CN102767240A

CN102767240A - Waterproof roll

Info

Publication number: CN102767240A
Application number: CN2011101149382A
Authority: CN
Inventors: 洪琼彬; 洪恩兰; 游捷
Original assignee: DONGSHUN PAINTS Co Ltd XIAMEN
Current assignee: DONGSHUN PAINTS Co Ltd XIAMEN
Priority date: 2011-05-05
Filing date: 2011-05-05
Publication date: 2012-11-07
Anticipated expiration: 2031-05-05
Also published as: CN102767240B

Abstract

The invention relates to a building roll, especially to a waterproof roll. The waterproof roll utilizes copper wire grids, energy storage silicon micro materials and regenerative PVC (polyvinyl chloride) materials as main materials, utilizes color paste and light calcium carbonate as fillers, and utilizes chlorinated paraffin, DOP (dioctyl-phthalate) and stearic acid as auxiliaries. The waterproof roll can be folded by various angles so as to greatly reduce the amount of the split joint parts, further can effectively reduce water penetration probability, simultaneously can have heat insulating and energy saving effects, and can be constructed simply.

Description

Waterproof roll

Technical field

The present invention relates to a kind of building coiled material, particularly a kind of building coiled material.

Background technology

Along with developing rapidly of China's building trade and becoming increasingly conspicuous of energy crisis, saving energy and reduce the cost of building is just important all the more.The building energy consumption of China accounts for 27% of national energy aggregate consumption, occupies first of the national all kinds of energy consumption.The energy consumption of heating and air-conditioning accounts for 55% of building total energy consumption, but also increases in the speed with annual 1 percentage point.Because of a little, the research and development insulating mold coating for construction has great economic benefit, environmental benefit and social benefit.

Traditional waterproof roll should cut clothing according to the shape amount of the carrying out body of waterproof matrix in waterproof construction, then need the polylith splicing for the basic unit of complex contour, and there is following defective in this kind joining method:

1, directly influences the attractive in appearance of waterproofing course;

2, because high-grade waterproof roll has the durability of decades, and the present domestic cementing agent that can be complementary with it that seldom has so, after cementing agent loses attachment function in advance, will cause the waterproof failure of waterproof roll;

3, protection and the maintenance difficult of waterproof roll after construction:, all will be to walk water layer between coiled material and the basic unit, no matter the penetrability at any position is damaged because no matter the bonding of waterproof roll and basic unit is Man Pu, Dian Pu, bar shop, empty shop; Come unstuck, leak glue; Even have only a place, the mistake that all will all decline of the whole coupled water-proof function that passes through aspect is if can not find breakage and rejected region; Then local repairing is just impossible, the waterproofing course of so only reforming.

Therefore, but it is folding to research and develop a kind of novel multi-angle, significantly reduces the quantity of jointing positions; Effectively reduce the infiltration probability; Have the heat-insulating and energy-saving effect simultaneously, easy construction, the waterproof roll that can be widely used in various senior constructure roofings, basement, washroom etc. is imperative.

Summary of the invention

The objective of the invention is to overcome the deficiency of prior art, but and provide a kind of multi-angle folding, significantly reduce the quantity of jointing positions, effectively reduce the infiltration probability, have the heat-insulating and energy-saving effect simultaneously, the waterproof roll of easy construction.

The object is achieved by the present invention, the following technical solution: the waterproofing membrane, by mass percent, which mainly includes: copper mesh grid 20 to 30%, the silicon micro material Chu 5-7% recycled PVC material 37 ~ 44%, 11 to 25% calcium carbonate, chlorinated paraffin 4.15 ~ 4.38%, 4.38 ~ 4.5% of plasticizer, stabilizer 1.32 to 1.41% stearic acid, 0.05 to 0.07%, 2.0 to 2.3% paste.

As a kind of improvement of the present invention, but said copper wire grid has favorable conductive, heat transfer, no magnetic, anticorrosive, low ductility, the wear-resistant multi-angle folding property that undermines.

A modification of the present invention, said material Chu appearance of the silicon micro-spherical particles, the density is smaller than glass beads, thermal conductivity is worse.

As a further improvement of the invention, the waterproofing membrane, by mass percentage, which mainly consists of: 20% of the copper mesh grid, Chu to 5% of silicon micro-material, recycled PVC material 37% calcium carbonate 25% chlorinated paraffin 4.15% 4.38% plasticizer, stabilizer, 1.41%, 0.05% stearic acid, 2.3% paste.

As a further improvement of the invention, the waterproofing membrane, by mass percentage, which mainly consists of: 23% of the copper mesh grid, Chu to 6% of silicon micro-material, recycled PVC material 44% calcium carbonate 15% chlorinated paraffin 4.2%, 4.4% plasticizer, stabilizer 1.32%, 0.06% stearic acid, 2.0% paste.

As a further improvement of the invention, the waterproofing membrane, by mass percentage, which mainly consists of: 24% of the copper mesh grid, Chu to 5.5% silicon micro materials, recycled PVC material 40% calcium carbonate 17% chlorinated paraffin 4.3%, 4.45% plasticizer, stabilizer 1.39%, 0.07% stearic acid, 2.1% paste.

