CN103289238A - 聚氯乙烯电缆料专用抗冲功能碳酸钙 - Google Patents
聚氯乙烯电缆料专用抗冲功能碳酸钙 Download PDFInfo
- Publication number
- CN103289238A CN103289238A CN2013102476287A CN201310247628A CN103289238A CN 103289238 A CN103289238 A CN 103289238A CN 2013102476287 A CN2013102476287 A CN 2013102476287A CN 201310247628 A CN201310247628 A CN 201310247628A CN 103289238 A CN103289238 A CN 103289238A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- impact function
- polyvinyl chloride
- special
- cable material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚氯乙烯电缆料专用抗冲功能碳酸钙,所述的专用抗冲功能碳酸钙包括以下组分及重量份:重质碳酸钙100;PVC抗冲功能调节剂SRC2~7;分散剂1~2。所述的聚氯乙烯电缆料专用抗冲功能碳酸钙的配制工艺包括:各组分的混料、搅拌均匀和卸料包装。本发明具有构思新颖、工艺简便、易于操作;采用本发明技术方案后,可提高聚氯乙烯电缆料韧性和强度,尤其可提高制品的抗冲击性能,提高产品的质量、弥补现有产品缺乏抗冲击性能的缺陷、填补了聚氯乙烯电缆料抗冲击性能产品的空白。本发明可以工业化批量生产,可以广泛地用于聚氯乙烯电缆料的加工领域。
Description
技术领域
本发明涉及一种用于塑料的调节剂,特别是涉及一种聚氯乙烯(PVC)电缆料专用抗冲功能碳酸钙。
背景技术
迄今为止,传统的用于聚氯乙烯电缆料的抗冲功能碳酸钙的配方生产出来的聚氯乙烯电缆料脆性大、强度差,缺乏抗冲击能力,且生产成本较高,不能适应市场的需求,限制了其推广应用。
发明内容
本发明的目的是为了克服上述背景技术的缺陷,提供一种能够提高聚氯乙烯电缆料的抗冲击性能、成本低廉的聚氯乙烯电缆料专用抗冲功能碳酸钙。
为了实现上述目的,本发明所述的聚氯乙烯电缆料专用抗冲功能碳酸钙的技术方案是这样的:
本发明所述的专用抗冲功能碳酸钙包括以下组分及重量份:重质碳酸钙100;PVC抗冲功能调节剂SRC2~7;分散剂1~2。
本发明所述的专用抗冲功能碳酸钙包括以下组分及重量份:重质碳酸钙100;PVC抗冲功能调节剂SRC3~6.5;分散剂1.1~1.8。
本发明所述的专用抗冲功能碳酸钙包括以下组分及重量份:重质碳酸钙100;PVC抗冲功能调节剂SRC3.5~6;分散剂1.2~1.7。
本发明所述的专用抗冲功能碳酸钙包括以下组分及重量份:重质碳酸钙100;PVC抗冲功能调节剂SRC4~5;分散剂1.3~1.6。
本发明所述的专用抗冲功能碳酸钙包括以下组分及重量份:重质碳酸钙100;PVC抗冲功能调节剂SRC4.5;分散剂1.5。
本发明所述的PVC抗冲功能调节剂SRC是由乙烯·醋酸乙脂与氯乙烯共聚物和铝酸酯偶联剂复合而成,其配比为:乙烯·醋酸乙脂与氯乙烯共聚物:铝酸酯偶联剂=1.5~2.5:0.05~0.1。
本发明所述的PVC抗冲功能调节剂SRC配比为:乙烯·醋酸乙脂与氯乙烯共聚物:铝酸酯偶联剂=2:0.07。
本发明所述的分散剂为乙撑双硬脂酸酰胺。
本发明所述的聚氯乙烯电缆料专用抗冲功能碳酸钙具有以下有益效果:构思新颖、工艺简便、易于操作;采用本发明技术方案后,可提高聚氯乙烯电缆料韧性和强度,尤其可提高制品的抗冲击性能,提高产品的质量、弥补现有产品缺乏抗冲击性能的缺陷、填补了聚氯乙烯电缆料抗冲击性能产品的空白。本发明可以工业化批量生产,可以广泛地用于聚氯乙烯电缆料的加工领域。
具体实施方式
下面结合实施例对本发明作进一步的详细描述,但该实施例不应理解为对本发明的限制。
实施例1
本发明所述的聚氯乙烯电缆料专用抗冲功能碳酸钙按下列工艺程序配制:
一、制取PVC抗冲功能调节剂SRC各组分及重量份的配制:
乙烯·醋酸乙烯共聚物1.5;铝酸酯偶联剂0.05。
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC2;乙撑双硬脂酸酰胺1。
三、所述的聚氯乙烯电缆料专用抗冲功能碳酸钙的配制:
1、混料:将上述配制好的各组分重量份混合,一起投入捏合机中混合搅拌均匀,加温至135℃即可停止加温,备用。
