CN102676864B - 紫色k金的配方和制备方法 - Google Patents
紫色k金的配方和制备方法 Download PDFInfo
- Publication number
- CN102676864B CN102676864B CN 201210185903 CN201210185903A CN102676864B CN 102676864 B CN102676864 B CN 102676864B CN 201210185903 CN201210185903 CN 201210185903 CN 201210185903 A CN201210185903 A CN 201210185903A CN 102676864 B CN102676864 B CN 102676864B
- Authority
- CN
- China
- Prior art keywords
- gold
- purple
- rare earth
- preparation
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种紫色K金的配方,包括以下各重量百分比的物质:铝21.2%~21.6%、铜0.3%~0.7%、稀土0.03%~0.5%,余量为金。本发明还公开了制备上述紫色K金的方法,包括以下步骤:(1)根据上述的配方范围选定一组配比,再根据所需制备的合金重量,计算出各物质的重量;(2)在坩埚中加入金块并加热至1100℃~1200℃使其完全融化;(3)再按配方先向坩埚中加入铝,再加入铜,最后加入稀土,搅拌均匀,在1100℃~1130℃保温0.5~1小时;(4)倒模成型,成型的粗胚在900℃~1100℃下进行25小时~50小时的退火处理制得。本发明在保证K金淡紫色的同时有效地改善了紫金的加工性能,增加了其延展性,从而使其能在更多的饰品中加工应用。
Description
技术领域
本发明涉及黄金的合金,尤其是涉及一种紫色K金的配方和制备方法。
背景技术
黄金的特点之一就是柔软,所以当镶嵌宝石时由于强度不够容易脱落。因此,人们在黄金中加入银、铜、锌等金属以增加黄金的强度和韧性,这样制成的金饰,又称K金。在珠宝首饰镶嵌中几乎都用不同K数的K金来镶嵌宝石。这样既达到黄金的高贵,又弥补它的不足,并可以根据需要配制成各种颜色,K金是珠宝首饰中最常用和变化最丰富的材料。K数与含金量的关系式:Au wt%=K/24×100%。K金可以根据需要配制成各种颜色,在国际上流行的K金首饰各种颜色都有,常见的一般有黄色和白色。彩金不但能使有色宝石的色彩更加浓重,还体现了金属材质的精致、细腻。彩金给人带来温暖与愉快;在款式上也是千姿百态。各种风格迥异的饰品,可谓璀璨耀眼,女性无论是着职业装还是晚礼服,与之相配都能显出高雅的气质。彩金一直是欧洲人很喜欢的首饰材料,它的寓意就跟中国人在翡翠中找到的“福禄寿”一样,代表着人们美好的愿望。彩金饰品因其重量较轻、价格稍低、工艺精美、款式新颖,越来越受到大家的喜欢。K金按颜色分为颜色金合金和白色金合金。在饰品中使用得最多的颜色金合金是Au-Ag-Cu(-Zn)系合金;白色金合金大多为Au-Ag-Ni(Cu、Zn)和Au-Ag-Pd(-Zn、Cu)系合金。紫色K金是金和铝形成的金属合金Au-Al,其淡紫色相当迷人,但由于性脆易碎,所以难以加工。
发明内容
针对以上提出的问题,本发明目的在于提供一种便于加工的的紫色K金的配方和制备方法。
本发明通过以下技术措施实现的,一种紫色K金的配方,包括以下各重量百分比的物质:铝21.2%~21.6%、铜0.3%~0.7%、稀土0.03%~0.5%,余量为金。
作为一种优选方式,包括以下各重量百分比的物质:铝21.4%、铜0.6%、稀土0.2%,余量为金。
其中,所述稀土中至少包含镧、铈、镨、钕、钆、铽、镝、钬、铒、铥、镥、钪、钇中的一种稀土金属。
特别优选的,所述稀土中至少包含镧、铈中的一种稀土金属。
本发明还公开了制备上述的任一种紫色K金的方法,包括以下步骤:
(1)、根据上述的配方范围选定一组配比,再根据所需制备的合金重量,计算出各物质的重量;
(2)、在坩埚中加入金块并加热至1100℃~1200℃使其完全融化;
(3)、再按配方先向坩埚中加入铝,再加入铜,最后加入稀土,搅拌均匀,在1100℃~1130℃保温0.5~1小时;
(4)、倒模成型,成型的粗胚在900℃~1100℃下进行25小时~50小时的退火处理制得。
具体的,所述步骤(4)中退火处理时间为36小时。
作为一种优选方式,所述步骤(2)和(3)中的熔融是在惰性气氛的保护下进行的。
作为一种优选方式,所述步骤(4)中的退火处理是在惰性气氛的保护下进行的。
