CN102701641A - Building finish material, composite raw material and dosage proportion - Google Patents
Building finish material, composite raw material and dosage proportion Download PDFInfo
- Publication number
- CN102701641A CN102701641A CN201210210298XA CN201210210298A CN102701641A CN 102701641 A CN102701641 A CN 102701641A CN 201210210298X A CN201210210298X A CN 201210210298XA CN 201210210298 A CN201210210298 A CN 201210210298A CN 102701641 A CN102701641 A CN 102701641A
- Authority
- CN
- China
- Prior art keywords
- building
- building facing
- meant
- powder
- silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a building finish material, in particular to composite a raw material and the dosage proportion of the building finish material as well as flexible plates and building decorative plates made of the building finish material. The building plates made of the building finish material has the characteristics of light weight, thinness, flexibility, and good adhesion to a wall body.
Description
Technical field
The present invention relates to a kind of building facing material, the thin flexible sheet material of spy and the decorative panel for building that particularly relate to constitutive material and the consumption proportion of this building facing material and make thus.
Background technology
For many years, people as external wall decorative material, have beautified people's living environment to ceramic veneer.As everyone knows, ceramic veneer mainly burns till through thousands of degree high temperature with clay etc., not only bad for the protection of land resources, and will expend fuel in producing, and the smog of discharge is contaminate environment also.The complex manufacturing of ceramic veneer, facility investment is big.Ceramic veneer is a hard and fragile material, and linear expansivity is different with external wall insulating layer, is unfavorable for very much adhering to of ceramic veneer, and expanding with heat and contract with cold repeatedly can cause ceramic veneer to come off.Ceramic veneer is heavier, can significantly increase the deadweight of external thermal insulation system, makes it attached to outside the wall, under certain blast effect, is unfavorable for the security of total system.The ventilation property of ceramic veneer is poor, makes the finishing mucilage resist be in dampness for a long time, and the phenomenon of external thermal insulation system generation freeze-thaw damage will become seriously when cold in the winter time, directly external thermal insulation system and finish coat thereof produced potential safety hazard.
For above-mentioned reasons, the ceramic veneer unfortunate event that injures the pedestrian by a crashing object that comes off happens occasionally.Because safety, building energy conservation, land resources protection and environmental protection, increasing province, city are banning use of ceramic veneer.For example the relevant departments in provinces such as Chongqing, Shanghai, Dalian, Xi'an, Liaoning, Anhui, Jiangsu, Fujian, city all expressly provide and forbid Highrise buildings and walk is arranged or stream of people's accumulative external wall use ceramic veneer.
In recent years, domestic some producer has developed porcelain tendre and has used in certain areas.The starting material of porcelain tendre are the earth by 80-90%, and 10% water-soluble additive forms through high temperature sintering more than 400 degrees centigrade.It is with original argillous performance change, comes through photoirradiation effect typing, and production principle and traditional ceramics are similar.Therefore, complex manufacturing is unfavorable for land resources protection and energy-conservation equally.The flexibility of porcelain tendre is its advantage, also be it shortcoming.Since gentle, can eliminate safe hidden trouble, but lack necessary hardness and intensity, and impact resistance is poor, also is not easy to construction, is damaged easily during construction, is prone to warpage behind the last wall.The stickup of porcelain tendre, jointing need be adopted the polymer cement caking agent, and cost is high.The weathering resistance of porcelain tendre is poor, and for example, the porcelain tendre that has is deliquescing all the more in summer high temperature weather, be attached on the exterior wall back easily warpage with come off.During winter construction, be placed on certain porcelain tendre of out of door and also be not attached to just warpage, cracking or fracture on the exterior wall.Therefore change not as ceramic plane the work-ing life of porcelain tendre.
In order to solve the problems referred to above that ceramic veneer and porcelain tendre exist, the inventor has developed the novel building finishing material from called after " the thin gentle porcelain of dragon ".
Summary of the invention
The purpose of this invention is to provide a kind of light and flexible building facing material.
The raw material and the proportioning that are used for producing above-mentioned building facing material have been another object of the present invention is to provide.
Building facing material of the present invention has frivolous, pliable and tough and good with body of wall sticking power characteristics.
