CN102329464A - 用于聚氯乙烯硬质板材的加工改性剂 - Google Patents
用于聚氯乙烯硬质板材的加工改性剂 Download PDFInfo
- Publication number
- CN102329464A CN102329464A CN201110141027A CN201110141027A CN102329464A CN 102329464 A CN102329464 A CN 102329464A CN 201110141027 A CN201110141027 A CN 201110141027A CN 201110141027 A CN201110141027 A CN 201110141027A CN 102329464 A CN102329464 A CN 102329464A
- Authority
- CN
- China
- Prior art keywords
- modifier
- agent
- rubber
- polyvinyl chloride
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于聚氯乙烯硬质板材的加工改性剂，所述加工改性剂包括以下组分及重量份：钙锌稳定剂3～5；润滑剂1.5～2；橡塑改性剂2～5；增塑剂2～5。所述的加工改性剂的制配工艺包括：各组分的制配、混料、搅拌、加温、冷却和卸料包装。本发明具有构思合理、工艺规范、操作简单、价格低廉、无污染；用于聚氯乙烯硬质板材加工可以提高硬质板材韧性和强度，降低产品的成本等有益效果。本发明可以批量生产，可以广泛用于聚氯乙烯硬质板材加工领域。
Description
技术领域
本发明涉及一种用于塑料的加工改性剂，特别是涉及一种用于聚氯乙烯硬质板材的加工改性剂。
背景技术
众所周知，传统的加工聚氯乙烯硬质板材使用的改性剂中添加的氯化聚乙烯等辅料比较多。因此，生产出来的聚氯乙烯硬质板材强度和韧性较差，而且生产成本比较高，质量不稳定，难以适应市场的需求，亦限制了它的推广应用。
发明内容
本发明的目的是为了克服上述背景技术的缺陷，替代传统改性助剂，提高硬质板材的质量，降低产品的生产成本，而提供一种用于聚氯乙烯硬质板材的加工改性剂。
为了实现上述目的，本发明所述的用于聚氯乙烯硬质板材的加工改性剂的技术方案是这样的：
本发明所述的加工改性剂包括以下组分及重量份：钙锌稳定剂3～5；润滑剂1.5～2.0；橡塑改性剂2～5；增塑剂2～5。
所述的加工改性剂包括以下组分及重量份：钙锌稳定剂3.2～4.8；润滑剂1.6～1.9；橡塑改性剂2.5～4.8；增塑剂2.2～4.8。
所述的加工改性剂包括以下组分及重量份：钙锌稳定剂4；润滑剂1.8；橡塑改性剂3.5；增塑剂3.5。
所述的橡塑改性剂是由乙烯·醋酸乙烯共聚物和铝酸脂偶联剂复合而成，其配比为：乙烯·醋酸乙烯共聚物∶铝酸脂偶联剂＝1.5～2.5∶0.05～0.1。
所述的橡塑改性剂的配比为：乙烯·醋酸乙烯共聚物∶铝酸脂偶联剂＝2∶0.07。
本发明所述的聚氯乙烯硬质板材的加工改性剂具有以下有益效果：构思新颖、工艺规范、操作便捷、价格低廉、无污染；用于聚氯乙烯硬质板材加工可以提高硬质板材的韧性和强度，降低产品生产成本，提升产品品质。本发明可以工业化批量生产，可以广泛用于聚氯乙烯硬质板材加工领域。
具体实施方式
下面结合实施例对本发明作进一步的详细描述，但该实施例不应理解为对本发明的限制。
实施例1
本发明所述的加工改性剂按下列工艺程序制配：
一、制取所述加工改性剂各组分及重量份的配制
1、橡塑改性剂的配制：