本发明在普通的紫金配方中添加了铜和稀土元素,在保证其淡紫色的同时有效地改善了紫金的加工性能,增加了其延展性,从而使其能在更多的饰品中加工应用。
具体实施方式
下面结合实施例并对本发明作进一步详细说明。
实施例1
一种用于戒指的紫色K金的配方,包括以下各重量百分比的物质:铝21.2%、铜0.7%、稀土0.5%,稀土中至少包含镧、铈中的一种,余量为金。
制备上述紫色K金戒指的方法,包括以下步骤:
(1)、根据上述的配方,再根据所需制备的合金重量,计算出各物质的重量;
(2)、在坩埚中加入金块并在惰性气氛的保护下加热至1100℃~1150℃使其完全融化;
(3)、再按配方先向坩埚中加入铝,再加入铜,最后加入稀土,搅拌均匀,在惰性气氛的保护下1130℃保温1小时;
(4)、倒模成型,将上一步骤所得熔化配料倒入石膏模中浇铸出戒指铸件,将铸件在惰性气氛的保护下1000℃进行36小时的退火处理制得戒指粗胚;
(5)、最后进行抛光、执模、压光、车花等工艺。
本发明加工的戒指颜色为淡紫色,外观光洁,显得高贵、典雅,多批加工的成品率为99.5%,与24K金加工的成品率相同。
实施例2
一种用于吊坠的紫色K金的配方,包括以下各重量百分比的物质:铝21.6%、铜0.3%、稀土0.03%,稀土中至少包含镧、铈、镨、钕、钆、铽、镝、钬、铒、铥、镥、钪、钇中的一种,余量为金。
制备上述紫色K金吊坠的方法,包括以下步骤:
(1)、根据上述的配方,再根据所需制备的合金重量,计算出各物质的重量;
(2)、在坩埚中加入金块并在惰性气氛的保护下加热至1150℃~1200℃使其完全融化;
(3)、再按配方先向坩埚中加入铝,再加入铜,最后加入稀土,搅拌均匀,在惰性气氛的保护下1100℃保温0.5小时;
(4)、倒模成型,将上一步骤所得熔化配料倒入石膏模中浇铸出吊坠铸件,将铸件在惰性气氛的保护下900℃进行25小时的退火处理制得吊坠粗胚;
(5)、最后进行抛光、执模、压光、车花等工艺。
本发明加工的吊坠颜色为淡紫色,外观光洁,显得高贵、典雅,多批加工的成品率为99.2%,与24K金加工的成品率相同。
实施例3
铝21.2%~21.6%、铜0.3%~0.7%、稀土0.03%~0.5%,余量为金。
一种用于钻戒的紫色K金的配方,包括以下各重量百分比的物质:铝21.3%、铜0.3%、稀土0.5%,稀土中至少包含镧、铈中的一种,余量为金。
制备上述紫色K金钻戒的方法,包括以下步骤:
(1)、根据上述的配方,再根据所需制备的合金重量,计算出各物质的重量;
(2)、在坩埚中加入金块并在惰性气氛的保护下加热至1150℃~1200℃使其完全融化;
(3)、再按配方先向坩埚中加入铝,再加入铜,最后加入稀土,搅拌均匀,在惰性气氛的保护下1100℃保温45分钟;
(4)、倒模成型,将上一步骤所得熔化配料倒入石膏模中浇铸出戒指铸件,将铸件在惰性气氛的保护下1100℃进行50小时的退火处理制得戒指粗胚;
(5)、最后进行抛光、执模、压光、车花、镶钻等工艺。
本发明加工的钻戒颜色为淡紫色,镶口延展性好,折弯三次还能保证合格的强度。
以上是对本发明紫色K金的配方和制备方法进行了阐述,用于帮助理解本发明,但本发明的实施方式并不受上述实施例的限制,任何未背离本发明原理下所作的改变、修饰、替代、组合、简化,均应为等效的置换方式,都包含在本发明的保护范围之内。
Claims (5)
1.一种紫色K金的制备方法,其特征在于包括以下步骤:
(1)根据重量百分比的铝21.4%、铜0.6%、稀土0.2%,余量为金的配比,再根据所需制备的合金重量,计算出各物质的重量,其中,所述稀土中至少包含镨、钕、钆、铽、镝、钬、铒、铥、镥、钪中的一种稀土金属;
(2)、在坩埚中加入金块并加热至1100℃~1200℃使其完全熔化;
(3)、再按配方先向坩埚中加入铝,再加入铜,最后加入稀土,搅拌均匀,在1100℃~1130℃保温0.5~1小时;
(4)、倒模成型,成型的粗坯在900℃~1100℃下进行25小时~50小时的退火处理制得紫色K的颜色为淡紫色,镶口延展性好,折弯三次还能保证合格的强度。
2.根据权利要求1所述的紫色K金的制备方法,其特征在于:所述步骤(4)中退火处理时间为36小时。
3.根据权利要求1所述的紫色K金的制备方法,其特征在于:所述步骤(2)和(3)是在惰性气氛的保护下进行的。
4.根据权利要求1或2或3所述的紫色K金的制备方法,其特征在于:所述步骤(4)中的退火处理是在惰性气氛的保护下进行的。
5.一种由上述权利要求1-4中所述方法制得的紫色K金,其特征在于,所述K金由重量百分比的铝21.4%、铜0.6%、稀土0.2%,余量为金的配方制得,其中,所述稀土中至少包含镨、钕、钆、铽、镝、钬、铒、铥、镥、钪中的一种稀土金属。