CN102816504A - Light-weight high-temperature heat-insulation electromagnetic-shielding composite casing pipe and production method thereof - Google Patents
Light-weight high-temperature heat-insulation electromagnetic-shielding composite casing pipe and production method thereof Download PDFInfo
- Publication number
- CN102816504A CN102816504A CN2012102767466A CN201210276746A CN102816504A CN 102816504 A CN102816504 A CN 102816504A CN 2012102767466 A CN2012102767466 A CN 2012102767466A CN 201210276746 A CN201210276746 A CN 201210276746A CN 102816504 A CN102816504 A CN 102816504A
- Authority
- CN
- China
- Prior art keywords
- heat
- slurry
- coating
- light
- pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a light-weight high-temperature heat-insulation electromagnetic-shielding composite casing pipe and a production method thereof. The production method comprises the following steps of coating preparation, coating of a fiberglass pipe as a base material, and film plating. The light-weight high-temperature heat-insulation electromagnetic-shielding composite casing pipe has strong functions of shielding heat and moisture and resisting electromagnetic interference, has light weight, and can promote improvement of a rate and a flying range of an aircraft. The production method has simple processes and high production efficiency.
Description
Technical field:
The present invention relates to a kind of light-type high-temperature heat insulation electromagnetic shielding composite bushing and working method thereof.
Background technology:
Carry-on instrument and cable system thereof are not only very high to the requirement of solar heat protection, protection against the tide, anti-EMI, and its quality is light more, and the speed of its flight is just faster, distance is far away more.
Summary of the invention:
The purpose of this invention is to provide a kind of light-type high-temperature heat insulation electromagnetic shielding composite bushing and working method thereof;
The present invention adopts following technical scheme to realize its goal of the invention, a kind of light-type high-temperature heat insulation electromagnetic shielding composite bushing and working method thereof, it by the substrate glass fibre pipe adopt system coating, be coated with pipe, its working method of three technical process completion of plated film;
System coating process flow process of the present invention is: one, alkyd resin and fire retardant proportional mixing are stirred into the polyester slurry; Two, use shredder to grind to form the slurry that fineness is 50 μ m in the polyester slurry; Three, use sand mill to be finish-ground to the slurry that fineness is 25 μ m again in the polyester slurry after grinding; Four, in the polyester slurry, add solidifying agent, catalyzer in proportion, the solution after stirring is heat-resistant paint required for the present invention; The proportioning of its coating raw material is: alkyd resin: fire retardant: solidifying agent: catalyzer=100:30:20:1;
The plumber's of being coated with process flow of the present invention is: one, the heat-resistant paint of processing is inserted in the steeping vat of coating machine; Two, fiberglass pipe is delivered in the steeping vat of coating machine through the conduction roller and fully floods levelling with heat-resistant paint; Three, will deliver to the drying in oven of coating machine attached to the heat-resistant paint on the fiberglass pipe through take off roll;
Coating process flow process of the present invention is: the fiberglass pipe after will drying plates metallic membranes such as silver, copper, aluminium, titanium, stainless steel through vacuum plating unit according to different demands.
Owing to adopted above technical scheme; The present invention has realized its goal of the invention preferably; The ability of the not only solar heat protection of a kind of light-type high-temperature heat insulation electromagnetic shielding composite bushing of design, protection against the tide, anti-EMI is strong, and lighter weight, and speed and the distance that improves aircraft had certain help; Its working method technology is simple, and production efficiency is higher.
Embodiment:
Below in conjunction with embodiment summary of the invention is described further:
Embodiment 1:
Can know by summary of the invention, a kind of light-type high-temperature heat insulation electromagnetic shielding composite bushing and working method thereof, it by the substrate glass fibre pipe adopt system coating, be coated with pipe, its working method of three technical process completion of plated film.
System coating of the present invention is meant: a technical process, and concrete flow process is: one, alkyd resin and fire retardant proportional mixing are stirred into the polyester slurry; Two, use shredder to grind to form the slurry that fineness is 50 μ m in the polyester slurry; Three, use sand mill to be finish-ground to the slurry that fineness is 25 μ m in the polyester slurry after grinding; Four, in the polyester slurry, add solidifying agent, catalyzer in proportion, the solution after stirring is heat-resistant paint required for the present invention; The proportioning of its coating raw material is: alkyd resin: fire retardant: solidifying agent: catalyzer=100:30:20:1.
The pipe that is coated with according to the invention is meant: a technical process, and concrete flow process is: one, the heat-resistant paint of processing is inserted in the steeping vat of coating machine; Two, fiberglass pipe is delivered in the steeping vat of coating machine through the conduction roller and fully floods levelling with heat-resistant paint; Three, will deliver to the drying in oven of coating machine attached to the heat-resistant paint on the fiberglass pipe through take off roll.
Plated film of the present invention is meant: a technical process specifically is meant the fiberglass pipe after the oven dry is plated metallic membranes such as silver, copper, aluminium, titanium, stainless steel through vacuum plating unit according to different demands.
Alkyd resin of the present invention is meant: be the abbreviation of saturated polyester tackiness agent, mainly be made up of saturated polyester resin, initiator, promotor, filler, thixotropic agent etc.; Be characterized in that sticking power is good, highly versatile, weather resisteant, snappiness are given prominence to.
Fire retardant of the present invention is meant: give the functional aid of polymkeric substance flame retardancy, its characteristic has heat-absorbing action, covering effect, suppresses the smothering action of chain reaction, non-flammable gas etc.
Solidifying agent of the present invention is meant: claiming linking agent again, is a kind of material or mixture of promoting or controlling curing reaction.
Catalyzer of the present invention is meant: be a kind ofly can improve chemical reaction rate, and the material or the solvent of permanent change do not take place this body structure.
Fiberglass pipe of the present invention is meant: be with in the high speed of polymerization device of photoelectric heat one, solidifying behind the glass fiber solvent impregnated resin, through the traction pultrusion; It has corrosion resistance and good, ageing resistance and resistance toheat, characteristics such as cold tolerance is good, in light weight, intensity is high, and wear resistance is good, and electrical insulating property is good.
Claims (1)
1. light-type high-temperature heat insulation electromagnetic shielding composite bushing and working method thereof, it by the substrate glass fibre pipe adopt system coating, be coated with pipe, its working method of three technical process completion of plated film;
It is characterized in that having adopted system coating process flow process: one, alkyd resin and fire retardant proportional mixing are stirred into the polyester slurry; Two, use shredder to grind to form the slurry that fineness is 50 μ m in the polyester slurry; Three, use sand mill to be finish-ground to the slurry that fineness is 25 μ m again in the polyester slurry after grinding; Four, in the polyester slurry, add solidifying agent, catalyzer in proportion, the solution after stirring is heat-resistant paint required for the present invention; The proportioning of its coating raw material is: alkyd resin: fire retardant: solidifying agent: catalyzer=100:30:20:1;
It is characterized in that having adopted and be coated with plumber's process flow: one, the heat-resistant paint of processing is inserted in the steeping vat of coating machine; Two, fiberglass pipe is delivered in the steeping vat of coating machine through the conduction roller and fully floods levelling with heat-resistant paint; Three, will deliver to the drying in oven of coating machine attached to the heat-resistant paint on the fiberglass pipe through take off roll;
It is characterized in that adopting the coating process flow process: the fiberglass pipe after will drying plates metallic membranes such as silver, copper, aluminium, titanium, stainless steel through vacuum plating unit according to different demands.