CN103088716A - Production technology of logical positioning laser transfer paper - Google Patents

Production technology of logical positioning laser transfer paper Download PDF

Info

Publication number
CN103088716A
CN103088716A CN 201210564980 CN201210564980A CN103088716A CN 103088716 A CN103088716 A CN 103088716A CN 201210564980 CN201210564980 CN 201210564980 CN 201210564980 A CN201210564980 A CN 201210564980A CN 103088716 A CN103088716 A CN 103088716A
Authority
CN
Grant status
Application
Patent type
Prior art keywords
technology
logical
transfer
production
positioning
Prior art date
Application number
CN 201210564980
Other languages
Chinese (zh)
Inventor
赵春光
熊建华
方建明
Original Assignee
绍兴京华激光材料科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

The invention discloses a production technology of logical positioning laser transfer paper. At present, a secondary printing protective layer is adopted for logical positioning transfer, aluminum washing and gold stamping treatment are carried out, and the work time is complicated and simple; moreover, because of the technical technology, logical transfer aluminized patterns and words usually have the quality defects that the edges of the patterns and words are rough or disconnected. The production technology comprises the following steps of film coating, seamless molding, vacuum aluminum plating, gravure electric roller making, positioning and gluing compounding of logical patterns or words, and peeling. The film is directly glued and compounded logically through the electric roller, so that the production technology is short in work time, low in cost, environment-friendly and safe; and the edges of the patterns and words after being transferred are prevented from being rough, so that the product quality is refined.

Description

ー种局部定位镭射转移纸的生产エ艺ー kinds of local positioning laser transfer paper production Ester Arts

技术领域 FIELD

[0001] 本发明涉及应用于香烟包装盒、酒类及高档礼品纸的印刷包装技术领域,具体地说是ー种局部定位错射转移纸的生产エ艺。 [0001] The present invention relates to printing packaging technology applied to cigarette pack, gift paper and high-grade alcohol, specifically ー wrong kind of localizing production of the transfer paper exit Ester arts.

背景技术 Background technique

[0002] 真空镀铝纸是20世纪70年后期开始应用于标签和装饰礼品包装上。 [0002] Vacuum Metallized paper in the late 1970s began to be used on the label and decorative gift wrap. 在90年代后期,才以其环保产品的良好形象及成熟的加工设备和エ艺风靡于欧美市场,随后登陆我国市场。 In the late 1990s, only a good image for its environmentally friendly products and sophisticated processing equipment and Ester arts popular in European and American markets, followed by the landing of China's market. 由于它具有高贵美观的金属质感,与同类产品相比较为低廉的价格成本,稳定可靠的印刷性能,良好的防潮、保湿性能,以及可降解、可回收的环保性能,越来越受到印刷和包装业的喜爱,应用范围越来越广。 Because of its noble metal texture in appearance, relatively low cost price compared with similar products, reliable printing performance, good moisture, moisturizing properties, and biodegradable, recyclable environmental performance, more and more printing and packaging favorite industry, increasingly wide range of applications. 而将纸张表面局部转移成喷铝层形成局部转移镀铝纸,这在特定方面具有更加明显的优势,如它可以作为纸张的ー种印刷方式,在白纸(板)表面一道银色印刷图案,然后进行进ー步印刷,形成印刷纸张;它也可以利用喷铝图案和白纸板之间强烈的视觉效果直接作为具有防伪功能的包装纸,另外,它也可以在某些方面取代印刷后道エ艺中的烫金工艺等等。 The partial transfer sheet and the surface layer is formed into a partial transfer of sprayed aluminum metallized paper, which has obvious advantages in more specific terms, it can serve as seed ー printing paper, white paper (sheet) surface of a printed pattern of silver, then feed ー printing step, the printing sheet is formed; it can also use a strong visual effect between the spray pattern and the aluminum directly as paperboard packaging with security features, in addition, it may be substituted after printing in some respects Ester stamping process in the arts and so on. 因此局部定位镭射转移纸产品受到了包装业的深深青睐,并与之相应提出了更加质量精细化的要求。 Therefore, local positioning laser transfer paper products have been deeply favored by the packaging industry, and with the corresponding proposed a more refined quality requirements. 现今国内外对包装产品的整饰,都是采用冷烫印刷技术,印刷完成后,离线冷烫转移。 Today at home and abroad for finishing packaging products, are based on cold-hot printing technology, printing is completed, the offline perm transfer. 离线エ艺会存在以下问题:其一、生产线繁多,生产效率低;其ニ、产品的エ序多,质量控制困难、产品消耗高,废品率高;其三、产品精度差。 Artistic offline Ester the following problems: First, many production lines, production efficiency is low; the Ni, the Eito program product, quality is difficult to control, high consumption, high rejection rate; Third, product accuracy is poor. 由于エ艺技术的原因,局部转移镀铝图案文字经常性出现图案文字边缘毛糙或断线的质量缺陷。 Since Ester reasons of process technology, local metastasis aluminum recurrent character pattern defect pattern quality text rough edges or disconnection occurs. 因此,开发一种质量更加精细化的局部定位镭射转移纸的生产エ艺方法势在必行。 Therefore, development of a method of producing mass Ester Arts more refined localizing laser transfer paper is imperative.

