CN102604278A - Formula of protective modified polyvinylidene fluoride - Google Patents
Formula of protective modified polyvinylidene fluoride Download PDFInfo
- Publication number
- CN102604278A CN102604278A CN201210064150XA CN201210064150A CN102604278A CN 102604278 A CN102604278 A CN 102604278A CN 201210064150X A CN201210064150X A CN 201210064150XA CN 201210064150 A CN201210064150 A CN 201210064150A CN 102604278 A CN102604278 A CN 102604278A
- Authority
- CN
- China
- Prior art keywords
- accounts
- modified polyvinilidene
- prescription
- polyvinilidene difluoroethylene
- difluoroethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a formula of protective modified polyvinylidene fluoride, which comprises modified polyvinylidene fluoride, stabilizer, anti-static agent, promoter and antiager, wherein the stabilizer is dibasic lead stearate, the anti-static agent is stearic acid polyoxyethylene ester, the promoter is hexamine, and the antiager is poly carbodiimide. The protective modified polyvinylidene fluoride prepared by the formula has the advantages of compact texture, ageing resistance and electrostatic resistance.
Description
Technical field
The present invention relates to a kind of plastic formula, be specifically related to a kind of prescription that protects the modified polyvinilidene difluoroethylene.
Background technology
PVDF is a kind of fluorocarbon resin of novelty, has very high physical strength and wear resistance, and weathering resistance and thermostability have outstanding erosion resistance in addition, so the raw material that must use in chemical industry, any metal all can't substitute.PVDF again in Fluroplast-4 physical strength the highest.Along with the depth development of various industries, PVDF is extensively adopted, and has good piezoelectricity, radiation hardness, and thermostability is also fine, so extensively adopted by electron trade, X-former manufacturing.Also be used in fields such as aerospace, military field, sea water desaltination, metallurgy, electric wire, electric elements, machinofacture.
But, reach in the requirement of component of machinofacture of some special dimension, or some is insufficient.As everyone knows, steel is the necessary material of manufacturing machine, but the strong acid, alkali, salt, the polar solvent aspect that are used in chemical industry are obsolete., perplexing for a long time that the material of this respect is a kind of well not to be developed, some material can be used but processing difficulties, and can not use repeatedly, so in the deep-etching chemical industry, every year is all costly.All do not reach requirement in effectiveness, performance, work-ing life.The task of top priority must solve the exotic materials of research and development this respect, makes chemical industry obtain stablizing long-range development.
Summary of the invention
The object of the present invention is to provide the prescription of tight, anti-aging, the anlistatig protection modified polyvinilidene of a kind of quality difluoroethylene.
Technical scheme of the present invention is; A kind of prescription that protects the modified polyvinilidene difluoroethylene; Comprise modified polyvinilidene difluoroethylene, stablizer, static inhibitor, promotor and protective agent, described stablizer is a dibasic lead stearate, and static inhibitor is a Triple Pressed Stearic Acid polyoxyethylene ester; Promotor is vulkacit H, and protective agent is a polycarbodiimide.
In preferred embodiment of the present invention; Each composition weight proportion of the prescription of said protection modified polyvinilidene difluoroethylene accounts for 80%-90% for the modified polyvinilidene difluoroethylene; Dibasic lead stearate accounts for 2%-4%; Triple Pressed Stearic Acid polyoxyethylene ester accounts for 3%-5%, and vulkacit H accounts for 1%-2%, and polycarbodiimide accounts for 4%-9%.
In preferred embodiment of the present invention; Each composition weight proportion of the prescription of said protection modified polyvinilidene difluoroethylene accounts for 75%-85% for the modified polyvinilidene difluoroethylene; Dibasic lead stearate accounts for 4%-5%; Triple Pressed Stearic Acid polyoxyethylene ester accounts for 4%-7%, and vulkacit H accounts for 2%-5%, and polycarbodiimide accounts for 5%-8%.
According to the invention is a kind of prescription that protects the modified polyvinilidene difluoroethylene, makes the protection modified polyvinilidene difluoroethylene that makes have tight, anti-aging, the anlistatig effect of quality.
Embodiment
Set forth in detail in the face of preferred embodiment of the present invention down, thereby protection scope of the present invention is made more explicit defining so that advantage of the present invention and characteristic can be easier to it will be appreciated by those skilled in the art that.
According to the invention is a kind of prescription that protects the modified polyvinilidene difluoroethylene; Comprise modified polyvinilidene difluoroethylene, stablizer, static inhibitor, promotor and protective agent; Stablizer is a dibasic lead stearate; Static inhibitor is a Triple Pressed Stearic Acid polyoxyethylene ester, and promotor is vulkacit H, and protective agent is a polycarbodiimide.
Further; Each composition weight proportion of prescription of protection modified polyvinilidene difluoroethylene accounts for 80%-90% for the modified polyvinilidene difluoroethylene, and dibasic lead stearate accounts for 2%-4%, and Triple Pressed Stearic Acid polyoxyethylene ester accounts for 3%-5%; Vulkacit H accounts for 1%-2%, and polycarbodiimide accounts for 4%-9%.
Further; Each composition weight proportion of prescription of protection modified polyvinilidene difluoroethylene accounts for 75%-85% for the modified polyvinilidene difluoroethylene, and dibasic lead stearate accounts for 4%-5%, and Triple Pressed Stearic Acid polyoxyethylene ester accounts for 4%-7%; Vulkacit H accounts for 2%-5%, and polycarbodiimide accounts for 5%-8%.
Can debug according to different ratios according to different demands, thereby reach different results of use.
According to the invention is a kind of prescription that protects the modified polyvinilidene difluoroethylene, makes the protection modified polyvinilidene difluoroethylene that makes have tight, anti-aging, the anlistatig effect of quality.
The above is merely embodiment of the present invention; But protection scope of the present invention is not limited thereto; Any those of ordinary skill in the art are in the technical scope that the present invention disclosed; Variation or the replacement that can expect without creative work all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain that claims were limited.
Claims (3)
1. prescription that protects the modified polyvinilidene difluoroethylene; It is characterized in that: comprise modified polyvinilidene difluoroethylene, stablizer, static inhibitor, promotor and protective agent; Described stablizer is a dibasic lead stearate; Static inhibitor is a Triple Pressed Stearic Acid polyoxyethylene ester, and promotor is vulkacit H, and protective agent is a polycarbodiimide.
2. the prescription of protection modified polyvinilidene difluoroethylene according to claim 1; It is characterized in that: each composition weight proportion of the prescription of said protection modified polyvinilidene difluoroethylene accounts for 80%-90% for the modified polyvinilidene difluoroethylene; Dibasic lead stearate accounts for 2%-4%; Triple Pressed Stearic Acid polyoxyethylene ester accounts for 3%-5%, and vulkacit H accounts for 1%-2%, and polycarbodiimide accounts for 4%-9%.
3. the prescription of protection modified polyvinilidene difluoroethylene according to claim 1; It is characterized in that: each composition weight proportion of the prescription of said protection modified polyvinilidene difluoroethylene accounts for 75%-85% for the modified polyvinilidene difluoroethylene; Dibasic lead stearate accounts for 4%-5%; Triple Pressed Stearic Acid polyoxyethylene ester accounts for 4%-7%, and vulkacit H accounts for 2%-5%, and polycarbodiimide accounts for 5%-8%.