CN102676012A - 纯丙外墙乳胶涂料 - Google Patents
纯丙外墙乳胶涂料 Download PDFInfo
- Publication number
- CN102676012A CN102676012A CN201110064257XA CN201110064257A CN102676012A CN 102676012 A CN102676012 A CN 102676012A CN 201110064257X A CN201110064257X A CN 201110064257XA CN 201110064257 A CN201110064257 A CN 201110064257A CN 102676012 A CN102676012 A CN 102676012A
- Authority
- CN
- China
- Prior art keywords
- parts
- pure
- exterior wall
- latex coating
- wall latex
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纯丙外墙乳胶涂料,其组成成分及其各组分的重量分数比为:纯丙乳液250-280份、分散剂12-15份、增稠剂15-18份、成膜助剂8-10份、流平剂5-8份、钛白粉180-200份、重钙60-70份、轻钙60-70份、滑石粉80-90份、硅灰石粉28-32份、防腐剂0.5-1份、消泡剂1.2-1.5份、水250-300份、颜料浆10-20份。本发明综合性能良好,涂膜光亮,为绿色环保涂料,无毒、无味、无污染。
Description
技术领域
本发明属于精细化工领域,涉及一种外墙涂料,具体涉及一种纯丙外墙乳胶涂料。
背景技术
外墙涂料分为溶剂型涂料和乳胶涂料两种,溶剂型外墙涂料主要是以热塑性丙稀酸、有机硅改性丙稀酸树酯、聚氨酯树酯等为成膜物质加入溶剂、颜填料及各种助剂,经溶解分散、研磨而成,其的特点是装饰效果好,使用寿命长,但环保性能较差,乳胶涂料以水为散介质,以苯丙乳液、纯丙乳液、乙丙乳液作基料,加入颜填料及各种助剂,经搅拌、分散、研磨就制成,其特点是耐水性、保色性好,无毒无味,已成为目前国内外建筑涂刷材料发展的方向,但现有的乳胶涂料耐候性较差,长时间的日晒雨淋,涂膜的保持时间较短。
发明内容
发明目的:本发明为了解决现有技术的不足,提供了一种耐候性好、使用寿命长的纯丙外墙乳胶涂料。
本发明采用的技术方案:一种纯丙外墙乳胶涂料,包括纯丙乳液、分散剂、增稠剂、成膜助剂、流平剂、钛白粉、重钙、轻钙、滑石粉、硅灰石粉、防腐剂、消泡剂、水、颜料浆,其组成成分及其各组分的重量配比为:
纯丙乳液250-280份
分散剂12-15份
增稠剂15-18份
成膜助剂8-10份
流平剂5-8份
钛白粉180-200份
重钙60-70份
轻钙60-70份
滑石粉80-90份
硅灰石粉28-32份
防腐剂0.5-1份
消泡剂1.2-1.5份
水250-300份
颜料浆10-20份。
作为优选,所述的分散剂为丙烯酸酯高分子分散剂。
作为优选,所述的增稠剂为羟乙基纤维素。
作为优选,所述的成膜助剂为十二碳醇酯。
作为优选,所述的流平剂为有机硅流平剂。
作为优选,所述的防腐剂为异噻唑啉酮。
作为优选,所述的消泡剂为有机硅树脂类消泡剂。
有益效果:本发明为绿色环保涂料,无毒无味,其涂膜光亮,具有良好的耐水性、耐碱性、耐气候性,同时该涂料施工性能好,饰面抗腐蚀,不起泡,不掉粉,能保持长久的不褪色。
具体实施方式
下面结合具体实施方式对本发明作进一步说明。
实施例1
