CN102555120A - 一种低密度有机硅密封剂的成型工艺 - Google Patents
一种低密度有机硅密封剂的成型工艺 Download PDFInfo
- Publication number
- CN102555120A CN102555120A CN2010106038150A CN201010603815A CN102555120A CN 102555120 A CN102555120 A CN 102555120A CN 2010106038150 A CN2010106038150 A CN 2010106038150A CN 201010603815 A CN201010603815 A CN 201010603815A CN 102555120 A CN102555120 A CN 102555120A
- Authority
- CN
- China
- Prior art keywords
- organic silicon
- vulcanization
- under
- low
- silicon sealant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明的目的在于提供一种低密度有机硅密封剂的成型工艺，其特征在于：将低密度有机硅密封剂的双组份A和B按质量比为80~120：8~12的比例混合，搅拌均匀，将混合后的材料在40~120mbar的条件下抽真空30~60min；一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，在真空度为-0.4~-0.1MPa条件下保持1~5min，然后升温至140~160℃的硫化温度，在0.3~5MPa的硫化压力下硫化10~30min；二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内进行硫化，硫化条件：硫化温度195~210℃，硫化时间1~2h。
Description
技术领域
本发明涉及有机硅密封剂的成型工艺，特别提供一种低密度有机硅密封剂的成型工艺。
背景技术
密封剂(V-695)是一种新型的低密度有机硅密封剂，该低密度有机硅密封剂为双组分加成型有机硅密封剂，密封剂硫化过程中在铂催化剂的作用下，有机硅的不饱和键与硫化剂的硅氢键发生加成反应，形成交联网状结构。首先，由于配方有铂络合物，易引起机硅密封剂中毒失效，所以应避免与含硫化合物、含氮化合物、含磷化合物等物质接触，否则不易成型。第二，双组分有机硅密封剂按比例混合后会产生大量气泡，气泡若不去除，易使成型制品气孔较多，无法满足硫化橡胶的各项性能要求。
发明内容
本发明的目的在于提供一种新型低密度有机硅密封剂(V-695)的成型工艺，该工艺克服了加成型有机硅密封剂硫化过程中易造成密封剂中毒的缺点，提高了成型制品的外观质量及尺寸精度。
本发明提供的低密度有机硅密封剂的成型工艺，其特征在于：
将低密度有机硅密封剂的双组份A和B按质量比为80~120：8~12的比例混合，搅拌均匀，将混合后的材料在40~120mbar的条件下抽真空30~60min；
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，在真空度为-0.4~ -0.1MPa条件下保持1~5min，然后升温至140~160℃的硫化温度，在0.3~5MPa的硫化压力下硫化10~30min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内进行硫化，硫化条件：硫化温度195~210℃，硫化时间1~2h。
本发明还提供了所述低密度有机硅密封剂成型工艺的最佳工艺，其特征在于：将低密度有机硅密封剂的双组份A和B按质量比为100：10的比例混合，搅拌均匀，将混合后的材料在110mbar的条件下抽真空30min；
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，在真空度为-0.1MPa条件下保持1min，然后升温至150℃的硫化温度，在0.5MPa的硫化压力下硫化10min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内进行硫化，硫化条件：硫化温度200℃，硫化时间2h。
本发明提供的低密度有机硅密封剂的成型工艺，能够保证硫化后的橡胶制品无气泡、无边缘无中毒现象，也能保证橡胶制品的外观质量及尺寸精度。
具体实施方式
实施例1
将低密度有机硅密封剂的双组份A和B按质量比为100：10的比例混合，用平板刮刀搅拌30min，将混合后的材料在80mbar的条件下抽真空50min。
