CN102675803A - 纳米高分子复合材料交通线路标志 - Google Patents
纳米高分子复合材料交通线路标志 Download PDFInfo
- Publication number
- CN102675803A CN102675803A CN2012101706249A CN201210170624A CN102675803A CN 102675803 A CN102675803 A CN 102675803A CN 2012101706249 A CN2012101706249 A CN 2012101706249A CN 201210170624 A CN201210170624 A CN 201210170624A CN 102675803 A CN102675803 A CN 102675803A
- Authority
- CN
- China
- Prior art keywords
- parts
- mark
- traffic line
- sign
- polymer composites
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种纳米高分子复合材料交通线路标志,包括标志本体,其特征是:标志本体的材质成分组成按重量份是:纳米二氧化硅100份、聚苯乙烯600份、硬脂酸锌24份、固化剂3份、玻璃丝纤维100份、氧化镁3份、石英砂1000份、苯乙烯1400份、钛白粉20份、不饱和树脂400份。其优点是:本能够抵御太阳紫外线照射、风吹、雨淋等自然侵蚀,使用寿命长;表面光滑,可与大理石媲美,尺寸精确度高;产品密度高,油污无法侵入,颜色自然稳定,终身不用刷漆维护;生产效率高,适合批量生产;警示和提示性能明显,并可美化铁路、公路沿线环境;产品无二次回收利用价值,不易丢失,安装十分简便,是传统水泥制品的理想的换代产品。
Description
技术领域
本发明涉及一种纳米高分子复合材料交通线路标志,属于道路交通领域。
背景技术
传统的交通线路标志由水泥制成,产品外观粗糙。由于交通线路标志是露天设置,其抗老化、抗氧化等方面能力较差,受风吹、雨淋、日晒,水泥标志的表面先是出现蜂窝状,然后自然掉渣,甚至断裂。而且水泥标志每年都要在表面刷油漆进行维护,以增加其表面颜色,否则就会变成水泥本色,同时,标志上的数字标识每年也需要重新用油漆喷字。所以每年都要有人工、油漆等维护成本。
发明内容
本发明的目的是提供一种外观光洁、抗腐蚀、耐老化、不易破损、不褪色、无需维护、寿命长、警示和提示性能明显的纳米高分子复合材料交通线路标志。
本发明的技术方案如下:
本发明包括标志本体,标志本体的材质成分组成按重量份是:纳米二氧化硅100份、聚苯乙烯600份、硬脂酸锌24份、固化剂3份、玻璃丝纤维100份、氧化镁3份、石英砂1000份、苯乙烯1400份、钛白粉20份、不饱和树脂400份。
本发明的标志本体一般为三棱柱形或长方体形(碑形)。
本发明的制作工艺是:按原料配比将原料放入搅拌机中进行预混,再将混合均匀的原料放入金属模具内,在200±30℃温度下,采用350吨压力机模压成型。
本发明的优点是:本发明的交通线路标志采用纳米高分子复合材料模压成型,其配料的化学稳定性高,能够抵御太阳紫外线照射、风吹、雨淋等自然侵蚀,使用寿命长;表面光滑,可与大理石媲美,由模具控制其尺寸,所以尺寸精确度高;产品密度高,油污无法侵入,颜色自然稳定,终身不用刷漆维护;生产效率高,适合批量生产;颜色采用国家规定的标准颜色着色,警示和提示性能明显,并可美化铁路、公路沿线环境;产品无二次回收利用价值,不易丢失,安装十分简便,是传统水泥制品的理想的换代产品。
附图说明
图1为本发明的长方体形交通线路标志的主视图;
图2为图1的俯视图;
图3为图1的仰视图;
图4为本发明的三棱柱交通线路标志的主视图;
图5为图4的俯视图。
具体实施方式
参照附图,制作一个符合国家标准的长方体形或三棱柱形纳米高分子复合材料交通线路标志,其制作原料为:纳米二氧化硅0.5公斤、聚苯乙烯3公斤、硬脂酸锌0.12公斤、固化剂15克、玻璃丝纤维0.5公斤、氧化镁15克、石英砂5公斤、苯乙烯7公斤、钛白粉100克、不饱和树脂2公斤。将原料放入搅拌机中进行预混,再将混合均匀的原料放入金属模具内,在200±30℃温度下,采用350吨压力机模压成型。
使用时,在标志本体1的体身上粘贴相应的数字标识反光膜2,然后将其沿铁路或公路沿线按设计要求进行埋设竖立即可。该反光膜采用进口的高档反光膜,使用寿命可达10年以上。
Claims (2)
1.一种纳米高分子复合材料交通线路标志,包括标志本体,其特征是:标志本体的材质成分组成按重量份是:纳米二氧化硅100份、聚苯乙烯600份、硬脂酸锌24份、固化剂3份、玻璃丝纤维100份、氧化镁3份、石英砂1000份、苯乙烯1400份、钛白粉20份、不饱和树脂400份。
2.根据权利要求1所述的纳米高分子复合材料交通线路标志,其特征是:标志本体为三棱柱形或长方体形。