CN102756606B - 一种能够释放负离子和远红外线的炭雕 - Google Patents
一种能够释放负离子和远红外线的炭雕 Download PDFInfo
- Publication number
- CN102756606B CN102756606B CN201210257154.XA CN201210257154A CN102756606B CN 102756606 B CN102756606 B CN 102756606B CN 201210257154 A CN201210257154 A CN 201210257154A CN 102756606 B CN102756606 B CN 102756606B
- Authority
- CN
- China
- Prior art keywords
- far
- finished product
- active carbon
- powder
- semi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种能够释放负离子和远红外线的炭雕，其主要由下述重量百分比原料制成：电气石粉1－10%、远红外粉1－10%和活性炭半成品80－98%；所述活性炭半成品由下述方法制得：将牡丹原料用pH为1－3、质量浓度20－60%的氯化锌溶液浸渍吸收后，转入碳化炉中于300－500℃密闭碳化1－6小时，出料，冷却至室温得活性炭半成品；所述牡丹原料选自牡丹根、茎和叶中的一种或两种以上，所述氯化锌溶液的用量为牡丹原料重量的1－5倍。该炭雕不仅能吸附清除室内有害气体分子，消除室内异味，还能释放负离子和远红外线，起到净化空气、促进人体健康的保健作用。
Description
技术领域
本发明属于炭雕制备技术领域，具体涉及一种能够释放负离子和远红外线的炭雕，该炭雕不仅能吸附清除室内有害气体分子，消除室内异味，还能释放负离子和远红外线，起到净化空气、促进人体健康的保健作用。
背景技术
炭雕是由活性碳加工成型的艺术品，在赋予其优美的外形和文化底蕴的同时，最大限度地保留了活性炭的活性，是现代技术与传统工艺的完美结合。炭雕可以持续吸附空气中各种有害气体，净化室内空气，在关注大众健康的同时兼具装饰功能，是一种多功能环保产品。
负离子：原子失去或获得电子后所形成的带电粒子叫离子，而带一个或多个负电荷的离子称为“负离子”，亦称“阴离子”。氧的离子状态一般为负离子，也称负氧离子。十九世纪，德国物理学家菲利浦·莱昂纳第一个证明了负氧离子能对人的机体生理活动产生影响，对人体有益。此后，采用负离子治疗疾病的论文不胜枚举，被誉为“空气维生素”。世界卫生组织规定，清新空气的负氧离子标准浓度为每立方厘米空气中不低于1000—1500个。
但是，现代社会发展已破坏了自然界中离子的平衡、城市群，尤其是密闭的空间中，包括住宅、办公室、运输工具等，负氧离子更缺乏（城市住宅为每立方厘米100个，办公室为每立方厘米40 ~50个）。为了为人们提供更健康的环境，发展了很多人工负氧离子技术和设备，如负离子转换器和纳子富勒烯负离子释放器等。
电气石是一种多元素硅酸岩天然矿物，含有镁、铝、铁、硼等10多种对人体有利的微量元素。电气石是一种结构特殊的极性结晶体，其受热时会带上电荷（热释电效应），能使其周围的极性离子在平衡位置振动而引起偶极矩变化，将普通热能转换为波长在8—14μm远红外线，并产生电离子。电气石因其热电性和压电性释放的远红外线和负离子均对人体有益。在炭雕工艺中加入电气石，使其既具有装饰美化效果，还可以吸收空气中有害气体，释放负离子和远红外线，具有环保、保健功能。
发明内容
本发明目的在于提供一种能够释放负离子和远红外线的炭雕和其成型方法，该炭雕不仅能吸附清除室内有害气体分子，消除室内异味，还能释放负离子和远红外线，起到净化空气、促进人体健康的保健作用。
