CN102794051A - 一种空气过滤材料及其用途 - Google Patents

一种空气过滤材料及其用途 Download PDF

Info

Publication number
CN102794051A
CN102794051A CN 201110135455 CN201110135455A CN102794051A CN 102794051 A CN102794051 A CN 102794051A CN 201110135455 CN201110135455 CN 201110135455 CN 201110135455 A CN201110135455 A CN 201110135455A CN 102794051 A CN102794051 A CN 102794051A
Authority
CN
China
Prior art keywords
activated carbon
nonwoven
carbon granule
air
air filting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110135455
Other languages
English (en)
Inventor
马燕男
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Fibers and Textiles Research Laboratories China Co Ltd
Original Assignee
Toray Fibers and Textiles Research Laboratories China Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Fibers and Textiles Research Laboratories China Co Ltd filed Critical Toray Fibers and Textiles Research Laboratories China Co Ltd
Priority to CN 201110135455 priority Critical patent/CN102794051A/zh
Publication of CN102794051A publication Critical patent/CN102794051A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种空气过滤材料,该过滤材料至少由一层含有活性炭颗粒的无纺布构成,所述活性炭颗粒的直径为5~150μm,该空气过滤材料不仅具有良好的除尘、除臭功能,大大增加了吸附效果,而且工艺简单。可应用于在空气过滤领域,如空气净化器滤芯﹑室用空调用滤芯﹑汽车空调滤芯。

