CN102585677A - 一种风电机组叶片用涂料 - Google Patents

一种风电机组叶片用涂料 Download PDF

Info

Publication number
CN102585677A
CN102585677A CN2011103552397A CN201110355239A CN102585677A CN 102585677 A CN102585677 A CN 102585677A CN 2011103552397 A CN2011103552397 A CN 2011103552397A CN 201110355239 A CN201110355239 A CN 201110355239A CN 102585677 A CN102585677 A CN 102585677A
Authority
CN
China
Prior art keywords
agent
coating
generation unit
solvent
polyester ether
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011103552397A
Other languages
English (en)
Inventor
陈廷生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU MARING VICTORY COATING Co Ltd
Original Assignee
JIANGSU MARING VICTORY COATING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU MARING VICTORY COATING Co Ltd filed Critical JIANGSU MARING VICTORY COATING Co Ltd
Priority to CN2011103552397A priority Critical patent/CN102585677A/zh
Publication of CN102585677A publication Critical patent/CN102585677A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种风电机组叶片用涂料，由聚氨酯NEUKAPOL 1007、聚酯醚NEUKADUR 1036、固化剂、助剂、溶剂及钛白粉R930组成：本发明选用双组份的聚氨酯NEUKAPOL 1007、聚酯醚NEUKADUR 1036，由于选用的聚氨酯和聚酯醚为高羟值(羟值分别为550-590和160-170)低黏度的树脂，该树脂的分子量非常小，能形成一种高交联密度涂膜，其涂膜具有极高的表面硬度又具有优异的弹性、抗弯曲性能、柔韧性和卓越的物理力学性能，可避免应力集中，因此，该涂料形成的涂膜具有很好的拉伸强度、撕裂强度和抗石击性能，确保了风电机组的使用寿命。

