Summary of the invention
The object of this invention is to provide a kind of production method of high-temperature heat insulation electromagnetic shielding instrument protective jacket.
The present invention adopts following technical scheme to realize its goal of the invention, a kind of production method of high-temperature heat insulation electromagnetic shielding instrument protective jacket, it adopts coating processed, coating, shaping, plated film four technological processes to complete by base material alkali-free glass fiber cloth, A, have employed coating process flow process processed: one, by mylar and fire retardant in proportion mixing and stirring become polyester to starch; Two, polyester slurry grinder is ground to form the slurry that fineness is 50 μm; Three, the polyester slurry after grinding is finish-ground to sand mill the slurry that fineness is 25 μm again; Four, in polyester slurry, add curing agent, catalyst in proportion, the solution after stirring becomes required heat-resistant paint, and the proportioning of its coating raw material is: mylar: fire retardant: curing agent: catalyst=100:30:20:1; B, have employed coating process flow process: the dipping tank one, the heat-resistant paint made being placed in coating machine; Two, alkali-free glass fiber cloth is delivered to by deflector roll in the dipping tank of coating machine and is fully flooded levelling with heat-resistant paint; Three, by the drying in oven being caused coating machine by carry-over pinch rolls of the heat-resistant paint be attached on alkali-free glass fiber cloth, high-temperature heat insulation cloth is; C, have employed moulding process flow process: the protective coat high-temperature heat insulation cloth after drying being become instrument according to the specification excision forming of different instrument; D, have employed coating process flow process: the two sides of the high-temperature heat insulation protective jacket after shaping is plated silver, copper, aluminium, titanium, stainless steel metal film by vacuum coating equipment according to different demands.
Owing to have employed above technical scheme, the present invention achieves its goal of the invention preferably, and better, shielding external electromagnetic wave ability is comparatively strong, and its production method technique is simple, and production efficiency is higher for the solar heat protection of a kind of high-temperature heat insulation electromagnetic shielding instrument protective jacket and moistureproof effect.
Detailed description of the invention
Below in conjunction with embodiment, summary of the invention is described further:
Embodiment 1
A kind of production method of high-temperature heat insulation electromagnetic shielding instrument protective jacket, it adopts coating processed, coating, shaping, plated film four technological processes to complete by base material alkali-free glass fiber cloth, A, have employed coating process flow process processed: one, by mylar and fire retardant in proportion mixing and stirring become polyester to starch; Two, polyester slurry grinder is ground to form the slurry that fineness is 50 μm; Three, the polyester slurry after grinding is finish-ground to sand mill the slurry that fineness is 25 μm again; Four, in polyester slurry, add curing agent, catalyst in proportion, the solution after stirring becomes required heat-resistant paint, and the proportioning of its coating raw material is: mylar: fire retardant: curing agent: catalyst=100:30:20:1; B, have employed coating process flow process: the dipping tank one, the heat-resistant paint made being placed in coating machine; Two, alkali-free glass fiber cloth is delivered to by deflector roll in the dipping tank of coating machine and is fully flooded levelling with heat-resistant paint; Three, by the drying in oven being caused coating machine by carry-over pinch rolls of the heat-resistant paint be attached on alkali-free glass fiber cloth, high-temperature heat insulation cloth is; C, have employed moulding process flow process: the protective coat high-temperature heat insulation cloth after drying being become instrument according to the specification excision forming of different instrument; D, have employed coating process flow process: the two sides of the high-temperature heat insulation protective jacket after shaping is plated silver, copper, aluminium, titanium, stainless steel metal film by vacuum coating equipment according to different demands.Completing the product after this technological process is high-temperature heat insulation protective jacket.
Alkyd resin of the present invention refers to: the abbreviation being saturated polyester adhesive, primarily of compositions such as saturated polyester resin, initator, promoter, filler, thixotropic agent; Be characterized in that adhesive force is good, highly versatile, weather resisteant, pliability are outstanding.
Fire retardant of the present invention refers to: the functional aid giving polymer flame retardancy, and its characteristic has the smothering action etc. of heat-absorbing action, covering effect, suppression chain reaction, non-flammable compressive gas.
Curing agent of the present invention refers to: also known as curing agent, is a kind of material or mixture of promoting or controlling curing reaction.
Catalyst of the present invention refers to: be that one can improve chemical reaction rate, and material or the solvent of permanent change do not occur this body structure.
Alkali-free glass fiber cloth of the present invention refers to: the glass fabric that alkali metal oxide content is low, and its characteristic is that chemical stability is good, and electrical insulation capability, intensity are high.