CN102786790A - 一种无卤阻燃pc薄膜配方 - Google Patents
一种无卤阻燃pc薄膜配方 Download PDFInfo
- Publication number
- CN102786790A CN102786790A CN2012102900034A CN201210290003A CN102786790A CN 102786790 A CN102786790 A CN 102786790A CN 2012102900034 A CN2012102900034 A CN 2012102900034A CN 201210290003 A CN201210290003 A CN 201210290003A CN 102786790 A CN102786790 A CN 102786790A
- Authority
- CN
- China
- Prior art keywords
- raw material
- halogen
- black
- free flame
- retarded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种无卤阻燃PC薄膜配方,其成分具体描述如下:PC原料(所述PC原料为PC基础树脂、其熔融指数为5~20g/10min)、增韧剂(所述增韧剂的主要成分为全丙烯酸酯类核抗冲击剂)、抗氧化剂(所述抗氧化剂为受阻酚类主抗氧剂)、黑色色母(所述黑色色母是以PC为载体的碳黑色素母粒,碳黑含量40%~50%),所述PC原料可采用PC回收料代替,所述黑色色母可用白色色母或其他颜色色母代替。
Description
技术领域
本发明涉及一种无卤阻燃PC薄膜配方。
背景技术
PC薄膜是聚碳酸酯薄膜的简称,拥有良好韧性、良好的尺寸稳定性,可在-60~120℃下长期使用,随着世界绿色环保机构及欧盟相关标准的出台,用户对产品结构性能要求的发展,开发具有高阻燃性,无卤,超薄的PC薄膜具有重大意义。
发明内容
本发明提供了一种无卤阻燃PC薄膜配方。
本发明的技术方案是:
一种无卤阻燃PC薄膜配方,其成分具体描述如下:PC原料(所述PC原料为PC基础树脂、其熔融指数为5~20g/10min)、增韧剂(所述增韧剂的主要成分为全丙烯酸酯类核抗冲击剂)、抗氧化剂(所述抗氧化剂为受阻酚类主抗氧剂)、黑色色母(所述黑色色母是以PC为载体的碳黑色素母粒,碳黑含量40%~50%),所述PC原料可采用PC回收料代替,所述黑色色母可用白色色母或其他颜色色母代替。
本发明的有益效果是:本发明提供的改性PC配方在对PC树脂的力学性能和热力学性能等改变不大的基础上提高了其阻燃性,并且可将其厚度控制在一定范围,该配方不但可以满足RoHS指令,而且可以顺利通过欧盟WEEE指令中有关物料回收条款对总卤含量的苛刻要求。扩大了其在电子防火工程塑料领域及其出口领域的应用。本发明配方合理,改性后流动性好,质量稳定,制备工艺简单。
具体实施方式
一种无卤阻燃PC薄膜配方,其成分具体描述如下:PC原料(所述PC原料为PC基础树脂、其熔融指数为5~20g/10min)、增韧剂(所述增韧剂的主要成分为全丙烯酸酯类核抗冲击剂)、抗氧化剂(所述抗氧化剂为受阻酚类主抗氧剂)、黑色色母(所述黑色色母是以PC为载体的碳黑色素母粒,碳黑含量40%~50%),所述PC原料可采用PC回收料代替,所述黑色色母可用白色色母或其他颜色色母代替。本发明的有益效果是:本发明提供的改性PC配方在对PC树脂的力学性能和热力学性能等改变不大的基础上提高了其阻燃性,并且可将其厚度控制在一定范围,该配方不但可以满足RoHS指令,而且可以顺利通过欧盟WEEE指令中有关物料回收条款对总卤含量的苛刻要求。扩大了其在电子防火工程塑料领域及其出口领域的应用。本发明配方合理,改性后流动性好,质量稳定,制备工艺简单。
Claims (1)
1.一种无卤阻燃PC薄膜配方,其特征在于其成分具体描述如下:PC原料(所述PC原料为PC基础树脂、其熔融指数为5~20g/10min)、增韧剂(所述增韧剂的主要成分为全丙烯酸酯类核抗冲击剂)、抗氧化剂(所述抗氧化剂为受阻酚类主抗氧剂)、黑色色母(所述黑色色母是以PC为载体的碳黑色素母粒,碳黑含量40%~50%),所述PC原料可采用PC回收料代替,所述黑色色母可用白色色母或其他颜色色母代替。