按所述的橡塑改性剂配比取乙烯·醋酸乙烯共聚物1.5，铝酸脂偶联剂0.05，一起置入搅拌器内，在常温条件下搅拌，搅拌均匀后即可出料、备用。
2、所述的各组分及重量份的配制：
钙锌稳定剂3；润滑剂1.5；橡塑改性剂2；增塑剂2，备用。
二.所述的加工改性剂的配制：
1、混料：将上述配制好的各组分重量份混合，一起投入捏合机中混合搅拌均匀，加温至135℃～140℃即可停止加温，备用；
2、卸料包装：将上述加工好的混料冷却至常温后即可卸料包装，即成品——所述的加工改性剂包装。
实施例2
本实施例与实施例1基本相同，其不同之处在于：
一、加工改性剂各组分助剂及重量份的配制：
1、助剂橡塑改性剂配制：
按所述的橡塑改性剂配比取乙烯·醋酸乙烯共聚物2，铝酸脂偶联剂0.07，一起置入搅拌器内，在常温条件下搅拌，搅拌均匀后即可出料、备用。
2、所述的各组分及重量份的配制：
钙锌稳定剂3.2；润滑剂1.6；橡塑改性剂2.5；增塑剂2.2，备用。
实施例3
本实施例与实施例1基本相同，其不同之处在于：
一、加工改性剂各组分助剂及重量份的配制：
1、助剂橡塑改性剂配制：
按所述的橡塑改性剂配比取乙烯·醋酸乙烯共聚物2.5，铝酸脂偶联剂0.1，一起置入搅拌器内，在常温条件下搅拌，搅拌均匀后即可出料、备用。
2、所述的各组分及重量份的配制：
钙锌稳定剂4；润滑剂1.8；橡塑改性剂3.5；增塑剂3.5，备用。
实施例4
本实施例与实施例1基本相同，其不同之处在于：
一、加工改性剂各组分(即助剂)及重量份的配制：
1、助剂橡塑改性剂配制：
按所述的橡塑改性剂配比取乙烯·醋酸乙烯共聚物2.5，铝酸脂偶联剂0.1，一起置入搅拌器内，在常温条件下搅拌，搅拌均匀后即可出料、备用。
2、所述的各组分及重量份的配制：
钙锌稳定剂4.8；润滑剂1.9；橡塑改性剂4.8；增塑剂4.8，备用。
实施例5
本实施例与实施例1基本相同，其不同之处在于：
一、加工改性剂各组分助剂及重量份的配制：
1、助剂橡塑改性剂配制：
按所述的橡塑改性剂配比取乙烯·醋酸乙烯共聚物2.5，铝酸脂偶联剂0.1，一起置入搅拌器内，在常温条件下搅拌，搅拌均匀后即可出料、备用。
2、所述的各组分及重量份的配制：
钙锌稳定剂5；润滑剂2；橡塑改性剂5；增塑剂5，备用。
显然，本领域的技术人员可以对本发明进行各种改动和变型而不脱离本发明的精神和范围。这样，倘若本发明的这些修改和变型属于本发明权利要求及其等同技术的范围之内，则本发明也意图包含这些改动和变型在内。
本说明书中未作详细描述的内容属于本领域专业技术人员公知的现有技术。
Claims (5)
1.一种用于聚氯乙烯硬质板材的加工改性剂，其特征在于：所述加工改性剂包括以下组分及重量份：
钙锌稳定剂3～5；润滑剂1.5～2；橡塑改性剂2～5；增塑剂2～5。
2.根据权利要求1所述的用于聚氯乙烯硬质板材的加工改性剂，其特征在于：所述的加工改性剂包括以下组分及重量份：
钙锌稳定剂3.2～4.8；润滑剂1.6～1.9；橡塑改性剂2.5～4.8；增塑剂2.2～4.8。
3.根据权利要求1所述的用于聚氯乙烯硬质板材的加工改性剂，其特征在于：所述的加工改性剂包括以下组分及重量份：
钙锌稳定剂4；润滑剂1.8；橡塑改性剂3.5；增塑剂3.5。
4.根据权利要求1至3中任一权利要求所述的用于聚氯乙烯硬质板材的加工改性剂，其特征在于：所述的橡塑改性剂是由乙烯·醋酸乙烯共聚物和铝酸脂偶联剂等复合而成，其配比为：乙烯·醋酸乙烯共聚物∶铝酸脂偶联剂＝1.5～2.5∶0.05～0.1。
5.根据权利要求4所述的用于聚氯乙烯硬质板材的加工改性剂，其特征在于：所述的配比为乙烯·醋酸乙烯共聚物∶铝酸脂偶联剂＝2∶0.07。