CN102732986A - 一种耐高温含氯高聚物人工毛发及其制备方法 - Google Patents

一种耐高温含氯高聚物人工毛发及其制备方法 Download PDF

Info

Publication number
CN102732986A
CN102732986A CN2012102065497A CN201210206549A CN102732986A CN 102732986 A CN102732986 A CN 102732986A CN 2012102065497 A CN2012102065497 A CN 2012102065497A CN 201210206549 A CN201210206549 A CN 201210206549A CN 102732986 A CN102732986 A CN 102732986A
Authority
CN
China
Prior art keywords
temperature resistant
artificial hair
high temperature
chloride
polymer artificial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012102065497A
Other languages
English (en)
Inventor
许登堡
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Poly-Well (Nantong) Industry Co., Ltd.
Original Assignee
JINGYUAN (NANTONG) CHEMICAL FIBER PROEUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINGYUAN (NANTONG) CHEMICAL FIBER PROEUCTS CO Ltd filed Critical JINGYUAN (NANTONG) CHEMICAL FIBER PROEUCTS CO Ltd
Priority to CN2012102065497A priority Critical patent/CN102732986A/zh
Publication of CN102732986A publication Critical patent/CN102732986A/zh
Pending legal-status Critical Current

Abstract

一种耐高温含氯高聚物人工毛发，其特征在于：包括聚氯乙烯毛发，所述聚氯乙烯毛发中含有活性官能团-腈基；所述活性官能团-腈基在耐高温含氯高聚物人工毛发中的重量百分比为5％～30％。一种耐高温含氯高聚物人工毛发的制备方法，(1)引入腈基的氯乙烯类聚合物原材料，溶于纺丝溶剂中，配制成纺丝浆，采用湿法纺丝，制成单丝束；(2)将步骤(1)制得的单丝束浸于化学交联剂水溶液中，浸泡时间0.1～10小时；(3)将步骤(2)浸泡后的单丝束取出水洗，再汽蒸，然后经过表面涂硅油处理和烘干，即得一种耐高温含氯高聚物人工毛发。

Description

一种耐高温含氯高聚物人工毛发及其制备方法
技术领域
本发明属于人工毛发制造领域，尤其涉及一种耐高温含氯高聚物人工毛发及其制备方法。
背景技术
含氯高聚物是人工毛发制品的原材料，所制的人工毛发做成假发具有良好的弹性和发型保持性，但美中不足的是耐热性差，而且遇火易发生融粘，有伤及头皮的可能性。
发明内容
本发明的目的在于提供一种耐高温含氯高聚物人工毛发及其制备方法，以实现假发能用电热烫发制作发型及遇火不融粘等技术要求。
一种耐高温含氯高聚物人工毛发，包括聚氯乙烯毛发，在所述聚氯乙烯毛发中含有活性官能团-腈基；所述活性官能团-腈基在耐高温含氯高聚物人工毛发中的重量百分比为5％～30％。
进一步的，所述活性官能团-腈基在耐高温含氯高聚物人工毛发中的重量百分比为10％～25％。
一种耐高温含氯高聚物人工毛发的制备方法，包括以下步骤：
(1)引入腈基的氯乙烯类聚合物原材料，同时添加公知的颜料、抗静电剂等(此处不作特别限制)，溶于纺丝溶剂中，配制成纺丝浆，采用湿法纺丝；所述纺丝浆经齿轮泵从喷丝帽的喷丝孔挤出，挤出后在凝固浴水溶液中凝固成形，经30～50℃水洗，然后在100-110℃蒸汽中拉伸3～4倍，然后于110～135℃热风中松弛收缩25～35％，制成单丝束；
(2)将步骤(1)制得的单丝束浸于化学交联剂水溶液中，浸泡时间0.1～10小时；
(3)将步骤(2)浸泡后的单丝束取出水洗，再汽蒸，然后经过表面涂硅油处理和烘干，即得一种耐高温含氯高聚物人工毛发。
所述引入腈基的氯乙烯类聚合物，可以是丙烯腈或甲基丙烯腈与氯乙烯或偏二氯乙烯共聚所成共聚物，也可以是聚丙烯腈或聚甲基丙烯腈与聚氯乙烯共混物。
所述喷丝帽的微孔直径为0.35-0.45mm。
所述化学交联剂是肼、水合肼、羟胺、羟胺盐酸盐、胍中的一种；所述化学交联剂水溶液的浓度0.5～50wt％；所述化学交联剂水溶液的温度为80～100℃。
步骤(3)中，所述水洗的温度30～60℃，所述汽蒸的温度100～110℃；
所述的纺丝溶剂为二甲基甲酰胺，二甲基乙酰胺，二甲基亚砜中的一种；
所述凝固浴水溶液均含与所述的纺丝溶剂相一致的化学品；所述凝固浴水溶液为50～60wt％的二甲基甲酰胺，二甲基乙酰胺，二甲基亚砜中的一种。
有益效果：本发明提供的一种耐高温含氯高聚物人工毛发，可耐180℃以上电热烫发的要求，而且遇火不熔，只灼烧成灰烬。
具体实施方式
下面通过具体实施例对本发明做进一步说明，下述实施例仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在本发明内容说明的基础上还可以做出其它不同形式的变化或变动。这里无需对所有的实施方式予以例举。
具体实施例中所涉及的毛发机械性能按GB/T14335、GB/T14337及GB/T14343-2003测量纤度、抗张强度及伸长度。
实施例1
(1)称取10.0kg氯乙烯丙烯腈共聚树脂(丙烯腈的重量比51∶49；杭州广和化工有限公司制)溶于30.0kg二甲基甲酰胺中，同时添加公知的颜料、抗静电剂等(此处不作特别限制)，配制成纺丝浆，采用湿法纺丝，纺丝浆经齿轮泵从孔径为0.35mm的400孔喷丝帽挤出，挤出后在60wt％二甲基甲酰胺的水溶液中凝固成形，经35℃水洗后，湿丝束在100℃蒸汽中拉伸4倍，然后于130℃热风中松弛收缩30％，制成单丝束。
(2)将上述单丝束浸于98℃的2.5wt％水合肼的水溶液中，浸泡90分钟。
(3)将步骤(2)浸泡后的单丝束取出水洗，水洗温度40℃；再汽蒸1小时，汽蒸温度98℃，然后表面涂硅油、烘干，即得一种耐高温含氯高聚物人工毛发。(上述表面涂硅油、烘干为公知方法，此处不做特别限制)
该人工毛发的单丝纤度50dtex，抗张强度2.0CN/dtex，伸长度30％。
交联反应的程度以180℃电热烫发夹子轻夹人工毛发二遍后，测量其收缩率，收缩率小于5％，即为合格。
由此制成的一种耐高温含氯高聚物人工毛发，其耐热性达180℃，遇火不熔，只能残留灰烬。
实施例2
(1)称取6.0kg氯乙烯丙烯腈共聚树脂(丙烯腈的重量比60∶40；杭州广和化工有限公司制)溶于25.0kg二甲基乙酰胺中，同时添加公知的颜料、抗静电剂等(此处不作特别限制)，配制成纺丝浆，采用湿法纺丝，纺丝浆经齿轮泵从孔径为0.35mm的400孔喷丝帽挤出，挤出后在58wt％二甲基乙酰胺的水溶液中凝固成形，经40℃水洗后，湿丝束在105℃蒸汽中拉伸3.5倍，然后于125℃热风中松弛收缩28％，制成单丝束。
(2)将上述单丝束浸于99℃的2wt％水合肼的水溶液中，浸泡120分钟。
(3)将步骤(2)浸泡后的单丝束取出水洗，水洗温度60℃；再汽蒸2小时，汽蒸温度105℃，然后表面涂硅油、烘干，即得一种耐高温含氯高聚物人工毛发。(上述表面涂硅油、烘干为公知方法，此处不做特别限制)
该人工毛发的单丝纤度52dtex，抗张强度2.1CN/dtex，伸长度32％。
交联反应的程度以180℃电热烫发夹子轻夹人工毛发二遍后，测量其收缩率，收缩率小于5％，即为合格。
由此制成的一种耐高温含氯高聚物人工毛发，其耐热性达180℃，遇火不熔，只能残留灰烬。
比较例1
按实施例1相同方法操作，省略化学交联反应。制成的人工毛发耐热性125℃，遇火半融，有粘皮肤的危险性。
比较例2
按实施例2相同方法操作，省略化学交联反应。制成的人工毛发耐热性125℃，遇火半融，有粘皮肤的危险性。

