CN102814462A - 一种铸铁脱模用耐高温水性涂料 - Google Patents
一种铸铁脱模用耐高温水性涂料 Download PDFInfo
- Publication number
- CN102814462A CN102814462A CN2012102838828A CN201210283882A CN102814462A CN 102814462 A CN102814462 A CN 102814462A CN 2012102838828 A CN2012102838828 A CN 2012102838828A CN 201210283882 A CN201210283882 A CN 201210283882A CN 102814462 A CN102814462 A CN 102814462A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- wetting agent
- cast iron
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种铸铁脱模用耐高温水性涂料，特别涉及一种可用于水泥管桩端头板的一种水性耐高温涂料。主要采用如下的技术配方和工艺来实现：先用10％－20％的水分散0.2-0.5%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入10-30%3500型白乳胶及0.3-0.5%CF10润湿剂及0.5-1％SN5040水性润湿剂、0.1-0.5%EPW防腐剂、0.2-0.8%LFM防霉剂；然后在1500r/min高速搅拌下慢慢加入30%-50%250目重钙、5%-10%500目滑石粉及3%-5%的1250目石英粉，使其细度≤100μm，最后加入0.5-1%200号溶剂油、2%-5%丙二醇、0.2-0.4%消泡剂和水200r/min搅拌10min。本发明是一种无溶剂的环保、脱模性与基材匹配的耐高温水性涂料。
Description
技术领域
本发明涉及一种水性涂料，特别涉及一种铸铁脱模用耐高温水性涂料。
背景技术
目前，油性耐高温脱模硅涂料广泛用于铸铁和铝合金等基材，但其本身含有溶剂，达不到环保要求，且作为脱模剂使用时，需乳化后使用，而油性耐高温脱模硅涂料价格贵，性价比不好。
发明内容
本发明的目的是提供一个无溶剂的环保、铸铁脱模用耐高温水性涂料。
本发明是采用如下的技术配方和工艺来实现的，所述涂料其使用的原材料及其具体配比如下：
组分 重量百分比％
羟乙基纤维素 0.2-0.5
白乳胶 10-25
水性分散剂 0.5-1.0
水性消泡剂 0.2-0.4
水性润湿剂 0.3-0.5
水性防腐剂 0.1-0.5
水性防霉剂 0.2-0.8
重钙 30-45
滑石粉 5-10
石英粉 3-5
200号溶剂油 0.5-1
丙二醇 2-5
水 余量。
所述的铸铁脱模用耐高温水性涂料，其特征在于：所述涂料的制备工艺如下：先用10％－20％的水分散0.2-0.5%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入10-30%3500型白乳胶及0.3-0.5%CF10润湿剂及0.5-1％SN5040水性润湿剂、0.1-0.5%EPW防腐剂、0.2-0.8%LFM防霉剂；然后在1500r/min高速搅拌下慢慢加入30%-50%250目重钙、5%-10%500目滑石粉及3%-5%的1250目石英粉，使其细度≤100μm，最后加入0.5-1%200号溶剂油、2%-5%丙二醇、0.2-0.4%消泡剂和水200r/min搅拌10min。
采用上述的配方和工艺制备的涂料，其与现有技术相比，有如下优点：
1、本发明涂料无溶剂，比较环保；
2、且作为脱模剂使用时，不需乳化后使用；
3、价格低,性价比高。
具体实施方式
一、一种铸铁脱模用耐高温水性涂料的主要成分及重量配比如下：
| 组分 | 重量 ％ |
| 羟乙基纤维素 | 0.2-0.5 |
| 白乳胶 | 10-25 |
| 水性分散剂 | 0.5-1 |
| 水性润湿剂 | 0.3-0.5 |
| 水性消泡剂 | 0.2-0.4 |
| 水性防腐剂 | 0.1-0.5 |
| 水性防霉剂 | 0.2-0.8 |
| 重钙 | 30-45 |
| 滑石粉 | 5-10 |
| 石英粉 | 3-5 |
| 200号溶剂油 | 0.5-1 |
| 丙二醇 | 2-5 |
| 水 | 余量 |
原料说明如下：
羟乙基纤维素：型号250HBR,美国亚跨龙公司产品；
白乳胶：SK3500，三棵树涂料公司产品；
水性分散剂：SN5040，德国汉高公司产品；
水性润湿剂 ：CF10，美国陶氏化学公司产品；
水性消泡剂：CF246 ，英国布莱克本公司产品；