The objective of the invention is to realize through following measure:
A kind of building facing material is characterized in that raw material comprises silicate 30%-50%, particles of aggregates 10%-35%; Filler 15%-45%, properties-correcting agent 0.5%-18%, toughening material 0.3%-3%; High efficiency water reducing agent 0.1%-1.3%, an amount of water is in weight ratio; Said properties-correcting agent is meant one or more in building emulsion, water soluble resin, the water-soluble re-dispersible glue powder, preferred environmental protection emulsion, for example, polyacrylate emulsion, organosilicon crylic acid latex etc.; Said toughening material is meant man-made polymer's fiber, preferred polyamide fiber, trevira, Vestolen PP 7052 (PP) fiber, polyacrylonitrile fibre, Z 150PH (PVA) fiber, nylon fiber.Water is preferably the tap water of cleaning.The interpolation of properties-correcting agent has improved the pliability of building facing material effectively, and the interpolation of toughening material has improved the toughness of building facing material effectively.
Better for the performance that makes building facing material, above-mentioned building facing material compositing formula is silicate 30%-46%, and particles of aggregates is 10-32%; Filler 20%-45%; Properties-correcting agent is 0.3%-15%, toughening material 0.4%-1.5%, high efficiency water reducing agent 0.1%-1.3%; An amount of water is in weight ratio.
Above-mentioned silicate is meant the compound of being made up of element silicon, oxygen element and metallic element, comprises Calucium Silicate powder, water glass, pure aluminium silicate, silicate product.Above-mentioned particles of aggregates is meant sand, stone grain.Be preferably silica sand.Above-mentioned filler is meant powder-material.Be preferably one or more of silica powder, State of Blast Furnace ground-slag, ultra-fine wollastonite powder, dry powder, terra alba, talcum powder, flyash, hollow ceramic microspheres, perlite powder, stone flour, SILICA FUME.But the space in the filler filling compound, the compactness of raising building facing material, but consumption is unsuitable excessive, because consumption is crossed the water-intake rate that conference increases product.
Also comprise additive in the raw material of above-mentioned building facing material.Additive comprises hydrophober, skimmer, tinting material.Inorganic colourant and above-mentioned starting material have good consistency, can be evenly dispersed in the raw material, obtain uniform color tone, and alkaline-resisting, the acidproof rain of inorganic colourant, UV resistant irradiation, and are colour-fast in the atmosphere midium or long term.So the preferred inorganic colourant of tinting material, like red iron oxide, yellow oxide of iron, iron oxide black.
Above-mentioned building facing material composition of raw materials is silicate 30%-50%, particles of aggregates 10%-35%, filler 15%-45%; Properties-correcting agent 0.5%-18%, toughening material 0.3%-3%, high efficiency water reducing agent 0.1%-1.3%; Skimmer 0.3%-0.6%, tinting material 0.5%-4%; An amount of water is preferably the tap water of cleaning, in weight ratio.
Above-mentioned building facing material composition of raw materials is silicate 30%-46%, particles of aggregates 10-32%, filler 20%-45%; Properties-correcting agent 3%-15%, toughening material 0.4%-1.5%, high efficiency water reducing agent 0.1%-1.3%; Skimmer 0.3%-0.6%, red iron oxide 0.5%-4%, an amount of water; Be preferably the tap water of cleaning, in weight ratio.When an amount of water was meant all raw material summation less thaies 100%, water was supplied.
Above-mentioned building facing material adopts after the raw materials mix, stirs, and processes slurry, makes according to ordinary method.
Another object of the present invention realizes through following measure:
The thin flexible sheet material of the spy that the 2mm-4mm that adopts above-mentioned raw materials and proportioning to make is thick.
The thin flexible sheet material of above-mentioned spy is made up of bottom, middle layer, surface layer, and bottom and surface layer are to be processed by said raw material, and the middle layer is an enhancement layer; Said enhancement layer is a mesh reinforcements, comprises grid cloth or wire cloth, is preferably grid cloth.Synoptic diagram is seen Fig. 1.Also can not add grid cloth, process the special thin flexible sheet material of globality, other performance is unaffected.