2、卸料包装:将上述加工好的混料冷却至常温即可卸料包装,即成品—所述的聚氯乙烯电缆料专用抗冲功能碳酸钙。
实施例2
本实施例与实施例1基本相同,其不同之处在于:
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC3;分散剂1.1。
实施例3
本实施例与实施例1基本相同,其不同之处在于:
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC3.5;分散剂1.2。
实施例4
本实施例与实施例1基本相同,其不同之处在于:
一、制取PVC抗冲功能调节剂SRC各组分及重量份的配制:
乙烯·醋酸乙烯共聚物2;铝酸酯偶联剂0.07。
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC4;乙撑双硬脂酸酰胺1.3。
实施例5
本实施例与实施例4基本相同,其不同之处在于:
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC4.5;分散剂1.5。
实施例6
本实施例与实施例4基本相同,其不同之处在于:
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC5;分散剂1.6。
实施例7
本实施例与实施例1基本相同,其不同之处在于:
一、制取PVC抗冲功能调节剂SRC各组分及重量份的配制:
乙烯·醋酸乙烯共聚物2.5;铝酸酯偶联剂0.1。
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC6;分散剂1.7。
实施例8
本实施例与实施例7基本相同,其不同之处在于:
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC6.5;分散剂1.8。
实施例9
本实施例与实施例7基本相同,其不同之处在于:
二、制取所述聚氯乙烯电缆料专用抗冲功能碳酸钙各组分及重量份的配制:
重质碳酸钙100;PVC抗冲功能调节剂SRC7;分散剂2。
显然,本领域的技术人员可以对本发明进行各种改动和变化而不脱离本发明的精神和范围。这样,倘若本发明的这些修改和变化属于本发明权利要求及其等同技术的范围之内,则本发明也意图包含这些改动和变动在内。
本说明书中未作详细描述的内容属于本领域专业技术人员公知的现有技术。
Claims (8)
1.一种聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的专用抗冲功能碳酸钙包括以下组分及重量份:
重质碳酸钙100;PVC抗冲功能调节剂SRC2~7;分散剂1~2。
2.根据权利要求1所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的专用抗冲功能碳酸钙包括以下组分及重量份:
重质碳酸钙100;PVC抗冲功能调节剂SRC3~6.5;分散剂1.1~1.8。
3.根据权利要求2所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的专用抗冲功能碳酸钙包括以下组分及重量份:
重质碳酸钙100;PVC抗冲功能调节剂SRC3.5~6;分散剂1.2~1.7。
4.根据权利要求3所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的专用抗冲功能碳酸钙包括以下组分及重量份:
重质碳酸钙100;PVC抗冲功能调节剂SRC4~5;分散剂1.3~1.6。
5.根据权利要求4所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的专用抗冲功能碳酸钙包括以下组分及重量份:
重质碳酸钙100;PVC抗冲功能调节剂SRC4.5;分散剂1.5。
6.根据权利要求1所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的PVC抗冲功能调节剂SRC是由乙烯·醋酸乙脂与氯乙烯共聚物和铝酸酯偶联剂复合而成,其配比为:乙烯·醋酸乙脂与氯乙烯共聚物:铝酸酯偶联剂=1.5~2.5:0.05~0.1。
7.根据权利要求6所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的配比为:乙烯·醋酸乙脂与氯乙烯共聚物:铝酸酯偶联剂=2:0.07。
8.根据权利要求1所述的聚氯乙烯电缆料专用抗冲功能碳酸钙,其特征在于:所述的分散剂为乙撑双硬脂酸酰胺。