CN102585687A - 一种聚羟基脂肪酸酯耐高温防腐涂料 - Google Patents

一种聚羟基脂肪酸酯耐高温防腐涂料 Download PDF

Info

Publication number
CN102585687A
CN102585687A CN2012100039657A CN201210003965A CN102585687A CN 102585687 A CN102585687 A CN 102585687A CN 2012100039657 A CN2012100039657 A CN 2012100039657A CN 201210003965 A CN201210003965 A CN 201210003965A CN 102585687 A CN102585687 A CN 102585687A
Authority
CN
China
Prior art keywords
polyhydroxyalkanoate
parts
fire
temperature
anticorrosion paint
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100039657A
Other languages
English (en)
Other versions
CN102585687B (zh
Inventor
钱祖其
钱晨娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yibo Construction Group Co., Ltd.
Original Assignee
JIANGSU GESANGHUA PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU GESANGHUA PAINT CO Ltd filed Critical JIANGSU GESANGHUA PAINT CO Ltd
Priority to CN201210003965.7A priority Critical patent/CN102585687B/zh
Publication of CN102585687A publication Critical patent/CN102585687A/zh
Application granted granted Critical
Publication of CN102585687B publication Critical patent/CN102585687B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种聚羟基脂肪酸酯耐高温防腐涂料及其制备方法。按重量份计，包含聚羟基脂肪酸酯50～70份、锌粉15～25份、漂浮型铝粉2～10份、活性稀释剂10～20份和助剂0.05～5份。本发明的耐高温防腐涂料采用的聚羟基脂肪酸酯为高分子材料，无毒无害，其制备过程中不产生污染，环境友好。用聚羟基脂肪酸酯部分代替有机硅树脂作为主要成膜层，减少有害物质的应用。使用时不会放出刺激性气味，不影响人体健康。且所生产的耐高温防腐涂料可耐强紫外线辐射，耐高温和防腐性能优越。