Description

一种空气过滤材料及其用途
技术领域
本发明涉及到一种空气过滤材料及其用途,该空气过滤材料能够降低或消除空气中的臭味或异味,可应用于空气过滤领域。
背景技术
随着社会的迅猛发展,环境污染也日趋严重,工业废气﹑汽车尾气等严重困扰着人类的生活。对空气的清新程度有了新的认知,对空气净化能力有了更高的要求。
如中国专利CN200920295665.4公开了一种空气净化器含有活性炭滤芯装置,活性炭层是由粘附层和大量的活性炭颗粒组成,采用硅胶涂刷在粘附层上使其表面具有可黏性,使活性炭颗粒粘附在黏附层上。该专利提出了活性炭应用在空气净化器滤芯上,但采用的是刷硅胶再黏附活性碳,这样黏附的活性碳颗粒只有表层,所粘附的活性的量比较少。
发明内容
本发明的目的在于提供一种不仅具有良好的除尘、除臭功能,大大增加了吸附效果,而且工艺简单的空气过滤材料及其用途。
本发明的技术解决方案是:本发明的空气过滤材料,该过滤材料是至少由一层含有活性炭颗粒的无纺布构成,所述活性炭颗粒的直径为5~150μm。含有活性炭颗粒的无纺布可以为一层或两层或多层,层数越多,形成过滤材料的吸附能力就越强,则经过滤后的空气中含有的有毒﹑异味﹑粉尘粒子等就越少。当然,并不是层数越多越好,如果含有活性炭颗粒的无纺布层数越多,空气阻力就越大,能耗就会越高,这样就容易造成堵塞,而且层数的增加也会使加工工艺复杂,增加加工成本。优选该过滤材料是由一层或两层含有活性炭颗粒的无纺布构成。上述活性炭颗粒的直径为5~150μm,优选10~100μm,如果活性炭颗粒的直径过小,容易从过滤材料的纤维空隙中漏出;如果活性炭颗粒的直径过大,不易粘附在无纺布上。
本发明的空气过滤材料,上述含有活性炭颗粒的无纺布是通过混合溶液浸渍处理而得的。先将一定量的胶黏剂和其他助剂放入水中配成溶液,然后将活性炭颗粒加入上述溶液中,进行不断地搅拌,使活性炭颗粒与胶剂和其他助剂按照一定配比混合形成混合溶液。其中,上述活性炭颗粒占该混合溶液的重量比为5~80%。然后将无纺布浸渍于该混合溶液中,浸渍时间为1~30s,虽然浸渍时间越长,活性炭颗粒渗入无纺布中越充分,但是能耗使用就高,这样会影响成本,优选浸渍时间为5~15s。最后对浸渍后的含有活性炭颗粒的无纺布进行干燥处理,干燥温度为80~150℃,速度为5~30m/min。如果干燥温度过低,可能导致干燥不良,活性炭颗粒就不能稳定的粘附在无纺布上;如果干燥温度过高,可能会影响滤材的其他性能。如果速度过慢,可能就会导致能耗增加;如果速度过快,可能会导致干燥不良,活性炭颗粒就不能充分粘附在无纺布上。
本发明的空气过滤材料,上述活性颗粒粘附在无纺布的纤维层表面或粘附在无纺布的纤维间的空隙中。粒径小的活性炭颗粒更容易渗透至纤维层内部。
本发明的空气过滤材料,该过滤材料中活性炭颗粒的克重为10~100g/m2。如果过滤材料中活性炭颗粒的克重小于10g/m2的话,对异味、异物的吸附能力就越差;如果过滤材料中活性炭颗粒的克重大于100g/m2的话,虽对异味、异物的吸附能力很强,但同时滤材阻力越大,成本越高,活性炭就容易掉落。
本发明的空气过滤材料,构成上述无纺布的纤维为聚丙烯纤维、聚对苯二甲酸乙二醇酯纤维、玻璃纤维、粘胶纤维中的一种或几种。优选聚丙烯纤维。
一般,制造过滤材料的纤维可以为聚苯乙烯、聚酯、聚乙烯、聚丙烯、尼龙、玻璃纤维等合成纤维,以及麻纤维和竹纤维等天然纤维的任何一种或几种。优选杨氏模量在70CN/dtex以上的纤维,更优选杨氏模量在130CN/dtex以上的纤维,最优选杨氏模量在300CN/dtex以上的纤维。另一方面,杨氏模量上限在3000CN/dtex以下较好。如果纤维的杨氏模量超过3000CN/dtex的话,如芳纶纤维(4400CN/dtex)、超高分子量的聚乙烯(8000CN/dtex)、玻璃纤维(326000CN/dtex),使用这些纤维做成的无纺布拉伸强力就会降低,而且打褶后褶角顶部由于不耐褶,经常会发生断裂,所以不适合用作过滤材料。因此,可以使用杨氏模量较高的尼龙纤维和价格比较低廉的聚酯纤维混合制造出骨材材料,这样制得的过滤材料不仅成本较低且强度较高。
使用上述的纤维制成的无纺布可以形成湿式无纺布、化学粘合无纺布、热粘合无纺布、纺粘无纺布、水刺无纺布。其中,化学粘合可以把不同种类纤维和不同纤度的纤维混在一起,纺粘无纺布的价格比较低,湿式无纺布的硬挺度较高,以上三种都是作骨材的理想材料。化学粘合无纺布使用的树脂玻璃化温度至少在30℃以上,以及基本没有异味的丙烯酸树脂、苯乙烯丙烯酸树脂、丙烯酸树脂和环氧树脂的一种或几种。
一般,过滤材料的克重为10~500 g/m2,优选30~100 g/m2。过滤材料的克重优选此范围的话,后续打褶加工比较容易,压损较低。 
本发明的空气过滤材料,上述含有活性炭颗粒的无纺布可以直接打褶或与其他无纺布复合再打褶。含有活性炭颗粒的无纺布可以与熔喷无纺布通过低熔点热熔胶粉或低熔点纤维或超声波复合方式进行复合,形成熔喷活性炭过滤材料,该过滤材料不仅具有优越的捕集性能,又具有除臭功效。该过滤材料的捕集效率在10.0~99.9999%,优选捕集效率在80.0~99.9999%,捕集效率越高对灰尘的拦截效果越好,拦截后出去的空气质量就越好。
本发明的空气过滤材料可应用于在空气过滤领域,如空气净化器滤芯﹑室用空调用滤芯﹑汽车空调滤芯。
本发明的空气过滤材料不仅具有良好的除尘、除臭功能,大大增加了吸附效果,而且工艺简单。
具体实施方式
下面结合实施例对本发明作进一步说明,本说明书中所述的性能测试方法如下。
【捕集效率】
把片状的过滤材料放到0.1m2开口面积的机器上,固定住,使面风速6.5m/min的空气通过,用粒子计数器(日本RION公司制)测定过滤材料上下流的空气粒子数(粒径0.3~0.5um),从而计算出该测定滤材的捕集效率,其计算公式如下:
捕集效率(%)=1-(下流粒子数/上流粒子数)×100%。在测定样品中的任意5个地方取样并且测定,得到平均值。
【活性炭颗粒的克重】
过滤材料在浸渍之前的克重为m1,通过活性炭浸渍干燥处理后的克重为m2,则过滤材料上所增加的克重为m,将克重m定义为活性炭的克重,其计算公式如下:
活性炭颗粒的克重m=浸渍干燥处理后的克重m2-浸渍之前的克重m1
实施例1
一种空气过滤材料,将用聚丙烯纤维制成的无纺布浸渍在含有活性炭颗粒的混合溶液中,上述活性炭颗粒占整个混合溶液的重量比为30%,浸渍10s后,再在温度为130℃下进行干燥处理,得到含有直径为5~50um活性炭颗粒的无纺布作为过滤材料,测得该过滤材料中活性炭颗粒的克重为10g/m2,该过滤材料的捕集效率为5%,然后将该过滤材料打褶成滤芯,该滤芯的长、宽、高分别为400mm、200mm、20mm。放置在甲醛浓度一定的环境中,经过4小时的作用,甲醛浓度下降60%。
实施例2
    一种空气过滤材料,将用聚丙烯纤维制成的无纺布浸渍在含有活性炭颗粒的混合溶液中,上述活性炭颗粒占整个混合溶液的重量比为60%,浸渍12s后,再在温度为130℃下进行干燥处理,得到直径为25~80um含有活性炭颗粒的无纺布,然后再采用化学粘合剂将该无纺布与聚丙烯熔喷无纺布进行复合加工后的作为过滤材料,测得该过滤材料中活性炭颗粒的克重为25g/m2,该过滤材料的捕集效率为99.5%。最后将该过滤材料进行打褶成滤芯,该滤芯的长、宽、高分别为400mm、200mm、20mm。放置在甲醛浓度一定的环境中,经过4小时的作用,甲醛浓度下降85%。
实施例3
一种空气过滤材料,将用聚丙烯纤维制成的无纺布浸渍在含有活性炭颗粒的混合溶液中,上述活性炭颗粒占整个混合溶液的重量比为30%,浸渍10s后,再在温度为130℃下进行干燥处理,得到含有直径为5~50um活性炭颗粒的无纺布作为过滤材料A,测得该过滤材料A中活性炭颗粒的克重为10g/m2。再继续将用聚丙烯纤维制成的无纺布浸渍在含有活性炭颗粒的另一个混合溶液中,上述活性炭颗粒占该混合溶液的重量比为50%,浸渍10s后,再在温度为130℃下进行干燥处理,得到含有直径为5~50um活性炭颗粒的无纺布作为过滤材料B,测得该过滤材料中活性炭颗粒的克重为18g/m2。然后再采用化学粘合剂将上述过滤材料A,B与聚丙烯熔喷无纺布进行复合加工,制得过滤材料C,测得该过滤材料C的捕集效率为99.9%。最后将该过滤材料C进行打褶成滤芯,该滤芯的长、宽、高分别为400mm、200mm、20mm。放置在甲醛浓度一定的环境中,经过4小时的作用,甲醛浓度下降90%。