The working method of the thin flexible sheet material of above-mentioned spy is after above-mentioned raw materials is mixed, to stir, and processes slurry, then smooth slab is processed in the slurry tiling and is got.
Adopt above-mentioned raw materials and proportioning, also can make the thin rigid sheet material of the thick spy of 2mm-4mm, the decorative panel for building that 5mm-25mm is thick.
Description of drawings
The special thin flexible sheet material of Fig. 1 is formed synoptic diagram.Special thin flexible sheet material is divided into bottom, middle layer, surface layer, and bottom and surface layer are to be processed by raw material described in the summary of the invention, and the middle layer is made up of enhancement layer.
2 group of 3 snappiness lab diagram of Fig. 2 embodiment
Beneficial effect
1. because select materials and proportioning, building facing material provided by the invention has light and flexible characteristics, heavily about 6Kg/m
2, being merely about 1/6 of common facing tile weight, the flexible sheet material that makes has thin characteristics concurrently, and thick about 3mm is merely about 1/8 of common ceramic tile thickness.Effectively practice thrift space, alleviate building bearing greatly; Be convenient to carrying in producing and transporting, reducing labor intensity reaches more than 60%, saves freight charges; Outside exterior wall, external heat insulation protecting layer, scraping 3mm left and right sides adhesive mortar in the construction is this flexible sheet material of Pasting, thereby the deadweight beyond the thermal insulation layer only reaches about 10kg, is merely 1/4 of common facing tile.
2. the toughening material in this building facing material raw material, and the existence of enhancement layer makes building facing material have good intensity and snappiness.Band certain degree of hardness in gently and not scratching, softening.Also can not use enhancement layer, the disposable slab that makes.
3. the material of this building facing material and body of wall is close, and its physicochemical property are close, like thermal expansivity etc., has solved thermal stresses and has amplified the puzzlement that brings.
4. thermal stress issues is able to solve, and its frivolous flexible performance makes this building facing material good with the sticking power and the consistency of body of wall in addition; Only need the thick adhesive mortar of 3-4mm on the building facing material during wall; Save cost, and coating performance is good after going up wall, being difficult for curling upwarps.
5. the raw material of this building facing material is main with mineral material, like silicate, particles of aggregates, has good weathering resistance and shock resistance; And do not fire, waterproof, Vermins-proof mildew-proof, antibiotic; Durable in use, need not follow-up maintenance and repairing, also can effectively protect thermal insulation layer and external wall heat insulation system; Have ventilation property, can make inside and outside the building facing material, and and body of wall between aqueous vapor reach balance.
6. this building facing material surface has the gloss of ceramic tile, also can make mute light product.Have the automatically cleaning ability, daily wind and rain can be removed dustiness on it.
7. the main raw material of product of the present invention is available nontoxic industrial waste salvage material, and the earth that does not need the mankind to depend on for existence helps the land resources protection.
8. owing to the frivolous flexible characteristic of this building facing material, also can change the suppleness or the sheet thickness of building facing materials according to different purposes.For example, be used for nonplanar protection and decorations such as cylinder and cylinder, can increase flexibility, coat cylinder fully, and without detriment to their shape, this is that similar building materials can't be accomplished.The protection and the decoration that are used for tunnel-side can increase to product thickness about 6-7mm, and be time saving and energy saving in the construction, accelerates speed of application, the reduction of erection time, reduces cost; Also be used as wear-resisting floor wearing floor to it so long, when walking above that, flexible sense.
9. product of the present invention is very smooth, and thickness is very even, and densification is indeformable, not stratified.
10. building facing material of the present invention can have different surfaces texture and color and luster; For example; Plane, male and fomale(M&F), pitted skin, parian face, decorative pattern, various texture, hole, mute light, high light and versicolor product, expressive force is abundant, has the excellent decoration effect.
11. adopt raw material of the present invention and proportioning, also can make the thin rigid sheet material of the thick spy of 2mm-4mm, decorative panel for building that 5mm-25mm is thick.
Embodiment
Below in conjunction with embodiment, the present invention is done further explain, but embodiment of the present invention is not limited thereto.
The data of embodiment all by weight percentage.
