CN102689464A - 一种超材料复合板及加工方法 - Google Patents

一种超材料复合板及加工方法 Download PDF

Info

Publication number
CN102689464A
CN102689464A CN2012101281906A CN201210128190A CN102689464A CN 102689464 A CN102689464 A CN 102689464A CN 2012101281906 A CN2012101281906 A CN 2012101281906A CN 201210128190 A CN201210128190 A CN 201210128190A CN 102689464 A CN102689464 A CN 102689464A
Authority
CN
China
Prior art keywords
composite plate
ultra material
processing method
pur
metamaterial
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101281906A
Other languages
English (en)
Other versions
CN102689464B (zh
Inventor
刘若鹏
季春霖
金曦
沈旭
龚小林
王旭伟
王文剑
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kuang Chi Innovative Technology Ltd
Original Assignee
Kuang Chi Innovative Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuang Chi Innovative Technology Ltd filed Critical Kuang Chi Innovative Technology Ltd
Priority to CN201210128190.6A priority Critical patent/CN102689464B/zh
Publication of CN102689464A publication Critical patent/CN102689464A/zh
Application granted granted Critical
Publication of CN102689464B publication Critical patent/CN102689464B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种超材料复合板的加工方法，包括以下步骤，在聚苯乙烯基板上和/或下表面依次覆上热熔胶、金属箔形成预压复合板；将预压复合板放入热辊压机中热压形成超材料复合板，其辊压温度为90℃～120℃、辊压压力为1～6kg/cm2、辊压速度为0.1～1.0m/min。还涉及该方法制备的超材料复合板。聚苯乙烯的介电损耗小于0.001，而且成本低，是制备超材料基板的理想材料；采用热辊压机热压的方式在聚苯乙烯基板上覆金属箔(例如铜箔)的加工方法，该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆金属箔结合力满足了超材料的加工要求，因此该超材料复合板可以广泛应用在超材料加工领域。

