Background technology
Grouan is the volcanic rock that a kind of magma condenses below the face of land and forms, and staple is feldspar and quartz.Because grouan is plutonite, often can form physically well develop, mineral grain that naked eyes can be distinguished, thereby gain the name.Grouan is easy-weathering not, and color is attractive in appearance, and appearance luster can keep more than a century, because its hardness is high, wear-resistant, and except being used as senior building decorative engineering, ground, hall, or the material of the first-selection of open-air engraving.The natural formation of grouan need pass through a century in addition thousands of before; Because human constantly exploitation, the reserves of natural granite constantly reduce, and in the course of processing of grouan, can produce the waste material and the granite powder of many grouan; The words that these waste materials and granite powder are not used; Will produce severe contamination, destroy environment, the restriction expanding economy.The method of traditional digestion granite powder adopts low temperature, mixes sticking technology making twice-laid stuff, and its density of product is big, reaches 2.5 tons/m
3, it is fast to conduct heat, and in making processes, needs to add chemical adhesive.
Also have a kind of application number to be 200710142893.3 to be called the Chinese invention patent application of " utilize granite powder waste material artificial compound board prepared " to disclose a kind of novel artificial composite plank, process by the grouan waste material.Prescription comprises resin, solidifying agent, promotor, granite powder, gravel particle or the like.This artificial composite plank, pattern is many, and length can accomplish enough big, thereby can be applied to various places.But owing to used inflammable or deleterious chemicals in the prescription of said artificial composite plank, people's cognition is damaged, and density is big, deal is heavy, and transportation and installation be inconvenience all, is difficult for insulation again, nor can reuses.Therefore, the structure of this composition board also need be done further improvement.
Summary of the invention
Technical problem to be solved by this invention be a kind of insulation, fire prevention, in light weight and environmental protection be provided to above-mentioned prior art present situation utilize the generative foaming material of granite powder for raw material.
The present invention solves the problems of the technologies described above the technical scheme that is adopted: this utilizes the generative foaming material of granite powder for raw material; It is characterized in that: the prescription of this generative foaming material consists of: granite powder is 70%~90%; The filler of fluxing is 6%~25%; Pore creating agent is 1%~5%, and the polymerization material is 1%~5%, and above-mentioned per-cent is mass percent.
As improvement, the said filler of fluxing may be selected to be in talcum powder, silicon powder, wollastonite material, mica powder, the dry powder any two kinds with the combined compsn of Feldspar Powder.
As improvement; The component ratio of said compsn can be preferably: A: B: C=5: 1.5: 1.5; Wherein A representes Feldspar Powder; B is a kind of in talcum powder, silicon powder, wollastonite material, mica powder, the dry powder, and C is a kind of in talcum powder, silicon powder, wollastonite material, mica powder, the dry powder, and B and C are two kinds of materials inequality.
As improvement, said pore creating agent can be preferably zeyssatite, white titanium pigment, silit, lime carbonate, any two kinds of compsns in the barium carbonate.
Improve, the component ratio of said compsn may be selected to be 1: 1 again.
As improvement, said polymerization material may be selected to be the compsn of clay, wilkinite, borax.
Improve, the component ratio of said compsn can be preferably clay: wilkinite: borax=1: 1: 1 again.
Compared with prior art, the invention has the advantages that: generative foaming material of the present invention has following product performance:
(1) all raw materials are inorganic materials, no chemical pollution.
(2) high temperature burns till, more than high temperature resistant 1100 degree, and fire-resistant A level.
(3) cellular unicellular structure is airtight, and is waterproof, and heat conduction is slow.Waterproof, sound insulation, insulation.
(4) 0.3 ton/m of density range
3~1.2 tons/m
3, pressure-proof and snap-resistent, physical property is good.
(5) can reuse, still can burn till after dead meal is prepared burden again.
According to above-mentioned characteristic, the advantage of product of the present invention is, can fully digest the granite powder waste material, can solve the long-standing severe environmental pollution problem in grouan processing base, reaches environmental requirement.This product stable physical property, lightweight, insulation, resistance to compression, anti-folding can be used for construction wall or decoration of exterior wall, reaches building loss of weight and energy-conservation target.Also have this product also to have fire prevention, waterproof, sound damping performance, can be used for fire-retardant material, the body of wall barrier material.
