CN105401045A - Abrasion-resistant anti-corrosion material - Google Patents
Abrasion-resistant anti-corrosion material Download PDFInfo
- Publication number
- CN105401045A CN105401045A CN201510760172.3A CN201510760172A CN105401045A CN 105401045 A CN105401045 A CN 105401045A CN 201510760172 A CN201510760172 A CN 201510760172A CN 105401045 A CN105401045 A CN 105401045A
- Authority
- CN
- China
- Prior art keywords
- parts
- carbon
- weight
- abrasion
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an abrasion-resistant anti-corrosion material. Carbon, iron and copper serve as the main components of the material. The abrasion-resistant anti-corrosion material further comprises, by weight, 2-8 parts of aluminum, 5-9 parts of magnesium, 1-3 parts of zinc, 0.5 -1 part of chrome, 0.05-0.08 part of cobalt, 3-6 parts of silver, 0.01-0.04 part of iridium, 0.01-0.05 part of lithium, 1.5-3.8 parts of oxygen, 0.02-0.05 part of sodium, 8-12 parts of the carbon, 40-45 parts of the iron and 30-35 parts of the copper. The abrasion-resistant anti-corrosion material has the beneficial effects that the abrasion resistance of the material can be effectively improved by combining the carbon and the other metallic elements; meanwhile, the other metallic elements are added so that the anti-corrosion effect of the material can be greatly improved, and the stability of the material is greatly improved; moreover, the production cost is low, and thus the material is suitable for the development of enterprises.
Description
Technical field
The present invention relates to a kind of Wear-resistant corrosion-resistant material, particularly relate to a kind of material.
Background technology
At present at corrosion and wear working condition, materials most particularly used in the industry such as electric power, chemical industry is duplex stainless steel, but duplex stainless steel due to the low wear resistance of hardness not high, the cost of dual phase steel is higher simultaneously, be not suitable for producing in enormous quantities, considerably increase cost, Simultaneous Stabilization is lower, is not suitable for the development of enterprise.
Therefore, for solving the problem, spy provides a kind of new technical scheme.
Summary of the invention
The invention provides a kind of Wear-resistant corrosion-resistant material.
The technical solution used in the present invention is:
A kind of Wear-resistant corrosion-resistant material, with carbon, iron and copper for main component, also comprises following component, is by weight: aluminium 2-8 part; Magnesium 5-9 part; Zinc 1-3 part; Chromium 0.5-1 part; Cobalt 0.05-0.08 part; Silver 3-6 part; Iridium 0.01-0.04 part; Lithium 0.01-0.05 part; Oxygen 1.5-3.8 part; Sodium 0.02-0.05 part; Described carbon is 8-12 weight part, and described iron is 40-45 weight part, and described copper is 30-35 weight part.
Further, the tungsten of 0.12-0.15 weight part is also comprised.
Further, the yttrium of 0.005-0.008 weight part is also comprised.
The invention has the beneficial effects as follows: adopt the mode that carbon combines with other metallic element, effectively can improve the wear resistance of this material, the interpolation of other metallic element simultaneously, greatly can improve the anticorrosion effect of this kind of material, substantially increase the stability of material, production cost is low simultaneously, the development of suitable enterprise.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, and this embodiment, only for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A kind of Wear-resistant corrosion-resistant material, with carbon, iron and copper for main component, also comprises following component, is by weight: 2 parts, aluminium; 5 parts, magnesium; 1 part, zinc; Chromium 0.5 part; Cobalt 0.05 part; Silver 3 parts; 0.01 part, iridium; Lithium 0.01 part; Oxygen 1.5 parts; 0.02 part, sodium; 0.12 part, tungsten; Yttrium 0.005 part; Carbon is 8 weight parts, and iron is 40 weight parts, and copper is 30 weight parts.
Embodiment 2
A kind of Wear-resistant corrosion-resistant material, with carbon, iron and copper for main component, also comprises following component, is by weight: 5 parts, aluminium; 6 parts, magnesium; 2 parts, zinc; Chromium 0.7 part; Cobalt 0.065 part; Silver 4 parts; 0.03 part, iridium; Lithium 0.03 part; Oxygen 2.5 parts; 0.035 part, sodium; 0.13 part, tungsten; Yttrium 0.0065 part; Carbon is 10 weight parts, and iron is 42 weight parts, and copper is 32 weight parts.
Embodiment 3
A kind of Wear-resistant corrosion-resistant material, with carbon, iron and copper for main component, also comprises following component, is by weight: 8 parts, aluminium; 9 parts, magnesium; 3 parts, zinc; Chromium 1 part; Cobalt 0.08 part; Silver 6 parts; 0.04 part, iridium; Lithium 0.05 part; Oxygen 3.8 parts; 0.05 part, sodium; 0.15 part, tungsten; Yttrium 0.008 part; Carbon is 12 weight parts, and iron is 45 weight parts, and copper is 35 weight parts.
The invention has the beneficial effects as follows: adopt the mode that carbon combines with other metallic element, effectively can improve the wear resistance of this material, the interpolation of other metallic element simultaneously, greatly can improve the anticorrosion effect of this kind of material, substantially increase the stability of material, production cost is low simultaneously, the development of suitable enterprise.
The above is only preferred embodiment of the present invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (3)
1. a Wear-resistant corrosion-resistant material, is characterized in that: with carbon, iron and copper for main component, also comprises following component, is by weight: aluminium 2-8 part; Magnesium 5-9 part; Zinc 1-3 part; Chromium 0.5-1 part; Cobalt 0.05-0.08 part; Silver 3-6 part; Iridium 0.01-0.04 part; Lithium 0.01-0.05 part; Oxygen 1.5-3.8 part; Sodium 0.02-0.05 part; Described carbon is 8-12 weight part, and described iron is 40-45 weight part, and described copper is 30-35 weight part.
2. a kind of Wear-resistant corrosion-resistant material according to claim 1, is characterized in that: the tungsten also comprising 0.12-0.15 weight part.
3. a kind of Wear-resistant corrosion-resistant material according to claim 1, is characterized in that: the yttrium also comprising 0.005-0.008 weight part.