发明内容 SUMMARY

[0003] 本发明所要解决的技术问题是克服上述现有技术中存在的不足,提供ー种局部定位镭射转移纸的生产エ艺,以使生产出来的产品质量更加精细化。 [0003] The present invention solves the technical problem is to overcome the above-described deficiencies present in the prior art, to provide localized species ー positioned Ester laser transfer paper production arts, so that the quality of products produced more refined.

[0004] 为此,本发明采用的技术方案如下:ー种局部定位镭射转移纸的生产エ艺,其特征在于包括以下步骤: [0004] To this end, the present invention employs the following technical solution: Ester ー seed production arts localizing the laser transfer paper, characterized by comprising the steps of:

1)、薄膜涂布:将离型层转移涂料通过涂布机印刷在薄膜上,完成涂布后,通过烘箱进行一次烘干; 1), the coating film: The release coating layer is transferred on the film, after completion of the coating, once dried through an oven by applying a printing machine;

2)、无缝模压:将烘干得到的薄膜通过无缝模压机转移压印上镭射图案; 2), seamless embossing: The dried film obtained by transfer molding machine seamless embossing pattern on the CD;

3)、真空镀铝:对压印上镭射图案的薄膜用真空镀铝机进行真空镀铝或镀介质; 3), vacuum aluminum: a thin film on the embossing pattern is laser or metalised aluminum plating medium vacuum dryer;

4)、定制凹印电雕辊:根据产品图案或文字的需要,将相应的图案或文字雕在版辊上,做成局部图案或文字的网线辊(网线辊即将图案或者文字部位雕刻成网线,其它部位为光辊); 4), custom gravure electric carving roll: The required product pattern or character, the corresponding patterns or characters carved on the printing roller, made of engraved roll local patterns or characters (engraved roll is about a pattern or text portions carved into the cable other parts of calender rolls);

5)、定位上胶复合:将镀铝或镀介质得到的镭射镀铝转移膜通过电雕辊涂胶,同时与纸复合形成复合纸,并经烘箱烘干收卷; 5), positioning the composite plastic: the aluminum or aluminum plating medium laser transfer film obtained by electric carving roll coating, while forming a composite paper and paper composite, and winding the drying oven;

6)、剥离:将复合纸进行熟化处理,之后采用剥离机进行剥离,纸上面转移上相应的图案或文字的银色铝层。 6) Separation: The composite sheet for the aging treatment, after using the stripping machine peeling, the above transfer paper patterns or characters on the respective silver layer of aluminum. [0005] 本发明通过电雕辊局部定位涂胶,控制镭射镀铝转移膜与纸张局部定位复合,相对于热烫来说,其最大的优势就是投资少,无须制作昂贵的烫印版,结构简单,易于操作,性价比较高。 [0005] The present invention, by an electrical local positioning engraving roller coating, control local positioning the composite laser transfer film and aluminum sheet, blanching is with respect to its greatest advantage is low investment without making costly stamping Edition, structure simple, easy to operate, high cost performance. 所述的涂料要求可转移、剥离性好、涂层松,切边性好。 The coating requirements transferable peeling good coating loose, trimming good. 熟化处理指在放置一定时间(一般24小时)。 Aging treatment means disposed a predetermined time (typically 24 hours).

[0006] 作为优选,所述步骤I)中的薄膜为PET膜或BOPP膜。 [0006] Advantageously, the step I) of BOPP film is a PET film or a film.

[0007] 作为优选,所述的步骤I)中,涂布印刷速度为90-100 m/min,烘箱的五节温度分别为80°C、100°C、135°C、120°C和90。 [0007] Advantageously, according to step I), the coated printing speed of 90-100 m / min, temperature of the oven five sections were 80 ° C, 100 ° C, 135 ° C, 120 ° C, and 90 . . .

