CN102718542B - 一种防火外墙保温材料及其制备方法 - Google Patents
一种防火外墙保温材料及其制备方法 Download PDFInfo
- Publication number
- CN102718542B CN102718542B CN 201210059329 CN201210059329A CN102718542B CN 102718542 B CN102718542 B CN 102718542B CN 201210059329 CN201210059329 CN 201210059329 CN 201210059329 A CN201210059329 A CN 201210059329A CN 102718542 B CN102718542 B CN 102718542B
- Authority
- CN
- China
- Prior art keywords
- nano
- preparation
- insulation material
- hydrogen peroxide
- fire prevention
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种防火外墙保温材料,包括高锰酸钾、硬脂酸钙、聚丙烯纤维、硫铝酸盐水泥、粉煤灰、纳米水泥添加剂、水以及双氧水;能达到A级的防火性能,能够降低导热系数达到国家节能要求。
Description
技术领域
本发明涉及一种保温材料,特别是一种防火外墙保温材料及其制备方法。
背景技术
2009年10月公安部与住房和城乡建设部联合下发了《民用建筑外保温系统及外墙装饰防火暂行规定》,对保温材料的防火性能进行了要求。2011年3月15日公安消防总局发文明确规定,在今后民用建筑外墙保温必须使用不燃的A级材料。
现有技术中一直没有发现既防火又轻且导热系数低的好配方。目前市场上很多无机保温材料虽然防火但是密度大、导热系数高、防水性差,远远达不到节能指标,而有机保温板虽然具有密度小、可加工性好、保温隔热效果好,但是产品本身易燃,安全性能低。像岩棉、矿棉和玻璃棉的无机材料,保温性能好、防火性能高可以达到A级标准,但价格高、吸水率高、施工不方便。因此需要一种配方简单、制备方便、防火及保温性能优良的建筑外墙材料。
发明内容
本发明的目的是提供一种配方简单、制备方便的防火外墙保温材料,具有优良的防火及保温性能。
本发明提供了一种防火外墙保温材料,包括:硫铝酸盐水泥、粉煤灰以及水,还包括高锰酸钾、硬脂酸钙、聚丙烯纤维、纳米水泥添加剂以及双氧水。
进一步优选,其组分按重量份组成为:硫铝酸盐水泥500-600份、粉煤灰250-350份、水200-300份、高锰酸钾1-2份、硬脂酸钙10-20份、聚丙烯纤维5-10份、纳米水泥添加剂200-220份以及双氧水30-50份。
进一步优选,所述双氧水的质量百分含量为15-30%。
进一步优选,所述纳米水泥添加剂为纳米硅、甲基丙烯酸甲酯和苯乙烯的混合物,所述纳米硅、甲基丙烯酸甲酯和苯乙烯的质量比为1∶10∶10。
本发明还提供了一种防火外墙保温材料的制备方法,将按比例配置的硫铝酸盐水泥、粉煤灰、水、高锰酸钾、硬脂酸钙、聚丙烯纤维和纳米水泥添加剂混合进行第一搅拌均匀后,加入双氧水继续第二搅拌后浇注于模具中,室温静置及脱模后形成产品。
进一步优选,第一搅拌时间为3-5分钟;第二搅拌时间为3-5分钟;所述静置时间为35-45分钟;所述第一搅拌和第二搅拌的操作温度为45℃。
本发明还提供了一种防火外墙保温板,使用上述防火外墙保温材料制得。
使用本发明所述防火外墙保温材料,具有如下优点:配方简单,易操作、发泡均匀、产品密度小、导热系数低,既能达到节能标准,又能达到A级防火要求。
附图说明
图1是本发明所述一种防火外墙保温板的制备流程图。
具体实施方式
根据图1所述本发明一种防火外墙保温材料的制备方法,将按比例配置的硫铝酸盐水泥、粉煤灰、水、高锰酸钾、硬脂酸钙、聚丙烯纤维和纳米水泥添加剂混合进行第一搅拌均匀后,加入双氧水继续第二搅拌后浇注于模具中,所述第一搅拌和第二搅拌的操作温度为45℃。室温静置及脱模后形成产品。所述纳米水泥添加剂为纳米硅、甲基丙烯酸甲酯和苯乙烯的混合物,所述纳米硅、甲基丙烯酸甲酯和苯乙烯的质量比为1∶10∶10。
实施例1:
按重量份,将500份硫铝酸盐水泥、350份粉煤灰、200份水、1份高锰酸钾、20份硬脂酸钙、5份聚丙烯纤维和220份纳米水泥添加剂混合进行第一搅拌5分钟,搅拌均匀后,加入50份15%(质量百分含量)的双氧水继续第二搅拌5分钟后,浇注于模具中,室温静置35分钟,脱模后进行切割,养护和检验后形成防火外墙保温板。
实施例2:
按重量份,将550份硫铝酸盐水泥、300份粉煤灰、250份水、1.5份高锰酸钾、10份硬脂酸钙、10份聚丙烯纤维和200份纳米水泥添加剂混合进行第一搅拌5分钟,搅拌均匀后,加入40份30%(质量百分含量)的双氧水继续第二搅拌3分钟后,浇注于模具中,室温静置40分钟,脱模后进行切割,养护和检验后形成防火外墙保温板。
实施例3:
按重量份,将600份硫铝酸盐水泥、250份粉煤灰、200份水、2份高锰酸钾、10份硬脂酸钙、5份聚丙烯纤维和200份纳米水泥添加剂混合进行第一搅拌3分钟,搅拌均匀后,加入50份30%(质量百分含量)的双氧水继续第二搅拌3分钟后,浇注于模具中,室温静置45分钟,脱模后进行切割,养护和检验后形成防火外墙保温板。
实施例1-3制得的保温板,发泡均匀、产品密度小、导热系数低,防火性能高可以达到A级标准,且制备简单快捷。
Claims (7)
1.一种防火外墙保温材料,包括:硫铝酸盐水泥、粉煤灰以及水,其特征在于,还包括高锰酸钾、硬脂酸钙、聚丙烯纤维、纳米水泥添加剂以及双氧水,其组分按重量份组成为:硫铝酸盐水泥500-600份、粉煤灰250-350份、水200-300份、高锰酸钾1-2份、硬脂酸钙10-20份、聚丙烯纤维5-10份、纳米水泥添加剂200-220份以及双氧水30-50份,所述纳米水泥添加剂为纳米硅、甲基丙烯酸甲酯和苯乙烯的混合物,所述双氧水的质量百分含量为15-30%,所述纳米水泥添加剂中纳米硅、甲基丙烯酸甲酯和苯乙烯的质量比为1∶10∶10。
2.一种如权利要求1所述的防火外墙保温材料的制备方法,其特征在于:将按比例配置的硫铝酸盐水泥、粉煤灰、水、高锰酸钾、硬脂酸钙、聚丙烯纤维和纳米水泥添加剂混合进行第一搅拌均匀后,加入双氧水继续第二搅拌后浇注于模具中,室温静置及脱模后形成产品。
3.根据权利要求2所述的制备方法,其特征在于,第一搅拌时间为3-5分钟。
4.根据权利要求3所述的制备方法,其特征在于,第二搅拌时间为3-5分钟。
5.根据权利要求4所述的制备方法,其特征在于,所述静置时间为35-45分钟。
6.根据权利要求5所述的制备方法,其特征在于,所述第一搅拌和第二搅拌的操作温度为45℃。
7.一种防火外墙保温板,其特征在于使用如权利要求1所述防火外墙保温材料制得。