Embodiment
Below in conjunction with embodiment the present invention is described in further detail, the per-cent of following indication is mass percent;
Embodiment one, and the granite powder that utilizes of present embodiment consists of granite powder 70% for the prescription of the generative foaming material of raw material, the filler 22% of fluxing, pore creating agent 3%, polymerization material 5%.The said filler of fluxing is the feldspar powder, talcum powder, and the silicon powder compsn, its ratio is 5: 1.5: 1.5; Said pore creating agent is a zeyssatite, the silit compsn, and its ratio is 1: 1, said polymerization material is a clay; Wilkinite, the borax compsn, its ratio is 1: 1: 1.
According to above-mentioned prescription, the making method of generative foaming material may further comprise the steps successively:
One, through pulverizing, screening granite powder, the filler of fluxing, pore creating agent, polymerization material particles of powder fineness are controlled to be more than 100 orders;
Two, granite powder, the filler of fluxing, pore creating agent, polymerization material powder are mixed and process compound, again compound is processed required granulate material through mold pressing or roll extrusion;
Three, the granulated material is put into the die body of desired shape, stacked moulding;
Four, the material that will stack moulding is then put into High Temperature Furnaces Heating Apparatus together with die body and is slowly heated; Temperature up to High Temperature Furnaces Heating Apparatus reaches 1100~1400 degree; And in temperature is the High Temperature Furnaces Heating Apparatus of 1100~1400 degree, heated 50~70 minutes, be preferably 60 minutes, heat and from High Temperature Furnaces Heating Apparatus, take out after accomplishing; Naturally cooling took out from die body after 11~13 hours, was the generative foaming finished material.
Embodiment two, and the granite powder that utilizes of present embodiment for the prescription of the generative foaming material of raw material is: granite powder 76%, the filler 18% of fluxing, pore creating agent 3%, polymerization material 3%.The said filler of fluxing is the feldspar powder, the wollastonite material, and the mica powder compsn, its ratio is 5: 1.5: 1.5; Said pore creating agent is a zeyssatite, the barium carbonate compsn, and its ratio is 1: 1, said polymerization material is a clay; Wilkinite, the borax compsn, its ratio is 1: 1: 1.
According to above-mentioned prescription, the making method of generative foaming material may further comprise the steps successively:
One, through pulverizing, screening granite powder, the filler of fluxing, pore creating agent, polymerization material particles of powder fineness are controlled to be more than 100 orders;
Two, granite powder, the filler of fluxing, pore creating agent, polymerization material powder are mixed and process compound, again compound is processed required granulate material through mold pressing or roll extrusion;
Three, the granulated material is put into the die body of desired shape, stacked moulding;
Four, the material that will stack moulding is then put into High Temperature Furnaces Heating Apparatus together with die body and is slowly heated; Temperature up to High Temperature Furnaces Heating Apparatus reaches 1100~1400 degree; And in temperature is the High Temperature Furnaces Heating Apparatus of 1100~1400 degree, heated 50~70 minutes, be preferably 60 minutes, heat and from High Temperature Furnaces Heating Apparatus, take out after accomplishing; Naturally cooling took out from die body after 11~13 hours, was the generative foaming finished material.
Embodiment three, and the granite powder that utilizes of present embodiment for the prescription of the generative foaming material of raw material is: granite powder 75%, the filler 15% of fluxing, pore creating agent 4%, polymerization material 6%.The said filler of fluxing is the feldspar powder, mica powder, and the dry powder compsn, its ratio was followed successively by 5: 1.5: 1.5; Said pore creating agent is a white titanium pigment, the silit compsn, and its ratio is 1: 1, said polymerization material is a clay; Wilkinite, the borax compsn, its ratio is 1: 1: 1.
According to above-mentioned prescription, the making method of generative foaming material may further comprise the steps successively:
One, through pulverizing, screening granite powder, the filler of fluxing, pore creating agent, polymerization material particles of powder fineness are controlled to be more than 100 orders;
Two, granite powder, the filler of fluxing, pore creating agent, polymerization material powder are mixed and process compound, again compound is processed required granulate material through mold pressing or roll extrusion;
Three, the granulated material is put into the die body of desired shape, stacked moulding;
Four, the material that will stack moulding is then put into High Temperature Furnaces Heating Apparatus together with die body and is heated; Temperature up to High Temperature Furnaces Heating Apparatus reaches 1100~1400 degree; And in temperature is the High Temperature Furnaces Heating Apparatus of 1100~1400 degree, heated 50~70 minutes, be preferably 60 minutes, heat and from High Temperature Furnaces Heating Apparatus, take out after accomplishing; Naturally cooling took out from die body after 11~13 hours, was the generative foaming finished material.This generative foaming material can be processed into exterior wall thermal insulation brick or warming plate, also can be used as the wall brick of indoor separation etc.