[0008] 作为优选,所述的步骤2)中,无缝模压时模压版辊温度在165°C -170°C,车速在30-35m/min,压辊压カ为2_3kg,使图案或文字压亮压透且涂层不粘版。 [0008] Advantageously,) in the step 2, seamless embossing plate during molding roll temperature 165 ° C -170 ° C, the speed of 30-35m / min, roll nip grades of 2_3kg, so that the pattern or text pressure and light pressure through non-stick coating Edition.

[0009] 作为优选,所述的步骤3)中,真空镀铝的真空度为5.33X10—2帕〜6.54X10—2帕,以电阻、高频或电子束加热,使铝丝加热到1400°C〜1500°C气化,使气化后的铝丝迅速蒸发、扩散并沉积到薄膜的表面上,完成薄膜镀铝的过程。 [0009] Advantageously, said step 3), the degree of vacuum of aluminum ~6.54X10-2 5.33X10-2 Pa Pa, a resistance, high frequency heating or electron beam, so that an aluminum wire was heated to 1400 ° gasification C~1500 ° C, so that the aluminum wire gasified rapidly evaporated, diffused and deposited on the surface of the film, the aluminum film through the process.

[0010] 作为优选,所述的步骤4)中,制备的网线辊网线为250-300线,线深为5_7um。 [0010] Advantageously, said step 4), the cable rollers 250-300 preparation cable lines, deep lines 5_7um.

[0011] 作为优选,所述的步骤5)中,为防止胶水蔓延,转移后出现图案文字边缘毛糙,复合所用的胶水中加入质量分数为0.5%-1%的氨水,降低粘度,胶水的涂布量在3-4g/m2。 [0011] Advantageously, 5) in the step to prevent the spread of glue, after transferring a pattern character appears rough edges, the glue used in the composite mass fraction of 0.5% to 1% aqueous ammonia, decreasing the viscosity of the glue coating cloth amount 3-4g / m2.

[0012] 作为优选,所述的步骤5)中,复合的速度为100〜120米/分钟,复合机的烘道温区控制在70〜130°C。 [0012] Advantageously, 5) in said step, the composite speed of 100~120 m / min, drying temperature in the region of the multifunction peripheral control 70~130 ° C.

[0013] 作为优选,所述的复合机有五个烘道,设置的温度均不相同,相邻ニ个温区的温差在25°C以内。 [0013] Advantageously, the composite machine has five drying tunnel, the temperature of the same are not provided, adjacent temperature zones ni temperature difference is within 25 ° C.

[0014] 作为优选,所述的步骤6)中,熟化时间为12〜24小时,熟化环境为温度250C ±5°C、湿度55% ±10%,剥离速度为200 〜300m/min。 [0014] Advantageously,) in step 6, 12~24 hours aging time, aging temperature environment 250C ± 5 ° C, humidity of 55% ± 10%, the peeling rate was 200 ~300m / min.

[0015] 本发明具有的有益效果:通过电雕辊局部对薄膜直接上胶复合,エ时短,成本低,环保安全;在复合所用的胶水中加入氨水,降低粘度,防止了胶水蔓延,避免了转移后的图案文字边缘出现毛糙,使产品质量更加精细化。 [0015] The present invention has beneficial effects: by electric carving roller partially a thin film directly on the plastic composite, Ester is shorter, low cost, environmentally safe; added ammonia glue compound employed, the lower the viscosity, to prevent the glue spread, to avoid after the transfer of the pattern of text appears rough edges, so that product quality more refined.

具体实施方式 detailed description

[0016] 下面结合具体实施方式对本发明作进ー步说明。 [0016] DETAILED DESCRIPTION The following embodiments of the present invention will be described further ー feed.

[0017] ー种局部定位镭射转移纸的生产エ艺,其步骤如下: [0017] Ester Arts Production ー localizing seed laser transfer paper, comprises the following steps:

I)、薄膜涂布:将离型层转移涂料通过涂布机印刷在薄膜上,完成涂布后,通过烘箱进行一次烘干。 The I), film coating: The paint transfer release layer, after the completion of the coating, once dried by coater printing on the film through an oven. 薄膜为PET膜,涂料要求可转移、剥离性好、涂层松,切边性好。 Film is a PET film, the coating can transfer requirements, good releasability, a coating loose, trimming good. 涂布印刷速度为90-100m/min,烘箱的五节温度分别为80、100、135、120和90°C。 Coated printing speed is 90-100m / min, temperature of the oven five sections, respectively 80,100,135,120 and 90 ° C.

[0018] 2)、无缝模压:将烘干得到的薄膜通过无缝模压机转移压印上镭射图案,无缝模压时模压版辊温度在165°C _170°C,车速在30-35m/min,压辊压カ为2_3kg。 [0018] 2), seamless embossing: The dried film obtained by the laser seamless embossing pattern transfer molding machine, a seamless molding roll embossing plate temperature 165 ° C _170 ° C, the speed of 30-35m / min, roll nip grades of 2_3kg.

