CN102731061B - 一种陶瓷器物制作方法 - Google Patents

一种陶瓷器物制作方法 Download PDF

Info

Publication number
CN102731061B
CN102731061B CN201110095758.4A CN201110095758A CN102731061B CN 102731061 B CN102731061 B CN 102731061B CN 201110095758 A CN201110095758 A CN 201110095758A CN 102731061 B CN102731061 B CN 102731061B
Authority
CN
China
Prior art keywords
ceramic
thermal deformation
clay blank
clay
firing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201110095758.4A
Other languages
English (en)
Other versions
CN102731061A (zh
Inventor
周详
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai University of Engineering Science
Original Assignee
Shanghai University of Engineering Science
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai University of Engineering Science filed Critical Shanghai University of Engineering Science
Priority to CN201110095758.4A priority Critical patent/CN102731061B/zh
Publication of CN102731061A publication Critical patent/CN102731061A/zh
Application granted granted Critical
Publication of CN102731061B publication Critical patent/CN102731061B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及陶瓷器物的制作,属于陶瓷制作领域。一种陶瓷器物制作方法,包括制作粘土坯的步骤和烧制的步骤,其特征在于:在制作粘土坯的步骤中,包括在粘土坯内安放温度形变智能纤维的步骤,所述温度形变智能纤维在烧制步骤中开始烧制时发生形变,使烧制的器物形状改变。本发明的陶瓷器物制作方法利用温度形变智能纤维设置在粘土坯内,温度改变后温度形变智能纤维发生形状改变,缩小或伸长,如此根据外形或功能需要就可以使用不同种类和不同形变形式的温度形变智能纤维在制作粘土坯体时安放好,将粘土坯放入烧制炉内后,温度形变智能纤维发生形状变化后,待烧制完成后,温度形变智能纤维已和粘土坯融合。

