CN104562855A - Production process with local pattern vacuum aluminum plating and lasering multiple anti-counterfeiting lining paper for cigarettes - Google Patents

Production process with local pattern vacuum aluminum plating and lasering multiple anti-counterfeiting lining paper for cigarettes Download PDF

Info

Publication number
CN104562855A
CN104562855A CN201510012328.XA CN201510012328A CN104562855A CN 104562855 A CN104562855 A CN 104562855A CN 201510012328 A CN201510012328 A CN 201510012328A CN 104562855 A CN104562855 A CN 104562855A
Authority
CN
China
Prior art keywords
release layer
laser
lining paper
vacuum aluminum
paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510012328.XA
Other languages
Chinese (zh)
Inventor
王正国
黄群
杨峰
郁建松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI JINYE PACKING MATERIAL CO Ltd
Original Assignee
SHANGHAI JINYE PACKING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI JINYE PACKING MATERIAL CO Ltd filed Critical SHANGHAI JINYE PACKING MATERIAL CO Ltd
Priority to CN201510012328.XA priority Critical patent/CN104562855A/en
Publication of CN104562855A publication Critical patent/CN104562855A/en
Pending legal-status Critical Current

Abstract

The invention discloses a production process of local pattern vacuum aluminum plating and lasering multiple anti-counterfeiting lining paper for cigarettes. The process is characterized in that a release layer of the lining paper for cigarettes prepared by virtue of a process technology of laser information overlaid with silicon oil patterns has multiple-anti-counterfeiting performance after vacuum aluminum plating. The production process comprises the following steps: preparing the release layer; pressing laser mould; printing the silicon oil patterns; carrying out vacuum aluminum plating; compounding paper; and peeling a thin film. Compared with the prior art, the production process disclosed by the invention has the advantages that multiple-anti-counterfeiting performance is achieved, so that the a similar vivid dynamic effect cannot be simulated through a common printing process after the laser effect on the surface of paper and the effect of the local patterns subjected to vacuum aluminum plating are overlaid, so that the copying difficulty is greatly increased, the anti-counterfeiting grade is obviously improved, and moreover, the manufacturing process is simple and convenient to operate. The content of volatile organic compounds (VOCs) of the product meets the tobacco industrial standard YC264-2008.