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，调整好真空平板硫化机的工艺参数，在真空度为-0.4MPa条件下保持2min，然后升温至硫化温度：150℃士2℃，在3MPa的硫化压力下硫化20min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内，硫化条件：室温升至204℃，在204℃士2℃保温1.5h。
所得成型后的橡胶片无气泡、无边缘中毒现象，且外观质量优，尺寸精准，邵尔A硬度在57。
用洁净的棉布或毛刷浸润丙酮擦拭待粘接的零件表面，在空气中放置10min备用。用毛刷浸润无水乙醇擦拭橡胶的粘接面，然后用砂纸打磨橡胶的粘接面将光洁面去除即可，再用毛刷浸润无水乙醇擦拭橡胶的打磨面，在空气中放置至少30min后备用。
将硅橡胶胶粘剂按8：1的质量比混合，用平板刮刀仔细混合均匀备用，配制好的硅橡胶胶粘剂在2h内用完。
在金属零件和橡胶片的被粘接面均匀地涂一薄层硅橡胶胶粘剂，不允许有漏涂之处，涂后静置10min，然后立即叠合，加压、定位、清除挤出的余胶。在100℃士2℃固化3h，固化压力为0.3MPa。
实施例2
将低密度有机硅密封剂的双组份A和B按质量比为80：10的比例混合，用平板刮刀搅拌30min，将混合后的材料在50mbar的条件下抽真空30min。
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，调整好真空平板硫化机的工艺参数，在真空度为-0.2MPa条件下保持3min，然后升温至硫化温度：140℃士2℃，在1MPa的硫化压力下硫化15min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内，硫化条件：室温升至196℃，在196℃士2℃保温2h。
所得成型后的橡胶制品无气泡、无边缘中毒现象，且外观质量优，尺寸精准，邵尔A硬度在58。
实施例3
将低密度有机硅密封剂的双组份A和B按质量比为120：9的比例混合，用平板刮刀搅拌30min，将混合后的材料在120mbar的条件下抽真空40min。
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，调整好真空平板硫化机的工艺参数，在真空度为-0.3MPa条件下保持5min，然后升温至硫化温度：160℃士2℃，在0.5MPa的硫化压力下硫化10min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内，硫化条件：室温升至210℃，在210℃士2℃保温1h。
所得成型后的橡胶制品无气泡、无边缘中毒现象，且外观质量优，尺寸精准，邵尔A硬度在55。
实施例4
将低密度有机硅密封剂的双组份A和B按质量比为100：10的比例混合，用平板刮刀搅拌30min，将混合后的材料在110mbar的条件下抽真空30min。
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，调整好真空平板硫化机的工艺参数，在真空度为-0.1MPa条件下保持1min，然后升温至硫化温度：150℃士2℃，在0.5MPa的硫化压力下硫化10min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内，硫化条件：室温升至200℃，在200℃士2℃保温2h。
所得成型后的橡胶制品无气泡、无边缘中毒现象，且外观质量优，尺寸精准，邵尔A硬度在56。
Claims (2)
1. 一种低密度有机硅密封剂的成型工艺，其特征在于：
将低密度有机硅密封剂的双组份A和B按质量比为80~120：8~12的比例混合，搅拌均匀，将混合后的材料在40~120mbar的条件下抽真空30~60min；
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，在真空度为-0.4~ -0.1MPa条件下保持1~5min，然后升温至140~160℃的硫化温度，在0.3~5MPa的硫化压力下硫化10~30min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内进行硫化，硫化条件：硫化温度195~210℃，硫化时间1~2h。
2.按照权利要求1所述低密度有机硅密封剂的成型工艺，其特征在于：将低密度有机硅密封剂的双组份A和B按质量比为100：10的比例混
合，搅拌均匀，将混合后的材料在110mbar的条件下抽真空30min；
一段硫化工艺：采用真空平板硫化机进行一段硫化，将混合料置于冷模具中，模具放在平板硫化机的加热台上，在真空度为-0.1MPa条件下保持1min，然后升温至150℃的硫化温度，在0.5MPa的硫化压力下硫化10min；
二段硫化工艺：采用电热鼓风烘箱进行二段硫化，将一段硫化完的制品放入烘箱内进行硫化，硫化条件：硫化温度200℃，硫化时间2h。