CN102675989A - 一种用于环保石头纸表面的涂布液 - Google Patents
一种用于环保石头纸表面的涂布液 Download PDFInfo
- Publication number
- CN102675989A CN102675989A CN2012101887884A CN201210188788A CN102675989A CN 102675989 A CN102675989 A CN 102675989A CN 2012101887884 A CN2012101887884 A CN 2012101887884A CN 201210188788 A CN201210188788 A CN 201210188788A CN 102675989 A CN102675989 A CN 102675989A
- Authority
- CN
- China
- Prior art keywords
- rotating speed
- minutes
- stirrer
- add
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于环保石头纸表面的涂布液,解决了现有产品使纸张表面手感粗糙,缺少光泽,强度低,弯折性能差等问题。所述的涂布液成分及其质量百分比为:丁苯橡胶乳液14.8%~17.2%,无机矿粉31.0%~36.0%,纯水33.5%~42.7%,乙二醇0.4%~0.5%,分散剂0.22%~0.25%,消泡剂0.11%~0.13%,增稠剂0.18%~0.21%,PVA-S 9.7%~11.3%,润滑剂0.8%~1.0%。本发明还具体提供了上述涂布液的制备方法。本发明可显著改善环保纸表面手感、平整性、柔性、印刷性能以及提高纸张的表面强度。
Description
技术领域:
本发明涉一种涂布液,更确切地说涉及一种用于纸张的涂布液。
背景技术:
环保纸(石头纸),最早出现于20世纪六七十年代的日本和德国等,到20世纪80年代,苏联也成功研制了“石头纸”,我国最早生产的“石头纸”出现在台湾地区。其是一种非木浆、非纸浆为原料的生态纸,以地壳内最为丰富的矿产资源碳酸钙为主要原料,以高分子材料及多种无机物为辅助原料,利用高分子界面化学原理和填充改性技术,经特殊工艺加工而成的一种可逆性循环利用、具有现代技术特点的新型造纸。
但这种纸张(未涂布的纸也称原纸),表面手感粗糙,缺少光泽,强度低,弯折性能差等不足,因而需要对原纸进行表面处理,改善性能,满足文化用纸、包装用纸和装潢用纸的不同需求。
发明内容:
本发明的目的在于克服现有技术的不足,提供一种可改善原纸表面性能的涂布液。
本发明所述的用于环保纸原纸表面的涂布液,其特征在于:所述的涂布液成分及其质量百分比为:
丁苯橡胶乳液14.8%~17.2%,无机矿粉31.0%~36.0%,纯水33.5%~42.7%,
乙二醇0.4%~0.5%,分散剂0.22%~0.25%,消泡剂0.11%~0.13%,增稠剂0.18%~0.21%,PVA-S 9.7%~11.3%,润滑剂0.8%~1.0%。
所述的无机矿粉是轻质碳酸钙,滑石粉。
所述的常用消泡剂为有机硅型消泡剂,分散剂为聚丙烯酸磷有机分散剂,增稠剂为CMC,润滑剂是液态石蜡。上述成分中,乙二醇为抗冻剂,丁苯橡胶乳液和PVA-S为胶粘剂,无机矿粉为填料。
制备上述用于环保纸表面的涂布液的方法是:将适量的乙二醇加入到一定量的纯水中搅拌后加入分散剂、消泡剂、CMC、PVA-S,通过机械搅拌混合均匀,再加入定量的轻质碳酸钙、滑石粉进一步搅拌,混合,然后加入一定量的丁苯橡胶乳液搅拌一定时间后加入润滑剂,继续搅拌后静置待用。
所用原料的重量如上所述,具体包括以下步骤:
1.称取纯水,倒入容器中,开启搅拌机。
2.加入乙二醇,搅拌机开到300转,直至搅拌均匀。
3.加入分散剂,搅拌机转速不变,直至搅拌均匀。
4.加入消泡剂,搅拌机转速不变,直至搅拌均匀。
5.慢慢加入CMC,搅拌机转速不变,搅拌约30分钟。
6.慢慢加入PVA-S,搅拌机转速不变,搅拌约10分钟。
7.将转速调至800转,然后分别慢慢加入轻质碳酸钙和滑石粉,然后搅拌90分钟。
8.将搅拌机转速调整至700转,慢慢加入丁苯橡胶乳液,搅拌90分钟。
9.将搅拌机转速调整至400转,慢慢加入润滑剂,搅拌20分钟。
10.将转速调整至200转,搅拌10分钟,静置待用。
按照配方和对涂布液粘度的不同要求,在上述步骤9中保持转速不变,加入一定量的纯水,搅拌20分钟。