以总分量为1000份计算,其中纯丙乳液280份、分散剂12份、增稠剂15份、成膜助剂8份、流平剂5份、钛白粉180份、重钙60份、轻钙60份、滑石粉90份、硅灰石粉28份、防腐剂0.5份、消泡剂1.5份、水250份、颜料浆10份,按上述比例,在分散容器中加入水,再放入分散剂、消泡剂、钛白粉,高速搅拌20分钟;再陆续加入重钙、轻钙、滑石粉、硅灰石粉、颜料浆后搅拌均匀;用胶体磨机研磨至所需要的细度;加入纯丙乳液,启动搅拌机,投入成膜助剂、防腐剂、消泡剂,用氨水调节pH值到8;把增稠剂和平流剂缓慢加入低速搅拌罐中,边加边搅拌至所需要的粘度为止,待制成后分罐密封储,其中,分散剂为丙烯酸酯高分子分散剂,增稠剂为羟乙基纤维素,成膜助剂为十二碳醇酯,流平剂为有机硅流平剂,防腐剂为异噻唑啉酮,消泡剂为有机硅树脂类消泡剂。
实施例2
以总分量为1000份计算,其中纯丙乳液250份、分散剂15份、增稠剂15份、成膜助剂10份、流平剂5份、钛白粉200份、重钙65份、轻钙65份、滑石粉85份、硅灰石粉28份、防腐剂0.5份、消泡剂1.5份、水250份、颜料浆10份。按上述比例,在分散容器中加入水,再放入分散剂、消泡剂、钛白粉,高速搅拌20分钟;再陆续加入重钙、轻钙、滑石粉、硅灰石粉、颜料浆后搅拌均匀;用胶体磨机研磨至所需要的细度;加入纯丙乳液,启动搅拌机,投入成膜助剂、防腐剂、消泡剂,用氨水调节pH值到8;把增稠剂和平流剂缓慢加入低速搅拌罐中,边加边搅拌至所需要的粘度为止,待制成后分罐密封储,其中,分散剂为丙烯酸酯高分子分散剂,增稠剂为羟乙基纤维素,成膜助剂为十二碳醇酯,流平剂为有机硅流平剂,防腐剂为异噻唑啉酮,消泡剂为有机硅树脂类消泡剂。
实施例3
以总分量为1000份计算,其中纯丙乳液260份、分散剂15份、增稠剂15份、成膜助剂10份、流平剂5份、钛白粉190份、重钙60份、轻钙60份、滑石粉85份、硅灰石粉28份、防腐剂0.5份、消泡剂1.5份、水260份、颜料浆10份。按上述比例,在分散容器中加入水,再放入分散剂、消泡剂、钛白粉,高速搅拌20分钟;再陆续加入重钙、轻钙、滑石粉、硅灰石粉、颜料浆后搅拌均匀;用胶体磨机研磨至所需要的细度;加入纯丙乳液,启动搅拌机,投入成膜助剂、防腐剂、消泡剂,用氨水调节pH值到8;把增稠剂和平流剂缓慢加入低速搅拌罐中,边加边搅拌至所需要的粘度为止,待制成后分罐密封储,其中,分散剂为丙烯酸酯高分子分散剂,增稠剂为羟乙基纤维素,成膜助剂为十二碳醇酯,流平剂为有机硅流平剂,防腐剂为异噻唑啉酮,消泡剂为有机硅树脂类消泡剂。
Claims (7)
1.一种纯丙外墙乳胶涂料,包括纯丙乳液、分散剂、增稠剂、成膜助剂、流平剂、钛白粉、重钙、轻钙、滑石粉、硅灰石粉、防腐剂、消泡剂、水、颜料浆,其特征在于:各组分的重量分数比为:
纯丙乳液250-280份
分散剂12-15份
增稠剂15-18份
成膜助剂8-10份
流平剂5-8份
钛白粉180-200份
重钙60-70份
轻钙60-70份
滑石粉80-90份
硅灰石粉28-32份
防腐剂0.5-1份
消泡剂1.2-1.5份
水250-300份
颜料浆10-20份。
2.根据权利要求1所述的纯丙外墙乳胶涂料,其特征在于:所述的分散剂为丙烯酸酯高分子分散剂。
3.根据权利要求1所述的纯丙外墙乳胶涂料,其特征在于:所述的增稠剂为羟乙基纤维素。
4.根据权利要求1所述的纯丙外墙乳胶涂料,其特征在于:所述的成膜助剂为十二碳醇酯。
5.根据权利要求1所述的纯丙外墙乳胶涂料,其特征在于:所述的流平剂为有机硅流平剂。
6.根据权利要求1所述的纯丙外墙乳胶涂料,其特征在于:所述的防腐剂为异噻唑啉酮。
7.根据权利要求1所述的纯丙外墙乳胶涂料,其特征在于:,所述的消泡剂为有机硅树脂类消泡剂。