CN102765880A - 浮法玻璃 - Google Patents
浮法玻璃 Download PDFInfo
- Publication number
- CN102765880A CN102765880A CN2012102668193A CN201210266819A CN102765880A CN 102765880 A CN102765880 A CN 102765880A CN 2012102668193 A CN2012102668193 A CN 2012102668193A CN 201210266819 A CN201210266819 A CN 201210266819A CN 102765880 A CN102765880 A CN 102765880A
- Authority
- CN
- China
- Prior art keywords
- glass
- cao
- float glass
- mgo
- float
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种浮法成型的钠硅钙玻璃。玻璃组成及重量百分比为:SiO271.7~71.9%,Al2O3 0.8~1.1%,Fe2O3 0.1~0.13%,CaO 8.5~8.8%,MgO 3.8~4.2%,R2O 14~14.5%,SO3 0.18~0.25%,R为K和/或Na。优选地,玻璃组成及重量百分比为:SiO2 71.8%,Al2O3 1%,Fe2O3 0.1%,CaO 8.7%,MgO 4%,R2O 14.2%,SO3 0.2%,R为K和/或Na。本发明通过合理设计玻璃组分,并通过浮法工艺生产的玻璃,其具有弯曲强度高、透过率高、气泡个数少等优点。
Description
技术领域
本发明公开了一种浮法成型的钠硅钙玻璃。
背景技术
钠硅钙玻璃,属于硅酸盐玻璃系列,是目前实用价值最大的一类玻璃产品。
发明内容
为了解决现有技术中存在的技术问题,本发明的目的在于提供一种质量优廉的浮法玻璃。
本发明采用的技术方案如下:
浮法玻璃,其特征在于,玻璃组成及重量百分比为:SiO2 71.7~71.9%,Al2O30.8~1.1%,Fe2O3 0.1~0.13%,CaO 8.5~8.8%,MgO 3.8~4.2%,R2O 14~14.5%,SO3 0.18~0.25%,R为K和/或Na。
优选地,玻璃组成及重量百分比为:SiO2 71.8%,Al2O3 1%,Fe2O3 0.1%,CaO 8.7%,MgO 4%,R2O 14.2%,SO3 0.2%,R为K和/或Na。
本发明通过合理设计玻璃组分,并通过浮法工艺生产的玻璃,其具有弯曲强度高、透过率高、气泡个数少等优点。
本发明生产的浮法玻璃,其性能测试参数如下:
具体实施方式
以下结合实施例对本发明作进一步的说明。
实施例1
玻璃组成及重量百分比为:SiO2 71.7%,Al2O3 1.1%,Fe2O3 0.1%,CaO 8.8%,MgO 3.8%,K2O 14.32%,SO3 0.18%。
据此生产的浮法玻璃,具有如下性能:
玻璃澄清温度为1458.3℃,作业温度为1100℃,软化点为731.3℃,Tg转变温度为547℃。
实施例2
玻璃组成及重量百分比为:SiO2 71.9%,Al2O3 0.8%,Fe2O3 0.13%,CaO 8.5%,MgO4.2%,Na2O 14.22%,SO3 0.25%。
据此生产的浮法玻璃,具有如下性能:
玻璃澄清温度为1459.3℃,作业温度为1108℃,软化点为731.5℃,Tg转变温度为546.5℃。
实施例3
玻璃组成及重量百分比为:SiO2 71.8%,Al2O3 1%,Fe2O3 0.1%,CaO 8.7%,MgO4%,K2O 8.2%,Na2O 6%,SO3 0.2%。
据此生产的浮法玻璃,具有如下性能:
玻璃澄清温度为1458.5℃,作业温度为1113℃,软化点为730.8℃,Tg转变温度为546.8℃。
以上内容仅仅是对本发明构思所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明的构思或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。
Claims (2)
1.浮法玻璃,其特征在于,玻璃组成及重量百分比为:SiO2 71.7~71.9%,Al2O3 0.8~1.1%,Fe2O3 0.1~0.13%,CaO 8.5~8.8%,MgO 3.8~4.2%,R2O 14~14.5%,SO3 0.18~0.25%,R为K和/或Na。
2.根据权利要求1所述的浮法玻璃,其特征在于,玻璃组成及重量百分比为:SiO2 71.8%,Al2O3 1%,Fe2O3 0.1%,CaO 8.7%,MgO 4%,R2O 14.2%,SO30.2%,R为K和/或Na。