Description

一种风电机组叶片用涂料
技术领域
本发明涉及一种涂料，特别涉及一种用于风电机组叶片的涂料，属于涂料的技术领域。
背景技术
随着社会的发展，风力发电越来越广泛。风电机组叶片是风电机组的核心部件之一，目前叶片主要采用玻璃钢复合材料，设计使用寿命通常为20年。由于风电机组常期工作在恶劣的环境中，对其耐腐蚀、耐磨损、耐候、耐紫外、抗结冰等性能要求较高，因此，要对其进行有效的保护。
目前国内风电机组叶片一般采用进口聚氨酯涂料、环氧树脂涂料、或进口胶衣来保护玻璃钢叶片，但由于风电场的位置，大多分布在风沙大的荒漠地区，现有的胶衣或涂料抗风沙性能不好，无法解决雨雪、风沙、冰雹和风沙对叶片表面的冲击和破坏的问题，常常造成叶片磨损，从而，影响了风电机组的使用寿命。
发明内容
本发明所要解决的技术问题是提供一种风电机组叶片用涂料，该涂料抗石击、耐磨、耐撞击、耐侯性极优、附着力极强，从而，延长了风电机组的使用寿命。
为了解决上述技术问题，本发明一种风电机组叶片用涂料，由以下成份(按体积百分比)组成：
Figure BDA0000107284990000011
溶剂由丁酯、MPA、100#溶剂油组成，
溶剂比例为：丁酯/100#溶剂油/MPA＝3/1/1(体积比)。
助剂由以下成分组成：分散剂BYK 161、防沉剂Thixatrol ST、抗流挂剂6900-HV、流平剂BYK 300、消泡剂Tego Airex 940；分散剂BYK 161、防沉剂Thixatrol ST∶抗流挂剂6900-HY∶流平剂BYK 300∶消泡剂Tego Airex940＝4∶8∶2∶3∶1.5(体积比)。
上述一种风电机组用涂料，其中，所述固化剂为脂肪族聚异氰酸酯。
本发明选用双组份的聚氨酯NEUKAPOL 1007、聚酯醚NEUKADUR 1036，由于选用的聚氨酯和聚酯醚为高羟值(羟值分别为550-590和160-170)低黏度的树脂，该树脂的分子量非常小，能形成一种高交联密度涂膜，其涂膜具有极高的表面硬度又具有优异的弹性、抗弯曲性能、柔韧性和卓越的物理力学性能，可避免应力集中，因此，该涂料形成的涂膜具有很好的拉伸强度、撕裂强度和抗石击性能，确保了风电机组的使用寿命；另外，由于涂料具有弹性，在使用时，可吸收一定的砂石冲击力，从而，使该涂料的抗石击性能更加出众。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
为了解决上述技术问题，本发明一种风电机组叶片用涂料，由以下成份(按体积百分比)组成：
Figure BDA0000107284990000031
溶剂由丁酯、MPA、100#溶剂油组成，
溶剂比例为：丁酯/100#溶剂油/MPA＝3/1/1(体积比)。
助剂由以下成分组成：分散剂BYK 161、防沉剂Thixatrol ST、抗流挂剂6900-HV、流平剂BYK 300、消泡剂Tego Airex 940，分散剂BYK 161、防沉剂Thixatrol ST∶抗流挂剂6900-HY∶流平剂BYK 300∶消泡剂Tego Airex 940＝4∶8∶2∶3∶1.5(体积比)。
聚氨酯NEUKAPOL 1007及聚酯醚NEUKADUR 1036都是德国啊尔特罗公司(altropol)生产的树脂，该选用的树脂具有高羟值(羟值分别为550-590和160-170)低黏度且分子量非常小的特点。固化剂选用德国拜尔(BAYER)公司生产的脂肪族聚异氰酸酯Desmodur 3390、Desmodur 3800；钛白粉R930选用日本石原公司生产的。Thixatrol ST改性氢化蓖麻油，具有良好的触变性，增稠性及防沉性。有利于颜料和填料和悬浮；控制流动性和流平性；控制液体在多孔表面上的渗透；可提供抗流挂特性；具有优异的存储稳定性；不与颜料和基料反应，很容易分散。
实施例一
一种风电机组叶片用涂料，由以下成份(按体积百分比)组成：
聚氨酯NEUKAPOL 100719.7％；聚酯醚NEUKADUR 103623％；固化剂脂肪族聚异氰酸酯35％；助剂3.3％；溶剂14％；钛白粉R93020％，溶剂由丁酯、MPA、100#溶剂油组成，丁酯∶100#溶剂油∶MPA＝3∶1∶1(体积比)；助剂由以下成分组成：分散剂BYK 161、防沉剂ThixatrolST、抗流挂剂6900-HV、流平剂BYK 300、消泡剂Tego Airex 940；分散剂BYK 161∶防沉剂Thixatrol ST∶抗流挂剂6900-HV∶流平剂BYK 300∶消泡剂TegoAirex 940＝4∶8∶2∶3∶1.5(体积比)。按照配方比例量称取聚酯和部分溶剂，加入颜料钛白粉，分散研磨至粒度≤25μm，再加入助剂和溶剂，通过搅拌分散均匀，调制成油漆，即可。
经国家涂料质量监督检验中心根据(ASTM D 3170-2003)标准本发明抗石击性能检测结果为6.5A；根据GB/T 5210-2006标准本发明涂料附着力(拉开法)为7Mpa，有力地保证涂膜不会从基材上脱落，长久地保护风电机组叶片。
实施例二
一种风电机组叶片用涂料，由以下成份(按体积百分比)组成：聚氨酯NEUKAPOL 100722％、聚酯醚NEUKADUR 103617.3％、固化剂42.5％、助剂2.5％、溶剂17％，钛白粉R930 20％，溶剂由丁酯、MPA、100#溶剂油组成，丁酯∶100#溶剂油∶MPA＝3∶1∶1(体积比)；助剂由以下成分组成：分散剂BYK 161、防沉剂Thixatrol ST、抗流挂剂6900-HV、流平剂BYK 300、消泡剂Tego Airex 940：分散剂BYK 161∶防沉剂Thixatrol ST∶抗流挂剂6900-HV∶流平剂BYK 300∶消泡剂Tego Airex 940＝4∶8∶2∶3∶1.5(体积比)。按照配方比例量称取聚酯和部分溶剂，加入颜料钛白粉，分散研磨至粒度≤25μm，再加入助剂和溶剂，通过搅拌分散均匀，调制成油漆，即可。经国家涂料质量监督检验中心根据(ASTM D 3170-2003)标准本发明抗石击性能检测结果为7A；根据GB/T 5210-2006标准本发明涂料附着力(拉开法)为9Mpa，有力地保证涂膜不会从基材上脱落，长久地保护风电机组叶片。
实施例三
一种风电机组叶片用涂料，由以下成份(按体积百分比)组成：
聚氨酯NEUKAPOL 1007 26％、聚酯醚NEUKADUR 1036 17％、固化剂46％、助剂2.7％、溶剂14％、钛白粉R930 20.3％；溶剂由丁酯、MPA、100#溶剂油组成，丁酯∶100#溶剂油∶MPA＝3∶1∶1(体积比)；助剂由以下成分组成：分散剂BYK 161、防沉剂Thixatrol ST、抗流挂剂6900-HV、流平剂BYK 300、消泡剂Tego Airex 940；分散剂BYK 161∶防沉剂ThixatrolST∶抗流挂剂6900-HV∶流平剂BYK 300∶消泡剂Tego Airex 940＝4∶8∶2∶3∶1.5(体积比)。按照配方比例量称取聚酯和部分溶剂，加入颜料钛白粉，分散研磨至粒度≤25μm，再加入助剂和溶剂，通过搅拌分散均匀，调制成油漆，即可。
经国家涂料质量监督检验中心根据(ASTM D 3170-2003)标准本发明抗石击性能检测结果为6A；根据GB/T 5210-2006标准本发明涂料附着力(拉开法)为8Mpa，有力地保证涂膜不会从基材上脱落，长久地保护风电机组叶片。
以上说明书中描述的只是本发明的具体实施方式，该举例说明不对本发明的实质内容构成限制，所属技术领域的普通技术人员在阅读了说明书后可以对前面所述的具体实施方式做修改或者变形，而不背离发明的实质和范围。

Claims (2)

1.一种风电机组叶片用涂料，其特征在于，由以下成份(按体积百分比)组成：
溶剂由丁酯、MPA、100#溶剂油组成，
丁酯∶100#溶剂油∶MPA＝3∶1∶1(体积比)；
助剂由以下成分组成：分散剂BYK 161、防沉剂ThixatrolST、抗流挂剂6900-HV、流平剂BYK 300、消泡剂Tego Airex 940；分散剂BYK 161∶防沉剂ThixatrolST∶抗流挂剂6900-HV∶流平剂BYK300∶消泡剂Tego Airex 940＝4∶8∶2∶3∶1.5(体积比)。
2.如权利要求1所述一种风电机组用涂料，其特征在于，所述固化剂为脂肪族聚异氰酸酯。
CN2011103552397A 2011-11-10 2011-11-10 一种风电机组叶片用涂料 Pending CN102585677A (zh)