CN102673079A - 一种用于tmd(模内装饰技术)的聚脂膜 - Google Patents
一种用于tmd(模内装饰技术)的聚脂膜 Download PDFInfo
- Publication number
- CN102673079A CN102673079A CN2012101218993A CN201210121899A CN102673079A CN 102673079 A CN102673079 A CN 102673079A CN 2012101218993 A CN2012101218993 A CN 2012101218993A CN 201210121899 A CN201210121899 A CN 201210121899A CN 102673079 A CN102673079 A CN 102673079A
- Authority
- CN
- China
- Prior art keywords
- polyester film
- tmd
- layer
- diaphragm
- scraping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用于TMD(模内装饰技术)的聚脂膜，包括顺次层叠的前保护膜、抗刮层、聚脂膜、吸附层以及后保护膜，所述抗刮层通过在所述聚脂膜的其中一个表面用30线-300线表面处理轮涂上硬化溶剂，再使用UV灯烤将干燥制得，所述吸附层为在附着有所述抗刮层的聚脂膜的另一个表面用30线-300线表面处理轮涂上油墨附着剂，通过烘干箱烘干制得，所述聚脂膜是厚度为0.125mm-0.3mm的PET膜。本发明公开的用于一种用于TMD(模内装饰技术)的聚脂膜，其制造工艺简单，制造成本低，抗刮性能好、印刷效果佳、吸塑成型效果好，且不会爆裂、分层。
Description
技术领域
本发明涉及TMD(模内装饰技术)的薄膜，尤其涉及一种用于TMD(模内装饰技术)的聚脂膜。
背景技术
随着电子行业快速发展，手机、平板电脑、游戏机等电子产品成为人们的生活必备品，对于这些电子产品的外壳保护也就变得日常化，外壳保护膜市场应运逐渐走向了繁荣，但是当前市场上的外壳保护膜产品表面层的抗刮能力及印刷层附着力显得不足，尤其经过200-300℃高温吸塑成型后，抗刮层及印刷层遭到破坏，常出现爆裂或分层等现象。
有鉴于此，提供一种抗刮性能好、印刷效果佳、吸塑成型效果好，且不会爆裂、分层的TMD(模内装饰技术)的薄膜成为必要。
发明内容
本发明的目的是提供一种用于TMD(模内装饰技术)的聚脂膜，其抗刮性能好、印刷效果佳、吸塑成型效果好，且不会爆裂、分层。
为了实现上述目的，本发明提供一种用于TMD(模内装饰技术)的聚脂膜，包括顺次层叠的前保护膜、抗刮层、聚脂膜、吸附层以及后保护膜，所述抗刮层通过在所述聚脂膜的其中一个表面用30线-300线表面处理轮涂上硬化溶剂，再使用UV灯烤将干燥制得，所述吸附层为在附着有所述抗刮层的聚脂膜的另一个表面用30线-300线表面处理轮涂上油墨附着剂，通过烘干箱烘干制得，所述聚脂膜是厚度为0.125mm-0.3mm的PET膜。
进一步地，所述前保护膜为聚脂膜单页。
进一步地，所述前保护膜为聚丙稀单页。
进一步地，所述前保护膜为聚乙稀薄膜单页。
进一步地，所述前保护膜为聚脂膜单页。
进一步地，所述后保护膜为聚丙稀单页。
进一步地，所述后保护膜为聚乙稀单页。
进一步地，所述抗刮层为雾面。
进一步地，所述抗刮层为透明面。
与现在技术相比，本发明提供的一种用于TMD(模内装饰技术)的聚脂膜，其制造工艺简单，制造成本低，抗刮性能好、印刷效果佳、吸塑成型效果好，且不会爆裂、分层，具有重要意义。
附图说明
附图用于对本发明的进一步理解，并且构成说明书的一部分，与本发明的实施例一起用于解释本发明，并不构成对本发明的限制。在附图中：
图1为本发明提供的一种用于TMD(模内装饰技术)的聚脂膜的结构示意图。
具体实施方式
下面结合附图详细说明本发明，其作为本说明书的一部分，通过实施例来说明本发明的原理，本发明的其他方面，特征及其优点通过该详细说明将会变得一目了然。
