CN102825697A - 聚乙烯灰色管道的加工工艺 - Google Patents

聚乙烯灰色管道的加工工艺 Download PDF

Info

Publication number
CN102825697A
CN102825697A CN2012103144941A CN201210314494A CN102825697A CN 102825697 A CN102825697 A CN 102825697A CN 2012103144941 A CN2012103144941 A CN 2012103144941A CN 201210314494 A CN201210314494 A CN 201210314494A CN 102825697 A CN102825697 A CN 102825697A
Authority
CN
China
Prior art keywords
powder
polyethylene
steel pipe
temperature
grey
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103144941A
Other languages
English (en)
Inventor
丁红女
徐律征
丁恒标
肖荣才
栾宇飞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU SHUANGDA ENGINEERING TECHNOLOGY RESEARCH CENTER Co Ltd
Original Assignee
JIANGSU SHUANGDA ENGINEERING TECHNOLOGY RESEARCH CENTER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU SHUANGDA ENGINEERING TECHNOLOGY RESEARCH CENTER Co Ltd filed Critical JIANGSU SHUANGDA ENGINEERING TECHNOLOGY RESEARCH CENTER Co Ltd
Priority to CN2012103144941A priority Critical patent/CN102825697A/zh
Publication of CN102825697A publication Critical patent/CN102825697A/zh
Pending legal-status Critical Current

Abstract

聚乙烯灰色管道的加工工艺，是将钢管内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将预热后的钢管放置带有保温箱并旋转的滚轮架上，保温箱温度控制在190℃—210℃，离心速度调至290—310转/分钟；将调好的灰色混合粉末均匀倒入离心旋转的钢管内；在保温箱内保温30分钟；冷却成型后的管道进行电火花检测，合格的产品进行油漆包装。本发明保温箱温度控制在190℃—210℃，能让白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉三种原料都能充分熔解，从而达到较为理想的状态冷却成型，提高了耐磨性能。

Description

聚乙烯灰色管道的加工工艺
技术领域：本发明涉及到聚乙烯灰色管道的加工工艺。
     背景技术；普通的塑料PE管具有一定的耐腐性，但不具备耐磨性，在含固量20%的工况环境下，普通的塑料PE管使用寿命极短。而较为耐磨的双金属复合管，价格贵，重量大，成本高。
     发明内容：本发明的目的就是要提供一种聚乙烯灰色管道的加工工艺，它能克服现有以上产品所存在的问题。本发明的目的是这样
实现的，聚乙烯灰色管道的加工工艺，其特征于：直管的加工步骤，是将钢管内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将预热后的钢管放置带有保温箱并旋转的滚轮架上，保温箱温度控制在190℃—210℃，离心速度调至290—310转/分钟；将适量调好的灰色混合粉末均匀倒入离心旋转的钢管内，借助离心力使其均匀粘附在钢管内壁；在保温箱内保温30分钟后取出管道，冷却至常温成型；冷却成型后的管道进行电火花检测，合格的产品进行油漆包装处理。三通、弯头、大小头管件的加工步骤，是将管件内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将配合好的灰色混合粉末填满预热后的管件内部，待5—8分钟后清理多余灰色混合粉末；用干净平整的磨具压平法兰密封面；放入保温箱，保温箱温度控制在190℃—210℃，灰色混合粉末溶解成型；冷却成型后的管件进行电火花检测，合格的产品进行油漆包装处理。本发明保温箱温度控制在190℃—210℃，能让白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉三种原料都能充分熔解，从而达到较为理想的状态冷却成型。分子量达到200万以上，所以具有一定的耐磨性。经批量检测，一次合格率在98%以上。该管道口径25mm-1200mm，最长可至12米。
     具体实施方式；
      聚乙烯灰色管道的加工工艺，其特征于：直管的加工步骤，是将钢管内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将预热后的钢管放置带有保温箱并旋转的滚轮架上，保温箱温度控制在190℃—210℃，离心速度调至290—310转/分钟；将适量调好的灰色混合粉末均匀倒入离心旋转的钢管内，借助离心力使其均匀粘附在钢管内壁；在保温箱内保温30分钟后取出管道，冷却至常温成型；冷却成型后的管道进行电火花检测，合格的产品进行油漆包装处理。三通、弯头、大小头管件的加工步骤，是将管件内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将配合好的灰色混合粉末填满预热后的管件内部，待5—8分钟后清理多余灰色混合粉末；用干净平整的磨具压平法兰密封面；放入保温箱，保温箱温度控制在190℃—210℃，灰色混合粉末溶解成型；冷却成型后的管件进行电火花检测，合格的产品进行油漆包装处理。

Claims (2)

1.聚乙烯灰色管道的加工工艺，其特征于：直管的加工步骤，是将钢管内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将预热后的钢管放置带有保温箱并旋转的滚轮架上，保温箱温度控制在190℃—210℃，离心速度调至290—310转/分钟；将适量调好的灰色混合粉末均匀倒入离心旋转的钢管内，借助离心力使其均匀粘附在钢管内壁；在保温箱内保温30分钟后取出管道，冷却至常温成型；冷却成型后的管道进行电火花检测，合格的产品进行油漆包装处理。
2.聚乙烯灰色管道的加工工艺，其特征于：三通、弯头、大小头管件的加工步骤，是将管件内表面喷砂除锈，放置烘箱内加热，温度控制在250℃—265℃；将白色PE聚乙烯粉、黑色U-PE聚乙烯粉、泰克纳粉，按照7:2:1的比例配比均匀混合；将配合好的灰色混合粉末填满预热后的管件内部，待5—8分钟后清理多余灰色混合粉末；用干净平整的磨具压平法兰密封面；放入保温箱，保温箱温度控制在190℃—210℃，灰色混合粉末溶解成型；冷却成型后的管件进行电火花检测，合格的产品进行油漆包装处理。
CN2012103144941A 2012-08-30 2012-08-30 聚乙烯灰色管道的加工工艺 Pending CN102825697A (zh)