CN102765907A - 一种利用高炉矿渣生产加气空心砖方法 - Google Patents

一种利用高炉矿渣生产加气空心砖方法 Download PDF

Info

Publication number
CN102765907A
CN102765907A CN2012102217080A CN201210221708A CN102765907A CN 102765907 A CN102765907 A CN 102765907A CN 2012102217080 A CN2012102217080 A CN 2012102217080A CN 201210221708 A CN201210221708 A CN 201210221708A CN 102765907 A CN102765907 A CN 102765907A
Authority
CN
China
Prior art keywords
blast
furnace slag
parts
hollow brick
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012102217080A
Other languages
English (en)
Other versions
CN102765907B (zh
Inventor
强晓震
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Original Assignee
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN2012102217080A priority Critical patent/CN102765907B/zh
Publication of CN102765907A publication Critical patent/CN102765907A/zh
Application granted granted Critical
Publication of CN102765907B publication Critical patent/CN102765907B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用高炉矿渣生产加气空心砖方法，该方法包括有以下步骤：1）将水泥、石膏和磷矿渣混合进行破碎后，并按质量份取5-10份的水泥、1-3份的石膏和12-35份的磷矿渣等；2）在细磨前的质量份取50-70份的高炉矿渣和1-3份的铝粉，并将破碎后的水泥、石膏和磷矿渣与高炉矿渣及铝粉等混合均匀后细磨；本发明高炉矿渣用量大、节能环保，缓解高炉矿渣堆存处理带来的环境污染问题，同时为空心砖提供了新的原料来源。

Description

一种利用高炉矿渣生产加气空心砖方法
技术领域
本发明涉及新型建材领域，具体属于一种利用高炉矿渣生产加气空心砖方法。
背景技术
高炉矿渣是冶炼生铁时从高炉中排出的一种废渣。在高炉冶炼生铁时，从高炉加入的原料，除了铁矿石和燃料(焦炭)外，还要加入助熔剂。当炉温达到1400一1600℃时，助熔剂与铁矿石发生高温反应生成生铁和矿渣。高炉矿渣是由脉石、灰分、助熔剂和其他不能进入生铁中的杂质组成的，是一种易熔混合物。从化学成分来看，高炉矿渣是属于硅酸盐质材料。每生产1t生铁，高炉矿渣的排放量随着矿石品位和冶炼方法不同而变化。例如采用贫铁矿炼铁时，每吨生铁产出1．0一1．2t高炉渣；用富铁矿炼铁时，每t生铁只产出0．25t高炉渣。由于近代选矿和炼铁技术的提高，每吨生铁产出的高炉矿渣量已经大大下降。
　　长期以来，高炉矿渣的综合利用一直是个世界性难题，尽管国内外对高炉矿渣的综合利用进行了大量的研究，但是由于技术上和经济上的种种原因，大多数未付诸工业实现。
综合所述，用高炉矿渣为辅助原料生产水泥、墙体砖、道路材料已有报道，以建筑垃圾作为主要原料用于加气砌块的生产还未见报导。
发明内容
本发明的目的在于提供一种利用高炉矿渣生产加气空心砖方法，高炉矿渣用量大、节能环保，缓解高炉矿渣堆存处理带来的环境污染问题，同时为空心砖提供了新的原料来源。
本发明的技术方案如下：
一种利用高炉矿渣生产加气空心砖方法，其特征在于，该方法包括有以下步骤：
    1）、按质量份取5-10份的水泥、1-3份的石膏和12-35份的磷矿渣、2-5份的可再分散性乳胶粉，混合进行破碎；
2）、按质量份取40-50份的高炉矿渣和0.05-0.08份的铝粉，并将破碎后的水泥、石膏和磷矿渣与高炉矿渣及铝粉混合均匀后细磨；
3）、将城市无机垃圾进行破碎，并按质量份取10-20份的城市无机垃圾；
4）、将破碎后城市无机垃圾和细磨后的干料、8-12份生石灰放入到搅拌设备中，并加水、相当于水泥质量10-15%的环氧四氢邻苯二甲酸二辛酯进行充分搅拌；
5）将上述步骤（4）搅拌后的浆料在65-75℃温度下，发泡时间30-40min；
6）、将发泡浆料注入到成型模具内形成生坯，生坯经过蒸汽养护得加气空心砖成品。
本发明与现有技术相比具有如下优点：
与其他建筑砌块相比，本发明生产的加气砌块容重轻，强度高，特别适用于高层建筑的承重墙或内墙隔断用。
与加气砌块相比，本发明的主要原料为高炉矿渣，有利于解决高炉矿渣堆存处理而带来的环境污染问题。
总之，本发明结合我国高炉矿渣量大、利用率低的实际情况，产品性能符合建筑用承重和非承重墙体材料质量要求。砌块主要原材料为废建筑垃圾，使用量大，有利于解决高炉矿渣堆存处理而带来的环境污染问题，为城市无机垃圾的资源化利用开辟了一条新的利用途径。
具体实施方式
一种利用高炉矿渣生产加气空心砖方法，该方法包括有以下步骤：
1）、按质量份取8份的水泥、2份的石膏和25份的磷矿渣、4份的可再分散性乳胶粉，混合进行破碎；
2）、按质量份取50份的高炉矿渣和0.05份的铝粉，并将破碎后的水泥、石膏和磷矿渣与高炉矿渣及铝粉混合均匀后细磨；
3）、将城市无机垃圾进行破碎，并按质量份取10份的城市无机垃圾；
4）、将破碎后城市无机垃圾和细磨后的干料、10份生石灰放入到搅拌设备中，并加水、相当于水泥质量10-15%的环氧四氢邻苯二甲酸二辛酯进行充分搅拌；
5）将上述步骤（4）搅拌后的浆料在65-75℃温度下，发泡时间30-40min；
6）、将发泡浆料注入到成型模具内形成生坯，生坯经过蒸汽养护得加气空心砖成品。
将本发明生产的空心砖切割成100mm×100mm×100mm的立方体进行性能检测，检测结果如下：抗压强度3.18Mpa，容重0.63g/m3，收缩值0.45mm/m，重量损失3.91%，抗冻性强度损失18.81%。

Claims (1)

1.一种利用高炉矿渣生产加气空心砖方法，其特征在于，该方法包括有以下步骤：
    1）、按质量份取5-10份的水泥、1-3份的石膏和12-35份的磷矿渣、2-5份的可再分散性乳胶粉，混合进行破碎；
2）、按质量份取40-50份的高炉矿渣和0.05-0.08份的铝粉，并将破碎后的水泥、石膏和磷矿渣与高炉矿渣及铝粉混合均匀后细磨；
3）、将城市无机垃圾进行破碎，并按质量份取10-20份的城市无机垃圾；
4）、将破碎后城市无机垃圾和细磨后的干料、8-12份生石灰放入到搅拌设备中，并加水、相当于水泥质量10-15%的环氧四氢邻苯二甲酸二辛酯进行充分搅拌；
5）将上述步骤（4）搅拌后的浆料在65-75℃温度下，发泡时间30-40min；
6）、将发泡浆料注入到成型模具内形成生坯，生坯经过蒸汽养护得加气空心砖成品。
CN2012102217080A 2012-06-30 2012-06-30 一种利用高炉矿渣生产加气空心砖方法 Active CN102765907B (zh)