CN102767240B

CN102767240B - Waterproof roll

Info

Publication number: CN102767240B
Application number: CN201110114938.2A
Authority: CN
Inventors: 洪琼彬; 洪恩兰; 游捷
Original assignee: DONGSHUN PAINTS Co Ltd XIAMEN
Current assignee: DONGSHUN PAINTS Co Ltd XIAMEN
Priority date: 2011-05-05
Filing date: 2011-05-05
Publication date: 2014-06-25
Anticipated expiration: 2031-05-05
Also published as: CN102767240A

Abstract

The invention relates to a building roll, especially to a waterproof roll. The waterproof roll utilizes copper wire grids, energy storage silicon micro materials and regenerative PVC (polyvinyl chloride) materials as main materials, utilizes color paste and light calcium carbonate as fillers, and utilizes chlorinated paraffin, DOP (dioctyl-phthalate) and stearic acid as auxiliaries. The waterproof roll can be folded by various angles so as to greatly reduce the amount of the split joint parts, further can effectively reduce water penetration probability, simultaneously can have heat insulating and energy saving effects, and can be constructed simply.

Description

Waterproof roll

Technical field

The present invention relates to a kind of building coiled material, particularly a kind of building coiled material.

Background technology

Along with developing rapidly of China's building trade and becoming increasingly conspicuous of energy crisis, saving energy and reduce the cost of building is just important all the more.The building energy consumption of China accounts for 27% of national energy aggregate consumption, occupies first of national all kinds of energy consumption.The energy consumption of heating and air-conditioning accounts for 55% of building total energy consumption, but also increases in the speed with annual 1 percentage point.Because of a little, research and development insulating mold coating for construction has great economic benefit, environmental benefit and social benefit.

Traditional waterproof roll should cut clothing according to the shape amount of the carrying out body of waterproof matrix in waterproof construction, needs polylith splicing for the basic unit of complex contour, and this kind of joining method exists following defect:

1, directly affect the attractive in appearance of waterproofing course;

2, there is the durability of decades due to high-grade waterproof roll, and the current domestic cementing agent that can match with it that seldom has so, when cementing agent loses after attachment function in advance, will cause the waterproof failure of waterproof roll;

3, protection and the maintenance difficult of waterproof roll after construction: because no matter the bonding of waterproof roll and basic unit is Man Pu, Dian Pu, bar paving, empty paving; between coiled material and basic unit, will be all to walk water layer; no matter the penetrability breakage at any position; come unstuck, leak glue; even only have a place, the mistake that all will all decline of the whole coupled water-proof function that passes through aspect, if can not find breakage and rejected region; local repairing is just impossible, the waterproofing course of so only reforming.

Therefore, research and develop a kind of novel can multi-angle folding, greatly reduce the quantity of stitching portion, effectively reduce infiltration probability, there is heat-insulating and energy-saving effect simultaneously, easy construction, the waterproof roll that can be widely used in various senior constructure roofings, basement, washroom etc. is imperative.

Summary of the invention

The object of the invention is to overcome the deficiencies in the prior art, and provide one multi-angle to fold, greatly reduce the quantity of stitching portion, effectively reduce infiltration probability, there is heat-insulating and energy-saving effect, the waterproof roll of easy construction simultaneously.

The object of the invention is to be achieved through the following technical solutions: waterproof roll, by quality percentage composition, it mainly comprises: copper wire grid 20 ~ 30%, accumulation of energy silicon particle 5 ~ 7%, regeneration PVC material 37 ~ 44%, precipitated calcium carbonate 11 ~ 25%, chlorinated paraffin wax 4.15 ~ 4.38%, plasticizing agent 4.38 ~ 4.5%, stabilizing agent 1.32 ~ 1.41%, stearic acid 0.05 ~ 0.07%, mill base 2.0 ~ 2.3%.

As a modification of the present invention, described copper wire grid has good conduction, heat transfer, without magnetic, anticorrosive, low ductility, wear-resistant undermining can multi-angle folding property.

As a modification of the present invention, described accumulation of energy silicon particle outward appearance is spheric granules, and density is less compared with glass microballoon, and thermal conductivity is poorer.

One improve again as of the present invention, described waterproof roll, by quality percentage composition, it mainly comprises: copper wire grid 20%, accumulation of energy silicon particle 5%, regeneration PVC material 37%, precipitated calcium carbonate 25%, chlorinated paraffin wax 4.15%, plasticizing agent 4.38%, stabilizing agent 1.41%, stearic acid 0.05%, mill base 2.3%.

One improve again as of the present invention, described waterproof roll, by quality percentage composition, it mainly comprises: copper wire grid 23%, accumulation of energy silicon particle 6%, regeneration PVC material 44%, precipitated calcium carbonate 15%, chlorinated paraffin wax 4.2%, plasticizing agent 4.4%, stabilizing agent 1.32%, stearic acid 0.06%, mill base 2.0%.

One improve again as of the present invention, described waterproof roll, by quality percentage composition, it mainly comprises: copper wire grid 24%, accumulation of energy silicon particle 5.5%, regeneration PVC material 40%, precipitated calcium carbonate 17%, chlorinated paraffin wax 4.3%, plasticizing agent 4.45%, stabilizing agent 1.39%, stearic acid 0.07%, mill base 2.1%.

