CN102825074A - 一种胎圈钢丝用盘条的控制冷却工艺 - Google Patents

一种胎圈钢丝用盘条的控制冷却工艺 Download PDF

Info

Publication number
CN102825074A
CN102825074A CN2012103404879A CN201210340487A CN102825074A CN 102825074 A CN102825074 A CN 102825074A CN 2012103404879 A CN2012103404879 A CN 2012103404879A CN 201210340487 A CN201210340487 A CN 201210340487A CN 102825074 A CN102825074 A CN 102825074A
Authority
CN
China
Prior art keywords
cooling
fan
water
air quantity
fan delivery
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103404879A
Other languages
English (en)
Inventor
彭学艺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nanjing Iron and Steel Co Ltd
Original Assignee
Nanjing Iron and Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanjing Iron and Steel Co Ltd filed Critical Nanjing Iron and Steel Co Ltd
Priority to CN2012103404879A priority Critical patent/CN102825074A/zh
Publication of CN102825074A publication Critical patent/CN102825074A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种胎圈钢丝用盘条的控制冷却工艺，该工艺利用RSM机组后水冷线和斯太尔摩风冷线进行控冷，在水冷线上设有正向喷嘴，跌落段调速实现工艺要求，水冷线中，冷却水管总管压力7.7bar，开度20%；3-1#水箱压力2.8bar，开度26%；3-2#水箱压力4.9bar，开度15%；风冷线中，1#风机风量100%,2#风机风量100%，3#风机风量100%，4#风机风量100%，5#风机风量100%，6#风机风量100%，7#风机风量100%，9-16#风机风量0；跌落段设置30%超前增速，辊道档位设置在8档。该工艺设备简单，可提高胎圈钢丝盘条的索氏体化率，抑制网状碳化物析出，同时解决翻丝乱卷的质量问题。

Description

一种胎圈钢丝用盘条的控制冷却工艺
技术领域
    本发明属于冶金领域，涉及一种钢材生产的控制冷却工艺，具体的说是一种胎圈钢丝用盘条的控制冷却工艺。解决胎圈钢丝用盘条翻丝乱卷、快速冷却的方法。
背景技术
在轧钢厂胎圈钢丝用盘条生产过程中，线材经过减定径机组后经过两个水箱水冷，然后在斯太尔摩风冷线上进行风冷，实现控制冷却。由于胎圈钢丝用盘条含碳量高，在经过水冷线和风冷线过程中需要25℃/s以上的冷速，才能保证索氏体化率和抑制网状碳化物的析出。低于此冷速，会导致形成大片层间距的珠光体，在700-900℃区间停留时间长，形成大量的网状碳化物，影响拉拔与使用性能。在风冷线上辊道速度控制不当，会造成大量的翻丝乱卷，形成12%不合格品。
发明内容
针对以上现有技术存在的缺点，本发明的目的是提供一种胎圈钢丝用盘条的控制冷却工艺，该工艺设备简单，可提高胎圈钢丝盘条的索氏体化率，抑制网状碳化物析出，同时解决翻丝乱卷的质量问题。
本发明的目的是通过以下技术方案来实现的：
一种胎圈钢丝用盘条的控制冷却工艺，其特征在于：该工艺利用RSM机组后水冷线和斯太尔摩风冷线进行控冷，在水冷线上设有正向喷嘴，跌落段调速实现工艺要求，具体如下：
1）水冷线中，冷却水管总管压力7.7bar，开度20%；3-1#水箱压力2.8bar，开度26%；3-2#水箱压力4.9 bar，开度15%；
2）风冷线中，1#风机风量100%,2#风机风量100%，3#风机风量100%，4#风机风量100%，5#风机风量100%，6#风机风量100%，7#风机风量100%，9-16#风机风量0；
3）跌落段设置30%超前增速，辊道档位设置在8档。
本发明在3-1#、3-2#水箱前部各加装1组正向喷嘴，提高冷却能力与均匀性。并且对原有的1#风机进行1.5倍的扩容，提高吐丝后的冷却能力，减少盘卷在700-900℃区间停留时间。在斯太尔摩跌落段设置30%的增速比，拉开盘条间距，同时总体转速下调30%，提高运行的稳定性。
本发明的优点是：设备简单，提高索氏体化率，抑制网状碳化物析出，减少翻丝乱卷，并确保胎圈钢丝用盘条的质量。
具体实施方式
一种本发明所述的胎圈钢丝用盘条的控制冷却工艺，该工艺利用RSM机组后水冷线和斯太尔摩风冷线进行控冷，在水冷线上设有正向喷嘴，跌落段调速实现工艺要求，具体如下：
1）水冷线中，冷却水管总管压力7.7bar，开度20%；3-1#水箱压力2.8bar，开度26%；3-2#水箱压力4.9 bar，开度15%；
2）风冷线中，1#风机风量100%,对原有的1#风机进行1.5倍的扩容，提高吐丝后的冷却能力，减少盘卷在700-900℃区间停留时间。2#风机风量100%，3#风机风量100%，4#风机风量100%，5#风机风量100%，6#风机风量100%，7#风机风量100%，9-16#风机风量0；
3）跌落段设置30%超前增速，辊道档位设置在8档，拉开盘条间距，同时总体转速下调30%，提高运行的稳定性，保持均匀性快冷的同时，防止盘卷卡进辊道缝隙或撞到护板形成翻丝。
本发明只需对原有设备进行简单改造即可实现，能提高索氏体化率，抑制网状碳化物析出，减少翻丝乱卷，并确保胎圈钢丝用盘条的质量。

Claims (3)

1.一种胎圈钢丝用盘条的控制冷却工艺，其特征在于：该工艺利用RSM机组后水冷线和斯太尔摩风冷线进行控冷，在水冷线上设有正向喷嘴，跌落段调速实现工艺要求，具体如下：
1）水冷线中，冷却水管总管压力7.7bar，开度20%；3-1#水箱压力2.8bar，开度26%；3-2#水箱压力4.9 bar，开度15%；
2）风冷线中，1#风机风量100%,2#风机风量100%，3#风机风量100%，4#风机风量100%，5#风机风量100%，6#风机风量100%，7#风机风量100%，9-16#风机风量0；
3）跌落段设置30%超前增速，辊道档位设置在8档。
2.根据权利要求1所述的胎圈钢丝用盘条的控制冷却工艺，其特征在于：在3-1#和3-2#水箱前部均设有1组能提高冷却能力与均匀性的正向喷嘴。
3.根据权利要求1所述的胎圈钢丝用盘条的控制冷却工艺，其特征在于：提高1#风机的冷却能力，减少盘卷在700-900℃区间停留时间。
CN2012103404879A 2012-09-14 2012-09-14 一种胎圈钢丝用盘条的控制冷却工艺 Pending CN102825074A (zh)