CN102560201A - 换热器翅片用耐蚀铝合金材料及其制备方法 - Google Patents

换热器翅片用耐蚀铝合金材料及其制备方法 Download PDF

Info

Publication number
CN102560201A
CN102560201A CN2012100139443A CN201210013944A CN102560201A CN 102560201 A CN102560201 A CN 102560201A CN 2012100139443 A CN2012100139443 A CN 2012100139443A CN 201210013944 A CN201210013944 A CN 201210013944A CN 102560201 A CN102560201 A CN 102560201A
Authority
CN
China
Prior art keywords
aluminum alloy
heat exchanger
fin
alloy material
percent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012100139443A
Other languages
English (en)
Inventor
管保清
吴晓君
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANYUN ALUMINUM CO Ltd
Original Assignee
GUANYUN ALUMINUM CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANYUN ALUMINUM CO Ltd filed Critical GUANYUN ALUMINUM CO Ltd
Priority to CN2012100139443A priority Critical patent/CN102560201A/zh
Publication of CN102560201A publication Critical patent/CN102560201A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种换热器翅片用耐蚀铝合金材料及其制备方法,所述铝合金材料由下列重量百分比材料构成:Si0.60,Fe0.70,Cu0.10,Mn1.0~1.50,Zn0.80~1.20,Zr0.12,余量为Al。本发明加入0.8-1.2%的锌,使翅片作为自耗阳极以提高其它热交换器部件的耐蚀性能。加入0.12%的锆提高了翅片的焊后强度。

Description

换热器翅片用耐蚀铝合金材料及其制备方法
技术领域
本发明涉及一种换热器翅片用耐蚀铝合金材料及其制备方法。
背景技术
铝合金是工业中应用最广泛的一类有色金属结构材料,在航空、航天、汽车、机械制造、船舶及化学工业中已大量应用。随着近年来科学技术以及工业经济的飞速发展,对铝合金结构件的需求日益增多,使铝合金的研究也随之深入。铝合金的广泛应用促进了铝合金技术的发展。 
纯铝的密度小(ρ=2.7g/cm3),大约是铁的 1/3,熔点低(660℃),铝是面心立方结构,故具有很高的塑性(δ:32~40%,ψ:70~90%),易于加工,可制成各种型材、板材。抗腐蚀性能好;但是纯铝的强度很低,退火状态 σb 值约为8kgf/mm2,故不宜作结构材料。
通过长期的生产实践和科学实验,人们逐渐以加入合金元素及运用热处理等方法来强化铝,这就得到了一系列的铝合金。 添加一定元素形成的合金在保持纯铝质轻等优点的同时还能具有较高的强度,σb 值分别可达 24~60kgf/mm2。这样使得其“比强度”(强度与比重的比值 σb/ρ)胜过很多合金钢,成为理想的结构材料,广泛用于机械制造、运输机械、动力机械及航空工业等方面,飞机的机身、蒙皮、压气机等常以铝合金制造,以减轻自重。采用铝合金代替钢板材料的焊接,结构重量可减轻50%以上。 
铝合金密度低,但强度比较高,接近或超过优质钢,塑性好,可加工成各种型材,具有优良的导电性、导热性和抗蚀性,工业上广泛使用,使用量仅次于钢。 
汽车的轻量化,就是在保证汽车的强度和安全性能的前提下,尽可能地降低汽车的整备质量,从而提高汽车的动力性,减少燃料消耗,降低排气污染。实验证明,若汽车整车重量降低10%,燃油效率可提高6%-8%;汽车整备质量每减少100公斤,百公里油耗可降低0.3-0.6升;汽车重量降低1%,油耗可降低0.7%。当前,由于环保和节能的需要,汽车的轻量化已经成为世界汽车发展的潮流。
目前汽车轻量化主要内容包括材料轻量化、设计轻量化、结构轻量化相结合的方式。
随着汽车轻量化的发展,在材料轻量化方面,以铝代铜已成超势。
随着汽车、化工、空分行业的发展,对换热器用翅片铝合金材料的要求越来越高。为了提高翅片料的焊后强度和提高换热器的使用寿命,需要研发出耐蚀、高强度的翅片用材料。
发明内容
本发明需要解决的技术问题就在于克服现有技术的缺陷,提供一种换热器翅片用耐蚀铝合金材料及其制备方法,它加入0.8-1.2%的锌,使翅片作为自耗阳极以提高其它热交换器部件的耐蚀性能。加入0.12%的锆提高了翅片的焊后强度。
为解决上述问题,本发明采用如下技术方案:
本发明提供了一种换热器翅片用耐蚀铝合金材料,所述铝合金材料由下列重量百分比材料构成:Si 0.60,Fe 0.70,Cu 0.10,Mn 1.0~1.50,Zn 0.80~1.20,Zr 0.12,余量为Al。
本发明同时提供了一种所述的换热器翅片用耐蚀铝合金材料的制备方法:将铝锭熔为铝水,分别按材料的重量百分比加入Si、Fe、Cu 、Mn,最后加入Zn和Zr,使材料充分熔融,形成铝合金材料;将铝合金材料轧制成板材,再加热后热轧成换热器翅片用耐蚀铝合金材料。
本发明的优点有:
1、加入0.8-1.2%的锌,使翅片作为自耗阳极以提高其它热交换器部件的耐蚀性能。
2、加入0.12%的锆提高了翅片的焊后强度。
具体实施方式
实施例1
将铝锭熔为铝水,分别按下表材料的重量百分比加入Si、Fe、Cu 、Mn,最后加入Zn和Zr,使材料充分熔融,形成铝合金材料;将铝合金材料轧制成板材,再加热后热轧成换热器翅片用耐蚀铝合金材料。
                                                 单位:%
材料 Si Fe Cu Mn Zn Zr Al
翅片料 0.60 0.70 0.10 1.0 1.20 0.12 余量
实施例2
单位:%
材料 Si Fe Cu Mn Zn Zr Al
翅片料 0.60 0.70 0.10 1.50 0.80 0.12 余量
实施例3
单位:%
材料 Si Fe Cu Mn Zn Zr Al
翅片料 0.60 0.70 0.10 1.20 1.0 0.12 余量
最后应说明的是:显然,上述实施例仅仅是为清楚地说明本发明所作的举例,而并非对实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引申出的显而易见的变化或变动仍处于本发明的保护范围之中。

Claims (2)

1.一种换热器翅片用耐蚀铝合金材料,其特征在于:所述铝合金材料由下列重量百分比材料构成:Si 0.60,Fe 0.70,Cu 0.10,Mn 1.0~1.50,Zn 0.80~1.20,Zr 0.12,余量为Al。
2.如权利要求1所述的换热器翅片用耐蚀铝合金材料的制备方法,其特征在于:将铝锭熔为铝水,分别按材料的重量百分比加入Si、Fe、Cu 、Mn,最后加入Zn和Zr,使材料充分熔融,形成铝合金材料;将铝合金材料轧制成板材,再加热后热轧成换热器翅片用耐蚀铝合金材料。
CN2012100139443A 2012-01-17 2012-01-17 换热器翅片用耐蚀铝合金材料及其制备方法 Pending CN102560201A (zh)