One improve again as of the present invention, described waterproof roll, by quality percentage composition, it mainly comprises: copper wire grid 30%, accumulation of energy silicon particle 7%, regeneration PVC material 39%, precipitated calcium carbonate 11%, chlorinated paraffin wax 4.38%, plasticizing agent 4.5%, stabilizing agent 1.38%, stearic acid 0.049%, mill base 2.2%.

Beneficial effect of the present invention: waterproof roll of the present invention, adopting copper wire grid, accumulation of energy silicon particle, regeneration PVC material % is main batching, mill base, precipitated calcium carbonate are filler, chlorinated paraffin wax, plasticizing agent, stearic acid are auxiliary agent, not only can multi-angle folding, thus greatly reduce the quantity of stitching portion, can also effectively reduce infiltration probability, there is heat-insulating and energy-saving effect, easy construction simultaneously.

The specific embodiment

Embodiment 1

Get 5 kilograms of accumulation of energy silicon particles, 37 kilograms, regeneration PVC material, 25 kilograms of precipitated calcium carbonates, 4.15 kilograms of chlorinated paraffin waxs, 4.38 kilograms, plasticizing agent, 1.41 kilograms of stabilizing agents, 0.05 kilogram of stearic acid, 2.3 kilograms of mill bases, in input mixer, high-speed stirred is to uniform paste, and then drop into 20 kilograms of copper wire grids, through high temperature compound make the present invention can the folding heat-insulating and energy-saving waterproof roll of multi-angle.

Embodiment 2

Get 6 kilograms of accumulation of energy silicon particles, 44 kilograms, regeneration PVC material, 15 kilograms of precipitated calcium carbonates, 4.2 kilograms of chlorinated paraffin waxs, 4.4 kilograms, plasticizing agent, 1.32 kilograms of stabilizing agents, 0.06 kilogram of stearic acid, 2.0 kilograms of mill bases, in input mixer, high-speed stirred is to uniform paste, and then drop into 23 kilograms of copper wire grids, through high temperature compound make the present invention can the folding heat-insulating and energy-saving waterproof roll of multi-angle.

Embodiment 3

Get 5.5 kilograms of accumulation of energy silicon particles, 40 kilograms, regeneration PVC material, 17 kilograms of precipitated calcium carbonates, 4.3 kilograms of chlorinated paraffin waxs, 4.45 kilograms, plasticizing agent, 1.39 kilograms of stabilizing agents, 0.07 kilogram of stearic acid, 2.1 kilograms of mill bases, in input mixer, high-speed stirred is to uniform paste, and then drop into 24 kilograms of copper wire grids, through high temperature compound make the present invention can the folding heat-insulating and energy-saving waterproof roll of multi-angle.

Embodiment 4

Get 7 kilograms of accumulation of energy silicon particles, 39 kilograms, regeneration PVC material, 11 kilograms of precipitated calcium carbonates, 4.38 kilograms of chlorinated paraffin waxs, 4.5 kilograms, plasticizing agent, 1.38 kilograms of stabilizing agents, 0.049 kilogram of stearic acid, 2.2 kilograms of mill bases, in input mixer, high-speed stirred is to uniform paste, and then drop into 30 kilograms of copper wire grids, through high temperature compound make the present invention can the folding heat-insulating and energy-saving waterproof roll of multi-angle.

The above only As preferred embodiment of the present invention, and not only above restriction the present invention, all any modifications of doing within the spirit and principles in the present invention, be equal to and replace and improvement etc., all should be included in protection scope of the present invention.

Claims

1. waterproof roll, it is characterized in that: by quality percentage composition, it mainly comprises: copper wire grid 20 ~ 30%, accumulation of energy silicon particle 5 ~ 7%, regeneration PVC material 37 ~ 44%, precipitated calcium carbonate 11 ~ 25%, chlorinated paraffin wax 4.15 ~ 4.38%, plasticizing agent 4.38 ~ 4.5%, stabilizing agent 1.32 ~ 1.41%, stearic acid 0.05 ~ 0.07%, mill base 2.0 ~ 2.3%.

2. the waterproof roll as described in claim 1, is characterized in that: described copper wire grid has good conduction, heat transfer, without magnetic, anticorrosive, low ductility, wear-resistant undermining can multi-angle folding property.

3. the waterproof roll as described in claim 1, is characterized in that: described accumulation of energy silicon particle outward appearance is spheric granules, and density is less than glass microballoon, and thermal conductivity is poorer than glass microballoon.

4. the waterproof roll as described in claim 1, it is characterized in that: by quality percentage composition, it mainly comprises: copper wire grid 20%, accumulation of energy silicon particle 5%, regeneration PVC material 37%, precipitated calcium carbonate 25%, chlorinated paraffin wax 4.15%, plasticizing agent 4.38%, stabilizing agent 1.41%, stearic acid 0.05%, mill base 2.3%.

5. the waterproof roll as described in claim 1, it is characterized in that: by quality percentage composition, it mainly comprises: copper wire grid 23%, accumulation of energy silicon particle 6%, regeneration PVC material 44%, precipitated calcium carbonate 15%, chlorinated paraffin wax 4.2%, plasticizing agent 4.4%, stabilizing agent 1.32%, stearic acid 0.06%, mill base 2.0%.

6. the waterproof roll as described in claim 1, it is characterized in that: by quality percentage composition, it mainly comprises: copper wire grid 24%, accumulation of energy silicon particle 5.5%, regeneration PVC material 40%, precipitated calcium carbonate 17%, chlorinated paraffin wax 4.3%, plasticizing agent 4.45%, stabilizing agent 1.39%, stearic acid 0.07%, mill base 2.1%.