CN102719039A - 聚氯乙烯型材专用增刚合化碳酸钙 - Google Patents
聚氯乙烯型材专用增刚合化碳酸钙 Download PDFInfo
- Publication number
- CN102719039A CN102719039A CN2012101975300A CN201210197530A CN102719039A CN 102719039 A CN102719039 A CN 102719039A CN 2012101975300 A CN2012101975300 A CN 2012101975300A CN 201210197530 A CN201210197530 A CN 201210197530A CN 102719039 A CN102719039 A CN 102719039A
- Authority
- CN
- China
- Prior art keywords
- lime carbonate
- polyvinyl chloride
- section bar
- calcium carbonate
- firm combination
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚氯乙烯型材专用增刚合化碳酸钙,所述增刚合化碳酸钙包括以下组分及重量份:碳酸钙90~120;聚氯乙烯功能调节剂5~11;硬脂酸1.5~2。所述的增刚合化碳酸钙的制配工艺为混料。本发明具有构思合理、工艺规范、操作简单、价格低廉、无污染;用于聚氯乙烯型材加工可以提高聚氯乙烯型材强度,降低产品的成本等有益效果。本发明可以尽快形成批量生产,可以广泛用于聚氯乙烯型材加工领域。
Description
技术领域
本发明涉及一种用于塑料的碳酸钙,特别是涉及一种聚氯乙烯型材专用增刚合化碳酸钙。
背景技术
众所周知,传统的聚氯乙烯型材使用的碳酸钙容易使聚氯乙烯型材变形变软,达不到理想的产品质量要求。因此,生产出来的聚氯乙烯型材强度和韧性较差,而且生产成本比较高,质量不稳定,难以适应市场的需求,亦限制了它的推广应用。
发明内容
本发明的目的是为了克服上述背景技术的缺陷,替代传统聚氯乙烯型材使用的碳酸钙,提高聚氯乙烯型材的质量,降低产品的生产成本,而提供一种聚氯乙烯型材专用增刚合化碳酸钙。
为了实现上述目的,本发明所述的聚氯乙烯型材专用增刚合化碳酸钙的技术方案是这样的:
本发明所述的增刚合化碳酸钙包括以下组分及重量份:碳酸钙90~120;聚氯乙烯功能调节剂5~11;硬脂酸1.5~2。
所述的增刚合化碳酸钙包括以下组分及重量份:碳酸钙105;聚氯乙烯功能调节剂8;硬脂酸1.75。
所述的聚氯乙烯功能调节剂(SRC)是由乙烯·醋酸乙烯脂与氯乙烯接枝共聚物和铝酸脂偶联剂复合而成,其配比为:1.5~2.5:0.05~0.10。
所述的聚氯乙烯功能调节剂(SRC)的配比为:乙烯·醋酸乙烯脂与氯乙烯接枝共聚物:铝酸脂偶联剂=2:0.08。
所述碳酸钙为重质碳酸钙。
所述碳酸钙为轻质碳酸钙。
本发明所述的聚氯乙烯型材专用增刚合化碳酸钙具有以下有益效果:构思新颖、工艺规范、操作便捷、价格低廉、无污染;用于聚氯乙烯型材加工可以提高聚氯乙烯型材的强度,降低产品生产成本,提升产品品质。本发明可以尽快形成工业化批量生产,可以广泛用于聚氯乙烯型材加工领域。
具体实施方式
下面结合实施例对本发明作进一步的详细描述,但该实施例不应理解为对本发明的限制。
实施例1
本发明所述的增刚合化碳酸钙按下列工艺程序制配:
一、制取所述增刚合化碳酸钙各组分及重量份的配制
1、聚氯乙烯功能调节剂的配制:
按所述的聚氯乙烯功能调节剂配比取乙烯·醋酸乙烯脂与氯乙烯接枝共聚物1.5,铝酸脂偶联剂0.05,一起置入搅拌器内,在常温条件下搅拌,搅拌均匀后即可出料备用。
2、所述的各组分及重量份的配制:
碳酸钙90;聚氯乙烯功能调节剂5;硬脂酸1.5,备用。(所述碳酸钙为重质碳酸钙或轻质碳酸钙)
二.所述的增刚合化碳酸钙的配制:
混料:将上述配制好的各组分重量份混合,一起投入捏合机中混合搅拌均匀即可。
实施例2
本实施例与实施例1基本相同,其不同之处在于:
一、制取所述增刚合化碳酸钙各组分及重量份的配制:
1、聚氯乙烯功能调节剂配制:
按所述的聚氯乙烯功能调节剂配比取乙烯·醋酸乙烯脂与氯乙烯接枝共聚物2,铝酸脂偶联剂0.08,一起置入搅拌器内,在常温条件下搅拌,搅拌均匀后即可出料备用。
2、所述的各组分及重量份的配制:
碳酸钙105;聚氯乙烯功能调节剂8;硬脂酸1.75,备用。(所述碳酸钙为重质碳酸钙或轻质碳酸钙)
实施例3
本实施例与实施例1基本相同,其不同之处在于:
一、制取所述增刚合化碳酸钙各组分及重量份的配制:
1、聚氯乙烯功能调节剂配制:
按所述的聚氯乙烯功能调节剂配比取乙烯·醋酸乙烯脂与氯乙烯接枝共聚物2.5,铝酸脂偶联剂0.10,一起置入搅拌器内,在常温条件下搅拌,搅拌均匀后即可出料备用。
2、所述的各组分及重量份的配制:
碳酸钙120;聚氯乙烯功能调节剂11;硬脂酸2,备用。(所述碳酸钙为重质碳酸钙或轻质碳酸钙)
显然,本领域的技术人员可以对本发明进行各种改动和变型而不脱离本发明的精神和范围。这样,倘若本发明的这些修改和变型属于本发明权利要求及其等同技术的范围之内,则本发明也意图包含这些改动和变型在内。
本说明书中未作详细描述的内容属于本领域专业技术人员公知的现有技术。
Claims (6)
1.一种聚氯乙烯型材专用增刚合化碳酸钙,其特征在于:所述增刚合化碳酸钙包括以下组分及重量份:
碳酸钙90~120;聚氯乙烯功能调节剂5~11;硬脂酸1.5~2。
2.根据权利要求1所述的聚氯乙烯型材专用增刚合化碳酸钙,其特征在于:所述增刚合化碳酸钙包括以下组分及重量份:
碳酸钙105;聚氯乙烯功能调节剂8;硬脂酸1.75。
3.根据权利要求1或2所述的聚氯乙烯型材专用增刚合化碳酸钙,其特征在于:所述的聚氯乙烯功能调节剂是由乙烯·醋酸乙烯脂与氯乙烯接枝共聚物和铝酸脂偶联剂复合而成,其配比为:1.5~2.5:0.05~0.10。
4.根据权利要求3所述的聚氯乙烯型材专用增刚合化碳酸钙,其特征在于:所述的配比为乙烯·醋酸乙烯脂与氯乙烯接枝共聚物:铝酸脂偶联剂=2:0.08。
5.根据权利要求1或2所述的聚氯乙烯型材专用增刚合化碳酸钙,其特征在于:所述碳酸钙为重质碳酸钙。
6.根据权利要求1或2所述的聚氯乙烯型材专用增刚合化碳酸钙,其特征在于:所述碳酸钙为轻质碳酸钙。