Description

The production technology of local pattern vacuum aluminium coating laser multiple anti-fake cigarette lining paper
Technical field
The present invention relates to cigarette package paper technical field, specifically a kind of production technology of local pattern vacuum aluminium coating laser multiple anti-fake cigarette lining paper.
Background technology
At present, domestic composite aluminium foil paper, straight plating or transfer aluminum plated paper, surface printing or colouring lining paper and the aluminizing laser paper of generally all adopting is as tobacco lining paper.Composite aluminium foil paper manufacture craft is simple, and the thick aluminum foil compound of paper and 6 ~ 7 μ is without antifalsification, but the non-environmental protection of product; Straight plating or transfer aluminum plated paper technique more complicated, need to be coated with, aluminize, the production process such as compound, few by aluminum amount, but without antifalsification, product environmental protection; Surface printing or colouring lining paper need printing word, pattern or various color and luster coating on the surface, and production technology is general, but without antifalsification, product environmental protection; The production processes such as aluminizing laser paper needs coating, molding laser, aluminizes, compound, complex process, need make false proof mother matrix, have antifalsification but more single, product environmental protection.
Prior art Problems existing is: antifalse effect is poor, and manufacture craft is single, easily copies, and especially some material environment friendly performance is low, and volatile organic matter total amount (VOCs) can not meet YC264-2008 tobacco business standard.
Summary of the invention
The object of the invention is the production technology of a kind of local pattern vacuum aluminium coating laser multiple anti-fake cigarette lining paper designed for the deficiencies in the prior art, adopt the vacuum aluminum-coated technology of molding laser information superposition silicone oil pattern, make paper surface laser effect and local pattern vacuum aluminum-coated go out effect superpose after cannot imitate out same dynamic effect true to nature by ordinary printing process, cigarette lining paper has multiple anti-fake performance, considerably increase imitated difficulty, false proof grade significantly improves, and manufacture craft is simple, easy to operate, the volatile organic matter total amount (VOCs) of product meets YC264-2008 tobacco business standard.
The technical scheme realizing the object of the invention is: a kind of production technology of local pattern vacuum aluminium coating laser multiple anti-fake cigarette lining paper, comprise release layer and vacuum aluminum-coated, be characterized in release layer prepared by cigarette lining paper employing laser information superposition silicone oil pattern process technology, after vacuum aluminum-coated, have multiple anti-fake performance, its production technology comprises the following steps:
Prepared by a, release layer
On polyester (BOPET) or polypropylene (BOPP) film, the dry moisture of coating is the mould release of 1.3 ± 0.5g/ ㎡, and mould release is on film, form release layer after 100 ~ 130 DEG C of dryings through temperature; Described coating, the dry speed of a motor vehicle are 120 ± 10m/mm.
B, laser molding
Nickel matter mold pressing roll making and has word, figure or its laser information combined, is then that laser information is transferred to above-mentioned release layer by the mold pressing roll of 170 ~ 185 DEG C by temperature.
C, silicone oil graphic-print
Adopt laser engraving to make and have word, figure or its resin pressure roller combined, the silicone oil of cable roll transmission is printed on above-mentioned on the release layer of laser molding by resin pressure roller, forms word, figure or its silicone oil pattern combined.
D, vacuum aluminum-coated
On the above-mentioned release layer being printed on silicone oil pattern, vacuum evaporating thickness is the aluminium lamination of 380, and the vacuum of described spraying plating is 4 × 10 -4mbar.
E, paper compound
Adopt water-based glue and cigarette lining paper to carry out wet type compound the film of above-mentioned spraying plating aluminium lamination, after compound, at 100 ~ 120 DEG C of temperature, carry out drying; Described compound, the dry speed of a motor vehicle are 150 ± 10m/mm.
F, film are peeled off
By after above-mentioned joint product stripping film for having the cigarette lining paper of multiple anti-fake, cut finished product after being then coated with the gloss oil of different color and luster.
The present invention compared with prior art has multiple anti-fake performance, make paper surface laser effect and local pattern vacuum aluminum-coated go out effect superpose after cannot imitate out same dynamic effect true to nature by ordinary printing process, considerably increase imitated difficulty, false proof grade significantly improves, and manufacture craft is simple, easy to operate, the volatile organic matter total amount (VOCs) of product meets YC264-2008 tobacco business standard.
Accompanying drawing explanation
Fig. 1 is production procedure schematic diagram of the present invention.
Detailed description of the invention
Accompanying drawings 1, the release layer that the present invention adopts laser information superposition silicone oil pattern process to prepare at cigarette lining paper, produce the dynamic effect that superposes with local pattern of laser effect with multiple anti-fake performance, concrete production technology comprises: release layer preparation, laser molding, silicone oil graphic-print, vacuum aluminum-coated, paper compound and film stripping process.
Below will the present invention is further elaborated by specific embodiment:
Embodiment 1
Prepared by a, release layer
On polyester (BOPET) film, the dry moisture of coating is the mould release of 1.3 ± 0.5g/ ㎡, and mould release is on film, form release layer after 120 DEG C of dryings through temperature; Described coating, the dry speed of a motor vehicle are 120 ± 10m/mm.
B, laser molding
According to the feature of different product, make personalized laser master plate, make laser information be transferred to table release layer by mother matrix.Nickel matter mold pressing roll makes and has word, figure or its laser information combined, surface effect light or dumb light, making laser light information diffraction strong, is then that laser information is transferred to above-mentioned release layer by the mold pressing roll of 175 DEG C by temperature.
C, silicone oil graphic-print
Can notify that the form laser engraving of word or word and combinations of patterns is in resin roll, the pattern in resin roll or word are indent, all the other position evaginations.The silicone oil of cable roll transmission is printed on the release layer of laser molding by resin pressure roller, forms word, figure or its silicone oil pattern combined.
D, vacuum aluminum-coated
On the above-mentioned release layer being printed on silicone oil pattern, vacuum evaporating thickness is the aluminium lamination of 380, and the vacuum of described spraying plating is 4 × 10 -4mbar, due to the silicone oil pattern conductively-closed when aluminizing on release layer, aluminium lamination can not plate, and forms so-called pattern or word.
E, paper compound
Adopt water-based glue and cigarette lining paper to carry out wet type compound the film of above-mentioned spraying plating aluminium lamination, after compound, at 110 DEG C of temperature, carry out drying; Described compound, the dry speed of a motor vehicle are 150 ± 10m/mm.
F, film are peeled off
By after above-mentioned joint product stripping film for having the cigarette lining paper of multiple anti-fake, cut finished product after being then coated with gloss oil rosy.
Embodiment 2
Prepared by a, release layer
On polypropylene (BOPP) film, the dry moisture of coating is the mould release of 1.3 ± 0.5g/ ㎡, and mould release is on film, form release layer after 130 DEG C of dryings through temperature; Described coating, the dry speed of a motor vehicle are 120 ± 10m/mm.
B, laser molding
According to the feature of different product, make personalized laser master plate, make laser information be transferred to table release layer by mother matrix.Nickel matter mold pressing roll makes and has word, figure or its laser information combined, surface effect light or dumb light, making laser light information diffraction strong, is then that laser information is transferred to above-mentioned release layer by the mold pressing roll of 185 DEG C by temperature.
C, silicone oil graphic-print
Can notify that the form laser engraving of word or word and combinations of patterns is in resin roll, the pattern in resin roll or word are indent, all the other position evaginations.The silicone oil of cable roll transmission is printed on the release layer of laser molding by resin pressure roller, forms word, figure or its silicone oil pattern combined.
D, vacuum aluminum-coated
On the above-mentioned release layer being printed on silicone oil pattern, vacuum evaporating thickness is the aluminium lamination of 380, and the vacuum of described spraying plating is 4 × 10 -4mbar, due to the silicone oil pattern conductively-closed when aluminizing on release layer, aluminium lamination can not plate, and forms so-called pattern or word.
E, paper compound
Adopt water-based glue and cigarette lining paper to carry out wet type compound the film of above-mentioned spraying plating aluminium lamination, after compound, at 120 DEG C of temperature, carry out drying; Described compound, the dry speed of a motor vehicle are 150 ± 10m/mm.
F, film are peeled off
By after above-mentioned joint product stripping film for having the cigarette lining paper of multiple anti-fake, cut finished product after being then coated with golden gloss oil.
More than just the present invention is further illustrated, and be not used to limit this patent, allly implements for the present invention's equivalence, within the right that all should be contained in this patent.