Description

一种超材料复合板及加工方法
【技术领域】
本发明涉及超材料领域，尤其涉及用于制备超材料的超材料复合板及该超材料复合板的加工方法。
【背景技术】
超材料是指一些具有天然材料所不具备的超常物理性质的人工复合结构或复合材料。通过在材料的关键物理尺度上的结构有序设计，可以突破某些表面自然规律的限制，从而获得超出自然界固有的普通性质的超常材料功能。超材料的性质和功能主要来自于其内部的结构而非构成它们的材料，因此为设计和合成超材料。
目前超材料结构的实现是在刚性PCB板上制作金属线完成。超材料的主要介质基板材料为PCB所使用的绝缘材料：FR4、PTFE、聚酰亚胺等。使用FR4、聚酰亚胺为基材，其介电损耗较大，影响整个超材料性能，使用PTFE，其成本高，导致超材料成本上升。聚苯乙烯的介电损耗小于0.001，而且成本低，是制备超材料的理想材料。
但由于PS表面极性较小，导致其表面粘结性较差，因此其与铜的结合差，无法满足要求。目前一种是使用电镀的方式对PS表面进行覆铜，但电镀方式的成本高，废水废液多，具有较高的污染，并且电镀线占地面积大。另一种是真空压机热压方式，该方式操作复杂，真空压机设备占地面积大，热压时间长，生产效率低。
【发明内容】
本发明所要解决的技术问题是：提供一种使用热辊压机对聚苯乙烯基板表面覆金属箔的加工方法，获得所需的超材料复合板。
本发明解决上述技术间题所采用的技术方案是：一种超材料复合板的加工方法，包括以下步骤，
在聚苯乙烯基板上和/或下表面依次覆上热熔胶、金属箔形成预压复合板；
将预压复合板放入热辊压机中热压形成超材料复合板，其辊压温度为90℃～120℃、辊压压力为1～6kg/cm2、辊压速度为0.1～1.0m/min。
所述热熔胶为TPU热熔胶、PU热熔胶、PO热熔胶或EVA热熔胶。
所述金属箔为铜箔、银箔或铝箔。
一种超材料复合板，所述超材料复合板包括聚苯乙烯基板、贴覆在所述聚苯乙烯基板表面的金属箔及粘结所述聚苯乙烯基板和金属箔的热熔胶层。
本发明的有益效果为：由于聚苯乙烯的介电损耗小于0.001，而且成本低，是制备超材料基板的理想材料；采用热辊压机热压的方式在聚苯乙烯基板上覆金属箔(例如铜箔)的加工方法，该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆金属箔结合力满足了超材料的加工要求，因此该复合板可以广泛应用在超材料加工领域。
【附图说明】
图1本发明的超材料复合板的加工流程图。
【具体实施方式】
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
一种超材料复合板的加工方法，包括以下步骤，如图1所示
a、在聚苯乙烯基板上和/或下表面依次覆上热熔胶、金属箔形成预压复合板；
b、将预压复合板放入热辊压机中热压形成超材料复合板，其辊压温度为90℃～120℃、辊压压力为1～6kg/cm2、辊压速度为0.1～1.0m/min。
该加工方法使用熔点低于100℃的热熔胶作为聚苯乙烯与金属箔(例如铜箔、银箔或铝箔等)的粘结材料。热熔胶粘合是通过热力把热熔胶熔解，熔胶后的胶成为一种液体，热熔胶冷却后即完成了粘合。本发明中热熔胶可使用TPU热熔胶、PU热熔胶、PO热熔胶或EVA热熔胶等。
由于聚苯乙烯的介电损耗小于0.001，而且成本低，是制备超材料基板的理想材料；上述加工方法制备的超材料复合板包括聚苯乙烯基板、贴覆在聚苯乙烯基板表面的金属箔及粘结聚苯乙烯基板和金属箔(例如铜箔)的热熔胶层。该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆金属箔结合力满足了超材料的加工要求，因此该复合板可以广泛应用在超材料加工领域。
实施例一
a、在聚苯乙烯基板上、下表面依次覆上EVA热熔胶、厚度为0.01毫米的铜箔形成预压复合板；
b、将预压复合板放入热辊压机中热压形成复合板，其辊压温度为90℃、辊压压力为1kg/cm2、辊压速度为0.1m/min，冷却后获得所需的超材料复合板。
当然也可以单面覆铜箔，该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆铜箔结合力满足了超材料的加工要求，因此该超材料复合板可以广泛应用在超材料加工领域。
实施例二
a、在聚苯乙烯基板上、下表面依次覆上TPU热熔胶、厚度为0.075毫米的铜箔形成预压复合板；
b、将预压复合板放入热辊压机中热压形成超材料复合板，其辊压温度为100℃、辊压压力为3kg/cm2、辊压速度为0.4m/min，冷却后获得所需的超材料复合板。
当然也可以单面覆铜箔，该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆铜箔结合力满足了超材料的加工要求，因此该超材料复合板可以广泛应用在超材料加工领域。
实施例三
a、在聚苯乙烯基板上、下表面依次覆上PU热熔胶、厚度为0.15毫米的铜箔形成预压复合板；
b、将预压复合板放入热辊压机中热压形成复合板，其辊压温度为110℃、辊压压力为5kg/cm2、辊压速度为0.6m/min，冷却后获得所需的超材料复合板。
当然也可以单面覆铜箔，该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆铜箔结合力满足了超材料的加工要求，因此该超材料复合板可以广泛应用在超材料加工领域。
实施例四
a、在聚苯乙烯基板上、下表面依次覆上PO热熔胶、厚度为0.15毫米的铜箔形成预压复合板；
b、将预压复合板放入热辊压机中热压形成复合板，其辊压温度为120℃、辊压压力为6kg/cm2、辊压速度为1.0m/min，冷却后获得所需的超材料复合板。
当然也可以单面覆铜箔，该加工方法简化了生产工艺、设备简单、操作简便、降低了成本，并且无污染，而且覆铜箔结合力满足了超材料的加工要求，因此该超材料复合板可以广泛应用在超材料加工领域。
在上述实施例中，仅对本发明进行了示范性描述，但是本领域技术人员在阅读本专利申请后可以在不脱离本发明的精神和范围的情况下对本发明进行各种修改。

Claims (4)

1.一种超材料复合板的加工方法，其特征在于，包括以下步骤，在聚苯乙烯基板上和/或下表面依次覆上热熔胶、金属箔形成预压复合板；将预压复合板放入热辊压机中热压形成超材料复合板，其辊压温度为90℃～120℃、辊压压力为1～6kg/cm2、辊压速度为0.1～1.0m/min。
2.根据权利要求1所述的超材料复合板的加工方法，其特征在于，所述热熔胶为TPU热熔胶、PU热熔胶、PO热熔胶或EVA热熔胶。
3.根据权利要求1所述的超材料复合板的加工方法，其特征在于，所述金属箔为铜箔、银箔或铝箔。
4.一种超材料复合板，其特征在于，所述超材料复合板包括聚苯乙烯基板、贴覆在所述聚苯乙烯基板表面的金属箔及粘结所述聚苯乙烯基板和金属箔的热熔胶层。
CN201210128190.6A 2012-04-27 2012-04-27 一种超材料复合板及加工方法 Active CN102689464B (zh)