丁苯橡胶因为具有分子结构软硬度的可调节、耐低温、柔软性好和耐磨性好等优点,广泛用于涂料、涂饰剂弹性体、印染助剂和胶粘剂等领域。随着人们对环保意识的增强,以水为分散介质的丁苯橡胶成为研究和应用的重要方向。
由上述技术方案可知,本发明具有以下有益效果:显著改善环保纸表面手感、平整性、柔性、印刷性能以及提高纸张的表面强度。经过实验证明,涂布过的纸张其平滑度提高5-8倍,挺度提高2-3倍,撕裂度提高20%-40%,表面剥离强度提高1倍以上,印刷的着墨效果也大大提高。
具体实施方式:
实施例1
所用涂布液的原料及重量如下表所示:表中原料重量单位为克
原料 | 配方一 | 配方二 | 配方三 | 配方四 | 配方五 |
纯水 | 620 | 654 | 626 | 575 | 552 |
EG(乙二醇) | 7 | 7.4 | 7.6 | 7.9 | 8.1 |
分散剂 | 3.7 | 3.9 | 4 | 4.2 | 4.3 |
消泡剂 | 1.8 | 1.9 | 2 | 2.1 | 2.2 |
CMC | 3 | 3.1 | 3.2 | 3.4 | 3.5 |
PVA-S | 161 | 170 | 174 | 183 | 187 |
轻质碳酸钙 | 426 | 450 | 461 | 484 | 500 |
滑石粉 | 84 | 88 | 91 | 95 | 92 |
丁苯橡胶乳液 | 245 | 258 | 265 | 278 | 284 |
润滑剂 | 13.7 | 15 | 15.4 | 16.2 | 16.6 |
纯水 | 84 | 0 | 0 | 0 | 0 |
总重量 | 1649.2 | 1649.3 | 1649.2 | 1648.8 | 1649.7 |
固成分(质量分数)% | 39±1 | 41.1±1 | 42.2±1 | 44.3±1 | 45.3±1 |
粘度(Pa·s) | 100±20 | 150±20 | 210±20 | 300±20 | 260±20 |
实施例2
采用上述配方的制备方法的具体工艺步骤为:以配方1为例
1.称取纯水620克,倒入容器中,开启搅拌机。
2.加入7克乙二醇,搅拌机开到300转,直至搅拌均匀。
3.加入3.7克分散剂,搅拌机转速不变,直至搅拌均匀。
4.加入1.8克消泡剂,搅拌机转速不变,直至搅拌均匀。
5.慢慢加入3克CMC,搅拌机转速不变,搅拌约30分钟。
6.慢慢加入16克PVA-S,搅拌机转速不变,搅拌约10分钟。
7.将转速调至800转,然后分别慢慢加入426克轻质碳酸钙和84克滑石粉,然后搅拌90分钟。
8.将搅拌机转速调整至700转,慢慢加入245克丁苯橡胶乳液,搅拌90分钟。
9.将搅拌机转速调整至400转,慢慢加入13.7克润滑剂,搅拌20分钟。
10.将转速调整至200转,搅拌10分钟,静置待用。此时所得涂布液的粘度为140Pa·s左右。
在上述步骤9:保持转速不变,加入84克纯水,搅拌20分钟,再将转速调整至200转,搅拌10分钟,静置待用。此时所得涂布液的粘度为100Pa·s左右。
Claims (4)
1.一种用于环保石头纸表面的涂布液,其特征在于:所述的涂布液成分及其质量百分比为:
丁苯橡胶乳液14.8%~17.2%,无机矿粉31.0%~36.0%,纯水33.5%~42.7%,
乙二醇0.4%~0.5%,分散剂0.22%~0.25%,消泡剂0.11%~0.13%,增稠剂0.18%~0.21%,PVA-S 9.7%~11.3%,润滑剂0.8%~1.0%。
2.如权利要求1所述的用于环保石头纸表面的涂布液,其特征在于:所述的无机矿粉是轻质碳酸钙,滑石粉。
3.一种制备如权利要求1所述的用于环保石头纸表面的涂布液的方法,其特征在于包括以下步骤:
(1)称取纯水,倒入容器中,开启搅拌机。
(2)加入乙二醇,搅拌机开到300转,直至搅拌均匀。
(3)加入分散剂,搅拌机转速不变,直至搅拌均匀。
(4)加入消泡剂,搅拌机转速不变,直至搅拌均匀。
(5)慢慢加入CMC,搅拌机转速不变,搅拌约30分钟。
(6)慢慢加入PVA-S,搅拌机转速不变,搅拌约10分钟。
(7)将转速调至800转,然后分别慢慢加入轻质碳酸钙和滑石粉,然后搅拌90分钟。
(8)将搅拌机转速调整至700转,慢慢加入丁苯橡胶乳液,搅拌90分钟。
(9)将搅拌机转速调整至400转,慢慢加入润滑剂,搅拌20分钟。
(10)将转速调整至200转,搅拌10分钟,静置待用。
4.如权利要求3所述的方法,其特征在于:在上述步骤(9)保持转速不变,加入一定量的纯水,搅拌20分钟。