CN102585641B - 一种环保型耐候性防水外墙涂料及其制备方法 - Google Patents
一种环保型耐候性防水外墙涂料及其制备方法 Download PDFInfo
- Publication number
- CN102585641B CN102585641B CN201210045164.7A CN201210045164A CN102585641B CN 102585641 B CN102585641 B CN 102585641B CN 201210045164 A CN201210045164 A CN 201210045164A CN 102585641 B CN102585641 B CN 102585641B
- Authority
- CN
- China
- Prior art keywords
- powder
- environment
- wall coating
- friendly type
- stir
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种环保型耐候性防水外墙涂料及其制备方法,该涂料按质量百分比含量由组分:GHS98A硅丙乳液为45-55%,金红石钛白粉R-930为8-12%,醇脂十二为3-6%,超细方解石粉为3-7%,超细硅灰石粉为3-7%,超细二氧化硅粉为3-7%,超细云母粉为3-7%,重质碳酸钙为2-6%,GH5050分散剂为0.4-0.8%,流平剂2为0.1-0.3%,增稠剂102为0.5-1%,防腐剂981为0.1-0.5%,消泡剂202为0.1-0.3%,水为5-12%组成。本发明的一种环保型耐候性防水外墙涂料具有极佳的高耐候性、防水性、耐化学腐蚀性、耐水性、耐擦洗性和耐人工老化等优点。是换代环保型外墙涂料。
Description
技术领域
本发明涉及一种环保型耐候性防水外墙涂料及其制备方法,属于建筑涂料技术领域。
背景技术
近年来,对外墙涂料的研究已取得了一定的成果,但仍有不少待解决的问题。如耐候性、防水性、环保性相对较差等缺点。研究表明,采用GHS98A硅丙乳液及超细填料和各种助剂来研制新型环保耐候性防水外墙涂料能克服现有技术所存在的缺陷。因为GHS98A硅丙乳液和超细填料在各种助剂的条件下可以形成高耐候性极好的耐水性涂膜,具有极佳的防水功能。所以,如何进一步提高涂膜的耐候性、防水性,耐化学腐蚀性、耐擦洗性和耐人工老化等性能,已成为本领域技术人员关注的重点和研究的主题。
发明内容
本发明的目的是针对上述现有技术所存在的问题,克服所存在的不足和缺陷,而提供一种环保型耐候性防水外墙涂料及其制备方法。
为了达到上述目的,本发明实现目的所采取的技术方案是:
一种环保型耐候性防水外墙涂料,按质量百分比含量由组分GHS98A硅丙乳液为45-55%,金红石钛白粉R-930为8-12%,醇脂十二为3-6%,超细方解石粉为3-7%,超细硅灰石粉为3-7%,超细二氧化硅粉为3-7%,超细云母粉为3-7%,重质碳酸钙为2-6%,GH5050分散剂为0.4-0.8%,流平剂2为0.1-0.3%,增稠剂102为0.5-1%,防腐剂981为0.1-0.5%,消泡剂202为0.1-0.3%,水为5-12%组成。
为了达到上述目的,本发明的另一个技术方案是:
上述的一种环保型耐候性防水外墙涂料的制备方法,包括如下步骤:
将水加入搅拌灌中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌18-21min;加入GHS98A硅丙乳液和醇脂十二搅拌15-18min;再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌23-26min;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌29-32min,制得环保弄耐候性防水外墙涂料;最后将制得的环保型耐候性防水外墙涂料进入沙磨机研磨两遍,过滤,出料装桶。
本发明的环保型耐候性防水外墙涂料,具有极佳的高耐候性、防水性、耐化学腐蚀性、耐水性、耐擦洗性和耐人工老化等优点。产品达到并优于GB/T9755-2001和GB18583-2001国家标准,是换代环保型外墙涂料。
具体实施方式
结合具体实例进一步详细说明本发明的技术方案:
实施例1
一、按质量百分比配称各组分
二、制备方法
先将水加入搅拌灌中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌20min;加入GHS98A硅丙乳液和醇脂十二搅拌15min,再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌25min;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌30min,制得环保型耐候性防水外墙涂料;将制得的环保型耐候性防水外墙涂料进入沙磨机研磨两遍,过滤,出料装桶。
三、本实施例的有益效果(见表1)
表1:丙烯酸外墙涂料与耐候性防水外墙涂料的性能对比
实施例2
一、按质量百分比配称各组分
二、制备方法
将水加入搅拌灌中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌18min;加入GHS98A硅丙乳液和醇脂十二搅拌17min;再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌23min;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌32min,即制得环保型耐候性防水外墙涂料;最后将环保型耐候性防水外墙涂料进入沙磨机研磨两遍,过滤,出料装桶。
三、本实施例的有益效果(见表2)
表2:丙烯酸外墙涂料与耐候性防水外墙涂料的性能对比
实施例3
一、按质量百分比配称各组分
二、制备方法
将水加入搅拌灌中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌19min;加入GHS98A硅丙乳液和醇脂十二搅拌16min;再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌24min;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌31min,即制得环保型耐候性防水外墙涂料;最后将环保型耐候性防水外墙涂料进入沙磨机研磨两遍,过滤,出料装桶。
三、本实施例的有益效果(见表3)
表3:丙烯酸外墙涂料与耐候性防水外墙涂料的性能对比
实施例4
一、按质量百分比配称各组分
二、制备方法
将水加入搅拌灌中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌21min;加入GHS98A硅丙乳液和醇脂十二搅拌18min;再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌26min均匀;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌29min,即制得环保型耐候性防水外墙涂料;最后将环保型耐候性防水外墙涂料进入沙磨机研磨两遍,过滤,出料装桶。
三、本实施例的有益效果(见表4)
表4:丙烯酸外墙涂料与耐候性防水外墙涂料的性能对比
实施例5
一、按质量百分比配称各组分
二、制备方法
将水加入搅拌灌中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌20min;加入GHS98A硅丙乳液和醇脂十二搅拌15min;再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌25min;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌30min,即制得环保型耐候性防水外墙涂料;最后将环保型耐候性防水外墙涂料进入沙磨机研磨两遍,过滤,出料装桶。
三、本实施例的有益效果(见表5)
表5:丙烯酸外墙涂料与耐候性防水外墙涂料的性能对比
Claims (2)
1.一种环保型耐候性防水外墙涂料,其特征在于,按质量百分比含量由组分GHS98A硅丙乳液为45-55%,金红石钛白粉R-930为8-12%,醇脂十二为3-6%,超细方解石粉为3-7%,超细硅灰石粉为3-7%,超细二氧化硅粉为3-7%,超细云母粉为3—7%,重质碳酸钙为2-6%,GH5050分散剂为0.4-0.8%,流平剂2为0.1—0.3%,增稠剂102为0.5-1%,防腐剂981为0.1-0.5%,消泡剂202为0.1-0.3%,水为5-12%组成。
2.一种如权利要求1所述的环保型耐候性防水外墙涂料的制备方法,其特征在于,制备步骤是:先将水加入搅拌罐中,启动搅拌器,分别加入金红石钛白粉R-930、超细方解石粉、超细硅灰石粉搅拌18-21min,然后加入GHS98A硅丙乳液和醇脂十二搅拌15-18min;再分别加入超细二氧化硅粉、超细云母粉、重质碳酸钙搅拌23-26min;再分别加入GH5050分散剂、流平剂2、增稠剂102、防腐剂981、消泡剂202搅拌29-32min,即制得环保型耐候性防水外墙涂料;最后将制得的环保型耐候性防水外墙涂料进入砂磨机研磨两遍,过滤,出料装桶。