Claims (1)

1. the production technology of a local pattern vacuum aluminium coating laser multiple anti-fake cigarette lining paper, comprise release layer and vacuum aluminum-coated, it is characterized in that release layer prepared by cigarette lining paper employing laser information superposition silicone oil patterning technique, after vacuum aluminum-coated, have multiple anti-fake performance, its production technology comprises the following steps:
Prepared by a, release layer
On polyester (BOPET) or polypropylene (BOPP) film, the dry moisture of coating is the mould release of 1.3 ± 0.5g/ ㎡, and mould release is on film, form release layer after 100 ~ 130 DEG C of dryings through temperature; Described coating, the dry speed of a motor vehicle are 120 ± 10m/mm;
B, laser molding
Nickel matter mold pressing roll making and has word, figure or its laser information combined, is then that laser information is transferred to above-mentioned release layer by the mold pressing roll of 170 ~ 185 DEG C by temperature;
C, silicone oil graphic-print
Adopt laser engraving to make and have word, figure or its resin pressure roller combined, the silicone oil of cable roll transmission is printed on above-mentioned on the release layer of laser molding by resin pressure roller, forms word, figure or its silicone oil pattern combined;
D, vacuum aluminum-coated
On the above-mentioned release layer being printed on silicone oil pattern, vacuum evaporating thickness is the aluminium lamination of 380, and the vacuum of described spraying plating is 4 × 10 -4mbar;
E, paper compound
Adopt water-based glue and cigarette lining paper to carry out wet type compound the film of above-mentioned spraying plating aluminium lamination, after compound, at 100 ~ 120 DEG C of temperature, carry out drying; Described compound, the dry speed of a motor vehicle are 150 ± 10m/mm;
F, film are peeled off
By after above-mentioned joint product stripping film for having the cigarette lining paper of multiple anti-fake, cut finished product after being then coated with the gloss oil of different color and luster.
CN201510012328.XA 2015-01-12 2015-01-12 Production process with local pattern vacuum aluminum plating and lasering multiple anti-counterfeiting lining paper for cigarettes Pending CN104562855A (en)