如图1所示，本发明提供一种用于TMD(模内装饰技术)的聚脂膜包括顺次层叠的前保护膜1、抗刮层2、聚脂膜3、吸附层4以及后保护膜5，所述抗刮层2通过在所述聚脂膜3的其中一个表面用30线-300线表面处理轮涂上硬化溶剂，再使用UV灯烤至干燥制得，所述吸附层4为在附着有所述抗刮层2的聚脂膜3的另一个表面用30线-300线表面处理轮涂上油墨附着剂，通过烘干箱烘干制得，所述聚脂膜3是厚度为0.125mm-0.3mm的PET膜。
作为一种优先方案，所述前保护膜1为聚脂膜单页。
作为一种优先方案，所述前保护膜1为聚丙稀单页。
作为一种优先方案，所述前保护膜1为聚乙稀薄膜单页。
作为一种优先方案，所述后保护膜为聚丙稀单页。
作为一种优先方案，所述后保护膜为聚乙稀单页。
作为一种优先方案，所述抗刮层2为雾面。
作为一种优先方案，所述抗刮层2为透明面。
本发明提供的一种聚脂类屏幕保护膜，其包括前保护膜1、抗刮层2、聚脂膜3、吸附层4和后保护膜5，其前保护膜1为聚脂膜单页、聚丙稀单页、乙稀薄膜单页；后保护膜为聚丙稀单页、聚丙稀单页、或聚脂膜单页之一；通过前保护膜1及后保护膜5，使其在运输过程及粘贴过程中，使保护主体不易脏污。
聚脂膜3(PET)具有良好的柔韧、吸附性，而在其表面印刷附着性较差，且其抗刮性能弱，本发明通过对其性能进行优化，通过在其其中一个表面以30线-300线表面处理轮涂上硬化溶剂(聚脂丙稀酸树脂、聚胺脂丙稀酸树脂、压克力丙稀酸树脂以上任意一种溶液)，经UV灯将其烤干，使其附着于聚脂膜3上，使得聚脂膜3得到硬化和增强抗刮性能；在其另一面以30线-300线表面处理轮涂上硬化溶剂涂上油墨附着剂(聚脂酸树脂)，并放入烘干箱中烘干，使得油墨附着剂良好地附着于聚脂膜3的表面，并使得聚脂膜3的另一个表面具有了良好的油墨印刷附着效果。
本发明提供的用于屏幕保护膜一种用于TMD(模内装饰技术)的聚脂膜，其制造工艺简单，制造成本低，抗刮性能好、印刷效果佳、吸塑成型效果好，且不会爆裂、分层。
以上所揭示的仅为本发明的较佳实施例而已，当然不能以此来限定本发明之权利范围，因此依本发明申请专利范围所作的等同变化，仍属于本发明所涵盖的范围。
Claims (9)
1.一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：包括顺次层叠的前保护膜、抗刮层、聚脂膜、吸附层以及后保护膜，
所述抗刮层通过在所述聚脂膜的其中一个表面用30线-300线表面处理轮涂上硬化溶剂，再使用UV灯烤将干燥制得，
所述吸附层为在附着有所述抗刮层的聚脂膜的另一个表面用30线-300线表面处理轮涂上油墨附着剂，通过烘干箱烘干制得，
所述聚脂膜是厚度为0.125mm-0.3mm的PET膜。
2.根据权利要求1所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述前保护膜为聚脂膜单页。
3.根据权利要求1所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述前保护膜为聚丙稀单页。
4.根据权利要求1所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述前保护膜为聚乙稀薄膜单页。
5.根据权利要求1-4中任意权利要求所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述前保护膜为聚脂膜单页。
6.根据权利要求1-4中任意权利要求所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述后保护膜为聚丙稀单页。
7.根据权利要求1-4中任意权利要求所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述后保护膜为聚乙稀单页。
8.根据权利要求1所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述抗刮层为雾面。
9.根据权利要求1所述的一种用于TMD(模内装饰技术)的聚脂膜，其特征在于：所述抗刮层为透明面。