As a further improvement of the invention, the waterproofing membrane, by mass percentage, which mainly consists of: 30% of the copper mesh grid, Chu to 7% of silicon micro-material, recycled PVC material 39% calcium carbonate 11% 4.38% chlorinated paraffin, 4.5% plasticizer, stabilizer 1.38%, 0.049% stearic acid, 2.2% paste.

The beneficial effects of the invention: The present invention waterproof membrane, made of copper mesh grid, Chu able silicon micro-materials, recycled PVC material% based ingredients? Colorants, light calcium carbonate as filler, chlorinated paraffin, plasticized agent, stearic acid as additives, not only multi-angle folding, thus greatly reducing the number of splices, but also reduce the chances of water seepage, but also has thermal insulation energy saving, easy construction.

The specific embodiment

Embodiment 1

Chu silicon micro material can take 5kg, recycled PVC material 37 kg, 25 kg precipitated calcium carbonate, chlorinated paraffin 4.15 kg, 4.38 kg plasticizers, stabilizers 1.41 kg, 0.05 kg stearic acid, paste 2.3 kg, input mixer, high speed stirring until a uniform paste, and then put copper mesh grid 20 kg, high temperature composite of the present invention can be prepared by multi-angle folding saving insulation waterproofing membrane.

Embodiment 2

Take Chu able silicon micro material 6 kg, recycled PVC material 44 kg, 15 kg calcium carbonate, chlorinated paraffin 4.2 kg, 4.4 kg plasticizers, stabilizers, 1.32 kg, 0.06 kg stearate, paste 2.0 kg, input mixer, high speed stirring until a uniform paste, and then put copper mesh grid 23 kg, high temperature composite of the present invention can be prepared by multi-angle folding saving insulation waterproofing membrane.

Embodiment 3

Take Chu able to feed 5.5 kg silicon micro, recycled PVC material 40 kg, 17 kg calcium carbonate, chlorinated paraffin 4.3 kg, 4.45 kg plasticizers, stabilizers, 1.39 kg, 0.07 kg stearate, paste 2.1 kg, input mixer, high speed stirring until a uniform paste, and then put copper mesh grid 24 kg, high temperature composite of the present invention can be prepared by multi-angle folding saving insulation waterproofing membrane.

Embodiment 4

Take Chu can feed 7 kg silicon micro, recycled PVC material 39 kg, 11 kg calcium carbonate, chlorinated paraffin 4.38 kg, 4.5 kg plasticizers, stabilizers, 1.38 kg, stearic acid 0.049 kg, paste 2.2 kg, input mixer, high speed stirring until a uniform paste, and then put copper mesh grid 30 kg, high temperature composite of the present invention can be prepared by multi-angle folding saving insulation waterproofing membrane.

The above only is preferred embodiment of the present invention, and not only above restriction the present invention, all any modifications of within spirit of the present invention and principle, being done, is equal to and replaces and improvement etc., all should be included in protection scope of the present invention.

Claims

A waterproof membrane, wherein:? Percentage by mass, which mainly include:? Copper mesh grid 20 to 30 percent, Chu able silicon micro feed 5 to 7%, recycled PVC material 37 ~ 44%, light 11 to 25% calcium carbonate, chlorinated paraffin 4.15 ~ 4.38%, 4.38 ~ 4.5% of plasticizer, stabilizer, 1.32 to 1.41% stearic acid, 0.05 to 0.07%, 2.0 to 2.3% paste.
2. waterproof roll as claimed in claim 1 is characterized in that: but described copper wire grid has favorable conductive, heat transfer, no magnetic, anticorrosive, low ductility, the wear-resistant multi-angle folding property that undermines.
3 as claimed in claim 1, wherein the waterproof membrane, characterized in that: said material Chu appearance of the silicon micro-spherical particles, the density is less than glass beads, poor thermal conductivity than glass beads.
4 as claimed in claim 1, wherein said waterproofing membrane, characterized in that: the content by mass percent, mainly comprising: 20% copper mesh grid, Chu material to silicon micro 5% 37% recycled PVC material, light 25% calcium chloride, 4.15% paraffin plasticizer 4.38%, 1.41% stabilizer, 0.05% stearic acid, 2.3% paste.
5 as claimed in claim 1, wherein the waterproof membrane, characterized in that: percentage by mass, which mainly consists of: 23% of the copper mesh grid, Chu to 6% of silicon micro-material, 44% of recycled PVC material, light 15% calcium chloride, 4.2% paraffin, 4.4% plasticizer, stabilizer, 1.32%, 0.06% stearic acid, 2.0% paste.
As claimed in claim 1, wherein the waterproof membrane, characterized in that: percentage by mass, which mainly consists of: 24% of the copper mesh grid, Chu to 5.5% silicon micro-material, 40% of recycled PVC material, light 17% calcium carbonate, 4.3% chlorinated paraffin plasticizer 4.45%, 1.39% stabilizer, 0.07% stearic acid, 2.1% paste.
As claimed in claim 1, wherein the waterproof membrane, characterized in that: percentage by mass, which mainly consists of: 30% of the copper mesh grid, Chu material to silicon micro 7% 39% recycled PVC material, light 11% calcium chloride, 4.38% paraffin, 4.5% plasticizer, stabilizer 1.38%, 0.049% stearic acid, 2.2% paste.