为实现上述目的，本发明采用如下技术方案：
一种能够释放负离子和远红外线的炭雕，其主要由下述重量百分比原料制成：电气石粉1－10%、远红外粉1－10%和活性炭半成品80－98%，所述活性炭半成品由下述方法制得：将牡丹原料用pH为1－3、质量浓度20－60%的氯化锌溶液浸渍吸收后，转入碳化炉中于300－500℃密闭碳化1－6小时，出料，冷却至室温得活性炭半成品；所述牡丹原料选自牡丹根、茎和叶中的一种或两种以上，所述氯化锌溶液的用量为牡丹原料重量的1－5倍。
所述能够释放负离子和远红外线的炭雕的成型方法，其包括以下步骤：将电气石粉、远红外粉和活性炭半成品混匀，用质量浓度40－60%的磷酸溶液于120－180℃浸渍吸收后，加入硅丙乳液，混匀，置模具中采用分子吸压成型技术制成块状无缝炭雕，然后移入火化炉中于400－500℃活化40－60min，出料；出料后用清水煮沸，固液分离后，固体用清水洗涤至pH为5－6，再经脱水、烘干即得；其中，所述磷酸溶液的用量为电气石粉、远红外粉和活性炭半成品总重量的2－5倍，硅丙乳液的用量为电气石粉、远红外粉和活性炭半成品总重量的0.2－0.4倍。
活性炭半成品制备过程中所用的氯化锌溶液可通过添加盐酸将pH调至1－3，牡丹原料在浸渍时可间隔三、五个小时充分搅拌，以利于氯化锌溶液被完全吸收，一般10h左右可充分吸收。原料电气石粉、远红外粉和活性炭半成品在用磷酸溶液浸渍时可间隔半小时左右充分搅拌，以利于磷酸溶液被完全吸收，一般9－13h左右可充分吸收。
以植物牡丹为原料获得的活性炭，其焦糖脱色率可达110%以上，亚甲基蓝的吸附值可达200mg/g以上，是优质的人造疏水性吸附剂。应用于清除室内环境污染的活性炭应具备与室内有害气体分子大小相匹配的孔隙结构，牡丹炭尤其适宜，可吸附甲醛、苯系物、氨、氡等所有对人体有害的气体及空气中的浮游菌，具有吸味、去毒、除臭、去湿、防霉、杀菌、净化等综合功能。
本发明炭雕以电气石粉、远红外粉和活性炭半成品为主要原料，可以依靠活性炭有效吸附空气中对人体有害的苯、甲醛、酮、氨等有害气体，还能释放出的负离子与空气中带正电粒子的细菌、灰尘、烟雾微粒以及水滴等物质中和沉降，从而达到净化空气的目的。此外，该炭雕还可依靠所含具有热电性和压电性的电气石粉和远红外粉，发射8－14μm波长的远红外线（发射密度略高于0.04W/cm2），对人体有一定的理疗作用。被人体吸收的远红外线能够使大脑皮层功能及脑力活动加强，精神振奋，消除疲劳，改善睡眠，也可起到扩张毛细血管，增强血液循环，促进新陈代谢等作用，可强化和激活人体的生理活动，促进人体健康。
本发明所述炭雕可以直接作为完整的雕塑成品，也可以通过常规雕塑手段雕塑成艺术品，不仅具有实用的观赏价值，而且释放出的负离子具有净化空气、消除室内异味和各种有害气体；释放的远红外线可促进人体健康的保健作用。持续发散的负氧离子和远红外线对人体有很好的协调性，被誉为“空气维生素”，具有增加呼吸系数，改善肺功能，促进新陈代谢，调节免疫。镇静，缓解精神疲劳等良好的保健作用。
具体实施方式
以下以通过优选实施例对本发明工艺作进一步的详细说明，但本发明的保护范围并不局限于此。
实施例1
一种能够释放负离子和远红外线的炭雕，其主要由下述重量百分比原料制成：电气石粉2%、远红外粉3%和活性炭半成品95%，所述活性炭半成品由下述方法制得：将牡丹原料（即牡丹根、茎）用pH为1、质量浓度42%的氯化锌溶液浸渍吸收后（约10h），转入碳化炉中于400℃密闭碳化4小时，其间每隔30分钟彻底搅拌一次，搅拌前将炉温降至100℃以下，搅拌后再升至400℃，碳化结束后出料，冷却至室温得黑焦色半成品；所述氯化锌溶液的用量为牡丹原料重量的2倍。