Composition, the parameter of embodiment 1 preparation building facing material
The snappiness experiment
Get the thin flexible sheet material of the spy that makes, be cut into 60mm wide * 240mm is long, thick about 3mm, along sheet material 240mm curved in length to the high arch of the about 15mm of formation till, sheet material does not crack or ruptures.Like Fig. 2.The sheet edge 10mm of portion does not consider with the variation that interior position occurs.Can be used for nonplanar protection and decorations such as cylinder and cylinder, sheet material is close to the slowly bending of periphery that diameter is 200mm, the sheet material art cracks or ruptures.
Composition, the parameter of embodiment 2 preparation building facing materials
The snappiness experiment
Get the thin flexible sheet material of the spy that makes, be cut into 60mm wide * 240mm is long, thick about 3mm, along sheet material 240mm curved in length to the high arch of the about 15mm of formation till, sheet material does not crack or ruptures.The sheet edge 10mm of portion does not consider with the variation that interior position occurs.Can be used for nonplanar protection and decorations such as cylinder and cylinder, sheet material is close to the slowly bending of periphery that diameter is 200mm, sheet material does not crack or ruptures.
Composition, the parameter of embodiment 3 preparation building facing materials
The snappiness experiment
Get the thin flexible sheet material of the spy that makes, be cut into 60mm wide * 240mm is long, thick about 3mm, along sheet material 240mm curved in length to the high arch of the about 15mm of formation till, sheet material does not crack or ruptures.Like Fig. 2.The sheet edge 10mm of portion does not consider with the variation that interior position occurs.Can be used for nonplanar protection and decorations such as cylinder and cylinder, sheet material is close to the slowly bending of periphery that diameter is 200mm, sheet material does not crack or ruptures.
Water consumption is with deciding season, and for example, use some summer more, and go easy winter.
Claims (9)
1. a building facing material is characterized in that raw material comprises silicate 30%-50%, particles of aggregates 10%-35%, and filler 15%-45%, properties-correcting agent 0.5%-18%, toughening material 0.3%-3%, high efficiency water reducing agent 0.1%-1.3%, an amount of water is in weight ratio; Said properties-correcting agent is meant one or more in building emulsion, water soluble resin, the water-soluble re-dispersible glue powder, and said toughening material is meant man-made polymer's fiber.
2. building facing material according to claim 1, raw material comprises silicate 30%-46%, and particles of aggregates is 10-32%, and filler 20%-45%, properties-correcting agent are 0.3%-15%, toughening material 0.4%-1.5%, high efficiency water reducing agent 0.1%-1.3%, an amount of water is in weight ratio.
3. building facing material according to claim 1 or claim 2, said properties-correcting agent is meant polyacrylate emulsion and/or organosilicon crylic acid latex.
4. like claim 1,2 or 3 said building facing materials, toughening material is one or more in tynex, trevira, polypropylene fibre, polyacrylonitrile fibre, Z 150PH (PVA) fiber, the nylon fiber.
5. like claim 1,2 or 4 said building facing materials, said silicate is meant one or more in Calucium Silicate powder, water glass, pure aluminium silicate, the silicate product; Said particles of aggregates is meant sand or/and the stone grain is preferably silica sand; Said filler is one or more of silica powder, State of Blast Furnace ground-slag, ultra-fine wollastonite powder, dry powder, terra alba, talcum powder, flyash, hollow ceramic microspheres, perlite powder, stone flour, SILICA FUME; Said high efficiency water reducing agent is meant high-efficiency water-reducing agent of poly-carboxylic acid.
6. like claim 1,2 or 5 said building facing materials, raw material also comprises additive, and said additive comprises hydrophober 0.1-0.2%, skimmer 0.3%-0.6%, tinting material 0.5%-4%.
7. like the said building facing material of claim 6, tinting material is an inorganic colourant, comprises red iron oxide, yellow oxide of iron, iron oxide black.
8. the 2mm-4mm sharp layer material or the thickness that adopt the raw material of the said building facing material of claim 1-7 to make are the decorative panel for building of 5mm-25mm.
9. like the said flexible sheet material of claim 8, be made up of bottom, middle layer, surface layer, bottom and surface layer are to be processed by said raw material, and the middle layer is an enhancement layer; Said enhancement layer is a mesh reinforcements, comprises grid cloth or wire cloth.