Description

一种陶瓷器物制作方法
技术领域
本发明涉及陶瓷器物的制作,尤其涉及一种陶瓷器物制作方法。
背景技术
举世闻名的中国陶瓷,是中国的伟大发明之一,也是中国对世界文明的一个伟大贡献。陶瓷,是由粘土或主要含粘土的混合物,经成形、干燥、烧制而成的制品的总称,主要分为陶器和瓷器。
陶器的烧制温度一般不超过摄氏1000度,胎质粗松,器表一般无釉或只涂有低温釉,故具有吸水性、敲击之声不清脆等特点。随着历史的发展,彩陶、釉陶、白陶等相继出现。唐代,制陶工艺达到相当高的水平。最为著名的陶器工艺品当推唐三彩。唐三彩是唐代低温铅釉陶质生活用具和陶塑艺术品的总称。它以黄、绿、蓝作基调,经过反复的窖变,呈现出深绿、浅绿、翠绿、蓝、黄、白、赭、褐等多种颜色,展示了盛唐时期文化艺术的风韵。其中,尤以唐三彩马最为有名。明代,江苏宜兴的紫砂陶工艺,驰名中外,紫砂陶壶堪称一绝,享有“世间茶壶称为首”的赞誉,在国际搏览会上屡获殊荣。
瓷器是以高岭土等作为原料,经过摄氏1200度的高温,并涂以高温釉烧制而成。瓷器是由陶器演变发展而来的。约在公元前16世纪的商代中期,就创烧出了原始青瓷器。自东汉时期始,瓷器工艺日见成熟。中国是世界上陶瓷出口最早的国家,素有“瓷国”美誉。世界各国人民通过陶瓷器皿来了解中华文明,并把陶瓷作为中国的代名词(China)。
成形后的粘土坯体,必须加以烧制,才能成为陶瓷。烧制是一个化腐朽为神奇的过程,松软的粘土经过烧制就能成为坚硬的陶瓷。烧制的温度区别了陶与瓷。陶器因为陶土自身原因,烧制温度通常不能超过1100℃,否则器物就会变形,而瓷器烧制温度通常都在1200℃以上。因此,1200℃就成为陶与瓷的分界线。
中国的陶瓷器物除了具有实际应用价值外,已经成了艺术品的一种,讲究色彩、外形等各方面,有些外形需要艺术表现和制作技艺的结合才能完成一件陶瓷器物,因此陶瓷方面也是有一些大家,需要很多年的成长。而且有些外形因为烧制的不易或粘土坯制作的不易,基本很难制作出来。而有些具有一些功能性的器物,更是非常难制作,如茶壶类的公道杯,或者其它希望发展的功能,在制作上的难度都是很高的。
发明内容
本发明所要解决的技术问题是提供一种陶瓷器物制作方法,解决现在传统陶瓷器物制作方法在一些外形或功能上难于制作,很难突破的缺陷。
技术方案
一种陶瓷器物制作方法,包括制作粘土坯的步骤和烧制的步骤,其特征在于:在制作粘土坯的步骤中,包括在粘土坯内安放温度形变智能纤维的步骤,所述温度形变智能纤维在烧制步骤中开始烧制时发生形变,使烧制的器物形状改变。
进一步,所述温度形变智能纤维采用螺旋式圆柱状。
进一步,所述温度形变智能纤维安放在粘土坯浅表层下。
有益效果
本发明的陶瓷器物制作方法利用温度形变智能纤维设置在粘土坯内,温度改变后温度形变智能纤维发生形状改变,缩小或伸长,如此根据外形或功能需要就可以使用不同种类和不同形变形式的温度形变智能纤维在制作粘土坯体时安放好,将粘土坯放入烧制炉内后,温度形变智能纤维发生形状变化后,待烧制完成后,温度形变智能纤维已和粘土坯融合。
附图说明
图1为本发明制作出的陶瓷器物示意图。
其中:1-陶瓷壶身平面,2-凸出的肋条。
具体实施方式
下面结合具体实施例和附图,进一步阐述本发明。
一种陶瓷器物制作方法,包括制作粘土坯的步骤和烧制的步骤,在制作粘土坯的步骤中,包括在粘土坯内安放温度形变智能纤维的步骤,所述温度形变智能纤维在烧制步骤中开始烧制时发生形变,使烧制的器物形状改变。
所述温度形变智能纤维采用螺旋式圆柱状。
附图1为采用上述方法制作的陶瓷壶示意图。按照传统的制作方法,如果需要在壶身平面1上作出细细的凸出的肋条2,则需要在制作粘土坯的时候,手工捏出那样的细细的肋条的形状,因此肋条的大小就不能太细,而且很难统一,就不能显出壶的精细来。而现在利用温度形变智能纤维,只要在制作粘土坯时,在壶身平面的浅表面内放置一根根同样直径的温度形变智能纤维,待放入烧制炉内时,温度形变智能纤维受热变长,变粗,就很容易将粘土坯壶身表面鼓起,只要掌握好温度形变智能纤维的变化温度,变化前后的直径和长度变化,则能轻易达到需要的效果。还可以在上壶身平面和下壶身平面的浅表面内各放置一个温度形变智能纤维,有产生新的效果。
温度形变智能纤维还可以安放在粘土坯内层表面,待温度升高后,温度形变智能纤维缩短产生气孔或小孔,还能用于制作一些具有一定功能的陶瓷器物。

Claims (3)

1.一种陶瓷器物制作方法,包括制作粘土坯的步骤和烧制的步骤,其特征在于:在制作粘土坯的步骤中,包括在粘土坯内安放温度形变智能纤维的步骤,所述温度形变智能纤维在烧制步骤中开始烧制时发生形变,使烧制的器物形状改变。
2.如权利要求1所述的陶瓷器物制作方法,其特征在于:所述温度形变智能纤维采用螺旋式圆柱状。
3.如权利要求1或2所述的陶瓷器物制作方法,其特征在于:所述温度形变智能纤维安放在粘土坯浅表层下。
CN201110095758.4A 2011-04-15 2011-04-15 一种陶瓷器物制作方法 Expired - Fee Related CN102731061B (zh)