CN102560311A - 一种镀锡线热镀过程中使用的合金 - Google Patents

一种镀锡线热镀过程中使用的合金 Download PDF

Info

Publication number
CN102560311A
CN102560311A CN2012100699002A CN201210069900A CN102560311A CN 102560311 A CN102560311 A CN 102560311A CN 2012100699002 A CN2012100699002 A CN 2012100699002A CN 201210069900 A CN201210069900 A CN 201210069900A CN 102560311 A CN102560311 A CN 102560311A
Authority
CN
China
Prior art keywords
tin
alloy
tinned wire
following
cerium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100699002A
Other languages
English (en)
Inventor
张书红
谭航
易晓勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
YINGTAN ZHONGXINCHENG COPPER CO Ltd
Original Assignee
YINGTAN ZHONGXINCHENG COPPER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by YINGTAN ZHONGXINCHENG COPPER CO Ltd filed Critical YINGTAN ZHONGXINCHENG COPPER CO Ltd
Priority to CN2012100699002A priority Critical patent/CN102560311A/zh
Publication of CN102560311A publication Critical patent/CN102560311A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种镀锡线热镀过程中使用的合金，由锡，锑，铋，铈，磷锡合金等原料配置而成，本发明生产出的合金具有抗氧化性和耐高温等特点。

Description

一种镀锡线热镀过程中使用的合金
技术领域
本发明涉及一种合金，尤其涉及一种镀锡线热镀过程中使用的合金。
背景技术
现有镀锡线热镀过程中大都使用纯金属锡，这种镀锡线不耐高温，容易被氧化，表面发黑。
发明内容
本发明的目的就是针对上述情况提供一种镀锡线热镀过程中使用的合金，铜线表面镀有这层合金能够耐高温并且具有抗氧性能不容易变色。本发明的目的可通过以下方案来实现：一种镀锡线热镀过程中使用的合金，由下列用量为重量份的原料配置而成：锡800-1200，锑10-30，铋5-10，铈1-2，磷锡合金13-19。上述原料用量优先配比如下：锡900-1100，锑15-25，铋7-9，铈1.2-1.8，磷锡合金15-18。上述原料用量最佳配比如下：锡1000，锑20，铋8，铈1.5，磷锡合金16。所述磷锡合金由广东潮州华鸿锡业有限公司生产。本发明的生产工艺如下：将上述配置好的原料放入熔炉中熔化即可。本发明生产出的合金具有如下有益效果：
（1）由于含有磷锡合金，从而可以增加其抗氧化性能；
（2）由于含有铋、锑和铈，从而可以保持线材上锡均衡、光亮；
（3）由于含有金属锑，从而可以耐高温，熔化温度达到500℃。

Claims (3)

1.一种镀锡线热镀过程中使用的合金，其特征是由下列用量为重量份的原料配置而成：锡800-1200，锑10-30，铋5-10，铈1-2，磷锡合金13-19，本发明的生产工艺如下：将上述配置好的原料放入熔炉中熔化即可。
2.根据权利要求1所述的合金，其特征是上述原料用量配比如下：锡900-1100，锑15-25，铋7-9，铈1.2-1.8，磷锡合金15-18。
3.根据权利要求1所述的合金，其特征是上述原料用量配比如下：锡1000，锑20，铋8，铈1.5，磷锡合金16。
CN2012100699002A 2012-03-16 2012-03-16 一种镀锡线热镀过程中使用的合金 Pending CN102560311A (zh)