CN102534442A - 铝铸件热处理工艺 - Google Patents

铝铸件热处理工艺 Download PDF

Info

Publication number
CN102534442A
CN102534442A CN2010105567640A CN201010556764A CN102534442A CN 102534442 A CN102534442 A CN 102534442A CN 2010105567640 A CN2010105567640 A CN 2010105567640A CN 201010556764 A CN201010556764 A CN 201010556764A CN 102534442 A CN102534442 A CN 102534442A
Authority
CN
China
Prior art keywords
temperature
quenching
furnace
aluminum
treatment process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2010105567640A
Other languages
English (en)
Inventor
黄霞
黄凌朱
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG XINJINGHUA ENTERPRISE MANAGEMENT SERVICE CO Ltd
Original Assignee
NANTONG XINJINGHUA ENTERPRISE MANAGEMENT SERVICE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG XINJINGHUA ENTERPRISE MANAGEMENT SERVICE CO Ltd filed Critical NANTONG XINJINGHUA ENTERPRISE MANAGEMENT SERVICE CO Ltd
Priority to CN2010105567640A priority Critical patent/CN102534442A/zh
Publication of CN102534442A publication Critical patent/CN102534442A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种铝铸件热处理工艺，包括以下步骤：将铝铸件放于不高于350℃炉温的淬火炉中，然后放于不超过100℃炉温的时效炉中，将铝铸件均匀堆放在淬火炉框内，且铝铸件之间保持一定的间隙，提高淬火炉和时效炉的温度，升温过程中检查炉温显示，发现异常立即断电检查，淬火炉保温时间达到后，打开炉门，在15-20秒内将铸件淬入水中，完成淬火和时效后，留一件铸件进行硬度检查。本发明具有操作方便、保证热处理质量，提高铸件的各种性能，有利于各种冷、热加工的优点。

Description

铝铸件热处理工艺
技术领域：
本发明涉及一种铝铸件热处理工艺。
背景技术：
金属热处理是机械制造中的重要工艺之一，与其它加工工艺相比，热处理一般不改变工件的形状和整体的化学成分，而是通过改变工件内部的显微组织，或改变工件表面的化学成分，赋予或改善工件的使用性能，热处理工艺一般包括加热、保温、冷却三个过程，有时只有加热和冷却两个过程，选择和控制温度，是保证热处理质量的主要问题，而传统的热处理工艺对温度的控制不够精确，不能保证热处理的质量，无法提高铸件的各种性能，不利于各种冷、热加工。
发明内容：
本发明的目的是为了克服以上的不足，提供一种操作方便、保证热处理质量，提高铸件的各种性能，有利于各种冷、热加工的铝铸件热处理工艺。
本发明的目的通过以下技术方案来实现：一种铝铸件热处理工艺，包括以下步骤：
A、将铝铸件放于不高于350℃炉温的淬火炉中，然后放于不超过100℃炉温的时效炉中；
B、将铝铸件均匀堆放在淬火炉框内，且铝铸件之间保持一定的间隙；
C、提高淬火炉和时效炉的温度，升温过程中检查炉温显示，发现异常立即断电检查；
D、淬火炉保温时间达到后，打开炉门，在15-20秒内将铸件淬入水中；
E、完成淬火和时效后，留一件铸件进行硬度检查。
本发明与现有技术相比具有以下优点：
1、将铝铸件均匀堆放在淬火炉框内，且铝铸件之间保持一定的间隙，防止铸件变形和加热不均匀；
2、提高淬火炉和时效炉的温度，升温过程中检查炉温显示，发现异常立即断电检查，保护铸件，保证热处理质量；
3、淬火炉保温时间达到后，打开炉门，在15-20秒内将铸件淬入水中，立即冷却，提高铸件的各种性能；
4、完成淬火和时效后，留一件铸件进行硬度检查，以免铸件的硬度达不到要求，浪费材料。
具体实施方式：
为了加深对本发明的理解，下面将结合实施例对本发明作进一步详述，该实施例仅用于解释本发明，并不构成对本发明保护范围的限定。
本发明铝铸件热处理工艺的一种具体实施方式，包括以下步骤：
A、将铝铸件放于不高于350℃炉温的淬火炉中，然后放于不超过100℃炉温的时效炉中；
B、将铝铸件均匀堆放在淬火炉框内，且铝铸件之间保持一定的间隙，防止铸件变形和加热不均匀；
C、提高淬火炉和时效炉的温度，升温过程中检查炉温显示，发现异常立即断电检查，保护铸件，保证热处理质量；
D、淬火炉保温时间达到后，打开炉门，在15-20秒内将铸件淬入水中，立即冷却，提高铸件的各种性能；
E、完成淬火和时效后，留一件铸件进行硬度检查，以免铸件的硬度达不到要求，浪费材料。
本发明经过加热、保温、冷却三个过程，具有操作方便、保证热处理质量，提高铸件的各种性能，有利于各种冷、热加工的优点。

Claims (1)

1.一种铝铸件热处理工艺，其特征在于：包括以下步骤：
A、将铝铸件放于不高于350℃炉温的淬火炉中，然后放于不超过100℃炉温的时效炉中；
B、将铝铸件均匀堆放在淬火炉框内，且铝铸件之间保持一定的间隙；
C、提高淬火炉和时效炉的温度，升温过程中检查炉温显示，发现异常立即断电检查；
D、淬火炉保温时间达到后，打开炉门，在15-20秒内将铸件淬入水中；
E、完成淬火和时效后，留一件铸件进行硬度检查。
CN2010105567640A 2010-11-23 2010-11-23 铝铸件热处理工艺 Pending CN102534442A (zh)