60%, the dry-coated amount of water base compound adhesive be 1.5-9 gram/square metre, to measure the viscosity of described compound adhesive be 40-150 second with examining No. 4 cups of grace down at 25 ℃, compound after with the oven dry of gained paper substrate, bake out temperature is 80-120 ℃;

(4) stripping film, peeling rate be 120-180 rice/minute, obtain with holographic information and meet the paper substrate of the moisture requirement of aluminizing;

(5) on the coating of gained paper substrate, aluminize, be not less than 4.0 * 10 with vacuum aluminum-coated machine -4Under the vacuum of milli handkerchief the aluminium atom of high temperature melting evaporation evenly is sprayed on the dry paper substrate coating after peeling off and forms aluminium coated, the speed of service of vacuum aluminum-coated machine is the 3-10 meter per second;

The subsequent treatment of (6) aluminizing is promptly coated the aluminium protective finish on aluminium coated, protection layer for paint is to be applicable to the coating that can shield or desired any coating painted and printing.

The forming process of holographic information image of the present invention on film is as follows:

Moulding replication is last procedure that forms embossed hologram, its technical process is: holographic metal matrix is heated to certain temperature, impress on thermoplastic with certain pressure, like this, just the meticulous embossment striped on the holographic metal matrix has been transferred to the surface of thermoplastic, typing to be cooled and after separating, just formed on the surface of thermoplastic with holographic metal form on identical striped, Here it is duplicated holographic moulding pattern.

For the hologram image that makes impression is convenient to look around under white light, on the PET film behind the good rainbow holography of impression, plate the layer of aluminum film again and constitute the reflecting layer, utilize aluminium can produce motley hologram image, reflective holographic information that Here it is to the reflection of light effect.

More popular theory, required information pattern is being burnt to the smooth transparent membrane surface of one deck exactly, and this transparent membrane can temperature distortion, carry information needed with the metal pattern carving, be impressed on the appointment film after being heated to uniform temperature, not obvious because hyaline membrane is observed, so plate the layer of aluminum film on the film surface, play the effect of a minute surface reflection, observation just presents motley visual effect under white light.

From above narration as can be known, the preparation method of this holography sputtering internal lining paper, core is: the coating that will be printed on hologram pattern is compound to the coating preliminary treatment that replaces on the paper substrate paper substrate, on coat side, directly carry out vacuum aluminum-coated, it both had been different from ordinary straight and had connect vacuum aluminum-coated method and the vacuum aluminum-coated method of common transfer, being different from again the vacuum aluminum-coated method of radium-shine transfer, is a kind of brand-new process, uses the beneficial effect of the direct vacuum aluminum-coated method of this holography to be:

1, the holographic internal lining paper product quality of gained height has been eliminated lacking of ordinary straight plating method internal lining paper fully Fall into.

2, processing step is simple, and because the BOPP film can repeatedly use, therefore can fall Low cost is suitable for batch production.

3, than ordinary straight plating internal lining paper, owing to increased hologram pattern, be conducive to the anti-of product The class of puppet and improving product.

Claims (7)

1, a kind of preparation method of holography sputtering internal lining paper is characterized in that comprising following operation:
(1) provide the surface to scribble the film of separation layer;
(2) carrying out laser holographic molding on above-mentioned film handles;
(3) on having the one side of hologram layer, above-mentioned film is coated with last layer compound adhesive coating, and compound with interior lining paper paper substrate then;
(4) stripping film obtains with holographic information and the paper substrate that meets the moisture requirement of aluminizing;
(5) on the coating of gained paper substrate, aluminize;
The subsequent treatment of (6) aluminizing is promptly coated the aluminium protective finish on aluminium coated.
2, a kind of preparation method of holography sputtering internal lining paper according to claim 1 is characterized in that:
In the operation (1), film adopts the surface to scribble the polypropylene screen of separation layer.
3, a kind of preparation method of holography sputtering internal lining paper according to claim 1 is characterized in that:
In the operation (2), described mold pressing treatment process is that laser holographic pattern is embossed on the surface that scribbles the isolation aspect of described film, it is radium raster to be replicated on the surface that scribbles the isolation aspect of described film with molding apparatus under 110 ℃-145 ℃ that mold pressing is handled, mold pressing speed be 20-50 rice/minute.
4, a kind of preparation method of holography sputtering internal lining paper according to claim 1 is characterized in that:
In the operation (3), the lining paper paper substrate is the single face art paper in described, quantitatively can determine according to product needed, as interior lining paper 30-120 gram/square metre, make the isolation aspect and the paper substrate of the described film that has a hologram pattern compound with water base compound adhesive, down to measure the viscosity of water base compound adhesive be 40-150 second with examining No. 4 cups of grace at 25 ℃, the solid content of water base compound adhesive is 20-60%, the dry-coated amount of water base compound adhesive be 1.5-9 gram/square metre, after compound the gained paper substrate is dried, bake out temperature is 80-120 ℃, recombination velocity be 80-110 rice/minute.
5, a kind of preparation method of holography sputtering internal lining paper according to claim 1 is characterized in that:
In the operation (4), peeling rate be 120-180 rice/minute.
6, a kind of preparation method of holography sputtering internal lining paper according to claim 1 is characterized in that:
In the operation (5), vacuum aluminum-coated machine is being not less than 4.0 * 10 -4Under the vacuum of milli handkerchief the aluminium atom of high temperature melting evaporation evenly is sprayed on the dry paper substrate coating after peeling off and forms aluminium coated, the speed of service of vacuum aluminum-coated machine is the 3-10 meter per second.
7, a kind of preparation method of holography sputtering internal lining paper according to claim 1 is characterized in that:
In the operation (6), protection layer for paint is to be applicable to the coating that can shield or desired any coating painted and printing.
CNA2008100159031A 2008-04-22 2008-04-22 Method for preparing holography sputtering internal lining paper CN101270557A (en)