CN102813336A - 一种绝热中底鞋材 - Google Patents

一种绝热中底鞋材 Download PDF

Info

Publication number
CN102813336A
CN102813336A CN2012103027365A CN201210302736A CN102813336A CN 102813336 A CN102813336 A CN 102813336A CN 2012103027365 A CN2012103027365 A CN 2012103027365A CN 201210302736 A CN201210302736 A CN 201210302736A CN 102813336 A CN102813336 A CN 102813336A
Authority
CN
China
Prior art keywords
nonwoven
heat insulation
hollow glass
mixed
pearl powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103027365A
Other languages
English (en)
Other versions
CN102813336B (zh
Inventor
陈罘杲
何秀英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210302736.5A priority Critical patent/CN102813336B/zh
Publication of CN102813336A publication Critical patent/CN102813336A/zh
Application granted granted Critical
Publication of CN102813336B publication Critical patent/CN102813336B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种绝热中底鞋材，属于鞋制造材料领域，该鞋材主要是由以下原料加工而成：苯炳乳液，纳米二氧化硅，空心玻璃微珠和珍珠粉。加工方法：首先将纳米二氧化硅、空心玻璃微珠和珍珠粉混合后加入到球磨机中进行球磨，球磨后的混合粉体加入到苯炳乳液中，搅拌均匀，然后将上述混合原料加入到浸料槽中；将无纺布通过浸料槽并反复挤压，使得上述混合原料充分浸入无纺布中，然后将带料后的无纺布送入烘干箱烘干制成无纺革，之后将铝箔贴在烘干的无纺革底面即制成该绝热中底鞋材。本发明的一种绝热中底鞋材和现有技术相比，具有加工工艺简单，生产成本低，绝热效果好等特点，能有效的避免地表的高温对鞋内温度的影响，达到保护脚掌的目的。

Description

一种绝热中底鞋材
技术领域
本发明涉及鞋制造材料领域，具体地说是一种绝热中底鞋材。
背景技术
野外施工人员在施工时、交警在户外执勤时、军人野外训练时，经常会因为地表温度过高而导致鞋内环境恶劣，不但会影响工作人员的足部健康，而且长时间在这样恶劣的环境中工作，会影响工作人员的心情进而影响工作质量和效率。目前，人们为了改善这些特殊工作人群的鞋内环境，将工作人员的鞋底加厚，或者在鞋内佩戴隔热鞋垫，但效果都不理想。
发明内容
本发明的技术任务是提供一种生产成本低，绝热效果好的绝热中底鞋材。
本发明的技术任务是按以下方式实现的，该鞋材主要是由以下重量份配比的原料加工而成：
苯炳乳液：40～60份，纳米二氧化硅：5～15份，空心玻璃微珠：20～40份，珍珠粉：10～30份；
加工方法：首先将纳米二氧化硅、空心玻璃微珠和珍珠粉混合后加入到球磨机中进行球磨，球磨后的混合粉体加入到苯炳乳液中，搅拌均匀，然后将上述混合原料加入到浸料槽中；将无纺布通过浸料槽并反复挤压，使得上述混合原料充分浸入无纺布中，然后将带料后的无纺布送入烘干箱烘干制成无纺革，之后将铝箔贴在烘干的无纺革底面即制成该绝热中底鞋材。
所述的纳米二氧化硅的粒径为：1～100nm，空心玻璃微珠的粒径为：10～50μm，珍珠粉的粒径为：10～50μm。
所述的无纺布厚1～3mm，铝箔厚0.1～0.5mm。
本发明的一种绝热中底鞋材和现有技术相比，具有加工工艺简单，生产成本低，绝热效果好等特点，能有效的避免地表的高温对鞋内温度的影响，达到保护足部的目的。
具体实施方式
实施例1：
取粒径为1nm的纳米二氧化硅5kg、粒径为10μm的空心玻璃微珠20kg以及粒径为10μm珍珠粉10kg混合后加入到球磨机中进行球磨，球磨后的混合粉体加入到40kg固含量35％的苯炳乳液中，搅拌均匀，然后将上述混合原料加入到浸料槽中；将厚1mm的无纺布通过浸料槽并反复挤压，使得上述混合原料充分浸入无纺布中，然后将带料后的无纺布送入烘干箱烘干制成无纺革，之后将厚0.1mm的铝箔贴在烘干的无纺革底面即制成该绝热中底鞋材。
实施例2：
取粒径为100nm的纳米二氧化硅15kg、粒径为50μm的空心玻璃微珠40kg以及粒径为50μm珍珠粉30kg混合后加入到球磨机中进行球磨，球磨后的混合粉体加入到60kg固含量35％的苯炳乳液中，搅拌均匀，然后将上述混合原料加入到浸料槽中；将厚3mm的无纺布通过浸料槽并反复挤压，使得上述混合原料充分浸入无纺布中，然后将带料后的无纺布送入烘干箱烘干制成无纺革，之后将厚0.5mm的铝箔贴在烘干的无纺革底面即制成该绝热中底鞋材。
实施例3：
取粒径为50nm的纳米二氧化硅10kg、粒径为30μm的空心玻璃微珠30kg以及粒径为30μm珍珠粉20kg混合后加入到球磨机中进行球磨，球磨后的混合粉体加入到50kg固含量35％的苯炳乳液中，搅拌均匀，然后将上述混合原料加入到浸料槽中；将厚2mm的无纺布通过浸料槽并反复挤压，使得上述混合原料充分浸入无纺布中，然后将带料后的无纺布送入烘干箱烘干制成无纺革，之后将厚0.3mm的铝箔贴在烘干的无纺革底面即制成该绝热中底鞋材。

Claims (3)

1.一种绝热中底鞋材，其特征在于该鞋材主要是由以下重量份配比的原料加工而成：
苯炳乳液：40～60份，纳米二氧化硅：5～15份，空心玻璃微珠：20～40份，珍珠粉：10～30份；
加工方法：首先将纳米二氧化硅、空心玻璃微珠和珍珠粉混合后加入到球磨机中进行球磨，球磨后的混合粉体加入到苯炳乳液中，搅拌均匀，然后将上述混合原料加入到浸料槽中；将无纺布通过浸料槽并反复挤压，使得上述混合原料充分浸入无纺布中，然后将带料后的无纺布送入烘干箱烘干制成无纺革，之后将铝箔贴在烘干的无纺革底面即制成该绝热中底鞋材。
2.根据权利要求1所述的绝热中底鞋材，其特征在于所述的纳米二氧化硅的粒径为：1～100nm，空心玻璃微珠的粒径为：10～50μm，珍珠粉的粒径为：10～50μm。
3.根据权利要求1所述的绝热中底鞋材，其特征在于所述的无纺布厚1～3mm，铝箔厚0.1～0.5mm。
CN201210302736.5A 2012-08-24 2012-08-24 一种绝热中底鞋材 Active CN102813336B (zh)