Claims (8)

1.一种空气过滤材料,其特征在于:该过滤材料是至少由一层含有活性炭颗粒的无纺布构成,所述活性炭颗粒的直径为5~150μm。
2.根据权利要求1所述的空气过滤材料,其特征在于:所述含有活性炭颗粒的无纺布是通过混合溶液浸渍处理而得的。
3.根据权利要求2所述的空气过滤材料,其特征在于:所述活性炭颗粒占整个混合溶液的重量比为5~80%。
4.根据权利要求1或2所述的空气过滤材料,其特征在于:所述活性颗粒粘附在无纺布的纤维层表面或粘附在无纺布的纤维间的空隙中。
5.根据权利要求1所述的空气过滤材料,其特征在于:该过滤材料中活性炭颗粒的克重为10~100g/m2
6.根据权利要求1或2所述的空气过滤材料,其特征在于:构成所述无纺布的纤维为聚丙烯纤维、聚对苯二甲酸乙二醇酯纤维、玻璃纤维、粘胶纤维中的一种或几种。
7.根据权利要求1或2所述的空气过滤材料,其特征在于:所述含有活性炭颗粒的无纺布可以直接打褶或与其他无纺布复合再打褶。
8.一种如权利要求1所述的空气过滤材料可应用于空气过滤领域。
CN 201110135455 2011-05-25 2011-05-25 一种空气过滤材料及其用途 Pending CN102794051A (zh)