Claims (5)

1.一种耐高温含氯高聚物人工毛发，其特征在于：包括聚氯乙烯毛发，在所述聚氯乙烯毛发中含有活性官能团-腈基，所述活性官能团-腈基在耐高温含氯高聚物人工毛发中的重量百分比为5％～30％。
2.根据权利要求1所述的一种耐高温含氯高聚物人工毛发，其特征在于：所述活性官能团-腈基在耐高温含氯高聚物人工毛发中的重量百分比为10％～25％。
3.一种耐高温含氯高聚物人工毛发的制备方法，其特征在于：
(1)引入腈基的氯乙烯类聚合物原材料，溶于纺丝溶剂中，同时添加公知的颜料、抗静电剂等，配制成纺丝浆，采用湿法纺丝；所述纺丝浆经齿轮泵从喷丝帽的喷丝孔挤出，挤出后在凝固浴水溶液中凝固成形，经30～50℃水洗，然后在100-110℃蒸汽中拉伸3～4倍，然后于110～135℃热风中松弛收缩25～35％，制成单丝束；
(2)将步骤(1)制得的单丝束浸于化学交联剂水溶液中，浸泡时间0.1～10小时；
(3)将步骤(2)浸泡后的单丝束取出水洗，再汽蒸，然后经过表面涂硅油处理和烘干，即得一种耐高温含氯高聚物人工毛发。
4.根据权利要求3所述的一种耐高温含氯高聚物人工毛发的制备方法，其特征在于：所述引入腈基的氯乙烯类聚合物，可以是丙烯腈或甲基丙烯腈与氯乙烯或偏二氯乙烯共聚所成共聚物，也可以是聚丙烯腈或聚甲基丙烯腈与聚氯乙烯共混物。
5.根据权利要求3所述的一种耐高温含氯高聚物人工毛发的制备方法，其特征在于：所述化学交联剂是肼、水合肼、羟胺、羟胺盐酸盐、胍中的一种；所述化学交联剂水溶液的浓度0.5～50wt％；所述化学交联剂水溶液的温度为80～100℃。
CN2012102065497A 2012-06-21 2012-06-21 一种耐高温含氯高聚物人工毛发及其制备方法 Pending CN102732986A (zh)