CN102584865A - 具有可调和白光发射的锌配合物制备方法 - Google Patents
具有可调和白光发射的锌配合物制备方法 Download PDFInfo
- Publication number
- CN102584865A CN102584865A CN201210020591XA CN201210020591A CN102584865A CN 102584865 A CN102584865 A CN 102584865A CN 201210020591X A CN201210020591X A CN 201210020591XA CN 201210020591 A CN201210020591 A CN 201210020591A CN 102584865 A CN102584865 A CN 102584865A
- Authority
- CN
- China
- Prior art keywords
- light emitting
- white light
- preparation
- zinc
- acid amides
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种具有可调和白光发射的锌配合物制备方法是以硝酸锌或氯化锌、对苯二甲酸和酰胺(N,N′-二甲基甲酰胺)按1:1:1比例原料,以水和DMF的混合溶液作为试剂,通过水热反应制得的锌配合物。本发明的具有可调和白光发射的锌配合物制备方法,制造成本低、工艺简单,它通过使用过渡金属与酰胺配合的方法,得到一种新型的具有发光可调和白光发射性质的过渡族元素Zn有机配合物材料,这种材料具有发光调节便利、白光效果好、重复性强,性能稳定等特点。
Description
技术领域
本发明涉及一种具有可调和白光发射的锌配合物制备方法。
背景技术
目前市场上使用的LED灯多为RGB LED和白光LED,两者都能达到白光的效果,只不过一个是以红绿蓝三色混光而成,一个则是直接以白光(荧光粉)呈现。在应用上RGB比白光LED要多元,要用某一波段的灯光时,RGB的混色可以随心所欲,效果也比白光LED要强。但如果从照明上来看白光LED就有明显的优势,因为用在照明方面主要还是看白光的光通量、寿命及纯色,所以RGB目前主要还是用在装饰灯方面。
锌配合物晶体可调节激发波长实现从蓝光到黄光的发光可调,当蓝光和黄光强度相当时可实现白光发射,锌配合物晶体材料作为白光发射介质,实现了白光发射的高效率同时,又保证了白光发射的高质量。这种新材料的应用克服了传统固体白光产生在发光效率和发光质量上很难同时兼顾的技术瓶颈,既达到了RGB灯、蓝光LED配合黄色荧光粉以及紫外LED配合RGB荧光粉在照明上效果,又解决了衰减与紫外线对人体影响。
发明内容
本发明的目的就是提供一种制造成本低、工艺简单的具有可调和白光发射的锌配合物制备方法。
本发明的具有可调和白光发射的锌配合物制备方法是以硝酸锌或氯化锌、对苯二甲酸和酰胺(N,N′-二甲基甲酰胺)按1:1: 1比例原料,以水和DMF的混合溶液作为试剂,通过水热反应制得的锌配合物。
本发明的具有可调和白光发射的锌配合物制备方法,制造成本低、工艺简单,它通过使用过渡金属与酰胺配合的方法,得到一种新型的具有发光可调和白光发射性质的过渡族元素Zn有机配合物材料,这种材料具有发光调节便利、白光效果好、重复性强,性能稳定等特点。
附图说明
图1为本发明的锌配合物的发射光谱图;
图2为本发明的锌配合物的紫外-可见光谱图。
具体实施方式
实施例1:
取0.2mmol氯化锌,0.2mmol 对苯二甲酸,0.2mmol酰胺(N4,N4'-di(pyridin-4-yl)biphenyl-4,4'-dicarboxamide)放入聚四氟乙烯反应釜中,再加5ml水和1ml DMF(N,N′-二甲基甲酰胺),加热到115-120℃,恒温65-70小时,自然风干得白色晶体。
实施例2:
取0.15mmol 硝酸锌,放入聚四氟乙烯反应釜中,加入0.15mmol对苯二甲酸后,再加入0.15mmol酰胺(N4,N4'-di(pyridin-4-yl)biphenyl-4,4'-dicarboxamide),加入4ml水和2ml DMF(N,N′-二甲基甲酰胺)作溶剂,放入马沸炉中加入到110-115℃,恒温65-70小时,得到白色晶体。
Claims (3)
1.一种具有可调和白光发射的锌配合物制备方法,其特征在于:它是以硝酸锌或氯化锌、对苯二甲酸和酰胺按1:1: 1比例原料,以水和DMF的混合溶液作为试剂,通过水热反应制得锌配合物。
2.如权利要求1所述的具有可调和白光发射的锌配合物制备方法,其特征在于:取0.2mmol氯化锌,0.2mmol 对苯二甲酸,0.2mmol酰胺放入聚四氟乙烯反应釜中,再加5ml水和1ml N,N′-二甲基甲酰胺 ,加热到115-120℃,恒温65-70小时,自然风干得白色晶体。
3.如权利要求1所述的具有可调和白光发射的锌配合物制备方法,其特征在于:取0.15mmol 硝酸锌,放入聚四氟乙烯反应釜中,加入0.15mmol对苯二甲酸后,再加入0.15mmol酰胺,加入4ml水和2ml N,N′-二甲基甲酰胺作溶剂,放入马沸炉中加入到110-115℃,恒温65-70小时,得到白色晶体。