水性防腐剂：EPW，英国索尔产品；
水性防霉剂：LFM, 德国汉高公司产品
重钙、滑石粉、石英粉、丙二醇：普通市售；
水：普通水。
上述铸铁脱模用耐高温水性涂料制备工艺如下：
先用10％－20％的水分散0.2-0.5%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入10-30%3500型白乳胶及0.3-0.5%CF10润湿剂及0.5-1％SN5040水性润湿剂、0.1-0.5%EPW防腐剂、0.2-0.8%LFM防霉剂；然后在1500r/min高速搅拌下慢慢加入30%-50%250目重钙、5%-10%500目滑石粉及3%-5%的1250目石英粉，使其细度≤100μm，最后加入0.5-1%200号溶剂油、2%-5%丙二醇、0.2-0.4%消泡剂和水200r/min搅拌10min。
实施例一：
组分 重量配比（共100份）
羟乙基纤维素 0.2份
白乳胶 10份
水性分散剂 0.5份
水性润湿剂 0.3份
水性消泡剂 0.2份
水性防腐剂 0.1份
水性防霉剂 0.2份
重钙 45份
滑石粉 5份
石英粉 3份
200号溶剂油 0.5份
丙二醇 2份
水 33份
上述铸铁脱模用耐高温水性涂料制备工艺如下：
先用10％的水分散0.2%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入10%3500型白乳胶及0.3%CF10润湿剂及0.5％SN5040水性润湿剂、0.1%EPW防腐剂、0.2%LFM防霉剂；然后在1500r/min高速搅拌下慢慢加入30%250目重钙、5%500目滑石粉及3%的1250目石英粉，使其细度≤100μm，最后加入0.5%200号溶剂油、2%丙二醇、0.2%消泡剂和水200r/min搅拌10min。
实施例二：
组分 重量配比（共100份）
羟乙基纤维素 0.4份
白乳胶 15份
水性分散剂 1份
水性润湿剂 0.5份
水性消泡剂 0.4份
水性防腐剂 0.5份
水性防霉剂 0.5份
重钙 35份
滑石粉 10份
石英粉 5份
200号溶剂油 1份
丙二醇 5份
水 25.7份
上述铸铁脱模用耐高温水性涂料制备工艺如下：
先用20％的水分散0.4%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入15%3500型白乳胶及0.5%CF10润湿剂及1％SN5040水性润湿剂、0.5%EPW防腐剂、0.5%LFM防霉剂；然后在1500r/min高速搅拌下慢慢加入35%250目重钙、10%500目滑石粉及5%的1250目石英粉，使其细度≤100μm，最后加入1%200号溶剂油、5%丙二醇、0.4%消泡剂和水200r/min搅拌10min。
实施例三：
组分 重量配比（共100份）
羟乙基纤维素 0.3份
白乳胶 20份
水性分散剂 1份
水性润湿剂 0.5份
水性消泡剂 0.4份
水性防腐剂 0.5份
水性防霉剂 0.5份
重钙 30份
滑石粉 8份
石英粉 4份
200号溶剂油 1份
丙二醇 5份
水 28.8份
上述铸铁脱模用耐高温水性涂料制备工艺如下：
先用15％的水分散0.3%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入20%3500型白乳胶及0.5%CF10润湿剂及1％SN5040水性润湿剂、0.5%EPW防腐剂、0.5%LFM防霉剂；然后在1500r/min高速搅拌下慢慢加入30%250目重钙、8%500目滑石粉及4%的1250目石英粉，使其细度≤100μm，最后加入1%200号溶剂油、5%丙二醇、0.4%消泡剂和水200r/min搅拌10min。
Claims (2)
1.一种铸铁脱模用耐高温水性涂料，其特征在于：所述涂料的组分及其重量配比如下：
组分 配比 ％
羟乙基纤维素 0.2-0.5
白乳胶 10-25
水性分散剂 0.5-1.0
水性消泡剂 0.2-0.4
水性润湿剂 0.3-0.5
水性防腐剂 0.1-0.5
水性防霉剂 0.2-0.8
重钙 30-45
滑石粉 5-10
石英粉 3-5
200号溶剂油 0.5-1
丙二醇 2-5
水 余量。
2.如权利要求1所述的铸铁脱模用耐高温水性涂料，其特征在于：所述涂料的制备工艺如下：先用10％－20％的水分散0.2-0.5%的羟乙基纤维素使其熔融，在500r/min分散时慢慢加入10-30%白乳胶及0.3-0.5%水性润湿剂及0.5-1％水性润湿剂、0.1-0.5%水性防腐剂、0.2-0.8%水性防霉剂；然后在1500r/min高速搅拌下慢慢加入30%-50%重钙、5%-10%滑石粉及3%-5%的石英粉，使其细度≤100μm，最后加入0.5-1%200号溶剂油、2%-5%丙二醇、0.2-0.4%消泡剂和水200r/min搅拌10min。