CN102816279A - 一种凝胶制造方法 - Google Patents
一种凝胶制造方法 Download PDFInfo
- Publication number
- CN102816279A CN102816279A CN2012102062431A CN201210206243A CN102816279A CN 102816279 A CN102816279 A CN 102816279A CN 2012102062431 A CN2012102062431 A CN 2012102062431A CN 201210206243 A CN201210206243 A CN 201210206243A CN 102816279 A CN102816279 A CN 102816279A
- Authority
- CN
- China
- Prior art keywords
- additional proportion
- gel
- sand
- ammonium chloride
- propanesulfonic acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于化工生产技术领域，提供了一种凝胶制造方法，所生产出的凝胶强度、抗冲刷能力及吸附能力高，防膨、抑砂效果显著，具有良好的抗温性、油水选择性和耐冲刷性；具有一定的控水能力，对渗透率的损失相对较小；通过对砂子的吸附以及形成的砂团之间的吸附，对高渗层起到封堵作用；化学性能稳定，合成生产方便，封堵有效期长，使用范围广，实用性强，具有较强的推广与应用价值。此外，该方法制造的两种凝胶都有较好的耐盐性能，通过调整原料配比，还可以对性能指标进行调整。
Description
技术领域
本发明属于化工生产技术领域，尤其涉及一种凝胶制造方法。
背景技术
多元共聚物选择性堵水剂的分子链上带有阴离子、阳离子和非离子基团，在地层的吸附和水化能力强，选择性好，遇水膨胀，遇油收缩，可用作油井堵水剂和水井调剖剂。
这类堵水剂形成的凝胶一般强度低，抗温性差，因而封堵有效期短，使用范围受到限制。
发明内容
本发明提供了一种凝胶制造方法，旨在解决现有技术提供的堵水剂形成的凝胶一般强度低、抗温性差，因而封堵有效期短，使用范围受到限制的问题。
本发明的目的在于提供一种凝胶制造方法，该方法包括以下步骤：
将丙烯酰胺、丙磺酸、二甲基二烯丙基氯化铵均匀混合；
向丙烯酰胺、丙磺酸、二甲基二烯丙基氯化铵构成的混合物中加入片碱、改良型淀粉及复合增强剂；
在60℃初步聚合三个小时，再升温到80℃，并保持五小时。
进一步，所述丙烯酰胺的加入比例为12.7％～14.7％；所述丙磺酸的加入比例为3.5％～5.5％；所述二甲基二烯丙基氯化铵的加入比例为18.5％～20％。
进一步，所述改良型淀粉的加入比例为0.5％～1％。
进一步，所述复合增强剂的加入比例为0.2％～0.8％。
进一步，所述复合增强剂由25.9甲醛、10苯酚及少量尿素组成。
进一步，所述凝胶包括两种：
一种耐高温200℃左右，可用于蒸汽吞吐调剖和高温地层的调驱；
另一种耐温90℃左右，用于2500m以内的井的调剖堵水以及调驱。
本发明提供的凝胶制造方法，所生产出的凝胶强度、抗冲刷能力及吸附能力高，防膨、抑砂效果显著，具有良好的抗温性、油水选择性和耐冲刷性；具有一定的控水能力，对渗透率的损失相对较小；通过对砂子的吸附以及形成的砂团之间的吸附，对高渗层起到封堵作用；化学性能稳定，合成生产方便，封堵有效期长，使用范围广，具有较强的推广与应用价值。此外，该方法制造的两种凝胶都有较好的耐盐性能，通过调整原料配比，还可以对性能指标进行调整。
附图说明
图1是本发明实施例提供的凝胶制造方法的实现流程图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步的详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定发明。
图1示出了本发明实施例提供的凝胶制造方法的实现流程。
该方法包括以下步骤：
在步骤S101中，将丙烯酰胺、丙磺酸、二甲基二烯丙基氯化铵均匀混合；
在步骤S102中，向丙烯酰胺、丙磺酸、二甲基二烯丙基氯化铵构成的混合物中加入片碱、改良型淀粉及复合增强剂；
在步骤S103中，在60℃初步聚合三个小时，再升温到80℃，保持五小时。
在本发明实施例中，丙烯酰胺的加入比例为12.7％～14.7％；所述丙磺酸的加入比例为3.5％～5.5％；所述二甲基二烯丙基氯化铵的加入比例为18.5％～20％。
在本发明实施例中，改良型淀粉的加入比例为0.5％～1％。
在本发明实施例中，复合增强剂的加入比例为0.2％～0.8％。
在本发明实施例中，复合增强剂由25.9甲醛、10苯酚及少量尿素组成。
在本发明实施例中，凝胶包括两种：一种耐高温200℃左右，可用于蒸汽吞吐调剖和高温地层的调驱；另一种耐温90℃左右，用于2500m以内的井的调剖堵水以及调驱。
本发明实施例提供的凝胶制造方法，所生产出的凝胶强度、抗冲刷能力及吸附能力高，防膨、抑砂效果显著；具有一定的控水能力，对渗透率的损失相对较小；通过对砂子的吸附以及形成的砂团之间的吸附，对高渗层起到封堵作用；化学性能稳定，合成生产方便，封堵有效期长，使用范围广，具有较强的推广与应用价值。此外，该方法制造的两种凝胶都有较好的耐盐性能，通过调整原料配比，还可以对性能指标进行调整。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种凝胶制造方法，其特征在于，所述方法包括以下步骤：
将丙烯酰胺、丙磺酸、二甲基二烯丙基氯化铵均匀混合；
向丙烯酰胺、丙磺酸、二甲基二烯丙基氯化铵构成的混合物中加入片碱、改良型淀粉及复合增强剂；
在60℃初步聚合三个小时，再升温到80℃，并保持五小时。
2.如权利要求1所述的方法，其特征在于，所述丙烯酰胺的加入比例为12.7％～14.7％；所述丙磺酸的加入比例为3.5％～5.5％；所述二甲基二烯丙基氯化铵的加入比例为18.5％～20％。
3.如权利要求1所述的方法，其特征在于，所述改良型淀粉的加入比例为0.5％～1％。
4.如权利要求1所述的方法，其特征在于，所述复合增强剂的加入比例为0.2％～0.8％。
5.如权利要求1或4所述的方法，其特征在于，所述复合增强剂由25.9甲醛、10苯酚及少量尿素组成。
6.如权利要求1所述的方法，其特征在于，所述凝胶包括两种：一种耐高温200℃左右，可用于蒸汽吞吐调剖和高温地层的调驱；另一种耐温90℃左右，用于2500m以内的井的调剖堵水以及调驱。