[0019] 3)、真空镀铝:对压印上镭射图案的薄膜用真空镀铝机进行真空镀铝,真空度为 [0019] 3), aluminum vacuum: a thin film on the embossing pattern is laser vacuum aluminum, aluminum vacuum degree of a vacuum dryer

5.33X10—2帕〜6.54X10—2帕,以电阻、高频或电子束加热,使铝丝加热到1400°C〜1500°C气化,使气化后的铝丝迅速蒸发、扩散并沉积到薄膜的表面上。 ~6.54X10-2 5.33X10-2 Pa Pa, a resistance, high frequency heating or electron beam, so that an aluminum wire was heated to 1400 ° C~1500 ° C gasifying the aluminum wire gasified rapid evaporation, diffusion and deposition on the surface of the film.

[0020] 4)、定制凹印电雕辊:根据产品图案或文字的需要,将相应的图案或文字雕在版辊上,做成局部图案或文字的网线辊,制备的网线辊网线为250-300线,线深为6um。 [0020] 4), custom gravure electric carving roll: The required product pattern or character, the corresponding patterns or characters carved on the printing roller, made of engraved roll local patterns or characters, the engraved roll cable Preparation 250 -300 line, the line deep 6um. 网线辊即将图案或者文字部位雕刻成网线,其它部位为光辊。 Engraved roll coming into patterns or characters engraved cable portion, other parts of rolls. [0021] 5)、定位上胶复合:将镀铝好的镭射镀铝转移膜通过电雕辊涂胶,同时与纸复合形成复合纸,并经烘箱烘干收卷。 [0021] 5), the positioning adhesive composite of: aluminum roller good laser engraving transfer film aluminum coating by electroporation, while forming a composite paper and paper composite, and oven dried by rolling. 复合所用的胶水中加入质量分数为0.5%-1%的氨水,降低粘度,防止胶水蔓延,胶水的涂布量在3-4g/m2。 The glue used in the composite mass fraction of 0.5% to 1% aqueous ammonia, to reduce viscosity, to prevent the spread of glue, the glue is applied in an amount of 3-4g / m2. 复合的速度为100〜120米/分钟,复合机的烘道温区控制在70〜130°C。 Composite speed of 100~120 m / min, drying temperature in the region of the multifunction peripheral control 70~130 ° C. 所述的复合机有五个烘道,设置的温度均不相同,相邻ニ个温区的温差在25°C以内。 The composite machine has five drying tunnel, the temperature of the same are not provided, adjacent temperature zones ni temperature difference is within 25 ° C.

[0022] 6)、剥离:将复合纸进行熟化处理,之后采用剥离机进行剥离,纸上面转移上相应的图案或文字的银色铝层。 [0022] 6), peeling: aging treatment for the composite sheet, after peeling machine using the release, the above transfer paper patterns or characters on the respective silver layer of aluminum. 熟化时间为12〜24小时,熟化环境为温度25°C ±5°C、湿度55% ±10%,剥离速度为200 〜300m/min。 12~24 hours aging time, aging temperature environment 25 ° C ± 5 ° C, humidity of 55% ± 10%, the peeling rate was 200 ~300m / min.

Claims (10)

