CN105401096A - High-hardness heat-resisting metal material - Google Patents
High-hardness heat-resisting metal material Download PDFInfo
- Publication number
- CN105401096A CN105401096A CN201510773238.2A CN201510773238A CN105401096A CN 105401096 A CN105401096 A CN 105401096A CN 201510773238 A CN201510773238 A CN 201510773238A CN 105401096 A CN105401096 A CN 105401096A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal material
- resisting metal
- improved
- hardness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-hardness heat-resisting metal material. The high-hardness heat-resisting metal material comprises, by weight, 10-15 parts of aluminum, 40-50 parts of iron, 30-35 parts of copper, 3-5 parts of nickel, 1-3 parts of zinc, 8-12 parts of platinum, 0.5-1.3 parts of silver, 0.02-0.05 part of chrome, 0.12-0.35 part of molybdenum, and 4-6 parts of tin. The high-hardness heat-resisting metal material has the beneficial effects that the abrasion resistance of the metal material can be improved through the added tin, platinum and nickel; meanwhile, the hardness of the metal material can be improved through the added iron, copper and molybdenum; the stability of the metal material is improved by adding other metal elements, the product quality is greatly improved, and requirements of enterprises are met.
Description
Technical field
The present invention relates to a kind of metallic substance, particularly relate to a kind of high rigidity heating resisting metal material.
Background technology
At present at corrosion and wear working condition, in the hygrometric state corrosive wear operating mode of the particularly industry such as electric power, chemical industry, material great majority used are duplex stainless steel, but resistance to wear because hardness is low have to be high for duplex stainless steel, simultaneously, the cost of dual phase steel is higher, can not meet the demand of industry.
Therefore, for solving the problem, spy provides a kind of new technical scheme.
Summary of the invention
The invention provides a kind of high rigidity heating resisting metal material.
The technical solution used in the present invention is:
A kind of high rigidity heating resisting metal material, comprises the component of following weight part:
Aluminium 10-15 part;
Iron 40-50 part;
Copper 30-35 part;
Nickel 3-5 part;
Zinc 1-3 part;
Platinum 8-12 part;
Silver 0.5-1.3 part;
Chromium 0.02-0.05 part;
Molybdenum 0.12-0.35 part;
Tin 4-6 part.
Further, the niobium of 0.042-0.056 weight part can also be added.
Further, the germanium of 0.1-0.35 weight part can also be added.
The invention has the beneficial effects as follows: the tin of interpolation, platinum and nickel, the wear resistance of metallic substance can be improved, the interpolation of iron, copper and molybdenum simultaneously, the hardness of metallic substance can be improved, the interpolation of other metallic element, improve the stability of metallic substance, substantially increase the quality of product, meet the demand of enterprise.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment, only for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A kind of high rigidity heating resisting metal material, comprises the component of following weight part:
10 parts, aluminium;
Iron 40 parts;
Copper 30 parts;
3 parts, nickel;
1 part, zinc;
8 parts, platinum;
Silver 0.5 part;
Chromium 0.02 part;
Molybdenum 0.12 part;
4 parts, tin;
Niobium 0.042 part;
0.1 part, germanium.
Embodiment 2
A kind of high rigidity heating resisting metal material, comprises the component of following weight part:
12 parts, aluminium;
Iron 45 parts;
Copper 32 parts;
4 parts, nickel;
2 parts, zinc;
10 parts, platinum;
Silver 1 part;
Chromium 0.035 part;
Molybdenum 0.25 part;
5 parts, tin;
Niobium 0.05 part;
0.25 part, germanium.
Embodiment 3
A kind of high rigidity heating resisting metal material, comprises the component of following weight part:
15 parts, aluminium;
Iron 50 parts;
Copper 35 parts;
5 parts, nickel;
3 parts, zinc;
12 parts, platinum;
Silver 1.3 parts;
Chromium 0.05 part;
Molybdenum 0.35 part;
6 parts, tin;
Niobium 0.056 part;
0.35 part, germanium.
The invention has the beneficial effects as follows: the tin of interpolation, platinum and nickel, the wear resistance of metallic substance can be improved, the interpolation of iron, copper and molybdenum simultaneously, the hardness of metallic substance can be improved, the interpolation of other metallic element, improve the stability of metallic substance, substantially increase the quality of product, meet the demand of enterprise.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (3)
1. a high rigidity heating resisting metal material, is characterized in that: the component comprising following weight part:
Aluminium 10-15 part;
Iron 40-50 part;
Copper 30-35 part;
Nickel 3-5 part;
Zinc 1-3 part;
Platinum 8-12 part;
Silver 0.5-1.3 part;
Chromium 0.02-0.05 part;
Molybdenum 0.12-0.35 part;
Tin 4-6 part.
2. a kind of high rigidity heating resisting metal material according to claim 1, is characterized in that: the niobium that can also add 0.042-0.056 weight part.
3. a kind of high rigidity heating resisting metal material according to claim 1, is characterized in that: the germanium that can also add 0.1-0.35 weight part.