CN102746010A - 铬铝质钢包引流砂 - Google Patents
铬铝质钢包引流砂 Download PDFInfo
- Publication number
- CN102746010A CN102746010A CN2012102592739A CN201210259273A CN102746010A CN 102746010 A CN102746010 A CN 102746010A CN 2012102592739 A CN2012102592739 A CN 2012102592739A CN 201210259273 A CN201210259273 A CN 201210259273A CN 102746010 A CN102746010 A CN 102746010A
- Authority
- CN
- China
- Prior art keywords
- sand
- parts
- ore
- chromium
- steel ladle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种铬铝质钢包引流砂，其包含60～70份的铬矿、10～20份的高铝矿、10～20的沙漠砂和10～20份性能调节剂。本发明采用铬、铝矿为主、添加适量性能调节剂制成的钢包导流材料，提高钢包的自动开浇率；采用固定含量的高铝矿，实现对烧结层厚度的精确控制，防止渗钢，烧结层厚度为6mm～8mm；另外由于高铝矿光滑度高，引流效果好，在很大程度上提高了引流砂的自动开浇率。
Description
技术领域
本发明属于连续铸钢技术领域，主要涉及一种铬铝质钢包引流砂。
背景技术
引流砂作为钢包底部水口填充材料，一方面要求能在较低的温度下烧结，以避免加入钢水时引流砂上浮造成事故，另一方面要求在高温和长时间精炼状态下迎钢面不能烧结过厚，否则影响自动开浇率，从而影响正常冶炼操作。
目前，国内普遍使用的是铬质、硅质或镁质等引流砂，硅质引流砂以石英砂为基料，配以长石低熔物作为促进烧结剂，但石英砂中的二氧化硅会降低中间包覆盖剂的碱度和侵蚀碱性包衬，给中间包碱性冶金环境带来不利的影响；镁质引流砂以镁橄榄石和镁砂为主要原料，成弱碱性，有利于中间包碱性环境的形成，但其烧结性能难于控制；铬质引流砂引流效果好，但是烧结层不稳定，容易处现渗钢，当钢水渗透到引流砂中就形成钢砂混合层，很难实现自开，严重的甚至无法用氧气枪烧开，引发断浇事故；另外，无论是硅质引流砂或镁质引流砂，其对连铸钢包自动开浇率低下，一般为85～90%，很难满足高温或长时间精炼条件下自动导流的需要。
发明内容
为了解决现有技术中存在的不足，本发明目的提出一种铬铝质钢包引流砂，该引流砂指以铬、铝矿为主、添加适量性能调节剂制成的钢包导流材料，提高钢包的自动开浇率。
为了实现上述发明目的，本发明采用如下所述的技术方案：
一种铬铝质钢包引流砂，其包含60～70份的铬矿、10～20份的高铝矿、10～20的沙漠砂和10～20份性能调节剂。
进一步，铬矿中Cr2O3的含量≥46%，粒径为0.5～2mm，且80目≤3%，20目≤2%，水份≤0.5%。
进一步，高铝矿中Al2O3的含量≥80%，粒径为0.5～2mm, 且0.5mm≤2%，2mm≤3%；水份≤0.5%。
进一步，沙漠砂中SiO2的含量≥98%,粒径为1～2mm。
更进一步，所述的的性能调节剂为土状石墨、鳞片石墨、中超炭黑、半补强炭黑任意比例的混合。
由于采用上述技术方案，本发明具有以下优越性：
1、流动性好，开浇率高、开浇率稳定；
2、耐火度高，抗烧结能力强，防渗透能力强；
3、单炉使用量少，降低成本；
4、使用简便，不用二次烘烤，可直接使用；
5、采用固定含量的高铝矿，实现对烧结层厚度的精确控制，防止渗钢，烧结层厚度为6mm～8mm；另外由于高铝矿光滑度高，引流效果好，在很大程度上提高了引流砂的自动开浇率。
具体实施方式
下面用非限定实施例对本发明作进一步的详细说明。
按制备1吨本发明铬铝质钢包引流砂为例：
实施例1
本发明铬铝质钢包引流砂其组成为：60份铬矿、10份高铝矿、20份沙漠砂和10份鳞片石墨。
将此配比的引流砂用于某钢厂，钢包的自动开浇率≥96%。
实施例2
本发明铬铝质钢包引流砂其组成为：65份的铬矿、15份的高铝矿、15份的沙漠砂和20份土状石墨。
将此配比的引流砂用于某钢厂，钢包的自动开浇率≥97%。
实施例3
本发明铬铝质钢包引流砂其组成为：70份铬矿、20份高铝矿、15份沙漠砂和10份鳞片石墨。
将此配比的引流砂用于某钢厂，钢包的自动开浇率达到≥98%。
在上述所有实施例中，铬矿中Cr2O3的含量≥46%，粒径为0.5～2mm，且80目粒度的含量≤3%，20目粒度的含量≤2%，水份≤0.5%；高铝矿中Al2O3的含量≥80%，粒径为0.5～2mm,且0.5mm粒度的含量≤2%，2mm粒度的含量≤3%，水份≤0.5%；沙漠砂中SiO2的含量≥98%,粒度为1～2mm。
Claims (5)
1.一种铬铝质钢包引流砂，其特征是：包含60～70份的铬矿、10～20份的高铝矿、10～20的沙漠砂和10～20份性能调节剂。
2.根据权利要求1所述的铬铝质钢包引流砂，其特征是：铬矿中Cr2O3的含量≥46%，粒径为0.5～2mm，且80目≤3%，20目≤2%，水份≤0.5%，按重量百分含量计。
3.根据权利要求1所述的铬铝质钢包引流砂，其特征是：高铝矿中Al2O3的含量≥80%，粒径为0.5～2mm, 且0.5mm≤2%，2mm≤3%；水份≤0.5%，按重量百分含量计。
4.根据权利要求1所述的铬铝质钢包引流砂，其特征是：沙漠砂中SiO2的含量≥98%,粒径为1～2mm。
5.根据权利要求1所述的铬铝质钢包引流砂，其特征是：所述的性能调节剂为土状石墨、鳞片石墨、中超炭黑、半补强炭黑任意比例的混合。