  1. 1.一种局部定位镭射转移纸的生产エ艺,其特征在于包括以下步骤: 1)、薄膜涂布:将离型层转移涂料通过涂布机印刷在薄膜上,完成涂布后,通过烘箱进行一次烘干; 2)、无缝模压:将烘干得到的薄膜通过无缝模压机转移压印上镭射图案; 3)、真空镀铝:对压印上镭射图案的薄膜用真空镀铝机进行真空镀铝或镀介质; 4)、定制凹印电雕辊:根据产品图案或文字的需要,将相应的图案或文字雕在版辊上,做成局部图案或文字的网线辊; 5)、定位上胶复合:将镀铝或镀介质得到的镭射镀铝转移膜通过电雕辊涂胶,同时与纸复合形成复合纸,并经烘箱烘干收卷; 6)、剥离:将复合纸进行熟化处理,之后采用剥离机进行剥离,纸上面转移上相应的图案或文字的银色铝层。 A local positioning Ester laser transfer paper production arts, characterized by comprising the following steps: 1), the coating film: The release layer is transferred by coater coating printed on the film after coating is completed, through an oven once dried; 2), seamless embossing: the dried film obtained by the laser seamless embossing pattern transfer molding machine; 3), vacuum aluminum: film for laser imprinted pattern by a vacuum dryer aluminum aluminum or vacuum plating medium; 4), custom electric carving gravure roll: the required product patterns or characters, corresponding character pattern carved on a plate or roll, made of local patterns or characters engraved roll; 5) , the positioning adhesive composite: the aluminum or aluminum-plated transfer film laser medium obtained by an electric carving roll coating, while forming a composite paper and paper composite, and winding the drying oven; 6), peeling: a composite paper subjected to aging treatment, after the peeling using the peeling machine, the above transfer paper patterns or characters on the respective silver layer of aluminum.
  2. 2.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述步骤I)中的薄膜为PET膜或BOPP膜。 Claim 2. localizing laser transfer paper production arts Ester claim 1, wherein said step I) in a thin film or a PET film BOPP film.
  3. 3.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述的步骤1)中,涂布印刷速度为90-100m/min,烘箱的五节温度分别为80°C、100°C、135°C、120°C和90。 3. claimed in claim localizing laser transfer paper production arts Ester claim 1, wherein said step 1), the coated printing speed is 90-100m / min, temperature of the oven five sections were 80 ° C, 100 ° C, 135 ° C, 120 ° C, and 90. . .
  4. 4.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述的步骤2)中,无缝模压时模压版辊温度在165°C _170°C,车速在30-35m/min,压辊压カ为2_3kg,使图案或文字压亮压透且涂层不粘版。 4. A laser according to claim localizing production Ester arts transfer paper of claim 1, wherein,) in the step 2, seamless molded printing roller during molding temperature 165 ° C _170 ° C, the vehicle speed 30 -35m / min, roll nip grades of 2_3kg, so that the pattern or text pressure nonstick coating and light-permeable pressure plate.
  5. 5.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述的步骤3)中,真空镀铝的真空度为5.33 X 10_2帕〜6.54 X 10_2帕,以电阻、高频或电子束加热,使铝丝加热到1400°C〜1500°C气化,使气化后的铝丝迅速蒸发、扩散并沉积到薄膜的表面上,完成薄膜镀铝的过程。 Ester according to claim 5 Arts Production localizing laser transfer paper of claim 1, wherein, in the step 3), the degree of vacuum of 5.33 X 10_2 aluminum ~6.54 X 10_2 Pa Pa, resistance to , high frequency heating or electron beam, so that an aluminum wire was heated to 1400 ° C~1500 ° C gasifying the aluminum wire gasified rapidly evaporated, diffused and deposited on the surface of the film, the aluminum film through the process.
  6. 6.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述的步骤4)中,制备的网线辊网线为250-300线,线深为5-7um。 6. claim localizing laser transfer paper production arts Ester claim 1, wherein,) in the step 4, anilox rollers 250-300 preparation cable lines, deep lines 5-7um.
  7. 7.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述的步骤5)中,复合所用的胶水中加入质量分数为0.5%-1%的氨水,胶水的涂布量在3-4g/m2。 Ester according to claim 7 Arts Production localizing laser transfer paper according to claim 1, wherein said step of glue 5), the compound used in the mass fraction of 0.5% to 1% aqueous ammonia, glue application amount 3-4g / m2.
  8. 8.按权利要求1所述的局部定位镭射转移纸的生产エ艺,其特征在于,所述的步骤5)中,复合的速度为100〜120米/分钟,复合机的烘道温区控制在70〜130°C。 8. A laser according to claim localizing production Ester arts transfer paper of claim 1, wherein said step 5), the composite speed of 100~120 m / min, drying temperature control zone copier at 70~130 ° C.
  9. 9.按权利要求8所述的局部定位镭射转移纸的生产エ艺,其特征在干,所述的复合机有五个烘道,设置的温度均不相同,相邻ニ个温区的温差在25°C以内。 9. The temperature difference according to claim localizing production Ester arts laser transfer paper according to claim 8, characterized in that the dry, the multifunction peripheral has five drying tunnel, are not the same set temperature, temperature zones of the adjacent Ni within 25 ° C.
  10. 10.按权利要求1所述的局部转移镀铝纸的生产エ艺,其特征在于,所述的步骤6)中,熟化时间为12〜24小时,熟化环境为温度25°C ±5°C、湿度55% ±10%,剥离速度为.200 〜300m/mino 10. The production according to claim 1, said partial transfer of Ester Art Metallized paper, wherein said step 6), the curing time is 12~24 hours aging ambient temperature 25 ° C ± 5 ° C humidity 55% ± 10%, the release rate of .200 ~300m / mino
CN 201210564980 2012-12-24 2012-12-24 Production technology of logical positioning laser transfer paper CN103088716A (en)