所述能够释放负离子和远红外线的炭雕的成型方法，其包括以下步骤：将电气石粉、远红外粉和活性炭半成品混匀，用质量浓度50%的磷酸溶液于140℃浸渍吸收后（约9h），加入硅丙乳液，混匀，置模具中采用分子吸压成型技术制成块状无缝炭雕，然后移入火化炉中于450℃活化50min，出料；出料后用清水煮沸，固液分离后，固体用清水洗涤至pH为6，再经脱水、烘干即得成品炭雕，密封包装；其中，所述磷酸溶液的用量为电气石粉、远红外粉和活性炭半成品总重量的3倍，硅丙乳液的用量为电气石粉、远红外粉和活性炭半成品总重量的0.4倍。
实施例2
一种能够释放负离子和远红外线的炭雕，其主要由下述重量百分比原料制成：电气石粉2%、远红外粉7%和活性炭半成品91%，所述活性炭半成品由下述方法制得：将牡丹原料（即去皮后的牡丹根、茎木质部）用pH为2、质量浓度40%的氯化锌溶液浸渍吸收后（约10h），转入碳化炉中于350℃密闭碳化5小时，其间每隔30分钟彻底搅拌一次，搅拌前将炉温降至100℃以下，搅拌后再升至350℃，碳化结束后出料，冷却至室温得黑焦色半成品；所述氯化锌溶液的用量为牡丹原料重量的3倍。
所述能够释放负离子和远红外线的炭雕的成型方法，其包括以下步骤：将电气石粉、远红外粉和活性炭半成品混匀，用质量浓度40%的磷酸溶液于170℃浸渍吸收后（约10h），加入硅丙乳液，混匀，置模具中采用分子吸压成型技术制成块状无缝炭雕，然后移入火化炉中于400℃活化60min，出料；出料后用清水煮沸，固液分离后，固体用清水洗涤至pH为6，再经脱水、烘干即得成品炭雕，密封包装；其中，所述磷酸溶液的用量为电气石粉、远红外粉和活性炭半成品总重量的4倍，硅丙乳液的用量为电气石粉、远红外粉和活性炭半成品总重量的0.2倍。
实施例3
一种能够释放负离子和远红外线的炭雕，其主要由下述重量百分比原料制成：电气石粉8%、远红外粉2%和活性炭半成品90%，所述活性炭半成品由下述方法制得：将牡丹原料（（即牡丹根、茎和叶））用pH为3、质量浓度48%的氯化锌溶液浸渍吸收后（约10h），转入碳化炉中于500℃密闭碳化2小时，其间每隔30分钟彻底搅拌一次，搅拌前将炉温降至100℃以下，搅拌后再升至500℃，碳化结束后出料，冷却至室温得黑焦色半成品；所述氯化锌溶液的用量为牡丹原料重量的4倍；
所述能够释放负离子和远红外线的炭雕的成型方法，其包括以下步骤：将电气石粉、远红外粉和活性炭半成品混匀，用质量浓度60%的磷酸溶液于125℃浸渍吸收后（约12h），加入硅丙乳液，混匀，置模具中采用分子吸压成型技术制成块状无缝炭雕，然后移入火化炉中于500℃活化40min，出料；出料后用清水煮沸，固液分离后，固体用清水洗涤至pH为5，再经脱水、烘干即得成品炭雕，密封包装；其中，所述磷酸溶液的用量为电气石粉、远红外粉和活性炭半成品总重量的2倍，硅丙乳液的用量为电气石粉、远红外粉和活性炭半成品总重量的0.3倍。
Claims (1)
1.一种能够释放负离子和远红外线的炭雕的成型方法，其特征在于，该炭雕主要由下述重量百分比原料制成：电气石粉1－10%、远红外粉1－10%和活性炭半成品80－98%；所述活性炭半成品由下述方法制得：将牡丹原料用pH为1－3、质量浓度20－60%的氯化锌溶液浸渍吸收后，转入碳化炉中于300－500℃密闭碳化1－6小时，出料，冷却至室温得活性炭半成品；所述牡丹原料选自牡丹根、茎和叶中的一种或两种以上，所述氯化锌溶液的用量为牡丹原料重量的1－5倍；
所述成型方法具体包括以下步骤：将电气石粉、远红外粉和活性炭半成品混匀，用质量浓度40－60%的磷酸溶液于120－180℃浸渍吸收后，加入硅丙乳液，混匀，置模具中采用分子吸压成型技术制成块状无缝炭雕，然后移入火化炉中于400－500℃活化40－60min，出料；出料后用清水煮沸，固液分离后，固体用清水洗涤至pH为5－6，再经脱水、烘干即得；其中，所述磷酸溶液的用量为电气石粉、远红外粉和活性炭半成品总重量的2－5倍，硅丙乳液的用量为电气石粉、远红外粉和活性炭半成品总重量的0.2－0.4倍。