Description

一种聚羟基脂肪酸酯耐高温防腐涂料
技术领域
本发明涉及一种聚羟基脂肪酸酯耐高温防腐涂料。
背景技术
耐高温防腐涂料适用于烟囱烟道、高温蒸汽管道、热交换器、高温炉、高温脱硫设备、石油石化裂解装备、发动机部件及排气管防腐。另外一些特殊的耐高温防腐涂料在航天航空、石油石化、冶金、电力、国防领域得到广泛应用，随着航空、航天工业的发展，耐高温防腐涂料的用途也会逐步得到推广应用。
耐高温涂料一般是指能经受200℃以上温度，涂膜颜色、光泽变化小且涂膜完整，无破裂现象，仍能保持适当的物理机械性能并起防护作用的涂料。耐高温涂料种类繁多，一般包括无机型涂料和有机树脂涂料。传统无机型耐高温涂料的耐热温度可达400～1000℃，甚至更高。无机型耐高温涂料虽然耐燃性好、硬度高，但漆膜较脆，在完全固化之前耐水性不好，对底材处理的要求也严格。目前一般采用有机硅树脂中添加无机填料的方法配制综合性能优良的有机涂料作为耐高温防腐涂料。该涂料的组成一般为主要为：有机硅树脂、填料(云母粉、滑石粉、玻璃粉)、颜料(铝粉、锌粉、炭黑)、助剂和溶剂以及催化剂。
目前国内外使用的有机硅树脂主要为溶剂型，通常情况下使用如二甲苯、芳烃和醇类等作为溶剂，有机硅树脂最大的缺点是生产中废水废气较多，污染环境、易燃、同时对人体有害。
聚羟基脂肪酸酯(PHA，polyhydroxyalkanoates)，是近20多年迅速发展起来的高分子材料，具有良好的塑料热加工性能，同时还具有非线性光学性、压电性、气体相隔性很多高附加值性能。研究证明，PHA具有良好的气体阻隔性，PHA还具有较好的水解稳定性，PHA还具有很好的紫外稳定性。
发明内容
本发明的目的在于提供一种聚羟基脂肪酸酯耐高温防腐涂料。
本发明的目的可以通过以下技术方案实现：
一种聚羟基脂肪酸酯耐高温防腐涂料，按重量份计，包含聚羟基脂肪酸酯50～70份、锌粉15～25份、漂浮型铝粉2～10份、活性稀释剂10～20份和助剂0.05～5份。优选为：包含聚羟基脂肪酸酯60份、锌粉20份、漂浮型铝粉5份、活性稀释剂15份和助剂0.1～3份。
上述的聚羟基脂肪酸酯耐高温防腐涂料，其在于所述的活性稀释剂为正丁基缩水甘油醚。
上述的聚羟基脂肪酸酯耐高温防腐涂料，其在于所述的聚羟基脂肪酸酯的制备方法为：向反应容器中投入多亚甲基多苯基多异氰酸酯65～75重量份，开机搅拌，升温至30～40度，滴加聚醚多元醇25～35重量份，滴加0.5～1.5小时，滴加完毕后，保温4～5个小时，冷却得聚羟基脂肪酸酯。
上述的聚羟基脂肪酸酯耐高温防腐涂料，其在于所述的助剂为消泡剂、分散剂、定向排列剂、流平剂、紫外线吸附剂中的任意一种或几种。
上述的聚羟基脂肪酸酯耐高温防腐涂料，其在于将聚羟基脂肪酸酯、锌粉、漂浮型铝粉、活性稀释剂和助剂投入高速分散机中高速分散后过滤得到。
本发明的有益效果：
本发明的耐高温防腐涂料采用的聚羟基脂肪酸酯为高分子材料，无毒无害，其制备过程中不产生污染，环境友好。用聚羟基脂肪酸酯部分代替有机硅树脂作为主要成膜层，减少有害物质的应用。使用时不会放出刺激性气味，不影响人体健康。且所生产的耐高温防腐涂料可耐强紫外线辐射，耐高温和防腐性能优越。
具体实施方式
下面结合具体实施例对本发明进行进一步详细说明：
实施例1聚羟基脂肪酸酯耐高温防腐涂料的制备
(1)制备聚羟基脂肪酸酯：向反应容器中投入多亚甲基多苯基多异氰酸酯(韩国锦湖三井，M-200)70重量份，开机搅拌，升温至35度，滴加聚醚多元醇(聚醚330N，上海比尤化工有限公司)30重量份，滴加1小时，滴加完毕后，保温5个小时，冷却得聚羟基脂肪酸酯。
(2)按重量份计，称取聚羟基脂肪酸酯60份、锌粉20份、漂浮型铝粉5份、正丁基缩水甘油醚(上海友盛化工科技有限公司)15份、聚羧酸钠盐分散剂(上虞市海利化工有限公司，型号：SN-5040)1.5份和紫外线吸附剂(UV-O，斯威特化工(深圳)有限公司)0.5份，将上述物料投入高速分散机中高速分散后过滤、包装。
实施例2聚羟基脂肪酸酯耐高温防腐涂料的制备
(1)制备聚羟基脂肪酸酯：向反应容器中投入多亚甲基多苯基多异氰酸酯(韩国锦湖三井，M-200)65重量份，开机搅拌，升温至35度，滴加聚醚多元醇(聚醚330N，上海比尤化工有限公司)35重量份，滴加1小时，滴加完毕后，保温5个小时，冷却得聚羟基脂肪酸酯。
(2)按重量份计，称取聚羟基脂肪酸酯70份、锌粉25份、漂浮型铝粉10份、正丁基缩水甘油醚20份、聚羧酸钠盐分散剂(上虞市海利化工有限公司，型号：SN-5040)2份和紫外线吸附剂(UV-O，斯威特化工(深圳)有限公司)0.5份，将上述物料投入高速分散机中高速分散后过滤、包装。
实施例3聚羟基脂肪酸酯耐高温防腐涂料的制备
(1)制备聚羟基脂肪酸酯：向反应容器中投入多亚甲基多苯基多异氰酸酯(韩国锦湖三井，M-200)75重量份，开机搅拌，升温至35度，滴加聚醚多元醇(聚醚330N，上海比尤化工有限公司)25重量份，滴加1小时，滴加完毕后，保温5个小时，冷却得聚羟基脂肪酸酯。
(2)按重量份计，称取聚羟基脂肪酸酯50份、锌粉15份、漂浮型铝粉3份、正丁基缩水甘油醚10份、消泡剂(江苏赛欧信越消泡剂有限公司，XPJ902消泡剂)1份、聚羧酸钠盐分散剂(上虞市海利化工有限公司，型号：SN-5040)2份和紫外线吸附剂(UV-O，斯威特化工(深圳)有限公司)0.5份，将上述物料投入高速分散机中高速分散后过滤、包装。
实施例4聚羟基脂肪酸酯耐高温防腐涂料的制备
(1)制备聚羟基脂肪酸酯：向反应容器中投入多亚甲基多苯基多异氰酸酯(韩国锦湖三井，M-200)68重量份，开机搅拌，升温至35度，滴加聚醚多元醇(聚醚330N，上海比尤化工有限公司)32重量份，滴加1小时，滴加完毕后，保温5个小时，冷却得聚羟基脂肪酸酯。
(2)按重量份计，称取聚羟基脂肪酸酯62份、锌粉22份、漂浮型铝粉6份、正丁基缩水甘油醚18份、钡锌热稳定剂(南通艾德旺化工有限公司)0.8份，将上述物料投入高速分散机中高速分散后过滤、包装。
实施例1～4所制备的产品的质量检测结果
Figure BDA0000129355030000041

Claims (6)

1.一种聚羟基脂肪酸酯耐高温防腐涂料，其特征在于按重量份计，包含聚羟基脂肪酸酯50～70份、锌粉15～25份、漂浮型铝粉2～10份、活性稀释剂10～20份和助剂0.05～5份。
2.根据权利要求1所述的聚羟基脂肪酸酯耐高温防腐涂料，其特征在于包含聚羟基脂肪酸酯60份、锌粉20份、漂浮型铝粉5份、活性稀释剂15份和助剂0.1～3份。
3.根据权利要求1所述的聚羟基脂肪酸酯耐高温防腐涂料，其特征在于所述的活性稀释剂为正丁基缩水甘油醚。
4.根据权利要求1所述的聚羟基脂肪酸酯耐高温防腐涂料，其特征在于所述的聚羟基脂肪酸酯的制备方法为：向反应容器中投入多亚甲基多苯基多异氰酸酯65～75重量份，开机搅拌，升温至30～40度，滴加聚醚多元醇25～35重量份，滴加0.5～1.5小时，滴加完毕后，保温4～5个小时，冷却得聚羟基脂肪酸酯。
5.根据权利要求1所述的聚羟基脂肪酸酯耐高温防腐涂料，其特征在于所述的助剂为消泡剂、分散剂、定向排列剂、流平剂、热稳定剂、紫外线吸附剂中的任意一种或几种。
6.根据权利要求1所述的聚羟基脂肪酸酯耐高温防腐涂料，其特征在于将聚羟基脂肪酸酯、锌粉、漂浮型铝粉、活性稀释剂和助剂投入高速分散机中高速分散后过滤得到。
CN201210003965.7A 2012-01-09 2012-01-09 一种聚羟基脂肪酸酯耐高温防腐涂料 Active CN102585687B (zh)